CN105369059A - High-pressure nozzle for roadway - Google Patents
High-pressure nozzle for roadway Download PDFInfo
- Publication number
- CN105369059A CN105369059A CN201510982307.0A CN201510982307A CN105369059A CN 105369059 A CN105369059 A CN 105369059A CN 201510982307 A CN201510982307 A CN 201510982307A CN 105369059 A CN105369059 A CN 105369059A
- Authority
- CN
- China
- Prior art keywords
- speed
- alloy material
- cooled
- room temperature
- min again
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-pressure nozzle for a roadway. The high-pressure nozzle comprises a metal body made of an alloy material subjected to thermal treatment, wherein the alloy material comprises components as follows: 1%-2% of Si, 0.3% of P, 0.7% of Te, 0.8% of Ca, 1.2% of Ge, 0.4% of W and the balance of Cu and inevitable impurities. The alloy material is subjected to thermal treatment in steps as follows: 1), the alloy material is heated to 680 DEG C at the speed of 25 DEG C/min and kept at the temperature for 3.5 h; 2), the alloy material is cooled to the room temperature at the speed of 35 DEG C/min; 3), the alloy material is heated to 780 DEG C at the speed of 20 DEG C/min and kept at the temperature for 2.5 h; 4), the alloy material is cooled to the room temperature at the speed of 15 DEG C/min. The performance of the metal body of the high-pressure nozzle for the roadway is good, and the service life is long.
Description
Technical field
The present invention relates to tunnel high pressure spray nozzle.
Background technology
The work under bad environment of tunnel high pressure spray nozzle, to its metal master performance requriements higher.
Summary of the invention
The object of the present invention is to provide a kind of tunnel high pressure spray nozzle, its metal master is made by through heat treated alloy material, and metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
For achieving the above object, technical scheme of the present invention is a kind of tunnel of design high pressure spray nozzle, and comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1~2%,
P:0.3%,
Te:0.7%,
Ca:0.8%,
Ge:1.2%,
W:0.4%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 35 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 20 DEG C/min again, be incubated 2.5 hours;
4) room temperature is cooled to the speed of 15 DEG C/min again.
Preferably, tunnel high pressure spray nozzle, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1%,
P:0.3%,
Te:0.7%,
Ca:0.8%,
Ge:1.2%,
W:0.4%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 35 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 20 DEG C/min again, be incubated 2.5 hours;
4) room temperature is cooled to the speed of 15 DEG C/min again.
Preferably, tunnel high pressure spray nozzle, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:2%,
P:0.3%,
Te:0.7%,
Ca:0.8%,
Ge:1.2%,
W:0.4%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 35 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 20 DEG C/min again, be incubated 2.5 hours;
4) room temperature is cooled to the speed of 15 DEG C/min again.
Advantage of the present invention and beneficial effect are: provide a kind of tunnel high pressure spray nozzle, its metal master is made by through heat treated alloy material, metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of tunnel high pressure spray nozzle, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1~2%,
P:0.3%,
Te:0.7%,
Ca:0.8%,
Ge:1.2%,
W:0.4%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 35 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 20 DEG C/min again, be incubated 2.5 hours;
4) room temperature is cooled to the speed of 15 DEG C/min again.
Embodiment 2
Tunnel high pressure spray nozzle, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1%,
P:0.3%,
Te:0.7%,
Ca:0.8%,
Ge:1.2%,
W:0.4%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 35 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 20 DEG C/min again, be incubated 2.5 hours;
4) room temperature is cooled to the speed of 15 DEG C/min again.
Embodiment 3
Tunnel high pressure spray nozzle, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:2%,
P:0.3%,
Te:0.7%,
Ca:0.8%,
Ge:1.2%,
W:0.4%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 35 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 20 DEG C/min again, be incubated 2.5 hours;
4) room temperature is cooled to the speed of 15 DEG C/min again.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. tunnel high pressure spray nozzle, is characterized in that, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1~2%,
P:0.3%,
Te:0.7%,
Ca:0.8%,
Ge:1.2%,
W:0.4%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 35 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 20 DEG C/min again, be incubated 2.5 hours;
4) room temperature is cooled to the speed of 15 DEG C/min again.
2. tunnel according to claim 1 high pressure spray nozzle, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1%,
P:0.3%,
Te:0.7%,
Ca:0.8%,
Ge:1.2%,
W:0.4%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 35 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 20 DEG C/min again, be incubated 2.5 hours;
4) room temperature is cooled to the speed of 15 DEG C/min again.
3. tunnel according to claim 1 high pressure spray nozzle, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:2%,
P:0.3%,
Te:0.7%,
Ca:0.8%,
Ge:1.2%,
W:0.4%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 35 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 20 DEG C/min again, be incubated 2.5 hours;
4) room temperature is cooled to the speed of 15 DEG C/min again.