CN105368108A - Anion photocureable coating - Google Patents
Anion photocureable coating Download PDFInfo
- Publication number
- CN105368108A CN105368108A CN201510931974.6A CN201510931974A CN105368108A CN 105368108 A CN105368108 A CN 105368108A CN 201510931974 A CN201510931974 A CN 201510931974A CN 105368108 A CN105368108 A CN 105368108A
- Authority
- CN
- China
- Prior art keywords
- negative ion
- parts
- agent
- anion
- formaldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anion photocureable coating. The anion photocureable coating is characterized by being prepared from, by weight, 20-40 parts of a formaldehyde catching agent, 25-45 parts of hexanediol diacrylate, 2-4 parts of a photosensitizer, 0.5-1.5 parts of a dispersing agent, 5-15 parts of a nanometer macromolecule polymer modifier, 0.1-0.3 part of a defoaming agent, 0.2-0.4 part of an organosilicon surfactant, 10-20 parts of multifunctional anion padding and 4-7 parts of extinction powder. The released anions can purify air, eliminate dust, remove noxious gas, achieve deodorization, resist bacteria, activate cells and soothe nerves.
Description
Technical field
The present invention relates to a kind of negative ion photo-cured coating.
Background technology
Forest Bath once fashionable for a time, obtains the power-assisted of negative aeroion abundant in virgin forest exactly, but forest is too far away, is not that each urbanite can arrive.Nowadays by high-tech development, for Domestic, negative aeroion, is not limited to Healthy People and patient, grownup and children, the related products of negative ion, thus achieves the effectiveness just carrying out health-care physiotherapeutic, purifying air at home.Negative ion from Forest Bath from afar, laboratory from professional researchist, really enter into thousands upon thousands ordinary other.
Summary of the invention
For problems of the prior art, the object of the present invention is to provide a kind of technical scheme of negative ion photo-cured coating.
Described negative ion photo-cured coating, it is characterized in that the component comprising following weight part: formaldehyde-trapping agent 20-40, hexanediyl ester 25-45, photosensitizers 2-4, dispersion agent 0.5-1.5, nano-high molecule polymkeric substance modification agent 5-15, defoamer 0.1-0.3, organic silicon surfactant 0.2-0.4, multifunction negative ion filler 10-20, flatting silica 4-7.
Described negative ion photo-cured coating, it is characterized in that the component comprising following weight part: formaldehyde-trapping agent 25-35, hexanediyl ester 30-40, photosensitizers 2.5-3.5, dispersion agent 0.7-1.3, nano-high molecule polymkeric substance modification agent 8-12, defoamer 0.15-0.25, organic silicon surfactant 0.25-0.35, multifunction negative ion filler 13-17, flatting silica 5-6.
Described negative ion photo-cured coating, it is characterized in that the component comprising following weight part: formaldehyde-trapping agent 30, hexanediyl ester 35, photosensitizers 3, dispersion agent 1, nano-high molecule polymkeric substance modification agent 10, defoamer 0.2, organic silicon surfactant 0.3, multifunction negative ion filler 15, flatting silica 5.5.
The negative ion of the present invention's release is capable of purifying air, the elimination cloud of dust; Remove obnoxious flavour, deodorizing; Antibacterial bacteriostatic; Active cells, stable spirit.
Embodiment
Embodiment 1
Negative ion photo-cured coating, comprise the component of following weight part: formaldehyde-trapping agent 20kg, hexanediyl ester 45kg, photosensitizers 4kg, dispersion agent 1.5kg, nano-high molecule polymkeric substance modification agent 15kg, defoamer 0.3kg, organic silicon surfactant 0.4kg, multifunction negative ion filler 20kg, flatting silica 7kg.
Preparation technology: get out above-mentioned batching, formaldehyde-trapping agent, photosensitizers, dispersion agent, nano-high molecule polymkeric substance modification agent, defoamer, organic silicon surfactant, multifunction negative ion filler, flatting silica carried out fragmentation by external force and is dispersed in hexanediyl ester, making it the suspended dispersion of a formation fine uniform structure.
