CN105385414A - 一种低温抗冻剂及其制备方法 - Google Patents
一种低温抗冻剂及其制备方法 Download PDFInfo
- Publication number
- CN105385414A CN105385414A CN201510789187.2A CN201510789187A CN105385414A CN 105385414 A CN105385414 A CN 105385414A CN 201510789187 A CN201510789187 A CN 201510789187A CN 105385414 A CN105385414 A CN 105385414A
- Authority
- CN
- China
- Prior art keywords
- parts
- antifreezing agent
- mixed solution
- aeo
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种低温抗冻剂，该抗冻剂包括按质量份数构成的如下组分，甲基硅油：13份-16份；聚二甲基硅氧烷：22份-27份；航空煤油：8份-12份；AEO-9：8份-12份；水：35份-45份；制备该低温抗冻剂的方法包括步骤：(1)按照质量份数将8份-12份的AEO-9以及35份-45份的水进行混合；(2)对AEO-9和水的混合液进行搅拌；(3)在AEO-9和水的混合液中加入按照质量份数计的13份-16份的甲基硅油、22份-27份的聚二甲基硅氧烷、8份-12份的航空煤油得到最终混合液；(4)对最终混合液进行搅拌得到最终产品。本发明的抗冻剂在极低温度条件下的抗冰性能比现有抗冻剂产品更加优秀。
Description
技术领域
本发明属于抗冻剂技术领域，特别是一种低温抗冻剂及其制备方法。
背景技术
水/二醇-基防冻剂用于除去冻结沉积物。二醇用作降低介质的凝固点，此外，还存在表面活性剂，表面活性剂可以减小防冻剂的表面张力并因此改善航空器表面的润湿状况。而且，防冻剂还可以含有腐蚀抑制剂、消泡剂、染料和阻燃物质。不同于纯防冻剂，抗冻剂还包含有增稠剂物质。因此，这些流体的粘度改善了对再冻结的防护，这是因为这种流体仅在静止状态才非常缓慢地从航空器表面流走，并因此能够在较长时间内吸收冻结沉积物。然而，不可避免的是，在机械载荷下，所述增稠剂或多或少都会受到破坏。由于高速搅拌器、泵或当流经小截面管子时，在强的剪切应力下不可避免地会发生粘度损失，机械载荷会引起聚合物链的断裂，因此，不可避免地会破坏聚合物网络。此外，在一定的外部条件下，所述增稠剂往往会形成凝胶。现有的抗冻剂的抗冻和抗冰性能较差。
发明内容
本发明的目的是针对现有技术的不足，而提出一种低温抗冻剂及其制备方法。
本发明解决其技术问题是采取以下技术方案实现的：
一种低温抗冻剂，该抗冻剂包括按质量份数构成的如下组分，
一种低温抗冻剂的制备方法，该方法包括如下步骤：
(1)按照质量份数将8份-12份的AEO-9以及35份-45份的水进行混合；
(2)对AEO-9和水的混合液进行搅拌；
(3)在AEO-9和水的混合液中加入按照质量份数计的13份-16份的甲基硅油、22份-27份的聚二甲基硅氧烷、8份-12份的航空煤油得到最终混合液；
(4)对最终混合液进行搅拌，均匀后得到最终产品。
而且，所述步骤(4)中搅拌的时间为30分钟。
本发明的优点和积极效果是：
本发明的抗冻剂在极低温度条件下的抗冰性能比现有抗冻剂产品更加优秀。
具体实施方式
以下对本发明实施做进一步详述，以下实施例只是描述性的，不是限定性的，不能以此限定本发明的保护范围。
一种低温抗冻剂，该抗冻剂包括按质量份数构成的如下组分，
其中，甲基硅油无色、无味、不易挥发，具有很小的蒸气压，较高的闪点和燃点。甲基硅油具有卓越的耐热性、电绝缘性、耐候性、疏水性、生理惰性和较小的表面张力，还具有低的黏温系数，较高的抗压缩性。
