CN105293551A - 一种优级纯硫酸铝的制备方法 - Google Patents
一种优级纯硫酸铝的制备方法 Download PDFInfo
- Publication number
- CN105293551A CN105293551A CN201410290694.7A CN201410290694A CN105293551A CN 105293551 A CN105293551 A CN 105293551A CN 201410290694 A CN201410290694 A CN 201410290694A CN 105293551 A CN105293551 A CN 105293551A
- Authority
- CN
- China
- Prior art keywords
- preparation
- aluminum sulfate
- guaranteed reagent
- temperature
- alumina
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种优级纯硫酸铝的制备方法,方法如下:⑴将纯铝粉,置于小白瓷罐内,慢慢加入10%的稀硫酸,反应温度控制在75℃,当pH=8时停止加酸,加热保温5小时,并不断补充蒸馏水,得到滤液A,⑵将步骤1得到得溶液A进行过滤浓缩小体积,浓缩温度280℃,浓缩至21°Be,停止浓缩,冷却结晶,干燥80℃,制得优级纯硫酸铝。本发明涉及制备的方法为纯铝粉与稀硫酸反应,经过滤,生成优级纯硫酸铝,步骤中不含有高温高压等反应,操作步骤容易控制,工艺技术先进,生产效率高。
Description
技术领域
本发明属于无机化合物制备方法领域,尤其是一种优级纯硫酸铝的制备方法。
背景技术
优级纯硫酸铝用途非常广泛,医药的收敛剂,显像器生产,故有造纸明矾之称。油脂的澄清剂等。目前采用的方法,氢氧化铝与硫酸反应,制得硫酸铝成品,该方法制得的硫酸铝纯度低,杂质含量高,只能用于印染的抗碱剂等,不能满足高端科技的需要。
发明内容
本发明的目的在于克服现有技术的不足,提供一种产品杂质含量低、纯度高的优级纯硫酸铝的制备方法。
本发明实现的目的技术方案是:
一种优级纯硫酸铝的制备方法,方法如下:
⑴将纯铝粉,置于小白瓷罐内,慢慢加入10%的稀硫酸,反应温度控制在75℃,当pH=8时停止加酸,加热保温5小时,并不断补充蒸馏水,得到滤液A;
⑵将步骤1得到得溶液A进行过滤浓缩小体积,浓缩温度280℃,浓缩至21°Be,停止浓缩,冷却结晶,干燥80℃,制得优级纯硫酸铝。
本发明的优点和有益效果为:
1、本发明涉及制备的方法为纯铝粉与稀硫酸反应,经过滤,生成优级纯硫酸铝,步骤中不含有高温高压等反应,操作步骤容易控制,工艺技术先进,生产效率高。
2、本发明提高的优级纯硫酸铝的制备方法工艺步骤简单,制得的优级纯硫酸铝纯度高,杂质含量低,满足市场的需求。
具体实施方式
以下结合实施例做进一步详述,以下实施例只是描述性的,不是限定性的,不能以此限定本发明的保护范围。
实施例1:
一种优级纯硫酸铝的制备方法,方法如下:
⑴将纯铝粉1kg,置于小白瓷罐内,慢慢加入10%的稀硫酸,反应温度控制在75℃,当PH=8时停止加酸,加热保温5小时,并不断补充蒸馏水,得到滤液A;
⑵将步骤1得到得溶液A进行过滤浓缩小体积,浓缩温度280℃,浓缩至21°Be,停止浓缩,冷却结晶,干燥80℃,制得优级纯硫酸铝。
实施例2:
一种优级纯硫酸铝的制备方法,方法如下:
⑴将纯铝粉1.5kg,置于小白瓷罐内,慢慢加入10%的稀硫酸,反应温度控制在70℃,当PH=7.5时停止加酸,加热保温4小时,并不断补充蒸馏水,得到滤液A;
⑵将步骤1得到得溶液A进行过滤浓缩小体积,浓缩温度275℃,浓缩至22°Be,停止浓缩,冷却结晶,干燥85℃,制得优级纯硫酸铝。
Claims (1)
1.一种优级纯硫酸铝的制备方法,其特征在于:方法如下:
⑴将纯铝粉,置于小白瓷罐内,慢慢加入10%的稀硫酸,反应温度控制在75℃,当pH=8时停止加酸,加热保温5小时,并不断补充蒸馏水,得到滤液A;
⑵将步骤1得到得溶液A进行过滤浓缩小体积,浓缩温度280℃,浓缩至21°Be,停止浓缩,冷却结晶,干燥80℃,制得优级纯硫酸铝。