CN105543656A - Sendesi wire bundling machine - Google Patents
Sendesi wire bundling machine Download PDFInfo
- Publication number
- CN105543656A CN105543656A CN201510983454.XA CN201510983454A CN105543656A CN 105543656 A CN105543656 A CN 105543656A CN 201510983454 A CN201510983454 A CN 201510983454A CN 105543656 A CN105543656 A CN 105543656A
- Authority
- CN
- China
- Prior art keywords
- speed
- alloy material
- hours
- room temperature
- min again
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a Sendesi wire bundling machine. The Sendesi wire bundling machine comprises a metal body produced by a thermally treated alloy material; the alloy material comprises the following components: 1-2% of As, 0.3% of P, 0.7% of Si, 0.6% of Li, 1.2% of Mn, 0.7% of Pt, and the balance of Fe and inevitable impurities; and the alloy material is thermally treated through the following steps: 1) a temperature of 600 DEG C is raised at a speed of 15 DEG C/min, and is kept by 3.5 hours; 2) the room temperature is reduced to at a speed of 25 DEG C/min; 3) a temperature of 700 DEG C is raised at a speed of 20 DEG C/min, and is kept by 3 hours; and 4) the room temperature is reduced to at a speed of 25 DEG C/min. The Sendesi wire bundling machine is excellent in performance of the metal body and long in service life.
Description
Technical field
The present invention relates to Sen Desi wire bander.
Background technology
The work under bad environment of Sen Desi wire bander, to its metal master performance requriements higher.
Summary of the invention
The object of the present invention is to provide a kind of Sen Desi wire bander, its metal master is made by through heat treated alloy material, and metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
For achieving the above object, technical scheme of the present invention is a kind of Sen Desi wire bander of design, and comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1~2%,
P:0.3%,
Si:0.7%,
Li:0.6%,
Mn:1.2%,
Pt:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 600 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 700 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Preferably, Sen Desi wire bander, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%,
P:0.3%,
Si:0.7%,
Li:0.6%,
Mn:1.2%,
Pt:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 600 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 700 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Preferably, Sen Desi wire bander, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%,
P:0.3%,
Si:0.7%,
Li:0.6%,
Mn:1.2%,
Pt:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 600 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 700 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Advantage of the present invention and beneficial effect are: provide a kind of Sen Desi wire bander, its metal master is made by through heat treated alloy material, metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of Sen Desi wire bander, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1~2%,
P:0.3%,
Si:0.7%,
Li:0.6%,
Mn:1.2%,
Pt:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 600 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 700 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Embodiment 2
Sen Desi wire bander, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%,
P:0.3%,
Si:0.7%,
Li:0.6%,
Mn:1.2%,
Pt:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 600 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 700 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Embodiment 3
Sen Desi wire bander, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%,
P:0.3%,
Si:0.7%,
Li:0.6%,
Mn:1.2%,
Pt:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 600 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 700 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. Sen Desi wire bander, is characterized in that, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1~2%,
P:0.3%,
Si:0.7%,
Li:0.6%,
Mn:1.2%,
Pt:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 600 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 700 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
2. Sen Desi wire bander according to claim 1, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%,
P:0.3%,
Si:0.7%,
Li:0.6%,
Mn:1.2%,
Pt:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 600 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 700 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
3. Sen Desi wire bander according to claim 1, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%,
P:0.3%,
Si:0.7%,
Li:0.6%,
Mn:1.2%,
Pt:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 600 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 700 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.