CN104276784B - 一种干混普通砂浆的防水稠化粉 - Google Patents

一种干混普通砂浆的防水稠化粉 Download PDF

Info

Publication number
CN104276784B
CN104276784B CN201410519898.3A CN201410519898A CN104276784B CN 104276784 B CN104276784 B CN 104276784B CN 201410519898 A CN201410519898 A CN 201410519898A CN 104276784 B CN104276784 B CN 104276784B
Authority
CN
China
Prior art keywords
parts
waterproof
densification powder
mortar
dry mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410519898.3A
Other languages
English (en)
Other versions
CN104276784A (zh
Inventor
袁为国
金卫土
元小琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hangzhou Tianxiang new building materials Limited by Share Ltd
Original Assignee
HANGZHOU TIANXIANG NEW BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANGZHOU TIANXIANG NEW BUILDING MATERIALS Co Ltd filed Critical HANGZHOU TIANXIANG NEW BUILDING MATERIALS Co Ltd
Priority to CN201410519898.3A priority Critical patent/CN104276784B/zh
Publication of CN104276784A publication Critical patent/CN104276784A/zh
Application granted granted Critical
Publication of CN104276784B publication Critical patent/CN104276784B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种用于干混普通砂浆的防水稠化粉，包括由以下组分及重量份数：改性纤维素醚5-7.5份、硬脂酸钠30-50份、高岭土200-300份、萘系减水剂5-10份、有机硅憎水剂10-20份、酒石酸5-8份、改性硅酸钠40-50份、UEA膨胀剂7-10份，总计为1000份，不足粉煤灰补足。该防水稠化粉添加了价格低廉的功能性外加剂，具有价格低廉、保水、增稠、增加强度、提高施工性能、与砂浆加水搅拌后具有填堵砂浆空隙作用，从而达到高抗渗性能。

