CN1053432C - Porcelain with decorative color drawings and its production process - Google Patents
Porcelain with decorative color drawings and its production process Download PDFInfo
- Publication number
- CN1053432C CN1053432C CN94100766A CN94100766A CN1053432C CN 1053432 C CN1053432 C CN 1053432C CN 94100766 A CN94100766 A CN 94100766A CN 94100766 A CN94100766 A CN 94100766A CN 1053432 C CN1053432 C CN 1053432C
- Authority
- CN
- China
- Prior art keywords
- glaze
- fired
- low temperature
- color
- kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a colored drawing ceramic article decorated by planar net glaze, and a preparation method of the article. In the method, a base blank is fired at a temperature of 1300DEG C for 8 to 10 hours; after the base blank is cooled, colored glaze at medium and low temperature is uniformly smeared on the base blank, and the base blank with glaze is fired in a kiln for 3 to 4 hours; the fired base blank is taken out of the kiln after the temperature of the fired base blank is cooled to 100DEG C; different kinds of colored glaze at medium and low temperature are smeared on the areas with formed clefts; the base blank with new glaze is fired in the kiln for 2 to 3 hours, and the article of the present invention is obtained after the fired base blank is cooled. The technological ceramic article seems like that the article is wrapped by a colored net, and the ceramic article brings smooth hand feeling and stereo perception to people.
Description
What the present invention relates to is art ceramics product and preparation method thereof, particularly ceramic flat surface net-like pattern product and preparation method thereof.
The magnificent pretty ease of China's ornamental ceramics has unique traditional style.From mid-term the Tang Dynasty so far, decorate to the five colours by monochromatic colored drawing, the development kind is more various, has become the garden with hundreds of flowers of the painted decoration that flowers blooming like a piece of brocade at present.Colored drawing is broadly divided under glazed and over-glaze decoration, and under glazed is that colorant is plotted on the biscuit of unfired, and then hangs up that the layer of transparent glaze is fired to form, and makes pattern on the porcelain facing, colored drawing clear, bright.As bright eternally happy, Xuande blue and white decorative ceramics in period, have abundant colors and change, deep or light bloom, go deep into the tire bone, the effect of ink and wash is arranged.Famous for another example " under-glaze red " is to draw pattern and be fired into reducing flame under glaze with the material of painting of copper, and as the Chinese traditional ceramics kind that shows unique characteristics, the implicit and graceful color that is presented is impayable.Over-glaze decoration then is to carry out polychromy with the colorant glaze on burned ground-coat enamel, then fires to form.Foremost traditional decoration, powder enamel and the colour enamels of surely belonging to, it is ornamental very strong, particularly colour enamels is thin a kind of of worker the most in the colored drawing, pursuit be exquisite careful, magnificent gorgeous.
The present invention provides a kind of colored drawing and sintering technology, can when over-glaze decoration the different color glaze be embedded hacking in the line of ground-coat enamel, and become the ceramic product of plane net glaze.
The method that the present invention recommended is: end tire was fired under 1300 ℃ 8～10 hours, cooling back with in, low temperature ground-coat enamel (can be any color) evenly coats, go into kiln in, fired 3～4 hours under the temperature of low temperature glaze requirement, be cooled to 100 ℃ of kiln discharges, the surface forms crackle naturally, cracks be coated be different from the ground-coat enamel color in, low temperature glaze, kiln-firing is 2～4 hours again, cooling promptly gets plane net glaze ceramic product.Employed two kinds of glaze all are the glaze that flow.Its plane of this plane net glaze product is smooth, and integral body resembles pottery and wraps with a bright net look, sight very attractive in appearance.Particularly can streakline very thick, its color can be selected arbitrarily.
Characteristics of the present invention are: (1) decorates webbed ceramics with color glaze is attractive in appearance and have the new meaning product, but particularly the net of any color all colored drawing and firing form, opening white net glaze as red line is the decorative porcelain that had not had so far.(2) sintering technology uniqueness, utilize fire, crackle appears hacking in process of cooling, inlays, infiltrates method in the ground-coat enamel with color glaze--in particularly using, cryogenic mobile glaze--makes feel smoothly and stereo netted glaze porcelain product are arranged.
Example 1
Behind the plain tire porcelain vase of making, it is gone into kiln, fired cooling, taking-up 8 hours in 1300 ℃, middle temperature white glaze brushing glazing with 1000 ℃, in 1000 ℃ of kilns, fired 4 hours, be cooled to 100 ℃ of kiln discharges, aging crack occurs, cracks with 1000 ℃ in warm red glaze along the line glazing, reenter kiln and under 1000 ℃, fired 2 hours, the cooling kiln discharge, the painted decoration pottery of the red net of white background.
Example 2
Sintering technology such as example 1, and be ground-coat enamel sky blue low temperature color glaze, and the cracks glazing is light brown low temperature color glaze, all fires under 800 ℃.Product is the light brown net of sky blue bottle.
Claims (2)
1, a kind of pottery with plane net glaze is characterized in that this ceramic surface is wrapped in another color by the netting twine of any color and hacks glaze, and its surfacing is smooth; This pottery is made by following process: on biscuit, the low temperature color glaze that flows, fired it is hacked, again the streakline place coat arbitrary color in, low temperature color glaze, fire once more.
2, a kind of making method with plane net glaze pottery, it is characterized in that biscuit burnt 8～10 hours down at 1300 ℃, cooling back with in any color, low temperature flows on the glaze to base, go into kiln in, burnt 3～4 hours under the temperature of low temperature glaze requirement, be cooled to 100 ℃ of kiln discharges, the surface is the formation crackle naturally, in cracks is coated with different colours, low temperature glaze, kiln-firing is 2～4 hours again, cooling.