CN105348714A - 消光改性聚丙烯复合材料 - Google Patents
消光改性聚丙烯复合材料 Download PDFInfo
- Publication number
- CN105348714A CN105348714A CN201510843796.1A CN201510843796A CN105348714A CN 105348714 A CN105348714 A CN 105348714A CN 201510843796 A CN201510843796 A CN 201510843796A CN 105348714 A CN105348714 A CN 105348714A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermoplastic polyester
- composite material
- polyester elastomer
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种消光改性聚丙烯复合材料,包含共混的以下组分:以聚丙烯为100重量份数计,K树脂和热塑性聚酯弹性体共10-45份,其中K树脂与热塑性聚酯的重量比为2:0.5-1.5,无机纳米粉末5-15份,全硫化粉末硅橡胶10-15份,其他助剂1-10份,所述其他助剂包括润滑剂、增韧剂和抗氧剂。本发明的聚丙烯产品具有优异的力学性能,耐划痕性能也较好,不仅如此,本发明产品的消光性能突出,相对现有技术具有更低的光泽度。
Description
技术领域
本发明涉及一种消光改性聚丙烯复合材料,属于高分子材料技术领域。
背景技术
聚丙烯树脂具有良好的物性及成型性,其还具有耐化学腐蚀性好、无异味、无毒等优点,作为一种环境友好型的材料,其使用范围正在迅速扩大。特别是在家电和汽车工业。随着汽车行业的发展,人们对汽车内外装饰材料提出了更高的要求:轻型、节能、美观、安全、环保等,尤其对驾驶室内舒适性及的要求也越来越高。如果驾驶舱内饰件的光泽度较高,就会有较强的光线反射,从而造成驾驶员眼睛疲劳,影响驾驶的安全性。
围绕如何降低聚丙烯材料光泽度的问题,人们开展了许多研究工作。一种是在材料表面喷涂亚光漆,但这种方法成本较高,且使用过程中容易造成漆皮脱落,长时间后需要重新处理,不能满足人们要求,另一种是直接生产低光泽度的聚丙烯材料,目前使用较多的方法是在聚丙烯中添加无机材料,无机材料添加虽然能够降低材料光泽度,但大量的添加往往会劣化材料的力学性能,无机材料添加的少对于降低光泽度有没有效果;申请号为201110144142.1的中国专利在无机材料的基础上又添加了粉末丁腈橡胶,虽然保持了材料比较好的力学性能,但光泽度仍然较高,还不能满足一定需求。现仍需开发低光泽度力学性能良好的聚丙烯树脂。
发明内容
本发明要解决的技术问题是提供一种消光改性聚丙烯复合材料。
为解决上述技术问题,本发明采用的技术方案是:
一种消光改性聚丙烯复合材料,包含共混的以下组分:以聚丙烯为100重量份数计,K树脂和热塑性聚酯弹性体共10-45份,其中K树脂与热塑性聚酯的重量比为2:0.5-1.5,无机纳米粉末5-15份,全硫化粉末硅橡胶10-15份,其他助剂1-10份,所述其他助剂包括润滑剂、增韧剂和抗氧剂。
优选地,以聚丙烯为100重量份数计,所述K树脂和热塑性聚酯弹性体共30份,其中K树脂与热塑性聚酯的重量比为2:1,无机纳米粉末10份,全硫化粉末硅橡胶12份,其他助剂8份,所述其他助剂为润滑剂、增韧剂和抗氧剂。
优选地,所述热塑性聚酯弹性体由聚萘二甲酸丁二醇酯所形成的硬段、和非结晶性的聚醚或聚酯软段结合而成的热塑性聚酯弹性体。
优选地,所述无机纳米粉末粒度为100-500nm,所述无机纳米粉末选自二氧化硅、氧化铝,碳酸钙,铁氧体及氢氧化镁中的一种或多种。