其中，聚二甲基硅氧烷的耐热性、耐寒性、黏度随温度变化小、防水性、表面张力小、具有导热性，导热系数为0.134-0.159W/M*K，为无毒品，透光性为透光率100％。具有优良的物理特性，可直接用于防潮绝缘，阻尼，减震，消泡，润滑，抛光等方面。，具有生理惰性、良好的化学稳定性、电绝缘性和耐候性、疏水性好，并具有很高的抗剪切能力，可在-50℃～200℃下长期使用。广泛用作绝缘润滑、防震、防油尘、介电液和热载体。以及用作消泡、脱模剂、油漆及日化品添加剂。
其中，航空煤油的密度适宜，热值高，燃烧性能好，能迅速、稳定、连续、完全燃烧，且燃烧区域小，积碳量少，不易结焦；低温流动性好，能满足寒冷低温地区和高空飞行对油品流动性的要求；热安定性和抗氧化安定性好，可以满足超音速高空飞行的需要；洁净度高，无机械杂质及水分等有害物质，硫含量尤其是硫醇性硫含量低，对机件腐蚀小。航空煤油主要用作航空涡轮发动机的燃料。汽油不安全，容易挥发，太容易燃烧，但是活塞发动机还在用。柴油黏度太大，在涡轮发动机里不适合，因为是要靠很细小的喷嘴把燃料喷成雾状的。
其中，AEO-9的化学名称为脂肪醇聚氧乙烯醚。其为非离子型表面活性剂。主要用作乳液类、膏霜类、香波类化妆品的乳化剂。水溶性优良，可用于制造水包油型乳液。另外还可用作抗静电剂。为亲水性乳化剂，能增强某些物质在水中的溶解度，可作为制作O/W型乳液的乳化剂。具有良好的乳化、去污、净洗等性能，广泛用于配制民用洗涤剂，用作工业乳化剂和金属清洗剂等。AEO仲醇系列，脂肪醇聚氧乙烯醚(C12～14仲醇结构),该产品是通过石蜡裂解生成α-烯烃，再进一步加工成为线性仲醇，其溶于水和多种有机溶剂，不含APEO，具有优良的乳化、分散、扩散、去污洗涤性。该系列产品能与各种阴离子、阳离子、非离子表面活性剂以及其他助剂组合使用，从而获得协同效应和高性能产品，从而减少助剂使用消耗，具有出众的性能价格比。该系列产品具有众多优异的性能和品质：1.粘度低，冻点低，几乎没有凝胶现象；2.超强的润湿乳化能力，以及出众的低温洗涤性能和增溶、分散、润湿性；3.均匀的起泡性能，良好的消泡性能；4.良好的生物降解性，环境友好，对皮肤的低刺激性；5.无臭，未反应醇含量极低。仲醇AEO-9是优良的渗透、乳化剂、润湿和净洗剂，具有比TX-10更为优异的净洗去污和渗透润湿乳化能力，且不含APEO，生物降解性好，环境友好；可与其他各类阴离子、非离子、阳离子表面活性剂复配使用，具有出众的协同效应，可以大大减少助剂的使用消耗量，达到良好的性价比；可以提高油漆用增稠剂效力和提高溶剂基系统的冲洗性。在高效精练清洗、油漆涂料、造纸、农药化肥、干洗、纺织品处理和油田开采上具有广泛的使用。
实例1
一种低温抗冻剂，该抗冻剂包括按质量份数构成的如下组分，
实验证明，在极低的温度条件下该抗冻剂的抗冰性能比现有的抗冻剂产品更加优秀。
实例2
一种低温抗冻剂，该抗冻剂包括按质量份数构成的如下组分，
实验证明，在极低的温度条件下该抗冻剂的抗冰性能比现有的抗冻剂产品更加优秀。
一种低温抗冻剂的制备方法，该方法包括如下步骤：
(1)按照质量份数将8份-12份的AEO-9以及35份-45份的水进行混合；
(2)对AEO-9和水的混合液进行搅拌；
(3)在AEO-9和水的混合液中加入按照质量份数计的13份-16份的甲基硅油、22份-27份的聚二甲基硅氧烷、8份-12份的航空煤油得到最终混合液；
(4)对最终混合液进行搅拌，均匀后得到最终产品。
在本发明的具体实施中，所述步骤(4)中搅拌的时间为30分钟。
Claims (3)
1.一种低温抗冻剂，其特征在于：该抗冻剂包括按质量份数构成的如下组分，
2.一种低温抗冻剂的制备方法，其特征在于：该方法包括如下步骤：
(1)按照质量份数将8份-12份的AEO-9以及35份-45份的水进行混合；
(2)对AEO-9和水的混合液进行搅拌；
(3)在AEO-9和水的混合液中加入按照质量份数计的13份-16份的甲基硅油、22份-27份的聚二甲基硅氧烷、8份-12份的航空煤油得到最终混合液；
(4)对最终混合液进行搅拌，均匀后得到最终产品。
3.根据权利要求2所述的低温抗冻剂的制备方法，其特征在于：所述步骤(4)中搅拌的时间为30分钟。