Description

一种干混普通砂浆的防水稠化粉
技术领域
本发明涉及一种建筑材料领域，特别是涉及一种干混普通防水砂浆的外加剂，具体的说是一种干混普通防水砂浆的防水稠化粉。
背景技术
近年来，随着我国绿色建筑和建筑节能的发展，干混普通砂浆已成为建材领域新兴的干混材料之一，由于具有可机械化作业，人力成本低，生产效率高，环境污染小，性能良好、质量稳定等优点，已广泛应用于各种建筑工程。干混普通砂浆是指将干粉状的骨料(砂子)、胶凝材料、化学添加剂等均匀混合，通过计算机计量控制、机械化生产、产品可以散装运到现场，作业时只要按一定比例加水搅匀，即可直接使用的新型干粉类砂浆。
干混砂浆是从上世纪五十年代的欧洲建筑市场发展壮大起来的，如今在德国、奥地利、芬兰等国家将干混砂浆作为主要的砂浆材料，仅德国就有年产10万吨以上的工厂200余家，平均每五十万人就拥有一个干混砂浆生产企业。在亚洲，新加坡、日本、韩国、香港等地的干混砂浆发展也十分迅速，如香港建筑领域抹灰砂浆中超过三成是干混砂浆。我国自上世纪九十年代至今，干混砂浆发展已成燎原之势，尤其随着我国“十二五”建筑业专项规划和建筑节能专项规划发布以来，越来越多的地方政府强制推广应用干混砂浆。然而由于干混普通砂浆存在孔隙率较多，加上成本的制约聚合物添加剂加量较少，所以砂浆抗渗性能是一个较为难达到的一个要求。
发明内容
本发明的目的在于提供一种用于干混普通砂浆的防水稠化粉，该防水稠化粉添加了价格低廉的功能性外加剂，具有价格低廉、保水、增稠、增加强度、提高施工性能、与砂浆加水搅拌后具有填堵砂浆空隙作用，从而达到高抗渗性能。
为实现该发明目的，本发明所采用的技术方案是：一种干混普通砂浆的防水稠化粉，由以下组分及重量份数：
改性纤维素醚5-7.5份
硬脂酸钠30-50份
高岭土200-300份
萘系减水剂5-10份
有机硅憎水剂10-20份
酒石酸5-8份
改性硅酸钠40-50份
UEA膨胀剂v7-10份
总计为1000份，不足粉煤灰补足。
优选的，上述各组分及重量份数为：
改性纤维素醚5.5份
硬脂酸钠38份
高岭土220份
萘系减水剂7份
有机硅憎水剂13份
酒石酸7份
改性硅酸钠42份
UEA膨胀剂8份
粉煤灰659.5份
优选的，所述的改性纤维素醚为疏水化纤维素醚，其粘度为45000mPa.s～120000mPa.s；所述的高岭土为高岭土经过急剧升温至1000℃，再快速冷却至室温制得。
本发明的干混普通砂浆的防水稠化粉的制备是将各组分按所描述的重量份数称量后进行混合均匀即可。
本发明产品在干混砂浆中的应用，将该防水稠化粉与水泥、粉煤灰、黄砂等一起混合均匀即可。防水稠化粉与水泥、粉煤灰、黄砂的重量比为1～2：10～20：8～10：74～78。
本发明，稠化粉中的改性纤维素醚能增加产品的和易性，保水性及抗流挂性能，硬脂酸钠具有提高砂浆防水性能，高岭土能增加砂浆的密实度，提高施工性，减水剂能减少砂浆的空隙率，降低用水量，提高密实度，有机硅憎水剂能防止水分侵入，UEA膨胀剂能增加抗裂防水能力，本发明将酒石酸和硅酸钠同时应用到稠化粉，不仅调整了砂浆凝结时间而且硅酸钠水化后可生成硅酸，形成凝胶状物质，非常有效堵住砂浆的毛细孔，从而防止水分进入，从而达到高抗渗性能。
将本发明的稠化粉应用到干混砂浆中，不仅能简化干混砂浆的生产工艺过程，而且还能确保干混砂浆产品质量。且与传统保水增稠材料相比，本发明的稠化粉在经济性和技术参数上更优，其避免了传统材料不利于水泥砂浆早期强度的缺陷，因传统材料防水性能较差，难达到国家标准对普通防水砂浆的要求，并且施工性，和易性等较差；或者传统干混普通防水砂浆通过添加大量聚合物能达到标准要求，但这样增加了稠化粉的成本，一般建筑领域不轻易采用。
本发明的有益效果是：
1.本发明所制得的防水稠化粉，具有具有价格低廉、保水、增稠、增加强度、提高施工性能、与砂浆加水搅拌后具有填堵砂浆空隙等作用，从而达到抗渗性能；
2.储存期限长，使用方法简单，效果好，对环境无污染，有效提高干混砂浆的各项性能指标；
3.制备工艺简单，且能部分利用工业固体废弃物，价格低廉，经济效益和社会效益突出，具有良好的市场应用前景。
具体实施方式
为了使本领域的技术人员更好地理解本发明的技术方案，下面结合具体实施例对本发明作进一步的详细说明。
实施例1防水稠化粉的组成及配比以及制备
一种用于干混普通砂浆的防水稠化粉，其组分及重量份数为：改性纤维素醚5份、硬脂酸钠30份、高岭土200份、萘系减水剂7份、有机硅憎水剂13份、酒石酸7份、改性硅酸钠40份、UEA膨胀剂(7)，制备方法为将各组分按所述的重量份数进行混合即可。
实施例2防水稠化粉的组成及配比以及制备
一种用于干混普通砂浆的防水稠化粉，其组分及重量份数为：改性纤维素醚5.5份、硬脂酸钠38份、高岭土220份、萘系减水剂5份、有机硅憎水剂10份、酒石酸7份、改性硅酸钠42份、UEA膨胀剂(8)，制备方法为将各组分按所述的重量份数进行混合即可。
实施例3防水稠化粉的组成及配比以及制备
一种用于干混普通砂浆的防水稠化粉，其组分及重量份数为：改性纤维素醚7.5份、硬脂酸钠50份、高岭土300份、萘系减水剂10份、有机硅憎水剂20份、酒石酸8份、改性硅酸钠50份、UEA膨胀剂(10)，制备方法为将各组分按所述的重量份数进行混合即可。
实施例4将上述制得的防水稠化粉应用到干混砂浆(水泥、粉煤灰、黄砂)中，具体见表1：
表1
从该实施例可以看出，在干混砂浆中加入本发明的稠化粉，在稠度70-80mm的条件下，保水率提高到92％以上，2h稠度损失率下降到了10％以下，28天抗渗压力提高到0.8Mpa以上，拉伸粘结强度也提高到0.50Mpa以上，泌水情况较少。

Claims (6)

1.一种干混普通砂浆的防水稠化粉，其特征在于由以下组分组成，及其重量份数为：
疏水化纤维素醚5-7.5份
硬脂酸钠30-50份
高岭土200-300份
萘系减水剂5-10份
有机硅憎水剂10-20份
酒石酸5-8份
改性硅酸钠40-50份
UEA膨胀剂7-10份
总计为1000份，不足粉煤灰补足。
2.根据权利要求1所述的干混普通砂浆的防水稠化粉，其特征在于由以下组分组成，及其重量份数为：疏水化纤维素醚5.5份
硬脂酸钠38份
高岭土220份
萘系减水剂7份
有机硅憎水剂13份
酒石酸7份
改性硅酸钠42份
UEA膨胀剂8份
粉煤灰659.5份。
3.根据权利要求1或2所述的干混普通砂浆的防水稠化粉，其特征在于所述的疏水化纤维素醚的粘度为45000mPa.s～120000mPa.s。
4.根据权利要求1或2所述的干混普通砂浆的防水稠化粉，其特征在于所述的高岭土为高岭土经过急剧升温至1000℃，再快速冷却至室温制得。
5.根据权利要求1或2所述的干混普通砂浆的防水稠化粉，其特征在于将所述的防水稠化粉与水泥、粉煤灰、黄砂一起混合均匀即可。
6.根据权利要求5所述的干混普通砂浆的防水稠化粉，其特征在于所述的防水稠化粉与水泥、粉煤灰、黄砂的重量比为1～2：10～20：8～10：74～78。
CN201410519898.3A 2014-09-30 2014-09-30 一种干混普通砂浆的防水稠化粉 Active CN104276784B (zh)