CN105463686A - Anti-transparent and ultraviolet-resistant warp-knitting fabric and purpose of same - Google Patents
Anti-transparent and ultraviolet-resistant warp-knitting fabric and purpose of same Download PDFInfo
- Publication number
- CN105463686A CN105463686A CN201410441854.3A CN201410441854A CN105463686A CN 105463686 A CN105463686 A CN 105463686A CN 201410441854 A CN201410441854 A CN 201410441854A CN 105463686 A CN105463686 A CN 105463686A
- Authority
- CN
- China
- Prior art keywords
- warp
- uvioresistant
- yarn
- face fabric
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-transparent and ultraviolet-resistant warp-knitting fabric and a purpose of the same. Yarns forming the warp-knitting fabric contain at least over 50% of ultraviolet-resistant terylene yarns; the ultraviolet-resistant terylene yarns are core sheath composite yarns with 65% to 90% of core yarns; titanium dioxide in the core yarns is 5% to 7%; the weight of the fabric is 130g/m<2>; and the surface layer tissue is 10/23. By the use of ultraviolet-resistant teryelene yarns of the core sheath structure and with a combination of specific tissues, a warp-knitting fabric is formed; although the warp-knitting fabric is thin, the fabric has excellent anti-transparent and ultraviolet-resistant effects, thereby being suitable for manufacturing of light sports shirts, T-shirts and Polo shirts used in summer.
Description
Technical field
The present invention relates to a kind of permeation-proof uvioresistant fabric and uses thereof, be specifically related to a kind of permeation-proof uvioresistant warp-knitted face fabric and uses thereof.
Background technology
In recent years, along with the raising of people's living standard, the Functional Requirement of people to fabric is also more and more higher, hot summer, and the light and thin fabric with uvioresistant permeation-proof function is then receive pursuing of consumers in general.
Wherein for the acquisition of uvioresistant fabric, there has been proposed a lot of method.Be two-layer comfortable UV-proof circle tricot as proposed a kind of institutional framework in patent document CN200510095072.X, comprise the skin formed by the yarn with anti-ultraviolet function and the nexine formed by the yarn with refrigerant water-absorbing fast-drying function, although the excellent result of uvioresistant and water-absorbing fast-drying, but well-known circle is compiled thing and is easily decoherenced, is out of shape, it is shorter to wear the life-span, and the words that reduce of grammes per square metre then there will be the problem of permeation-proof.
And for example propose a kind of Anti-ultraviolet elastic fabric in patent document CN200910151405.4, carry out water-absorbing fast-drying resin finishing again after interweaving by least adopting full-dull yarn and elastomeric yarn higher density and obtain, achieve the object having both permeation-proof uvioresistant, elasticity and water-absorbing fast-drying performance, and compile compared with thing with circle, not easily decoherence, be out of shape, but in order to realize the object of permeation-proof, need to adopt higher coverage coefficient, difficulty of weaving is large; Adopting elastomeric yarn to obtain elastic demand simultaneously, particularly using the words of bi-component yarn to increase cost.
For another example propose in patent document CN201410070893.7 and adopt uvioresistant spun polyester thread by least one in bottom layer tissue and staple tissue, combine the fabric that fluffing is processed and anti ultraviolet agent Final finishing acquisition UVResistant effect is lasting again, but this fabric is fluffing product, and do not possess water-absorbing fast-drying performance, be not suitable for the clothes making dress in summer.
Summary of the invention
The object of the invention is to provide a kind of and is applicable to dress in summer, anti-translucency effect and uvioresistant performance excellence, water-absorbing fast-drying function admirable, yielding, not cheap warp-knitted face fabric and purposes.
In permeation-proof uvioresistant warp-knitted face fabric of the present invention, to form in the yarn of this warp-knitted face fabric more than at least 50 % by weight for uvioresistant spun polyester thread, uvioresistant spun polyester thread is the core sheath complex yarn of heart yarn content 65 ~ 90%, and in heart yarn, content of titanium dioxide is 5 ~ 7%; And the grammes per square metre of this fabric is 130g/m
2below, textura epidermoidea is 10/23.