Embodiment 2
Negative ion photo-cured coating, comprise the component of following weight part: formaldehyde-trapping agent 40kg, hexanediyl ester 25kg, photosensitizers 2kg, dispersion agent 0.5kg, nano-high molecule polymkeric substance modification agent 5kg, defoamer 0.1kg, organic silicon surfactant 0.2kg, multifunction negative ion filler 10kg, flatting silica 4kg.
Preparation technology is with embodiment 1.
Embodiment 3
Negative ion photo-cured coating, comprise the component of following weight part: formaldehyde-trapping agent 25kg, hexanediyl ester 40kg, photosensitizers 3.5kg, dispersion agent 1.3kg, nano-high molecule polymkeric substance modification agent 12kg, defoamer 0.25kg, organic silicon surfactant 0.35kg, multifunction negative ion filler 17kg, flatting silica 6kg..
Preparation technology is with embodiment 1.
Embodiment 4
Negative ion photo-cured coating, comprise the component of following weight part: formaldehyde-trapping agent 35kg, hexanediyl ester 30kg, photosensitizers 2.5kg, dispersion agent 0.7kg, nano-high molecule polymkeric substance modification agent 8kg, defoamer 0.15kg, organic silicon surfactant 0.25kg, multifunction negative ion filler 13kg, flatting silica 5kg.
Preparation technology is with embodiment 1.
Embodiment 5
Negative ion photo-cured coating, comprise the component of following weight part: formaldehyde-trapping agent 30kg, hexanediyl ester 35kg, photosensitizers 3kg, dispersion agent 1kg, nano-high molecule polymkeric substance modification agent 10kg, defoamer 0.2kg, organic silicon surfactant 0.3kg, multifunction negative ion filler 15kg, flatting silica 5.5kg.
Preparation technology is with embodiment 1.
The coating that above-mentioned 5 groups of embodiments are made is carried out comparative test, draws following result:
Sample ID | Test item | Unit | Detected result | Testing tool |
Reference examples | Negative ion burst size | Individual/cm 3 | 4500-5000 | AIC-2MJ |
Embodiment 1 | Negative ion burst size | Individual/cm 3 | 6000-7000 | AIC-2MJ |
Embodiment 2 | Negative ion burst size | Individual/cm 3 | 6200-7200 | AIC-2MJ |
Embodiment 3 | Negative ion burst size | Individual/cm 3 | 6100-7000 | AIC-2MJ |
Embodiment 4 | Negative ion burst size | Individual/cm 3 | 6300-7200 | AIC-2MJ |
Embodiment 5 | Negative ion burst size | Individual/cm 3 | 6500-7500 | AIC-2MJ |
Note: experimental situation: temperature (23 ± 2) DEG C; Humidity (65 ± 10) %RH.
The effect of the embodiment of the present invention is far superior to the test effect of reference examples.
In the present invention, each composition all can be buied from market, and concrete model sees the following form.
Claims (3)
1. negative ion photo-cured coating, it is characterized in that the component comprising following weight part: formaldehyde-trapping agent 20-40, hexanediyl ester 25-45, photosensitizers 2-4, dispersion agent 0.5-1.5, nano-high molecule polymkeric substance modification agent 5-15, defoamer 0.1-0.3, organic silicon surfactant 0.2-0.4, multifunction negative ion filler 10-20, flatting silica 4-7.
2. negative ion photo-cured coating according to claim 1, it is characterized in that the component comprising following weight part: formaldehyde-trapping agent 25-35, hexanediyl ester 30-40, photosensitizers 2.5-3.5, dispersion agent 0.7-1.3, nano-high molecule polymkeric substance modification agent 8-12, defoamer 0.15-0.25, organic silicon surfactant 0.25-0.35, multifunction negative ion filler 13-17, flatting silica 5-6.
3. negative ion photo-cured coating according to claim 1, it is characterized in that the component comprising following weight part: formaldehyde-trapping agent 30, hexanediyl ester 35, photosensitizers 3, dispersion agent 1, nano-high molecule polymkeric substance modification agent 10, defoamer 0.2, organic silicon surfactant 0.3, multifunction negative ion filler 15, flatting silica 5.5.