CN105256444A - 阻燃防电弧面料及其制作的防护服 - Google Patents
阻燃防电弧面料及其制作的防护服 Download PDFInfo
- Publication number
- CN105256444A CN105256444A CN201510572661.6A CN201510572661A CN105256444A CN 105256444 A CN105256444 A CN 105256444A CN 201510572661 A CN201510572661 A CN 201510572661A CN 105256444 A CN105256444 A CN 105256444A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fire
- fabric
- electric arc
- arc fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种阻燃防电弧面料,经线采用第一纱线,纬线采用第二纱线,第一纱线和第二纱线均包含芳纶1313、芳纶1414,以质量百分比计,芳纶1313占据5%-35%、芳纶1414占据5%-20%,第一纱线和第二纱线纱支均为34S/2-37S/2,第一纱线密度为34-38根/cm,第二纱线密度为25-30根/cm。本发明的一种阻燃防电弧面料的有益效果在于:阻燃防电弧面料中含芳纶1313和芳纶1414,提高了防电弧面料的强度和防爆裂性能;面料强度高,防爆性能好,且具有优异的永久阻燃,抗静电,防电弧性能,由其为原料制作成的防电弧服能够于电力和社会企事业单位中专职或兼职电力员工日常工作、潜在电弧环境、电弧爆炸事故逃生时提供有效可靠的防护。
Description
【技术领域】
本发明设计纺织面料技术领域,具体说,涉及一种阻燃防电弧面料及其制作的防护服。
【背景技术】
电弧是一种气体放电现象,电流通过某些绝缘介质(例如空气)所产生的瞬间火花。当身体靠近高压电,但未接触,藉由身体的感应作为桥梁形成的跳电,它最高可产生29400摄氏度的高温,大概是太阳表面温度的四倍,引起激烈的气爆及电烧伤。电弧发生时,巨大的能量在极短的时间内释放,金属导电元件会汽化导致高温蒸汽和金属急剧膨胀,空气和金属汽化物迅速热膨胀会造成巨大声响的爆炸和巨大的压力。
在这种情况下,特殊防电弧服中的高科技材料会迅速地膨胀、织物炭化从而使防电弧服组织密度加大并变厚,迅速地形成保护层,从而使得人体皮肤与电弧热能的接触伤害降至最低。
所以人们制作防电弧服,且将其用于电力和社会企事业单位专职或兼职电力员工日常工作、潜在电弧环境、电弧爆炸事故逃生时穿着。
但,市面上大多数防电弧服采用阻燃棉面料,阻燃棉面料的阻燃性能是经过后整工艺加工而成,具有较好的防火作用,但是随着洗涤次数的增加,面料的强力及阻燃性能会逐渐降低,且面料厚重,纱支较粗,穿着舒适性差,尺寸稳定性不好,含甲醛,长时间接触会使皮肤过敏。另外其阻燃后整过程中需要氨气熏蒸,而氨气有强烈的刺激性气味,吸入过多对人体有害。
因此有必要提供一种阻燃防电弧面料及其制作的防护服解决上述问题。
【发明内容】
本发明的主要目的在于提供一种阻燃防电弧面料,其面料强度高,防爆性能好,且具有优异的永久阻燃,抗静电,防电弧性能,由其为原料制作成的防电弧服能够于电力和社会企事业单位中专职或兼职电力员工日常工作、潜在电弧环境、电弧爆炸事故逃生时提供有效可靠的防护。
本发明通过如下技术方案实现上述目的:
一种阻燃防电弧面料,经线采用第一纱线,纬线采用第二纱线,所述第一纱线和所述第二纱线均包含芳纶1313、芳纶1414,以质量百分比计,所述芳纶1313占据5%-35%、所述芳纶1414占据5%-20%,所述第一纱线和所述第二纱线纱支均为34S/2-37S/2,所述第一纱线密度为34-38根/cm,所述第二纱线密度为25-30根/cm。