The present invention is by using the uvioresistant spun polyester thread of core sheath structure, in conjunction with specific organization formation warp-knitted face fabric, although gained warp-knitted face fabric is frivolous, there is excellent permeation-proof and UVResistant effect also simultaneously, be applicable to the frivolous sweater, T-shirt, POLO shirt etc. that make summer.
Permeation-proof uvioresistant fabric of the present invention is warp-knitted face fabric, compared with compiling thing, not easily decoherences, is out of shape with circle; Compared with woven fabric, under the state not using elastomeric yarn on an equal basis, fabric aeration is excellent, is convenient to motion, comfortable and easy to wear.
Detailed description of the invention
In permeation-proof uvioresistant warp-knitted face fabric of the present invention, to form in the yarn of this warp-knitted face fabric more than at least 50 % by weight and use uvioresistant spun polyester thread, to obtain excellent permeation-proof and UVResistant effect.If permeation-proof uvioresistant spun polyester thread is lower than 50 % by weight, the permeation-proof of its fabric and UVResistant effect will reduce.The present invention's uvioresistant yarn used is core sheath structure, is specifically made up of the heart yarn of titanium dioxide high-load and the sheath yarn of titanium dioxide low content, can obtained good permeation-proof and UVResistant effect, and particle to be avoided again in braiding process in yarn the impact of knitting needle.In uvioresistant yarn, the content of heart yarn is 65 ~ 90%, preferably 70 ~ 85%.If heart yarn proportion is higher than 90%, yarn strength can be caused to decline, braiding difficulty; And heart yarn proportion is lower than 65%, be difficult to obtain good permeation-proof and UVResistant effect.
The present invention's uvioresistant yarn used, the content of titanium dioxide in heart yarn is 5 ~ 7%, preferably 6 ~ 7%.If the content of titanium dioxide in heart yarn is lower than 5%, be unfavorable for reflection and the absorption of light, permeation-proof uvioresistant performance is bad; Content of titanium dioxide in contrary heart yarn, higher than 7%, can cause yarn strength to decline, braiding difficulty.
The present invention's uvioresistant yarn used, in sheath yarn, content of titanium dioxide is 0.1 ~ 0.5%, preferably 0.2 ~ 0.4%.If the content of titanium dioxide in sheath yarn is lower than 0.1%, light is produced absorb and reflex hardly, permeation-proof uvioresistant performance extreme difference; Content of titanium dioxide in contrary sheath yarn, higher than 0.5%, can increase the friction between yarn and knitting needle, is difficult to braiding.
The present invention's uvioresistant denier count as received used is 30 ~ 100 DENIER.Consider that summer wears, the yarn compiled with its friendship is preferably the one in the ordinary polyester DTY of fiber number 30 ~ 50 DENIER, ordinary polyester FDY, PBT-DTY, PTT-FDY, to ensure that the grammes per square metre of fabric is at 130g/m
2below, thickness is at below 0.5mm.
In order to ensure excellent permeation-proof and uvioresistant performance, and the hook silk performance that underlap face is good, the textura epidermoidea of warp-knitted face fabric of the present invention uses 10/23.Textura epidermoidea selects 10/12, and permeation-proof and UVResistant effect can be undesirable; And textura epidermoidea selects 10/34 or 10/45, the hook silk performance in underlap face can be affected.The internal layer of warp-knitted face fabric of the present invention is organized as eyelet stitch, can ensure that venting quality is 100cm
3/ cm
2/ more than sec.
The production method of warp-knitted face fabric of the present invention is: at least select the uvioresistant yarn of more than 50 % by weight and ordinary polyester DTY, ordinary polyester FDY, PBT yarn, PTT yarn to weave on the tricot warp knitting machine of 28G ~ 32G, 130in ~ 220in, then carry out pre-treatment, dyeing, Final finishing processing, obtain product.Wherein in dyeing or rear processing finishing sizing, add hydrophilic resin, excellent water-absorbing fast-drying performance can be realized, when the warp knitting machine of wherein 200in ~ 220in weaves, wide cut grey cloth can be woven, and carry out when arranging sizing twoly cutting out engineering, cost is reduced.
