CN105255105A - 一种低密度泡沫制品 - Google Patents

一种低密度泡沫制品 Download PDF

Info

Publication number
CN105255105A
CN105255105A CN201510708741.XA CN201510708741A CN105255105A CN 105255105 A CN105255105 A CN 105255105A CN 201510708741 A CN201510708741 A CN 201510708741A CN 105255105 A CN105255105 A CN 105255105A
Authority
CN
China
Prior art keywords
parts
agent
mixture
low density
density foam
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510708741.XA
Other languages
English (en)
Inventor
王伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jieshou Xingan Plastic Products Co Ltd
Original Assignee
Jieshou Xingan Plastic Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jieshou Xingan Plastic Products Co Ltd filed Critical Jieshou Xingan Plastic Products Co Ltd
Priority to CN201510708741.XA priority Critical patent/CN105255105A/zh
Publication of CN105255105A publication Critical patent/CN105255105A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种低密度泡沫制品，由以下质量组分的物料组成：10～30份水性三聚氰胺、20～40份固体羟甲基三聚氰胺、10～30份性溶剂、3～10份表面活性剂、10～20份发泡剂、3～10份固化剂、2～10份添加剂，其中，溶剂为水或乙醇；表面活性剂为阴离子表面活性剂或非离子表面活性剂；发泡剂为低沸点的物理发泡剂或者易分解的化学发泡剂；固化剂为有机酸或无机酸；添加剂为光稳定剂、热稳定剂、防老化剂或者甲醛捕捉剂。该产品以及工艺能有效地获得低密度泡沫制品，能节约原材料，同时使用效果和强度不减小，生产工艺方便，所使用物料符合要求，方便根据需要使用。

