CN105295784A - 丙烯酸胶粘剂及其制备工艺 - Google Patents
丙烯酸胶粘剂及其制备工艺 Download PDFInfo
- Publication number
- CN105295784A CN105295784A CN201510733031.2A CN201510733031A CN105295784A CN 105295784 A CN105295784 A CN 105295784A CN 201510733031 A CN201510733031 A CN 201510733031A CN 105295784 A CN105295784 A CN 105295784A
- Authority
- CN
- China
- Prior art keywords
- adhesive
- acrylic acid
- acrylate
- vinyl acetate
- toluene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种丙烯酸胶粘剂及其制备工艺，其中丙烯酸胶粘剂包括反应釜胶粘剂配方以及滴加胶粘剂配方，丙烯酸异辛酯10～25g，丙烯酸正丁酯0～8g，醋酸乙烯酯2～10g，丙烯酸0.2～0.3g，丙烯酸羟乙酯0.2～0.3g，滴加胶粘剂配方包括丙烯酸异辛酯40～70g，丙烯酸正丁酯0～30g，醋酸乙烯酯0～10g，丙烯酸0.6～1g，丙烯酸羟乙酯0.6～1g。本发明通过改进了普通丙烯酸胶粘剂的配方以及制备工艺，使得制备得到的丙烯酸胶粘剂具备优良的结合力，在使用过程中不会与纸张分离。
Description
技术领域
本发明涉及胶粘剂及胶粘剂制品领域，尤其涉及一种丙烯酸胶粘剂及其制备工艺。
背景技术
丙烯酸酯胶黏剂原材料来源广泛，制备工艺简单，具有干燥成型迅速，透明性好，对多种材料具有良好的黏结性能，且耐候性、耐水性、耐化学药品性亦佳。特别是对疏水表面材料也具有优良的黏结性，此橡胶类胶黏剂的耐大气老化性能更优良，使用方便，粘接接头耐久性良好。
目前市场上普通的丙烯酸酯类胶水，本身就具备非常好的可转移性以及耐高温不残胶的优点，是常用的性能优良的保护用胶水。此类胶水的合成步骤一般如下：①反应釜中加入甲苯、乙酸乙酯、单体和初始过氧化苯甲酰加热至回流；②在2.5Hr内逐渐加入第一批过氧化苯甲酰引发剂和乙酸乙酯溶液；③滴完后继续保温反应2Hr；④在0.5Hr内均匀滴加第二批过氧化苯甲酰引发剂和乙酸乙酯溶液；⑤继续保温反应1.5Hr后降温至50℃；⑥根据用户需要加入稀释溶剂、特殊树脂，降温至40℃出料。
但是此类普通的丙烯酸酯胶水与纸张的结合力还有待提高，因此，无论是在胶水配方还是制备工艺上都需要进行改进来改变现有技术中的不足。
发明内容
本发明的目的在于提供一种丙烯酸胶粘剂及其制备工艺，所述丙烯酸胶粘剂对纸类基材具备优良的粘结力。
为实现上述发明目的，本发明提供了：
一种丙烯酸胶粘剂，包括反应釜胶粘剂配方以及滴加胶粘剂配方，反应釜胶粘剂配方包括以下成分
丙烯酸异辛酯10～25g
丙烯酸正丁酯0～8g
醋酸乙烯酯2～10g
丙烯酸0.2～0.3g
丙烯酸羟乙酯0.2～0.3g
滴加胶粘剂配方包括
丙烯酸异辛酯40～70g
丙烯酸正丁酯0～30g
醋酸乙烯酯0～10g
丙烯酸0.6～1g
丙烯酸羟乙酯0.6～1g。