Uvioresistant coefficient UPF value through compiling thing of the present invention is more than 50, can absorbing wavelength at the solar UV of 320 ~ 400nm, UVA value is below 5%, permeation-proof rate more than 90%, reduces ultraviolet to skin surface, deep layer and corium with the injury of the fine structure of the skin inside such as undertissue, collagen, elastic fibrous tissue.
The internal layer of warp-knitted face fabric of the present invention is organized as eyelet stitch, particularly coordinates again and carries out water-absorbing resin processing, fabric can be made to have superior water-absorbing fast-drying performance, and the height (water imbibition) of climbing of transverse and longitudinal is more than 80mm; Rapid-curing cutback speed is more than 0.3g/h.Snugness of fit when summer perspires can be ensured like this.
Permeation-proof uvioresistant warp-knitted face fabric of the present invention can be used for making the sweater in summer, T-shirt or POLO shirt.
Embodiment
The present invention is illustrated in greater detail below in conjunction with embodiment and comparative example.Wherein, the method for testing of each characteristic in embodiment is as follows.
(1) barrier property
The measured color value (Lw) of first assay standard look calico, the measured color value (LB) of reference colours black cloth, again test specimens is placed on reference colours calico, use D65 light source irradiation, colour examining L1 measured color value: (Lfw), then test specimens is placed on reference colours black cloth, uses D65 light source irradiation, colour examining L2 measured color value: (Lfb).Permeation-proof rate=[1-(Lfw-Lfb)/(Lw-LB)] * 100%.
(2) uvioresistant coefficient UPF value
Measure according to GB/T18830-2009.
(3) silk performance is hooked
Measure according to GB/T11047 nail hammer method (600 times).
(4) water absorbing properties
Measure according to JISL1907 method.
(5) rapid-drying properties
Measure according to the method that section agree, measure the rate of drying of water within 60min of 0.3ml.
(6) venting quality
Measure according to JISL1096 method (pressure 125MPa).
Embodiment 1
75D-36f-uvioresistant polyester DTY and 30D-36f-half delustring ordinary polyester DTY is adopted to weave on 28G*218in tricot warp knitting machine, knit stitches is GB1:10/23, GB2:23/21/10/12, then pre-treatment, dyeing, Final finishing processing (hydrophilizing agent 10g/l is carried out, two sanction processing), obtaining grammes per square metre of the present invention is 126g/m
2, thickness is the warp-knitted face fabric of 0.45mm.Wherein the mixed rate of uvioresistant polyester DTY is 89%, and the content of its heart yarn is 70%, and in heart yarn, the content of titanium dioxide is 6.4%, and in sheath yarn, content of titanium dioxide is 0.3%; GB1 during braiding: uvioresistant polyester DTY, completely wears; GB2: ordinary polyester DTY, one has worn.Refer to table 1.
Embodiment 2
75D-36f-uvioresistant polyester DTY and 30D-36f-half delustring ordinary polyester DTY is adopted to weave on 28G*218in tricot warp knitting machine, knit stitches is GB1:10/23, GB2:10/12/23/21, GB3:23/21/10/12, then pre-treatment, dyeing, Final finishing processing (hydrophilizing agent 10g/l is carried out, two sanction processing), obtaining grammes per square metre of the present invention is 119g/m
2, thickness is the warp-knitted face fabric of 0.43mm.Wherein the mixed rate of uvioresistant spun polyester thread is 65%, and its heart yarn content is 69%, and in heart yarn, content of titanium dioxide is 6.6%, and in sheath yarn, content of titanium dioxide is 0.3%; During braiding, GB1: uvioresistant polyester DTY, completely wears; GB2: ordinary polyester DTY, two have worn; GB3: ordinary polyester DTY, two have worn.Refer to table 1.
