CN105350092A - 一种椰炭纤维面料的制作工艺 - Google Patents

一种椰炭纤维面料的制作工艺 Download PDF

Info

Publication number
CN105350092A
CN105350092A CN201510625187.9A CN201510625187A CN105350092A CN 105350092 A CN105350092 A CN 105350092A CN 201510625187 A CN201510625187 A CN 201510625187A CN 105350092 A CN105350092 A CN 105350092A
Authority
CN
China
Prior art keywords
coconut
coconut palm
palm carbon
fiber fabric
carbon fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510625187.9A
Other languages
English (en)
Inventor
刘雪明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang Xin Tai Knitting Co Ltd
Original Assignee
Taicang Xin Tai Knitting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang Xin Tai Knitting Co Ltd filed Critical Taicang Xin Tai Knitting Co Ltd
Priority to CN201510625187.9A priority Critical patent/CN105350092A/zh
Publication of CN105350092A publication Critical patent/CN105350092A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种椰炭纤维面料的制作工艺，包括以下步骤：（1）选取吃剩的椰子壳作为原料，对其进行浸泡、清洗，（2）将上述清洗后的椰子壳进行纤维与壳的分离，并将椰子纤维洗净，敲打膨松并晒干，（3）将上述椰子纤维进行高温炭化处理，得到椰炭粉末，（4）将上述椰炭粉末加入到熔融的聚酯中混合，得到功能性色母粒，（5）将上述色母粒与聚酯切片混合后纺丝，制得椰炭纤维面料。通过上述方式，本发明椰炭纤维面料的制作工艺简单便于操控，采用废弃的椰子壳做为原料，符合可循环使用资源的趋势，同时也具有吸湿除味、透气性好、吸附能力强、产生负离子、发射远红外线、防紫外线等功能。

Description

一种椰炭纤维面料的制作工艺
技术领域
本发明涉及纺织领域，特别是涉及一种椰炭纤维面料的制作工艺。
背景技术
椰子是我国南方热带地区的重要树种之一，当椰子的果肉和椰汁被取出加工为食品后，硕大的椰壳废弃将给环境治理带来不小的压力，若能将椰壳没的纤维提取并应用到纺织领域，不仅可减少椰壳废弃给环境带来的压力，而且还能提高自然资源利用。
发明内容
本发明主要解决的技术问题是提供一种吸湿除味、透气性好、吸附能力强的椰炭纤维面料的制作工艺。
为解决上述技术问题，本发明提供一种椰炭纤维面料的制作工艺，包括以下步骤：
（1）选取吃剩的椰子壳作为原料，对其进行浸泡、清洗，
（2）将上述清洗后的椰子壳进行纤维与壳的分离，并将椰子纤维洗净，敲打膨松并晒干，
（3）将上述椰子纤维进行高温炭化处理，得到椰炭粉末，
（4）将上述椰炭粉末加入到熔融的聚酯中混合，得到功能性色母粒，
（5）将上述色母粒与聚酯切片混合后纺丝，制得椰炭纤维面料。
在本发明一个较佳实施例中，所述椰子壳浸泡时长为15-20小时。
在本发明一个较佳实施例中，所述高温炭化温度控制在1100-1300摄氏度。
在本发明一个较佳实施例中，所述椰炭粉末的粒径为0.2-0.5微米。
在本发明一个较佳实施例中，所述色母粒中椰炭粉末的含量为3-5%，此含量为重量百分比。
本发明的有益效果是：本发明椰炭纤维面料的制作工艺简单便于操控，采用废弃的椰子壳做为原料，符合可循环使用资源的趋势，同时也具有吸湿除味、透气性好、吸附能力强、产生负离子、发射远红外线、防紫外线等功能。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
本发明实施例包括：
一种椰炭纤维面料的制作工艺，包括以下步骤：
（1）选取吃剩的椰子壳作为原料，对其进行浸泡、清洗，
（2）将上述清洗后的椰子壳进行纤维与壳的分离，并将椰子纤维洗净，敲打膨松并晒干，
（3）将上述椰子纤维进行高温炭化处理，得到椰炭粉末，
（4）将上述椰炭粉末加入到熔融的聚酯中混合，得到功能性色母粒，
（5）将上述色母粒与聚酯切片混合后纺丝，制得椰炭纤维面料。
另外，所述椰子壳浸泡时长为15-20小时。
另外，所述高温炭化温度控制在1100-1300摄氏度。
另外，所述椰炭粉末的粒径为0.2-0.5微米。
另外，所述色母粒中椰炭粉末的含量为3-5%，此含量为重量百分比。
区别于现有技术，本发明椰炭纤维面料的制作工艺简单便于操控，采用废弃的椰子壳做为原料，符合可循环使用资源的趋势，同时也具有吸湿除味、透气性好、吸附能力强、产生负离子、发射远红外线、防紫外线等功能。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (5)

1.一种椰炭纤维面料的制作工艺，其特征在于，包括以下步骤：
（1）选取吃剩的椰子壳作为原料，对其进行浸泡、清洗，
（2）将上述清洗后的椰子壳进行纤维与壳的分离，并将椰子纤维洗净，敲打膨松并晒干，
（3）将上述椰子纤维进行高温炭化处理，得到椰炭粉末，
（4）将上述椰炭粉末加入到熔融的聚酯中混合，得到功能性色母粒，
（5）将上述色母粒与聚酯切片混合后纺丝，制得椰炭纤维面料。
2.根据权利要求1所述的椰炭纤维面料的制作工艺，其特征在于，所述椰子壳浸泡时长为15-20小时。
3.根据权利要求1所述的椰炭纤维面料的制作工艺，其特征在于，所述高温炭化温度控制在1100-1300摄氏度。
4.根据权利要求1所述的椰炭纤维面料的制作工艺，其特征在于，所述椰炭粉末的粒径为0.2-0.5微米。
5.根据权利要求1所述的椰炭纤维面料的制作工艺，其特征在于，所述色母粒中椰炭粉末的含量为3-5%，此含量为重量百分比。
CN201510625187.9A 2015-09-28 2015-09-28 一种椰炭纤维面料的制作工艺 Pending CN105350092A (zh)