作为本发明的进一步改进，所述反应釜配方还包括
乙酸乙酯30～50g
甲苯0～10g
过氧化苯甲酰0.05～0.1g。
作为本发明的进一步改进，所述滴加配方还包括
乙酸乙酯35～60g
甲苯10～40g
过氧化苯甲酰0.4～0.9g。
作为本发明的进一步改进，所述丙烯酸异辛酯、丙烯酸正丁酯、醋酸乙烯酯、丙烯酸、丙烯酸羟乙酯均为工业级标准。
一种丙烯酸胶粘剂的制备工艺，包括以下步骤
a、在反应釜中加入10-25g丙烯酸异辛酯、0-8g丙烯酸正丁酯、2-10g醋酸乙烯酯、0.2-0.3g丙烯酸、0.2-0.3g丙烯酸羟乙酯，30-50g乙酸乙酯、甲苯，然后升温至80～85℃，再加入0.05-0.1g过氧化苯甲酰，充分搅拌直至有回流；
b、在2.5小时内均匀滴加40-70g丙烯酸异辛酯、0-30g丙烯酸正丁酯、醋酸乙烯酯、0-10g醋酸乙烯酯、0.6-1.0g丙烯酸、0.6-1.0g丙烯酸羟乙酯，30-40g乙酸乙酯、0-10g甲苯、0.3-0.6g过氧化苯甲酰，均匀搅拌形成聚合物，滴加完毕后保持温度继续反应2小时；
c、在0.5小时内均匀滴加含有5-20g乙酸乙酯、10-30g甲苯、0.1-0.3g过氧化苯甲酰的溶液，滴加完毕后保持温度继续反应1.5小时，然后降温至50℃，即制得所述丙烯酸胶粘剂。
与现有技术相比，本发明的有益效果是：
本发明提供了一种丙烯酸胶粘剂及其制备工艺，其通过改进了普通丙烯酸胶粘剂的配方以及制备工艺，使得制备得到的丙烯酸胶粘剂具备优良的结合力，在使用过程中不会与纸张分离。
具体实施方式
下面通过具体实施方式来对本发明进行进一步的阐述：
本实施方式提供了一种丙烯酸胶粘剂，包括反应釜胶粘剂配方以及滴加胶粘剂配方，反应釜胶粘剂配方包括以下成分
丙烯酸异辛酯10～25g
丙烯酸正丁酯0～8g
醋酸乙烯酯2～10g
丙烯酸0.2～0.3g
丙烯酸羟乙酯0.2～0.3g
滴加胶粘剂配方包括
丙烯酸异辛酯40～70g
丙烯酸正丁酯0～30g
醋酸乙烯酯0～10g
丙烯酸0.6～1g
丙烯酸羟乙酯0.6～1g。
所述反应釜配方还包括
乙酸乙酯30～50g
甲苯0～10g
过氧化苯甲酰0.05～0.1g。
所述滴加配方还包括
乙酸乙酯35～60g
甲苯10～40g
过氧化苯甲酰0.4～0.9g。
所述丙烯酸异辛酯、丙烯酸正丁酯、醋酸乙烯酯、丙烯酸、丙烯酸羟乙酯均为工业级标准。
本实施方式还提供了一种丙烯酸胶粘剂的制备工艺，包括以下步骤
a、在反应釜中加入10-25g丙烯酸异辛酯、0-8g丙烯酸正丁酯、2-10g醋酸乙烯酯、0.2-0.3g丙烯酸、0.2-0.3g丙烯酸羟乙酯，30-50g乙酸乙酯、0-10g甲苯，然后升温至80～85℃，再加入0.05-0.1g过氧化苯甲酰，充分搅拌直至有回流；
b、在2.5小时内均匀滴加40-70g丙烯酸异辛酯、0-30g丙烯酸正丁酯、醋酸乙烯酯、0-10g醋酸乙烯酯、0.6-1.0g丙烯酸、0.6-1.0g丙烯酸羟乙酯，30-40g乙酸乙酯、0-10g甲苯、0.3-0.6g过氧化苯甲酰，均匀搅拌形成聚合物，滴加完毕后保持温度继续反应2小时；
c、在0.5小时内均匀滴加含有5-20g乙酸乙酯、10-30g甲苯、0.1-0.3g过氧化苯甲酰的溶液，滴加完毕后保持温度继续反应1.5小时，然后降温至50℃，即制得所述丙烯酸胶粘剂。
验证实施例：