Embodiment 3
75D-72f-uvioresistant polyester DTY and 30D-36f-half delustring ordinary polyester FDY is adopted to weave on 28G*218in tricot warp knitting machine, knit stitches is GB1:10/23, GB2:34/32/21/10/12/23, then carry out pre-treatment, dyeing (hydrophilizing agent 1.5%owf), Final finishing processing (two sanction processing), obtaining grammes per square metre of the present invention is 125g/m
2, thickness is the warp-knitted face fabric of 0.44mm.Wherein, the mixed rate of uvioresistant polyester DTY is 88%, and its heart yarn content is 86%, and in heart yarn, content of titanium dioxide is 6.0%, and in sheath yarn, content of titanium dioxide is 0.4%; During braiding, GB1: uvioresistant polyester DTY, completely wears; GB2: ordinary polyester FDY, one has worn.Refer to table 1.
Embodiment 4
40D-24f-uvioresistant polyester FDY and 50D-48f-PBTDTY is adopted to weave on 32G*186in tricot warp knitting machine, knit stitches is GB1:10/23, GB2:10/12/23/21, GB3:23/21/10/12, then carry out pre-treatment, dyeing (hydrophilizing agent 1.5%owf), Final finishing processing, obtaining grammes per square metre of the present invention is 103g/m
2, thickness is the warp-knitted face fabric of 0.41mm.The mixed rate of uvioresistant polyester FDY is 75%, and its heart yarn content is 76%, and in heart yarn, content of titanium dioxide is 6.6%, and in sheath yarn, content of titanium dioxide is 0.3%; During braiding, GB1: uvioresistant polyester FDY, completely wears; GB2: uvioresistant polyester FDY, two have worn; GB3:PBTDTY, two have worn.Refer to table 1.
Embodiment 5
75D-72f-uvioresistant polyester DTY and 30D-24f-full-dull ordinary polyester DTY is adopted to weave on 28G*218in tricot warp knitting machine, knit stitches is GB1:10/23, GB2:10/12/23/21, GB3:23/21/10/12, then pre-treatment, dyeing, Final finishing processing (hydrophilizing agent 10g/l is carried out, two sanction processing), obtaining grammes per square metre of the present invention is 117g/m
2, thickness is the warp-knitted face fabric of 0.42mm.Wherein the mixed rate of uvioresistant polyester DTY is 65%, and its heart yarn content is 80%, and in heart yarn, content of titanium dioxide is 5.3%, and in sheath yarn, content of titanium dioxide is 0.2%; During braiding, GB1: uvioresistant polyester DTY, completely wears; GB2: ordinary polyester DTY, two have worn one wears; GB3: ordinary polyester DTY, three have worn.Refer to table 1.
Embodiment 6
75D-36f-uvioresistant polyester DTY and 50D-36f-PTTFDY is adopted to weave on 28G*218in tricot warp knitting machine, knit stitches is GB1:10/23, GB2:34/32/21/10/12/23, then pre-treatment, dyeing, Final finishing processing (hydrophilizing agent 10g/l is carried out, two sanction processing), obtaining grammes per square metre of the present invention is 128g/m
2, thickness is the warp-knitted face fabric of 0.48mm.Wherein the mixed rate of uvioresistant polyester DTY is 80%, and its heart yarn content is 66%, and in heart yarn, content of titanium dioxide is 6.8%, and in sheath yarn, content of titanium dioxide is 0.4%; During braiding, GB1: uvioresistant polyester DTY, completely wears; GB2:PTTFDY, one has worn.Refer to table 1.
Embodiment 7
40D-24f-uvioresistant polyester FDY and 50D-96f-full-dull ordinary polyester DTY is adopted to weave on 32G*186in tricot warp knitting machine, knit stitches is GB1:10/23, GB2:23/21/10/12, then carry out pre-treatment, dyeing (hydrophilizing agent 1.5%owf), Final finishing processing, obtaining grammes per square metre of the present invention is 107g/m
2, thickness is the warp-knitted face fabric of 0.43mm.Wherein the mixed rate of uvioresistant polyester FDY is 72%, and its heart yarn content is 73%, and in heart yarn, content of titanium dioxide is 6.6%, and in sheath yarn, content of titanium dioxide is 0.3%; During braiding, GB1: uvioresistant polyester FDY, completely wears; GB2: ordinary polyester DTY, one has worn.Refer to table 1.
