CN105347753A - 一种机喷抹灰砂浆 - Google Patents

一种机喷抹灰砂浆 Download PDF

Info

Publication number
CN105347753A
CN105347753A CN201510689814.5A CN201510689814A CN105347753A CN 105347753 A CN105347753 A CN 105347753A CN 201510689814 A CN201510689814 A CN 201510689814A CN 105347753 A CN105347753 A CN 105347753A
Authority
CN
China
Prior art keywords
additive
flyash
cement
motar
sand
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510689814.5A
Other languages
English (en)
Other versions
CN105347753B (zh
Inventor
沈池清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Zhengchang New Material Co., Ltd
Original Assignee
TONGXIANG ZHENGCHANG NEW MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGXIANG ZHENGCHANG NEW MATERIAL CO Ltd filed Critical TONGXIANG ZHENGCHANG NEW MATERIAL CO Ltd
Priority to CN201510689814.5A priority Critical patent/CN105347753B/zh
Publication of CN105347753A publication Critical patent/CN105347753A/zh
Application granted granted Critical
Publication of CN105347753B publication Critical patent/CN105347753B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种机喷抹灰砂浆及添加剂，包括水泥、粉煤灰、砂和添加剂，所述水泥、粉煤灰、砂和添加剂的重量百分比如下：水泥10％～18％，粉煤灰5％～10％，砂75％～80％，添加剂0.5％，所述添加剂包括纤维素醚0.02％、蒙脱石粉0.01％、淀粉醚0.01％、减水剂0.05％、引气剂0.0035％、木质纤维0.1％。经优化抹灰砂浆配合比，掺入一定比例添加剂，使抹灰砂浆具有抗流挂性，较好的润滑性、保水性、流动性，较强的粘结力，达到抹灰砂浆机械泵送、喷涂施工的性能要求；降低了劳动强度、提高了施工效率，与人工抹灰相比工效提高二倍以上；墙体抹灰采用机械喷涂施工，压力大且均匀避免了抹灰层的空鼓、裂缝，提高了工程质量添加剂。