1、按照本发明制备工艺制备10组不同配比的丙烯酸胶粘剂，并取1组现有技术中普通丙烯酸胶粘剂，作为测试样品，其中10组丙烯酸胶粘剂具体配比成分如表1和表2所示。
表1丙烯酸胶粘剂测试样品-反应釜胶粘剂配方(单位g)
表2丙烯酸胶粘剂测试样品-滴加胶粘剂配方(单位g)
2、测试具体步骤
本测试方法采用对贴拉丝实验，通过将待测胶带的胶水面两两对贴，观察胶水面是否有移位来判断粘结性能。
本测试中包括了同款对贴和异款对贴两个实验。
同款对贴实验
将10组不同配比的丙烯酸胶粘剂制备成纸类胶带，然后将每一款纸类胶带取两块大小相同的纸类胶带进行对贴，对贴次数超过50次之后，发现胶面均无出现位移，由此可以判断，本发明中制备的丙烯酸胶粘剂适合应用于纸类。
异款对贴实验
将10组不同配比的丙烯酸胶粘剂以及现有技术中普通丙烯酸胶粘剂制备成纸类胶带，然后将每一款通过本发明制备的纸类胶带和现有技术制备的纸类胶带进行对贴，对贴20次之后，现有技术制备的纸类胶带的胶面逐一出现了脱落、移位等现象，由此可以得知，本发明制备的丙烯酸胶粘剂与纸类具备更加优良的粘结力。
应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施方式中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
上文所列出的一系列的详细说明仅仅是针对本发明的可行性实施方式的具体说明，它们并非用以限制本发明的保护范围，凡未脱离本发明技艺精神所作的等效实施方式或变更均应包含在本发明的保护范围之内。
Claims (5)
1.一种丙烯酸胶粘剂，包括反应釜胶粘剂配方以及滴加胶粘剂配方，其特征在于：反应釜胶粘剂配方包括以下成分
丙烯酸异辛酯10～25g
丙烯酸正丁酯0～8g
醋酸乙烯酯2～10g
丙烯酸0.2～0.3g
丙烯酸羟乙酯0.2～0.3g
滴加胶粘剂配方包括
丙烯酸异辛酯40～70g
丙烯酸正丁酯0～30g
醋酸乙烯酯0～10g
丙烯酸0.6～1g
丙烯酸羟乙酯0.6～1g。
2.根据权利要求1所述的丙烯酸胶粘剂，其特征在于：所述反应釜配方还包括
乙酸乙酯30～50g
甲苯0～10g
过氧化苯甲酰0.05～0.1g。
3.根据权利要求1所述的丙烯酸胶粘剂，其特征在于：所述滴加配方还包括
乙酸乙酯35～60g
甲苯10～40g
过氧化苯甲酰0.4～0.9g。
4.根据权利要求1所述的丙烯酸胶粘剂，其特征在于：所述丙烯酸异辛酯、丙烯酸正丁酯、醋酸乙烯酯、丙烯酸、丙烯酸羟乙酯均为工业级标准。
5.一种丙烯酸胶粘剂的制备工艺，其特征在于：包括以下步骤
a、在反应釜中加入10-25g丙烯酸异辛酯、0-8g丙烯酸正丁酯、2-10g醋酸乙烯酯、0.2-0.3g丙烯酸、0.2-0.3g丙烯酸羟乙酯，30-50g乙酸乙酯、0-10g甲苯，然后升温至80～85℃，再加入0.05-0.1g过氧化苯甲酰，充分搅拌直至有回流；
b、在2.5小时内均匀滴加40-70g丙烯酸异辛酯、0-30g丙烯酸正丁酯、0-10g醋酸乙烯酯、0.6-1.0g丙烯酸、0.6-1.0g丙烯酸羟乙酯，30-40g乙酸乙酯、0-10g甲苯、0.3-0.6g过氧化苯甲酰，均匀搅拌形成聚合物，滴加完毕后保持温度继续反应2小时；
c、在0.5小时内均匀滴加含有5-20g乙酸乙酯、10-30g甲苯、0.1-0.3g过氧化苯甲酰的溶液，滴加完毕后保持温度继续反应1.5小时，然后降温至50℃，即制得所述丙烯酸胶粘剂。