进一步的,所述第一纱线和所述第二纱线均包含阻燃腈纶,以质量百分比计,所述阻燃腈纶占据50%~70%。
进一步的,所述第一纱线密度支均为35.5S/2-36S/2,所述第一纱线密度为35-37根/cm,所述第二纱线密度为25-27根/cm。
进一步的,所述第一纱线和所述第二纱线均包含抗静电丝,以质量百分比计,所述抗静电丝占据0.5%-1.5%。
进一步的,所述阻燃防电弧面料为通过纺纱步骤、织坯步骤、染色后整步骤制备得到;
所述纺纱步骤包括纤维开松清理,然后梳棉、梳棉条、并条、制备粗纱、制备细纱、络筒、蒸纱、并线、倍捻、二次蒸纱得到纱线以及对纱线进行检测检测;
所述织坯步骤包括对纱线进行整经、穿综穿筘、上机织造制得胚布,以及对胚布进行坯布物性检测、修布、验坯;
所述染色后整步骤包括对胚布进行前处理、染色、水洗、烘干、剪毛、定型、罐蒸最后得到成品阻燃防电弧面料。
进一步的,所述纺纱步骤中,所述蒸纱和所述二次蒸纱均包括抽真空、蒸汽、抽真空、蒸汽、抽真空步骤。
进一步的,所述纺纱步骤中,所述并条次数为3次。
本发还提供一种以上述阻燃防电弧面料制备得到的防护服。
与现有技术相比,本发明的一种阻燃防电弧面料的有益效果在于:
1)阻燃防电弧面料中含芳纶1313和芳纶1414,提高了防电弧面料的强度和防爆裂性能;
2)阻燃防电弧面料含阻燃腈纶纤维,阻燃腈纶纤维手感柔软,提高面料的柔软性和穿着舒适性;
3)阻燃腈纶纤维是一种本质阻燃纤维,后整过程无需添加任何阻燃剂,安全环保;
4)面料强度高,防爆性能好,且具有优异的永久阻燃,抗静电,防电弧性能,由其为原料制作成的防电弧服能够于电力和社会企事业单位中专职或兼职电力员工日常工作、潜在电弧环境、电弧爆炸事故逃生时提供有效可靠的防护。
【具体实施方式】
实施例:
本实施例提供一种阻燃防电弧面料,经线采用第一纱线,纬线采用第二纱线,第一纱线和第二纱线均由芳纶1313、芳纶1414、阻燃腈纶抗静电丝组成,以质量百分比计,芳纶1313占据14%、芳纶1414占据20%、阻燃腈纶占据70%、抗静电丝占据1%,第一纱线和第二纱线纱支均为35.5S/2,第一纱线密度为37根/cm,第二纱线密度为27根/cm;
其中:
阻燃腈纶:主要通过共聚法得到永久阻燃腈氯纶纤维,是一种本质阻燃纤维,具有优异的永久阻燃性能和阻燃耐久性,遇火焰不熔融、不熔滴、不散发有害气体离开火焰后炭化,可以自行熄灭,LOI值大可达34~35%。且耐酸耐碱、热稳定性好、织物色泽鲜艳,色牢度优良;
芳纶1313:间位芳香族聚酰胺纤维,全称聚间苯二甲酰间苯二胺纤维。其断裂强度0.4~0.53牛/特,伸长率30~50%,回潮率6.5%。耐酸、碱、霉、老化,其摩擦性、抗腐蚀性最好,强度和弹性也好。芳纶1313最突出的特点就是耐高温性能好,可在220℃高下长期使用而不老化,其电气性能与机械性能可保持10年之久,而且尺寸稳定性极佳,在250℃左右的热收缩率仅为1%,短时间暴露于300℃高中也不会收缩、脆化、软化或者融熔,在超过370℃的强下才开始分解,400℃左右开始碳化。芳纶1313纤维是一种本质阻燃、耐高温的纤维,不会熔融、熔滴,不散发有害气体,在空气中也不会助燃,具有自熄性,极限氧指数大于28%,属于难燃纤维,所以不会在空气中燃烧,也不助燃,具有自熄性;
芳纶1414:是对位芳香族聚酰胺纤维,这种复合材料结合高强度及重量轻的优异特质,在同等重量条件下,为钢丝的5倍强度、E级玻璃纤维的2.5倍强度、铝的10倍强度,被认为是世界上最强的纤维。芳纶1414有优异的耐温性能,不仅能在负196度到正204度的温度范围内连续使用而不会有很明显的变化或减损,同时还具有不溶解、防火性(不助燃)、仅会在427度开始碳化、能忍受温度高达538度短暂时间接触的优异耐温性能。芳纶1414具有低延伸、高模数、断裂强度高、耐温性高、不熔解不助燃只会碳化、高抗化学性、高稳定性、低比重、优异电绝缘性等性能;
