CN105479607A - 一种绞线型高强度切割金属丝 - Google Patents

一种绞线型高强度切割金属丝 Download PDF

Info

Publication number
CN105479607A
CN105479607A CN201510861909.0A CN201510861909A CN105479607A CN 105479607 A CN105479607 A CN 105479607A CN 201510861909 A CN201510861909 A CN 201510861909A CN 105479607 A CN105479607 A CN 105479607A
Authority
CN
China
Prior art keywords
wire
alloy
type high
strength
nickel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510861909.0A
Other languages
English (en)
Inventor
王卫锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU HUIFENG MACHINERY EQUIPMENT Co Ltd
Original Assignee
SUZHOU HUIFENG MACHINERY EQUIPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU HUIFENG MACHINERY EQUIPMENT Co Ltd filed Critical SUZHOU HUIFENG MACHINERY EQUIPMENT Co Ltd
Priority to CN201510861909.0A priority Critical patent/CN105479607A/zh
Publication of CN105479607A publication Critical patent/CN105479607A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种绞线型高强度切割金属丝，所述金属丝是采用绞线机将多根极细高强度金属丝绞合而成的，所述极细高强度金属丝包括钢芯和镀合金层，所述镀合金层为镀铜镍合金，所述铜镍合金的成分及其各成分的质量配比为：铜75%-80%、镍14%-18%、锡0.05%-1%、钛0.02%-0.08%、钼0.2%-1%、铝2.8%-5%、铁0.5%-1.2%、磷0.01%-0.05%、硅0.2%-0.8%、其余为不可避免的杂质。通过上述方式，本发明由多根极细高强度金属丝绞合而成的，具有较好的强度和切削度，并且绞线结构能使磨料较好的吸附在其表面，从而提高切割速度和精度。

Description

一种绞线型高强度切割金属丝
技术领域
本发明涉及切割金属丝领域，特别是涉及一种绞线型高强度切割金属丝。
背景技术
多线切割原理是将金属丝适当地张紧，并以一定的速度和压力，相对于切割的工件作往复运动，在切割的过程中，在金属丝与工件之间不断添加混有磨料的切削液，便可对工件进行切割。为了减小切口的宽度，金属丝一般使用φ0.1-0.25mm的钨丝或钢丝，金属丝的速度可高达1000m/min，磨料可根据被切工件的硬度，选用碳化硅、氧化铝和金刚石，粒度为150号-180号，混在机油、煤油或水中使用。这种金属丝带动砂浆切割过程中，砂浆中的磨料容易从金属丝上剥落，从而影响切割质量。
发明内容
本发明主要解决的技术问题是提供一种绞线型高强度切割金属丝，能解决现有切割金属丝存在的缺陷。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种绞线型高强度切割金属丝，所述金属丝是采用绞线机将多根极细高强度金属丝绞合而成的，所述极细高强度金属丝包括钢芯和镀合金层，所述镀合金层为镀铜镍合金，所述铜镍合金的成分及其各成分的质量配比为：铜75%-80%、镍14%-18%、锡0.05%-1%、钛0.02%-0.08%、钼0.2%-1%、铝2.8%-5%、铁0.5%-1.2%、磷0.01%-0.05%、硅0.2%-0.8%、其余为不可避免的杂质。
在本发明一个较佳实施例中，所述极细高强度金属丝有2-4根。
在本发明一个较佳实施例中，所述极细高强度金属丝的线径为10-20μm。
本发明的有益效果是：本发明金属丝是由多根极细高强度金属丝绞合而成的，具有较好的强度和切削度，并且绞线结构能使磨料较好的吸附在其表面，从而提高切割速度和精度。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括：
实施例一：
一种绞线型高强度切割金属丝，所述金属丝是采用绞线机将多根极细高强度金属丝绞合而成的，所述极细高强度金属丝包括钢芯和镀合金层，所述镀合金层为镀铜镍合金，所述铜镍合金的成分及其各成分的质量配比为：铜75%、镍18%、锡1%、钛0.08%、钼1%、铝2.8%、铁1.2%、磷0.05%、硅0.8%、杂质0.07%。
其中，所述极细高强度金属丝有2根。
所述极细高强度金属丝的线径为20μm。
实施例二：
一种绞线型高强度切割金属丝，所述金属丝是采用绞线机将多根极细高强度金属丝绞合而成的，所述极细高强度金属丝包括钢芯和镀合金层，所述镀合金层为镀铜镍合金，所述铜镍合金的成分及其各成分的质量配比为：铜77%、镍16%、锡0.05%、钛0.08%、钼0.5%、铝4.8%、铁1%、磷0.03%、硅0.5%、杂质0.04%。
其中，所述极细高强度金属丝有3根。
所述极细高强度金属丝的线径为15μm。
实施例三：
一种绞线型高强度切割金属丝，所述金属丝是采用绞线机将多根极细高强度金属丝绞合而成的，所述极细高强度金属丝包括钢芯和镀合金层，所述镀合金层为镀铜镍合金，所述铜镍合金的成分及其各成分的质量配比为：铜80%、镍14%、锡0.05%、钛0.02%、钼0.2%、铝5%、铁0.5%、磷0.01%、硅0.2%、杂质0.02%。
其中，所述极细高强度金属丝有4根。
所述极细高强度金属丝的线径为10μm。
本发明揭示了一种绞线型高强度切割金属丝，是由多根极细高强度金属丝绞合而成的，具有较好的强度和切削度，并且绞线结构能使磨料较好的吸附在其表面，从而提高切割速度和精度。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (3)

1.一种绞线型高强度切割金属丝，其特征在于，所述金属丝是采用绞线机将多根极细高强度金属丝绞合而成的，所述极细高强度金属丝包括钢芯和镀合金层，所述镀合金层为镀铜镍合金，所述铜镍合金的成分及其各成分的质量配比为：铜75%-80%、镍14%-18%、锡0.05%-1%、钛0.02%-0.08%、钼0.2%-1%、铝2.8%-5%、铁0.5%-1.2%、磷0.01%-0.05%、硅0.2%-0.8%、其余为不可避免的杂质。
2.根据权利要求1所述的绞线型高强度切割金属丝，其特征在于，所述极细高强度金属丝有2-4根。
3.根据权利要求1或2所述的绞线型高强度切割金属丝，其特征在于，所述极细高强度金属丝的线径为10-20μm。
CN201510861909.0A 2015-12-01 2015-12-01 一种绞线型高强度切割金属丝 Pending CN105479607A (zh)