Description

一种低密度泡沫制品
技术领域
本发明涉及一种低密度泡沫制品，属于泡沫制品技术领域。
背景技术
现有的软质三聚氰胺泡沫是一种低密度、高开孔率的阻燃泡沫，具有优良的阻燃、
吸声、绝热、清洁功能，可广泛应用于建筑、交通、日用、工业领域。在实际应用中，一些领域例如坐垫、沙发、绝热保温、清洁等领域对三聚氰胺泡沫的密度和强度提出较高要求，以便能够根据需要获得较好的泡沫制品。
发明内容
本发明的目的在于提供一种低密度泡沫制品，以便获得低密度泡沫制品，能节约原材料，同时使用效果和强度不减小。
为了实现上述目的，本发明的技术方案如下。
一种低密度泡沫制品，由以下质量组分的物料组成：10～30份水性三聚氰胺、20～40份固体羟甲基三聚氰胺、10～30份性溶剂、3～10份表面活性剂、10～20份发泡剂、3～10份固化剂、2～10份添加剂，其中，溶剂为水或乙醇；表面活性剂为阴离子表面活性剂或非离子表面活性剂；发泡剂为低沸点的物理发泡剂或者易分解的化学发泡剂；固化剂为有机酸或无机酸；添加剂为光稳定剂、热稳定剂、防老化剂或者甲醛捕捉剂。
上述低密度泡沫制品，其制备方法，包括以下步骤：
(1)按上述质量份数将水性三聚氰胺、溶剂、表面活性剂和添加剂在恒温搅拌罐体中混合均匀得到混合物A；
(2)将混合物A与固体羟甲基三聚氰胺在恒温的单螺杆挤出机或双螺杆挤出机中混合均匀得到混合物B；
(3)将混合物B与发泡剂在双螺杆挤出机中混合均匀得到混合物C；
(4)混合物C与固化剂在恒温的高速混合器中混合均匀得到混合物D；
(5)混合物D在微波发泡装置中经过发泡、固化、干燥、淬火得到产品。
该发明的有益效果在于：该产品以及工艺能有效地获得低密度泡沫制品，能节约原材料，同时使用效果和强度不减小，生产工艺方便，所使用物料符合要求，方便根据需要使用。
具体实施方式
下面结合实施例对本发明的具体实施方式进行描述，以便更好的理解本发明。
实施例
本实施例中的低密度泡沫制品，由以下质量组分的物料组成：10份水性三聚氰胺、20份固体羟甲基三聚氰胺、10份性溶剂、3份表面活性剂、10份发泡剂、3份固化剂、2份添加剂，其中，溶剂为水；表面活性剂为阴离子表面活性剂；发泡剂为低沸点的物理发泡剂；固化剂为有机酸；添加剂为光稳定剂、热稳定剂。
上述低密度泡沫制品，其制备方法，包括以下步骤：
(1)按上述质量份数将水性三聚氰胺、溶剂、表面活性剂和添加剂在恒温搅拌罐体中混合均匀得到混合物A；
(2)将混合物A与固体羟甲基三聚氰胺在恒温的单螺杆挤出机或双螺杆挤出机中混合均匀得到混合物B；
(3)将混合物B与发泡剂在双螺杆挤出机中混合均匀得到混合物C；
(4)混合物C与固化剂在恒温的高速混合器中混合均匀得到混合物D；
(5)混合物D在微波发泡装置中经过发泡、固化、干燥、淬火得到产品。
实施例2
本实施例中的低密度泡沫制品，由以下质量组分的物料组成：30份水性三聚氰胺、40份固体羟甲基三聚氰胺、30份性溶剂、10份表面活性剂、20份发泡剂、10份固化剂、10份添加剂，其中，溶剂为乙醇；表面活性剂为非离子表面活性剂；发泡剂为易分解的化学发泡剂；固化剂为无机酸；添加剂为热稳定剂。
上述低密度泡沫制品，其制备方法，包括以下步骤：
(1)按上述质量份数将水性三聚氰胺、溶剂、表面活性剂和添加剂在恒温搅拌罐体中混合均匀得到混合物A；
(2)将混合物A与固体羟甲基三聚氰胺在恒温的单螺杆挤出机或双螺杆挤出机中混合均匀得到混合物B；
(3)将混合物B与发泡剂在双螺杆挤出机中混合均匀得到混合物C；
(4)混合物C与固化剂在恒温的高速混合器中混合均匀得到混合物D；
(5)混合物D在微波发泡装置中经过发泡、固化、干燥、淬火得到产品。
实施例3
本实施例中的低密度泡沫制品，由以下质量组分的物料组成：20份水性三聚氰胺、30份固体羟甲基三聚氰胺、20份性溶剂、6份表面活性剂、15份发泡剂、8份固化剂、6份添加剂，其中，溶剂为乙醇；表面活性剂为非离子表面活性剂；发泡剂为易分解的化学发泡剂；固化剂为无机酸；添加剂为防老化剂。
上述低密度泡沫制品，其制备方法，包括以下步骤：
(1)按上述质量份数将水性三聚氰胺、溶剂、表面活性剂和添加剂在恒温搅拌罐体中混合均匀得到混合物A；
(2)将混合物A与固体羟甲基三聚氰胺在恒温的单螺杆挤出机或双螺杆挤出机中混合均匀得到混合物B；
(3)将混合物B与发泡剂在双螺杆挤出机中混合均匀得到混合物C；
(4)混合物C与固化剂在恒温的高速混合器中混合均匀得到混合物D；
(5)混合物D在微波发泡装置中经过发泡、固化、干燥、淬火得到产品。
以上所述是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也视为本发明的保护范围。

Claims (2)

1.一种低密度泡沫制品，其特征在于：由以下质量组分的物料组成：10～30份水性三聚氰胺、20～40份固体羟甲基三聚氰胺、10～30份性溶剂、3～10份表面活性剂、10～20份发泡剂、3～10份固化剂、2～10份添加剂，其中，溶剂为水或乙醇；表面活性剂为阴离子表面活性剂或非离子表面活性剂；发泡剂为低沸点的物理发泡剂或者易分解的化学发泡剂；固化剂为有机酸或无机酸；添加剂为光稳定剂、热稳定剂、防老化剂或者甲醛捕捉剂。
2.根据权利要求1所述的低密度泡沫制品，其特征在于：上述低密度泡沫制品，其制备方法，包括以下步骤：
(1)按上述质量份数将水性三聚氰胺、溶剂、表面活性剂和添加剂在恒温搅拌罐体中混合均匀得到混合物A；
(2)将混合物A与固体羟甲基三聚氰胺在恒温的单螺杆挤出机或双螺杆挤出机中混合均匀得到混合物B；
(3)将混合物B与发泡剂在双螺杆挤出机中混合均匀得到混合物C；
(4)混合物C与固化剂在恒温的高速混合器中混合均匀得到混合物D；
(5)混合物D在微波发泡装置中经过发泡、固化、干燥、淬火得到产品。
CN201510708741.XA 2015-10-28 2015-10-28 一种低密度泡沫制品 Pending CN105255105A (zh)