CN105401137A - 一种空调轴承外套的表面处理工艺 - Google Patents
一种空调轴承外套的表面处理工艺 Download PDFInfo
- Publication number
- CN105401137A CN105401137A CN201510542759.7A CN201510542759A CN105401137A CN 105401137 A CN105401137 A CN 105401137A CN 201510542759 A CN201510542759 A CN 201510542759A CN 105401137 A CN105401137 A CN 105401137A
- Authority
- CN
- China
- Prior art keywords
- bearing outside
- surface treatment
- bearing outer
- air
- outer sleeve
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种空调轴承外套的表面处理工艺，包括（1）除油、（2）除锈、（3）磷化、（4）水洗、(5)烘干，工艺主要利用金属的磷化反应，在轴承外表面生成一层磷化膜，以使得轴承外套有着更好的防锈和防腐蚀能力，本发明提供的空调轴承外套的表面处理工艺，用时短，工艺步骤简单，处理后的轴承综合性能优异，形成的油膜延展性好，均匀度高，能够起到很好的保护作用。
Description
技术领域
本发明涉及一种轴承加工领域，具体地，涉及一种空调轴承外套的表面处理工艺。
背景技术
空调内部环境比较潮湿，其内部使用的金属工件需要进行防锈处理，防止长期使用导致金属工件上锈。磷化是一种化学与电化学反应形成磷酸盐化学转化膜的过程，所形成的磷酸盐转化膜称之为磷化膜。磷化的目的主要是：给基体金属提供保护，在一定程度上防止金属被腐蚀；用于涂漆前打底，提高漆膜层的附着力与防腐蚀能力；在金属冷加工工艺中起减摩润滑使用。
发明内容
本发明的目的在于提供一种空调轴承外套的表面处理工艺，将磷化工艺应用于空调轴承外套的防锈处理上，大大的增加了轴承的防锈和防腐蚀能力。
为了实现上述目的，本发明提供一种空调轴承外套的表面处理工艺，其中，所述工艺步骤为：
（1）除油：将轴承外套放入电解槽中进行脱脂除油，除油温度为60-75℃，时间为15-20min；
（2）除锈：将步骤（1）中除油结束后的轴承外套放入浓度为3-7%的除锈剂中处理，时间为3-5min；
（3）磷化：将步骤（2）中处理后的轴承外套放入磷化液中进行浸泡，浸泡时间为4-8min；
（4）水洗：用普通自来水水洗干净；
（5）烘干：将水洗后的轴承外套放入烘箱中，在温度为100-140℃下烘干，烘干时间为3-8min。
优选的，所述步骤（2）中除锈剂为盐酸和/或硝酸。
优选的，所述步骤（3）中磷化液的组成成分为磷酸二氢锌50-60%、磷酸锰10-25%、磷酸钙5-10%、余量水。
有益效果：本发明提供一种空调轴承外套的表面处理工艺，包括（1）除油、（2）除锈、（3）磷化、（4）水洗、(5)烘干，工艺主要利用金属的磷化反应，在轴承外表面生成一层磷化膜，以使得轴承外套有着更好的防锈和防腐蚀能力，本发明提供的空调轴承外套的表面处理工艺，用时短，工艺步骤简单，处理后的轴承综合性能优异，形成的油膜延展性好，均匀度高，能够起到很好的保护作用。
具体实施方式
以下对本发明的具体实施方式进行详细说明。应当理解的是，此处所描述的具体实施方式仅用于说明和解释本发明，并不用于限制本发明。
本发明提供一种空调轴承外套的表面处理工艺，其中，所述工艺步骤为：
（1）除油：将轴承外套放入电解槽中进行脱脂除油，除油温度为60℃，时间为15min；
（2）除锈：将步骤（1）中除油结束后的轴承外套放入浓度为3%的除锈剂中处理，时间为3min；
（3）磷化：将步骤（2）中处理后的轴承外套放入磷化液中进行浸泡，浸泡时间为4min；
（4）水洗：用普通自来水水洗干净；
（5）烘干：将水洗后的轴承外套放入烘箱中，在温度为100℃下烘干，烘干时间为3min。
其中，所述步骤（2）中除锈剂为盐酸，所述步骤（3）中磷化液的组成成分为磷酸二氢锌50%、磷酸锰10%、磷酸钙5%、余量水。
本发明提供一种空调轴承外套的表面处理工艺，包括（1）除油、（2）除锈、（3）磷化、（4）水洗、(5)烘干，工艺主要利用金属的磷化反应，在轴承外表面生成一层磷化膜，以使得轴承外套有着更好的防锈和防腐蚀能力，本发明提供的空调轴承外套的表面处理工艺，用时短，工艺步骤简单，处理后的轴承综合性能优异，形成的油膜延展性好，均匀度高，能够起到很好的保护作用。
通以上详细描述了本发明的优选实施方式，但是，本发明并不限于上述实施方式中的具体细节，在本发明的技术构思范围内，可以对本发明的技术方案进行多种简单变型，这些简单变型均属于本发明的保护范围。
另外需要说明的是，在上述具体实施方式中所描述的各个具体技术特征，在不矛盾的情况下，可以通过任何合适的方式进行组合，为了避免不必要的重复，本发明对各种可能的组合方式不再另行说明。
此外，本发明的各种不同的实施方式之间也可以进行任意组合，只要其不违背本发明的思想，其同样应当视为本发明所公开的内容。
Claims (3)
1.一种空调轴承外套的表面处理工艺，其特征在于，所述工艺步骤为：
（1）除油：将轴承外套放入电解槽中进行脱脂除油，除油温度为60-75℃，时间为15-20min；
（2）除锈：将步骤（1）中除油结束后的轴承外套放入浓度为3-7%的除锈剂中处理，时间为3-5min；
（3）磷化：将步骤（2）中处理后的轴承外套放入磷化液中进行浸泡，浸泡时间为4-8min；
（4）水洗：用普通自来水水洗干净；
（5）烘干：将水洗后的轴承外套放入烘箱中，在温度为100-140℃下烘干，烘干时间为3-8min。
2.根据权利要求1所述的空调轴承外套的表面处理工艺，其特征在于，所述步骤（2）中除锈剂为盐酸和/或硝酸。
3.根据权利要求1所述的空调轴承外套的表面处理工艺，其特征在于：所述步骤(3)中磷化液的组成成分为磷酸二氢锌50-60％、磷酸锰10-25％、磷酸钙5-10％、余量水。