优选地,所述全硫化粉末硅橡胶粒度为80-150nm,所述全硫化粉末硅橡胶的凝胶含量为65-80%。
优选地,所述聚丙烯为乙烯-丙烯嵌段共聚聚丙烯。
本发明所达到的有益效果:
本发明的聚丙烯产品具有优异的力学性能,耐划痕性能也较好,不仅如此,本发明产品的消光性能突出,相对现有技术具有更低的光泽度。
具体实施方式
下面结合具体实施例对本发明作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本实施例和对比例中所用原料均可从商业手段购买得到。
实施例一
先制备K树脂与热塑性聚酯弹性体的混合物,将质量比为2:1的K树脂与热塑性聚酯弹性体混合均匀,备用,
再将乙烯-丙烯嵌段共聚聚丙烯100份,以上制备的K树脂和热塑性聚酯弹性体混合物30份,100nm二氧化硅粉末10份,80nm全硫化粉末硅橡胶12份,其凝胶含量为70%,其他助剂8份共混搅拌均匀后,用双螺杆挤出机于200-250℃下造粒。
以上所称其他助剂包括润滑剂、增韧剂和抗氧剂;热塑性聚酯弹性体由聚萘二甲酸丁二醇酯所形成的硬段、和非结晶性的聚醚或聚酯软段结合而成的热塑性聚酯弹性体。
以上所得产品用注射机注射制样,进行消光性能、力学性能的测试和耐划痕性能测试,测试结果见表1。
实施例二
先制备K树脂与热塑性聚酯弹性体的混合物,将质量比为2:0.5的K树脂与热塑性聚酯弹性体混合均匀,备用,
再将乙烯-丙烯嵌段共聚聚丙烯100份,以上制备的K树脂和热塑性聚酯弹性体混合物45份,300nm氧化铝粉末5份,100nm全硫化粉末硅橡胶10份,其凝胶含量为65%,其他助剂5份共混搅拌均匀后,用双螺杆挤出机于200-250℃下造粒。
以上所称其他助剂包括润滑剂、增韧剂和抗氧剂;热塑性聚酯弹性体由聚萘二甲酸丁二醇酯所形成的硬段、和非结晶性的聚醚或聚酯软段结合而成的热塑性聚酯弹性体。
以上所得产品用注射机注射制样,进行消光性能、力学性能的测试和耐划痕性能测试,测试结果见表1。
实施例三
先制备K树脂与热塑性聚酯弹性体的混合物,将质量比为2:1.5的K树脂与热塑性聚酯弹性体混合均匀,备用,
再将乙烯-丙烯嵌段共聚聚丙烯100份,以上制备的K树脂和热塑性聚酯弹性体混合物12份,150nm氧化铝粉末15份,150nm全硫化粉末硅橡胶15份,其凝胶含量为80%,其他助剂3份共混搅拌均匀后,用双螺杆挤出机于200-250℃下造粒。
以上所称其他助剂包括润滑剂、增韧剂和抗氧剂;热塑性聚酯弹性体由聚萘二甲酸丁二醇酯所形成的硬段、和非结晶性的聚醚或聚酯软段结合而成的热塑性聚酯弹性体。
以上所得产品用注射机注射制样,进行消光性能、力学性能的测试和耐划痕性能测试,测试结果见表1。
对比例一
对比例一与实施例一的区别仅在于,用K树脂代替K树脂与热塑性聚酯弹性体的混合物。
将乙烯-丙烯嵌段共聚聚丙烯100份,K树脂30份,100nm二氧化硅粉末10份,80nm全硫化粉末硅橡胶12份,其凝胶含量为70%,其他助剂8份共混搅拌均匀后,用双螺杆挤出机于200-250℃下造粒。
以上所称其他助剂包括润滑剂、增韧剂和抗氧剂;热塑性聚酯弹性体由聚萘二甲酸丁二醇酯所形成的硬段、和非结晶性的聚醚或聚酯软段结合而成的热塑性聚酯弹性体。
以上所得产品用注射机注射制样,进行消光性能、力学性能的测试和耐划痕性能测试,测试结果见表1。
对比例二
对比例二与实施例一的区别仅在于,用热塑性聚酯弹性体代替K树脂与热塑性聚酯弹性体的混合物。
将乙烯-丙烯嵌段共聚聚丙烯100份,热塑性聚酯弹性体30份,100nm二氧化硅粉末10份,80nm全硫化粉末硅橡胶12份,其凝胶含量为70%,其他助剂8份共混搅拌均匀后,用双螺杆挤出机于200-250℃下造粒。
