CN105504979A - 一种水性冰爽油墨 - Google Patents
一种水性冰爽油墨 Download PDFInfo
- Publication number
- CN105504979A CN105504979A CN201410479741.2A CN201410479741A CN105504979A CN 105504979 A CN105504979 A CN 105504979A CN 201410479741 A CN201410479741 A CN 201410479741A CN 105504979 A CN105504979 A CN 105504979A
- Authority
- CN
- China
- Prior art keywords
- change material
- water
- phase change
- aqueous
- lauryl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水性冰爽油墨,当人体触碰由这种油墨印刷的产品时,能够产生冰凉感。其原料由如下组分组成,以重量百分含量计:复合相变材料20~50%,丙烯酸乳液28~36%,色料2~5%,水性防腐剂0.1~0.2%,水性增稠剂0.2~0.6%,水性润湿剂0.1~0.3%,水性分散剂0.3~0.6%,水性消泡剂0.1~0.5%,水性防霉剂0.1~0.3%,水性流平剂0.2~0.3%,清水余量。所述复合相变材料为二元有机相变材料/高岭土复合相变材料,或二元有机相变材料/膨胀石墨复合相变材料。所述二元有机相变材料为石蜡、十六醇/十二醇混合物,癸酸、十六醇/十二醇混合物,月桂酸、十六醇/十二醇混合物,肉豆寇酸、十六醇/十二醇混合物中的任意一种。
Description
技术领域
本发明涉及油墨领域,特别是涉及一种水性冰爽油墨。
背景技术
冰爽油墨是一种特种油墨,当人体触摸使用该水性冰爽油墨印刷的产品时,会有一种凉爽的感觉,原理是油墨中含有相变材料,人体接触该油墨时温度达到相变点,相变材料从固相变为液相,从而吸收热量,使人体感到清凉感。目前大多数一元有机相变材料的相变温度和相变焓热已不能充分满足实际应用要求,为有效拓展单一有机相变材料相变温度范围,利用有机物的混溶性,对两种有机相变材料按照一定比例进行混合,可以制得二元低共熔有机相变材料混合物,既改善了相变材料的应用效果,又可以拓展其应用范围。但其导热系数和密度都较小、单位体积的储热能力不足、热传递慢且在固-液相变过程中会出现液相,有泄漏的现象。
发明内容
本发明的目的是针对上述现有技术中的不足,提供一种相变效果显著、具有明显触感变化的冰爽油墨。
为达到上述目的,本发明的技术方案如下:
一种水性冰爽油墨,包括下述原料,复合相变材料20~50%,丙烯酸乳液28~36%,色料2~5%,水性防腐剂0.1~0.2%,水性增稠剂0.2~0.6%,水性润湿剂0.1~0.3%,水性分散剂0.3~0.6%,水性消泡剂0.1~0.5%,水性防霉剂0.1~0.3%,水性流平剂0.2~0.3%,清水余量。
所述复合相变材料为二元有机相变材料/高岭土复合相变材料,或二元有机相变材料/膨胀石墨复合相变材料。
所述二元有机相变材料为石蜡、十六醇/十二醇混合物,癸酸、十六醇/十二醇混合物,月桂酸、十六醇/十二醇混合物,肉豆寇酸、十六醇/十二醇混合物中的任意一种。
具体的工艺步骤为:
1、配制二元有机相变材料
用电子天平称取一定质量比的二元体系混合物(其中石蜡、十六醇/十二醇混合物混合质量比为40%∶60%,癸酸、十六醇/十二醇混合质量比为30%∶70%,月桂酸、十六醇/十二醇混合质量比为40%∶60%,肉豆寇酸、十六醇/十二醇混合质量比为50%∶50%),将其置于密封容器中混合,在80℃恒温水浴锅中加热直至全部熔融为液体,搅拌并保存一定时间,使体系充分混合,再将其放入50℃超声波水浴中振荡2min,再冷却至室温直至凝固。
2、配制复合相变材料
(1)配制二元有机相变材料/高岭土复合相变材料
将5g高岭土加入DMSO和蒸馏水的混合溶液中,其中DMSO和蒸馏水体积比为10∶1,将混合液置于超声波中,超声波强度200W,90℃恒温,振荡4h,接着蒸馏水洗涤,乙醇洗涤,抽滤,最后在60℃下真空干燥24h,得到DMSO/高岭土插层复合材料;