Description

一种机喷抹灰砂浆
技术领域：
本发明涉及预拌砂浆领域，具体涉及一种机喷抹灰砂浆。
背景技术：
在目前建筑使用的抹灰砂浆主要有二种：一种是工地现场自拌的抹灰砂浆，计量精度差，质量不稳定，容易造成空鼓、裂缝等质量事故；另一种是国家政策鼓励支持的工业化生产的预拌砂浆，计量精确、质量稳定，还具有利废环保等优点；但以上二种砂浆还有一个共同缺点：采用人工抹灰劳动强度大、施工效率低，还有使工质量造成的墙体质量隐患。抹灰砂浆鉴于以上缺陷开发一种满足泵送、机械喷涂性能的砂浆已刻不容缓。
发明内容：
本发明要解决的技术问题是，提供一种机喷抹灰砂浆，经优化抹灰砂浆配合比，掺入一定比例添加剂，使抹灰砂浆具有抗流挂性，较好的润滑性、保水性、流动性，较强的粘结力，达到抹灰砂浆机械泵送、喷涂施工的性能要求。
为解决上述技术问题，本发明提供一种机喷抹灰砂浆，包括水泥、粉煤灰、砂和添加剂，所述水泥、粉煤灰、砂和添加剂的重量百分比如下：水泥10％～18％，粉煤灰5％～10％，砂75％～80％，添加剂0.5％，所述添加剂包括纤维素醚0.02％、蒙脱石粉0.01％、淀粉醚0.01％、减水剂0.05％、引气剂0.0035％、木质纤维0.1％。
由于机械喷涂抹灰砂浆中添置加剂种类多、掺量少，在砂浆生产时设备配料精度要求难以达到，为便于生产控制，把以上添加剂复合，用粉煤灰为载体稀释放大，添加剂中各材料比例为纤维素醚:4.0％,蒙脱石粉:2.0％,淀粉醚:2.0％,减水剂:10.0％,引气剂:0.7％,木质纤维:20％,粉煤灰:61.3％，稀释放大后添加剂在砂浆中比例为0.5％。
作为优选，所述水泥选用强度等级42.5的普通硅酸盐水泥。普通硅酸盐水泥相比于复合水泥、火山灰水泥对添加剂的适应性较好。
进一步地，所述粉煤灰为二级粉煤灰。选用二级粉煤灰取代部分水泥，能减少砂浆用水量，提高和易性，降低水化热，减少收缩。
作为又一优选，所述砂为细度目数2.3～2.6的二区中砂，且最大粒径≦4.75㎜。
进一步低，所述添加剂中引气剂为三萜皂苷引气剂，减水剂为奈系高效减水剂。
上述添加剂的作用分别如下：纤维素醚：提高砂浆保水性、可操作性；蒙脱石粉：赋予砂浆触变润滑性、抗流挂性；淀粉醚：提高砂浆的抗流挂性、收光时的平滑性；减水剂：采用奈系高效减水剂，增加砂浆流动性,避免砂浆在高速流动过程中组份离析和堵泵；引气剂：使用三萜皂苷引气剂，在泵送、喷涂时砂浆与管壁之间产生滚珠轴承效应，减少阻力，使砂浆在管道中输送顺畅；木质纤维：提高砂浆的物理保水性，减少砂浆的塑性收缩裂缝。
本发明优点如下：经优化抹灰砂浆配合比，掺入一定比例添加剂，使抹灰砂浆具有抗流挂性，较好的润滑性、保水性、流动性，较强的粘结力，达到抹灰砂浆机械泵送、喷涂施工的性能要求；降低了劳动强度、提高了施工效率，与人工抹灰相比工效提高二倍以上；墙体抹灰采用机械喷涂施工，压力大且均匀避免了抹灰层的空鼓、裂缝，提高了工程质量添加剂。
具体实施方式
本发明提供一种机喷抹灰砂浆，包括水泥、粉煤灰、砂和添加剂，所述水泥、粉煤灰、砂和添加剂的重量百分比如下：水泥10％～18％，粉煤灰5％～10％，砂75％～80％，添加剂0.5％，所述添加剂包括纤维素醚0.02％、蒙脱石粉0.01％、淀粉醚0.01％、减水剂0.05％、引气剂0.0035％、木质纤维0.1％。所述添加剂的复合采用粉煤灰为载体稀释放大，添加剂中各材料比例为：纤维素醚:4.0％,蒙脱石粉:2.0％,淀粉醚:2.0％,减水剂:10.0％,引气剂:0.7％,木质纤维:20％,粉煤灰:61.3％，粉煤灰为载体稀释放大后添加剂在砂浆中比例为0.5％。
实施例1：该砂浆由以下重量百分比含量的组分组成：水泥10％、粉煤灰10％、砂79.5％、添加剂0.5％。
实施例2：该砂浆由以下重量百分比含量的组分组成：水泥13％、粉煤灰7.5％、砂79％、添加剂0.5％。
实施例3：该砂浆由以下重量百分比含量的组分组成：水泥15.5％、粉煤灰6％、砂78％、添加剂0.5％。
实施例4：该砂浆由以下重量百分比含量的组分组成：水泥18％、粉煤灰5％、砂76.5％、添加剂0.5％。
采用上述4个实施例的配比制成的机喷抹灰砂浆，其质量指标检测如表一所示。
质量指标 抗压强度mPa 抗拉强度mPa 保水率％ 2小时稠度损失率％ 密度㎏/m3
DPM5.0 ≥5.0 ≥0.2 ≥92 ≤10 1820～1880
DPM10 ≥10.0 ≥0.3 ≥92 ≤10 1820～1880
DPM15 ≥15.0 ≥0.3 ≥92 ≤10 1820～1880
DPM20 ≥20.0 ≥0.3 ≥92 ≤10 1820～1880

Claims (6)

1.一种机喷抹灰砂浆，其特征在于，包括水泥、粉煤灰、砂和添加剂，所述水泥、粉煤灰、砂和添加剂的重量百分比如下：水泥10％～18％，粉煤灰5％～10％，砂75％～80％，添加剂0.5％，所述添加剂包括纤维素醚0.02％、蒙脱石粉0.01％、淀粉醚0.01％、减水剂0.05％、引气剂0.0035％、木质纤维0.1％。
2.根据权利要求1所述的一种机喷抹灰砂浆，其特征在于，所述添加剂的复合采用粉煤灰为载体稀释放大，添加剂中各材料比例为：纤维素醚:4.0％,蒙脱石粉:2.0％,淀粉醚:2.0％,减水剂:10.0％,引气剂:0.7％,木质纤维:20％,粉煤灰:61.3％，粉煤灰为载体稀释放大后添加剂在砂浆中比例为0.5％。
3.根据权利要求1所述的一种机喷抹灰砂浆，其特征在于，所述水泥选用强度等级42.5的普通硅酸盐水泥。
4.根据权利要求1所述的一种机喷抹灰砂浆，其特征在于，所述粉煤灰为二级粉煤灰。
5.根据权利要求1所述的一种机喷抹灰砂浆，其特征在于，所述砂为细度目数2.3～2.6的二区中砂，且最大粒径≦4.75㎜。
6.根据权利要求1所述的一种机喷抹灰砂浆，其特征在于，所述添加剂中引气剂为三萜皂苷引气剂，减水剂为奈系高效减水剂。
CN201510689814.5A 2015-10-21 2015-10-21 一种机喷抹灰砂浆 Active CN105347753B (zh)