The permeation-proof uvioresistant warp-knitted face fabric of embodiment 1-7 is used to make sweater, T-shirt or POLO shirt.
Comparative example 1
75D-36f-uvioresistant polyester DTY and 30D-36f-half delustring ordinary polyester DTY is adopted to weave on 28G*136in tricot warp knitting machine, knit stitches is GB1:10/23, GB2:23/21/10/12, then carry out pre-treatment, dyeing, Final finishing processing (hydrophilizing agent 10g/l), obtaining grammes per square metre is 126g/m
2, thickness is the warp-knitted face fabric of 0.45mm.Wherein, the mixed rate of uvioresistant polyester DTY is 89%, and its heart yarn content is 60%, and in heart yarn, content of titanium dioxide is 3.0%, and in sheath yarn, content of titanium dioxide is 0.1%; During braiding, GB1: uvioresistant polyester DTY, completely wears; GB2: ordinary polyester DTY, one has worn.Refer to table 1.
Comparative example 2
75D-36f-uvioresistant polyester DTY and 30D-36f-half delustring ordinary polyester DTY is adopted to weave on 28G*136in tricot warp knitting machine, knit stitches is GB1:10/12, GB2:10/12/23/21, GB3:23/21/10/12, then carry out pre-treatment, dyeing, Final finishing processing (hydrophilizing agent 10g/l), obtaining grammes per square metre is 119g/m
2, thickness is the warp-knitted face fabric of 0.43mm.Wherein, the mixed rate of uvioresistant polyester DTY is 65%, and its heart yarn content is 69%, and in heart yarn, content of titanium dioxide is 6.6%, and in sheath yarn, content of titanium dioxide is 0.3%; During braiding, GB1: uvioresistant polyester DTY, completely wears; GB2: ordinary polyester DTY, two have worn; GB3: ordinary polyester DTY, two have worn.Refer to table 1.
Comparative example 3
Adopt 75D-36f-uvioresistant polyester DTY to be warp thread, adopt 75D-36 height crimp yarn to be weft yarn, its crimp recovery is 42%, be organized as twill, by warping, starching, preparation warp beam, be made into grey cloth and obtain grey cloth, by warping, starching, preparation warp beam, carry out weaving obtained grey cloth.Above-mentioned grey cloth, by concise → dyeing → arrangement processing (hydrophilizing agent 10g/l), obtains weft density: 192/inch*108 root/inch, grammes per square metre 185g/m
2finished product.Wherein the mixed rate of uvioresistant polyester DTY is 50%, and its heart yarn content is 70%, and in heart yarn, content of titanium dioxide is 6.4%, and in sheath yarn, content of titanium dioxide is 0.3%.Refer to table 1.
Table 1
Claims (5)
1. a permeation-proof uvioresistant warp-knitted face fabric, it is characterized in that: to form in the yarn of this warp-knitted face fabric more than at least 50 % by weight for uvioresistant spun polyester thread, described uvioresistant spun polyester thread is the core sheath complex yarn of heart yarn content 65 ~ 90%, and in heart yarn, content of titanium dioxide is 5 ~ 7%; And the grammes per square metre of this fabric is 130g/m
2below, textura epidermoidea is 10/23.
2. permeation-proof uvioresistant warp-knitted face fabric according to claim 1, is characterized in that: in the sheath yarn of described uvioresistant spun polyester thread, content of titanium dioxide is 0.1 ~ 0.5%.
3. permeation-proof uvioresistant warp-knitted face fabric according to claim 1 or 2, is characterized in that: the uvioresistant coefficient UPF value of this warp-knitted face fabric more than 50, the hook silk performance in underlap face is more than 3 grades.
4. permeation-proof uvioresistant warp-knitted face fabric according to claim 1 or 2, is characterized in that: the water imbibition of the transverse and longitudinal of this warp-knitted face fabric is more than 80mm, rapid-curing cutback speed is more than 0.3g/h.
5. sweater, T-shirt or the POLO shirt using the permeation-proof uvioresistant warp-knitted face fabric described in claim 1 obtained.