CN105271945A - 一种人造花岗石及制备方法 - Google Patents

一种人造花岗石及制备方法 Download PDF

Info

Publication number
CN105271945A
CN105271945A CN201510627978.5A CN201510627978A CN105271945A CN 105271945 A CN105271945 A CN 105271945A CN 201510627978 A CN201510627978 A CN 201510627978A CN 105271945 A CN105271945 A CN 105271945A
Authority
CN
China
Prior art keywords
grain
stone
stonite
granite
rubble
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510627978.5A
Other languages
English (en)
Inventor
李剑锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Zhongshan Zhongyuan Stone Co Ltd
Original Assignee
Guangxi Zhongshan Zhongyuan Stone Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Zhongshan Zhongyuan Stone Co Ltd filed Critical Guangxi Zhongshan Zhongyuan Stone Co Ltd
Priority to CN201510627978.5A priority Critical patent/CN105271945A/zh
Publication of CN105271945A publication Critical patent/CN105271945A/zh
Pending legal-status Critical Current

Abstract

本发明涉及建筑材料领域,具体为一种人造花岗石及制备方法,本发明的特征在于,该人造花岗石采用如下原料制成(按重量百分比计):碎石粒70%-75%,碎玻璃3%-4%,5%-10%炉灰渣子,不饱和树脂14%,过氧化环已酮糊2%,环烷酸钴1%;本发明构造均匀,可塑性强,比天然花岗石具有更好的成形机制,可以更方便的制造出人们需要的各种型材,还可以作良好的建筑材料或者用于石材雕刻;比天然花岗石具有更高的韧性和抗冲击性,比天然花岗石具有更高的抗水和抗腐蚀性;不具有天然花岗石的放射性,符合现代人的绿色环保意识。