称取已经制得的二元有机相变材料溶于无水乙醇配成溶液,并在50℃搅拌下保持熔化状态30min,倒入DMSO/高岭土前驱体的无水乙醇分散液中,其中二元有机相变材料溶液与DMSO/高岭土前驱体的无水乙醇分散液体积比为60%∶40%,实验温度控制在70℃,搅拌5h,产物经蒸馏、抽滤、干燥至恒重,即制得二元有机相变材料/高岭土复合相变材料。制备的复合相变材料在室温下呈现密实、厚实感的颗粒状态,使用台式粉末压片机在常温下加压10MPa制备片状复合材料;
(2)配制二元有机相变材料/膨胀石墨复合相变材料
将可膨胀石墨在真空干燥箱60℃干燥24h,干燥后的可膨胀石墨置于800℃马弗炉中膨化60s,即得膨胀石墨(EG);
称量已经制得的二元有机相变材料样品放入平底容器中,将膨胀石墨均匀的覆盖在二元有机相变材料的表面,样品抽真空1h,真空度为0.1MPa。然后在相同的真空条件下,将平底容器置于65℃的水浴中,浸透3h。卸去真空将复合物置于60℃烘箱中干燥,直至二元有机相变材料不再从空隙中流出为止。制备的复合相变材料在室温下呈现密实、厚实感的颗粒状态,使用台式粉末压片机在常温下加压10MPa制备片状复合材料;
3、配制冰爽油墨
按如下重量比配备原料:复合相变材料20~50%,丙烯酸乳液28~36%,色料2~5%,水性防腐剂0.1~0.2%,水性增稠剂0.2~0.6%,水性润湿剂0.1~0.3%,水性分散剂0.3~0.6%,水性消泡剂0.1~0.5%,水性防霉剂0.1~0.3%,水性流平剂0.2~0.3%,清水余量;
首先将清水、水性防腐剂、1/2水性增稠剂、水性润湿剂、水性分散剂、1/2水性消泡剂加入分散研磨机,在500转/分钟的转速下搅拌10分钟使各组分混合均匀;接着将复合相变材料在1000转/分钟的转速下加入到分散研磨机中,再在3000转/分钟下搅拌30分钟,使混合物的细度小于30μm;再依次向分散缸加入色料、丙烯酸乳液、剩余1/2水性消泡剂、剩余1/2水性增稠剂、水性防霉剂、水性流平剂,用氨水调节pH=8~9,在500转/分钟的转速下搅拌10分钟使各组分混合均匀;最后把制备的水性相变油墨在室温下放置24h。
与现有技术相比,本发明有益效果是:本发明提供了一种相变效果显著、具有明显触感变化的冰爽油墨。当人体触摸使用该水性冰爽油墨印刷的产品时,由于温度达到油墨中相变材料的相变点,相变材料从固相变为液相,从而吸收热量,使人体感到清凉感。
具体实施方式
下面结合具体实施例对本发明进行阐述:
实施例1:二元有机相变材料/高岭土复合相变材料40%,其中二元有机相变材料是质量比为40%∶60%的石蜡、十六醇/十二醇混合物,丙烯酸乳液35%,色料5%,水性防腐剂0.1%,水性增稠剂0.6%,水性润湿剂0.3%,水性分散剂0.6%,水性消泡剂0.5%,水性防霉剂0.3%,水性流平剂0.2%,清水余量;
实施例2:二元有机相变材料/膨胀石墨复合相变材料50%,其中二元有机相变材料是质量比为30%∶70%的癸酸、十六醇/十二醇混合物,丙烯酸乳液25%,色料3%,水性防腐剂0.2%,水性增稠剂0.5%,水性润湿剂0.3%,水性分散剂0.5%,水性消泡剂0.5%,水性防霉剂0.3%,水性流平剂0.2%,清水余量;
对所公开的实施例的上述说明,使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的,本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下,在其它实施例中实现。因此,本发明将不会被限制于本文所示的这些实施例,而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (3)
1.一种水性冰爽油墨,其特征在于:包括下述原料,复合相变材料20~50%,丙烯酸乳液28~36%,色料2~5%,水性防腐剂0.1~0.2%,水性增稠剂0.2~0.6%,水性润湿剂0.1~0.3%,水性分散剂0.3~0.6%,水性消泡剂0.1~0.5%,水性防霉剂0.1~0.3%,水性流平剂0.2~0.3%,清水余量。
2.根据权利要求1所述的水性冰爽油墨,其特征在于,所述复合相变材料为二元有机相变材料/高岭土复合相变材料,或二元有机相变材料/膨胀石墨复合相变材料。
3.根据权利要求3所述的水性冰爽油墨,其特征在于,所述二元有机相变材料为石蜡、十六醇/十二醇混合物,癸酸、十六醇/十二醇混合物,月桂酸、十六醇/十二醇混合物,肉豆寇酸、十六醇/十二醇混合物中的任意一种。