抗静电丝:具有碳芯成分,不易积聚静电荷,对于防静电的产生和静电的消散具有非常优异的性能。在油气田,燃气站,加油站,矿井等特殊工作环境,静电火花是非常危险的,抗静电丝可以有效阻止静电的产生,有效避免由静电产生的事故。
具体的,阻燃防电弧面料为通过纺纱步骤、织坯步骤、染色后整步骤制备得到;
纺纱步骤包括纤维开松清理,然后梳棉、梳棉条、并条、制备粗纱、制备细纱、络筒、蒸纱、并线、倍捻、二次蒸纱得到纱线以及对纱线进行检测检测;
织坯步骤包括对纱线进行整经、穿综穿筘、上机织造制得胚布,以及对胚布进行坯布物性检测、修布、验坯;
染色后整步骤包括对胚布进行前处理、染色、水洗、烘干、剪毛、定型、罐蒸最后得到成品阻燃防电弧面料。
纺纱步骤中,蒸纱和二次蒸纱均包括抽真空、蒸汽、抽真空、蒸汽、抽真空步骤。
纺纱步骤中,并条次数为3次。
本实施的一种阻燃防电弧面料可制作成防电弧服。
本实施例的一种阻燃防电弧面料的有益效果在于:阻燃防电弧面料中含芳纶1313和芳纶1414,提高了防电弧面料的强度和防爆裂性能;阻燃防电弧面料含阻燃腈纶纤维,阻燃腈纶纤维手感柔软,提高面料的柔软性和穿着舒适性;阻燃腈纶纤维是一种本质阻燃纤维,后整过程无需添加任何阻燃剂,安全环保;面料强度高,防爆性能好,且具有优异的永久阻燃,抗静电,防电弧性能,由其为原料制作成的防电弧服能够于电力和社会企事业单位中专职或兼职电力员工日常工作、潜在电弧环境、电弧爆炸事故逃生时提供有效可靠的防护。
以上所述的仅是本发明的一些实施方式。对于本领域的普通技术人员来说,在不脱离本发明创造构思的前提下,还可以做出若干变形和改进,这些都属于本发明的保护范围。
Claims (8)
1.一种阻燃防电弧面料,其特征在于:经线采用第一纱线,纬线采用第二纱线,所述第一纱线和所述第二纱线均包含芳纶1313、芳纶1414,以质量百分比计,所述芳纶1313占据5%-35%、所述芳纶1414占据5%-20%,所述第一纱线和所述第二纱线纱支均为34S/2-37S/2,所述第一纱线密度为34-38根/cm,所述第二纱线密度为25-30根/cm。
2.根据权利要求1所述的一种阻燃防电弧面料,其特征在于:所述第一纱线和所述第二纱线均包含阻燃腈纶,以质量百分比计,所述阻燃腈纶占据50%~70%。
3.根据权利要求1所述的一种阻燃防电弧面料,其特征在于:所述第一纱线和所述第二纱线纱支均为35.5S/2-36S/2,所述第一纱线密度为35-37根/cm,所述第二纱线密度为25-27根/cm。
4.根据权利要求1所述的一种阻燃防电弧面料,其特征在于:所述第一纱线和所述第二纱线均包含抗静电丝,以质量百分比计,所述抗静电丝占据0.5%-1.5%。
5.根据权利要求1所述的一种阻燃防电弧面料,其特征在于:所述阻燃防电弧面料为通过纺纱步骤、织坯步骤、染色后整步骤制备得到;
所述纺纱步骤包括纤维开松清理,然后梳棉、梳棉条、并条、制备粗纱、制备细纱、络筒、蒸纱、并线、倍捻、二次蒸纱得到纱线以及对纱线进行检测检测;
所述织坯步骤包括对纱线进行整经、穿综穿筘、上机织造制得胚布,以及对胚布进行坯布物性检测、修布、验坯;
所述染色后整步骤包括对胚布进行前处理、染色、水洗、烘干、剪毛、定型、罐蒸最后得到成品阻燃防电弧面料。
6.根据权利要求5所述的一种阻燃防电弧面料,其特征在于:所述纺纱步骤中,所述蒸纱和所述二次蒸纱均包括抽真空、蒸汽、抽真空、蒸汽、抽真空步骤。
7.根据权利要求5所述的一种阻燃防电弧面料,其特征在于:所述纺纱步骤中,所述并条次数为3次。
8.权利要求1-5任一项所述阻燃防电弧面料制备得到的防护服。