Description

一种人造花岗石及制备方法
技术领域
本发明涉及建筑材料领域,具体为一种人造花岗石及制备方法。
背景技术
花岗石是一种由火山爆发的熔岩在受到相当的压力熔融状态下隆起至地壳表层,岩浆不喷出地面,而在地底下慢慢冷却凝固形成的构造岩,是一种深成酸性火成岩,花岗石以石英、长石和云母为主要成分,其中长石含量为40-60%,石英含量为20-0%,其颜色决定于所含成分的种类和数量,花岗石结构致密,抗压强度高,吸水率低,表面硬度大,化学稳定性好,耐久性强,间隙小,吸水率不高,有良好的抗冻性能,是良好的建筑材料,但其开采和加工成本较高,石材内还含有有害放射性元素,为了扬长避短,人们研制出了物质性质比天然花岗更佳,且表面“绘”有图形的人造花岗石。
人造花岗石节能环保,不含放射性物质,它是采用天然大理石碎块、钙粉为主要原料,使用粘合剂经抽真空、常温、高压、震动、浇注而成,色彩图案自然均匀、结构耐密耐磨性强、抗压、抗拆强度高。吸水率低等特点,弥补了天然石材色差、孔洞、裂隙、裂纹、吸水率高等缺陷。
发明内容
本发明的目的是提供一种人造花岗石及制备方法。
本发明采用以下技术方案:
一种人造花岗石,其特征在于,该人造花岗石采用如下原料制成(按重量百分比计):碎石粒70%-75%,碎玻璃3%-4%,5%-10%炉灰渣子,不饱和树脂14%,过氧化环已酮糊2%,环烷酸钴1%。
作为本发明的一种优选,一种人造花岗石,其原料重量百分比为:碎石粒75%,碎玻璃3%,炉灰渣子5%,不饱和树脂14%,过氧化环已酮糊2%,环烷酸钴1%。
所述碎石粒为沉积岩石粒,变质岩石粒,氟石粒,芙蓉石粒,木化石粒,黑云母片石粒,鱼鳞石粒,腊石粒,英石粒,菊花石粒,户县石粒,龟纹石粒,吴壁石粒,昆山石粒,宣石粒,砂片石粒,千层石粒或鹅卵石粒中的一种或多种。
一种人造花岗石的制备方法,其特征在于,先将原料按重量比称重,将碎石粒,碎玻璃和炉灰渣子磨成粉末状,末粒越细越好,之后将细末状的碎石粒,碎玻璃和炉灰渣子混合均匀,加入固化剂不饱和树脂,交联剂过氧化环已酮糊和促进剂环烷酸钴,加适量水,搅拌混合均匀,最后上模具高压成型。
需要说明的是人造花岗石根据不同原料的选择,制备时会出现不同的色彩,下面为本发明人列举的一些选取不同原料制备人造花岗石时可能出现的色彩表现。
选用氟石作为主要原料制备人造花岗石可使花岗石呈现黄、绿、蓝、紫色彩;选用芙蓉石作为主要原理制备人造花岗石可使花岗石呈现玫瑰色、浅红色和白色;选用木化石作为主要原料制备人造虎岗石可使花岗石呈现灰色、黄褐色、褐色和黑色;选用蜡石作为主要原料制备人造花岗石可使花岗石呈现黄色、浅黄色和白色;选用鱼鳞石作为主要原料制备人造花岗石可使花岗石呈现青灰、青绿、黄红以及多色相杂;选用菊花石作为主要原料制备人造花岗石可使花岗石在白色、灰色或暗紫色上呈现有菊花形的花纹。
本发明的有益效果:
1、主要原料采用天然岩石粒,外观上和天然石材相似,质感好。
2、构造均匀,可塑性强,比天然花岗石具有更好的成形机制,可以更方便的制造出人们需要的各种型材,还可以作良好的建筑材料或者用于石材雕刻。
3、比天然花岗石具有更高的韧性和抗冲击性,比天然花岗石具有更高的抗水和抗腐蚀性。
4、导热系数更低,因此人造花岗石在冬天手感不冰,夏天手感不烫。
5、不具有天然花岗石的放射性,符合现代人的绿色环保意识。
具体实施方式
本发明创造了一种人造花岗石及制备方法,本发明创造的人造花岗石构造均匀,可塑性强,比天然花岗石具有更好的成形机制,可以更方便的制造出人们需要的各种型材,而且比天然花岗石具有更高的韧性和抗冲击性,比天然花岗石具有更高的抗水和抗腐蚀性,更符合现代人的审美追求和环保意识。
一种人造花岗石,其特征在于,该人造花岗石采用如下原料制成(按重量百分比计):碎石粒70%-75%,碎玻璃3%-4%,5%-10%炉灰渣子,不饱和树脂14%,过氧化环已酮糊2%,环烷酸钴1%。
作为本发明的一种优选,一种人造花岗石,其原料重量百分比为:碎石粒75%,碎玻璃3%,炉灰渣子5%,不饱和树脂14%,过氧化环已酮糊2%,环烷酸钴1%。
所述碎石粒为沉积岩石粒,变质岩石粒,氟石粒,芙蓉石粒,木化石粒,黑云母片石粒,鱼鳞石粒,腊石粒,英石粒,菊花石粒,户县石粒,龟纹石粒,吴壁石粒,昆山石粒,宣石粒,砂片石粒,千层石粒或鹅卵石粒中的一种或多种。
一种人造花岗石的制备方法,其特征在于,先将原料按重量比称重,将碎石粒,碎玻璃和炉灰渣子磨成粉末状,末粒越细越好,之后将细末状的碎石粒,碎玻璃和炉灰渣子混合均匀,加入固化剂不饱和树脂,交联剂过氧化环已酮糊和促进剂环烷酸钴,加适量水,搅拌混合均匀,最后上模具高压成型。
需要说明的是人造花岗石根据不同原料的选择,制备时会出现不同的色彩,下面为本发明人列举的一些选取不同原料制备人造花岗石时可能出现的色彩表现。
选用氟石作为主要原料制备人造花岗石可使花岗石呈现黄、绿、蓝、紫色彩;选用芙蓉石作为主要原理制备人造花岗石可使花岗石呈现玫瑰色、浅红色和白色;选用木化石作为主要原料制备人造虎岗石可使花岗石呈现灰色、黄褐色、褐色和黑色;选用蜡石作为主要原料制备人造花岗石可使花岗石呈现黄色、浅黄色和白色;选用鱼鳞石作为主要原料制备人造花岗石可使花岗石呈现青灰、青绿、黄红以及多色相杂;选用菊花石作为主要原料制备人造花岗石可使花岗石在白色、灰色或暗紫色上呈现有菊花形的花纹。
实施例
一种人造花岗石,该人造花岗石采用如下原料制成(重量按100kg计):碎石粒72kg,碎玻璃3kg,炉灰渣子8kg,不饱和树脂14kg,过氧化环已酮糊2kg,环烷酸钴1kg。
本实施例所述的碎石粒为氟石粒,芙蓉石粒,英石粒,菊花石粒,户县石粒,龟纹石粒和砂片石粒七种岩石碎粒的混合。
一种人造花岗石的制备方法,将氟石粒,芙蓉石粒,英石粒,菊花石粒,户县石粒,龟纹石粒和砂片石粒七种岩石碎粒称重72kg,碎玻璃称重3kg,炉灰渣子称重8kg,将碎石粒,碎玻璃和炉灰渣子磨成至精细粉末状,将细末状的碎石粒,碎玻璃和炉灰渣子混合均匀,加入固化剂不饱和树脂14kg,交联剂过氧化环已酮糊2kg和促进剂环烷酸钴1kg,加适量水,搅拌混合均匀,最后上模具高压成型。
最后说明的是,以上实施例仅用以说明本发明的技术方案而非限制,本领域普通技术人员对本发明的技术方案所做的其他修改或者等同替换,只要不脱离本发明技术方案的精神和范围,均应涵盖在本发明的权利要求范围当中。

Claims (4)

1.一种人造花岗石,其特征在于,所述人造花岗石采用如下原料制成(按重量百分比计):碎石粒70%-75%,碎玻璃3%-4%,5%-10%炉灰渣子,不饱和树脂14%,过氧化环已酮糊2%,环烷酸钴1%。
2.根据权利要求1所述的一种人造花岗石,其特征在于,其原料重量百分比为:碎石粒75%,碎玻璃3%,炉灰渣子5%,不饱和树脂14%,过氧化环已酮糊2%,环烷酸钴1%。
3.根据权利要求1所述的一种人造花岗石,其特征在于,所述碎石粒为沉积岩石粒,变质岩石粒,氟石粒,芙蓉石粒,木化石粒,黑云母片石粒,鱼鳞石粒,腊石粒,英石粒,菊花石粒,户县石粒,龟纹石粒,吴壁石粒,昆山石粒,宣石粒,砂片石粒,千层石粒或鹅卵石粒中的一种或多种。
4.一种人造花岗石的制备方法,其特征在于,将原料按重量比称重,将碎石粒,碎玻璃和炉灰渣子磨成粉末状,末粒越细越好,之后将细末状的碎石粒,碎玻璃和炉灰渣子混合均匀,加入固化剂不饱和树脂,交联剂过氧化环已酮糊和促进剂环烷酸钴,加适量水,搅拌混合均匀,最后上模具高压成型。
CN201510627978.5A 2015-09-29 2015-09-29 一种人造花岗石及制备方法 Pending CN105271945A (zh)