以上所称其他助剂包括润滑剂、增韧剂和抗氧剂;热塑性聚酯弹性体由聚萘二甲酸丁二醇酯所形成的硬段、和非结晶性的聚醚或聚酯软段结合而成的热塑性聚酯弹性体。
以上所得产品用注射机注射制样,进行消光性能、力学性能的测试和耐划痕性能测试,测试结果见表1。
对比例三
对比例三和实施例一的区别仅在于不使用K树脂与热塑性聚酯弹性体的混合物,同时将全硫化粉末硅橡胶的含量增至35份。
将乙烯-丙烯嵌段共聚聚丙烯100份,100nm二氧化硅粉末10份,80nm全硫化粉末硅橡胶35份,其凝胶含量为70%,其他助剂8份共混搅拌均匀后,用双螺杆挤出机于200-250℃下造粒。
以上所称其他助剂包括润滑剂、增韧剂和抗氧剂;热塑性聚酯弹性体由聚萘二甲酸丁二醇酯所形成的硬段、和非结晶性的聚醚或聚酯软段结合而成的热塑性聚酯弹性体。
以上所得产品用注射机注射制样,进行消光性能、力学性能的测试和耐划痕性能测试,测试结果见表1。
性能测试
以上所得产品用注射机注射制样,进行消光性能、力学性能的测试,测试结果见表1。
以上实施例和对比例的抗冲击性能测试按国际标准测试方法ISO179测试。光泽度测试角度为60°,测试标准为ISO2813,测试样片表面为皮纹面。
用划痕硬度测试仪进行耐划痕性能测试:注射成型样板尺寸150×100×3.2mm,负荷为10N,笔尖直径为1mm在样板表面进行划痕试验,划痕间隔2mm,纵向和横向各划20条线,记录材料的ΔL值,ΔL值越小表明耐划痕性能越好。测试结果见表1:
性能 | 实施例一 | 实施例二 | 实施例三 | 对比例一 | 对比例二 | 对比例三 |
光泽度(皮纹面) | 0.68 | 1.0 | 0.81 | 1.6 | 2.0 | 4.3 |
简支梁缺口冲击强度(KJ/m2 ,23℃) | 30.2 | 29.3 | 29.7 | 22.3 | 21.1 | 19.8 |
耐划痕性能△L | 0.3 | 0.7 | 0.5 | 0.9 | 1.3 | 1.7 |
由实施例和对比例可看出,本发明的聚丙烯产品具有优异的力学性能,耐划痕性能也较好,消光性能突出,相对现有技术具有更低的光泽度。
K树脂和热塑性聚酯弹性体综合影响聚丙烯材料的光泽度、力学性能和耐划痕性能,且在两者之间选择合适的比值能够使产品获得更好的综合性能。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和变形,这些改进和变形也应视为本发明的保护范围。
Claims (6)
1.一种消光改性聚丙烯复合材料,其特征在于,包含共混的以下组分:以聚丙烯为100重量份数计,K树脂和热塑性聚酯弹性体共10-45份,其中K树脂与热塑性聚酯的重量比为2:0.5-1.5,无机纳米粉末5-15份,全硫化粉末硅橡胶10-15份,其他助剂1-10份,所述其他助剂包括润滑剂、增韧剂和抗氧剂。
2.根据权利要求1所述的一种消光改性聚丙烯复合材料,其特征在于,以聚丙烯为100重量份数计,所述K树脂和热塑性聚酯弹性体共30份,其中K树脂与热塑性聚酯的重量比为2:1,无机纳米粉末10份,全硫化粉末硅橡胶12份,其他助剂8份,所述其他助剂为润滑剂、增韧剂和抗氧剂。
3.根据权利要求1或2所述的一种消光改性聚丙烯复合材料,其特征在于,所述热塑性聚酯弹性体由聚萘二甲酸丁二醇酯所形成的硬段、和非结晶性的聚醚或聚酯软段结合而成的热塑性聚酯弹性体。
4.根据权利要求3所述的一种消光改性聚丙烯复合材料,其特征在于,所述无机纳米粉末粒度为100-500nm,所述无机纳米粉末选自二氧化硅、氧化铝,碳酸钙,铁氧体及氢氧化镁中的一种或多种。
5.根据权利要求4所述的一种消光改性聚丙烯复合材料,其特征在于,所述全硫化粉末硅橡胶粒度为80-150nm,所述全硫化粉末硅橡胶的凝胶含量为65-80%。
6.根据权利要求1所述的一种消光改性聚丙烯复合材料,其特征在于,所述聚丙烯为乙烯-丙烯嵌段共聚聚丙烯。