CN105239249A - Weaving process for aloe fiber small jacquard fabric - Google Patents

Weaving process for aloe fiber small jacquard fabric Download PDF

Info

Publication number
CN105239249A
CN105239249A CN201510557901.5A CN201510557901A CN105239249A CN 105239249 A CN105239249 A CN 105239249A CN 201510557901 A CN201510557901 A CN 201510557901A CN 105239249 A CN105239249 A CN 105239249A
Authority
CN
China
Prior art keywords
yarn
weaving
warp thread
dobby
warp
Prior art date
Application number
CN201510557901.5A
Other languages
Chinese (zh)
Inventor
马顺彬
Original Assignee
江苏工程职业技术学院
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 江苏工程职业技术学院 filed Critical 江苏工程职业技术学院
Priority to CN201510557901.5A priority Critical patent/CN105239249A/en
Publication of CN105239249A publication Critical patent/CN105239249A/en

Abstract

The invention discloses a weaving process for an aloe fiber small jacquard fabric. The process comprises the following steps: a spooling process, a beaming process, a slashing process, a drawing-in process, and a weaving process. The produced fabric warp yarns and weft yarns respectively use yarns in extra white, grass green, and deep blue colors as mass tone, cooperated with organization design, color of the fabric is bright, grids and figures are clear, and cloth is smooth, and the fabric is comfortable to wear. The fabric has strong stereo perception, and is preferred by consumers. The fabric can be used for shirts, bedclothes, aviation trim, etc. Through analysis and optimization on manufacturing process, weaving efficiency reaches up to 93%, and the process satisfies requirement of improving product grade for enterprises.

Description

A kind of weaving process of aloe fibre dobby
Technical field
The invention belongs to fabric knitting field, be specifically related to a kind of weaving process of aloe fibre dobby.
Background technology
Along with the raising of people's quality of life and the raising of production technology level, the product of environmental protection is more and more welcome, and existing clothes are all generally that Chemical fiber component is made, inadequate environmental protection, and lacks health care.
Contain in aloe and have 75 kinds of elements and human body cell desired substance almost to fit like a glove, 7 kinds containing needed by human 8 kinds of Amino acids, 11 kinds of secondary Amino acid 12 kinds, vitamin A, E, C, B group, mineral matter reaches 10 kinds, Anthraquinone Complex, the 8 large materials such as Saponins lignin, single marrow and polysaccharide.Its a large amount of natural bioactivity substance; can effectively purify human epidermal free radical; the brute force with cell tissue composes the effect of living, protective effect; amino acid wherein and complex polysaccharide constitute natural moisture preserving factor (NMF); the moisture lost in skin can be supplemented; the function of recovery collagen protein, prevents facial wrinkles, and maintenance skin is soft and moist, smooth, high resilience.The material such as aloin and aloe-emodin has antiinflammatory action, both skin capable of washing, can prevent bacterial growth again, promotes cell metabolism and skin regeneration, eases the pain and itch, have obvious curative effects to some skin disease.In addition; the amino acid that asparatate in aloe, glycine, serine etc. are conducive to skin metabolism can form the invisible film of one deck on skin; long wave ultraviolet in sunlight can be stoped to the injury of epidermis and oxidation, to prevent the redness because Exposure to Sunlight causes, burning heat sensation, and protection skin exempts from burns.Thus the fiber of exploitation containing aloe, with clothes made by this fiber, has good effect to the skin of people.
Summary of the invention
Goal of the invention: in order to solve the deficiencies in the prior art, the invention provides a kind of weaving process of aloe fibre dobby.
Technical scheme: a kind of weaving process of aloe fibre dobby, comprises the steps: winding process---warping technology---slashing technique---passes technique---weaving process;
Described slashing technique, formula of size is as follows: animal glue 25kg ~ 30kg, carboxyl methyl cellulose 25kg ~ 30kg, glycerine 0.5kg ~ 1kg, saponification mineral oil 1kg ~ 1.5kg, penetrant JFC0.5kg ~ 1kg, 2-naphthols 0.5kg ~ 1kg.
As further optimization: described winding process, adopt AUTOCONER338 type bobbin winder, each technological parameter is as follows:
As further optimization: described warping technology, adopt Ben Ningge BENNINGER Sectional warping machines, the speed of a motor vehicle is 300m/min ~ 400m/min, and beaming speed is 350m/min ~ 450m/min, and rolling density is 0.51g/cm 3~ 0.54g/cm 3, every twisted flower number is 1 flower, and every twisted warp radical is 418, and warping hank number is 18 strands, and the 1st strand is 478, and the 2nd strand is 418 to 17 strands, and the 18th strand is 364.
As further optimization: described slashing technique: adopt field, Tianjin coltfoal HS20-II Sizing machines, slurry groove temperature 65 DEG C ~ 80 DEG C, stock tank viscosity is 8.5s ~ 9.5s, front and back squeezing roller pressure 5 ~ 6/9 ~ 11 (KN), preliminary drying temperature is 115 DEG C ~ 130 DEG C, bake out temperature is 100 DEG C ~ 110 DEG C, and the speed of a motor vehicle is 40m/min ~ 50m/min; The rate of sizing is 9.5% ~ 10.5%, and regain is 8.5% ~ 9.5%, percentage elongation < 3%, and slurry pH value is 6.5 ~ 7.5, and slurry temperature is 65 DEG C ~ 80 DEG C.
As further optimization: described in pass technique, technological parameter is as follows: heald frame 12 pages, method of wearing for (2,3,4,1) × 11,5,6,7,8,9,10,11,12,4, (1,2,3,4) × 91,1, each 60 of selvedge, the method for wearing is 2,3,4,1; 1st and each 1855 of 4 heald frame healds, the 2nd and each 1838 of 3 heald frame healds, the 5th, 6,7,8,9,10,11, each 18 of 12 heald frame healds; Porter is 120, and it is 2 to enter that every reed penetrates number.
As further optimization: described weaving process, adopt JAT710 type air-jet loom, the speed of a motor vehicle is 650r/min ~ 700r/min, warp tension is 2000N ~ 2300N, opening time is 285 ° ~ 315 °, back rest high and low position-1 ~+1, warp stop frame high-low-position-1 ~+1, main jet opening and closing time is 75 ° ~ 180 °, the opening and closing time of first group of pilot jet is 75 ° ~ 120 °, the opening and closing time of second group of pilot jet is 90 ° ~ 150 °, the opening and closing time of the 3rd group of pilot jet is 120 ° ~ 180 °, the opening and closing time of the 4th group of pilot jet is 150 ° ~ 220 °, the opening and closing time of the 5th group of pilot jet is 170 ° ~ 270 °, weft yarn reaches 230 ° ~ 240 °, angle, main jet air pressure 0.25MPa ~ 0.28MPa, pilot jet air pressure 0.3MPa ~ 0.33MPa.
As further optimization: described in the trimmed size of aloe fibre dobby produced as follows: Fabric width is 147cm, and grey cloth fabric width is 154cm, and upper machine reed width is 159.5cm, and total quantity of warps is 7530, wherein, 60 × 2, limit yarn; Warp thread and weft yarn are the aloe fibre Pure Yarn of 14.7tex, finished product weft density is respectively 512/10cm and 315/10cm, grey cloth weft density is respectively 492/10cm and 303/10cm, machine upper warp and woof is close is respectively 472/10cm and 276/10cm, full width spends several+304,17 flower, warp-wise tightness 59%, broadwise tightness 36.3%, total tightness degree 73.9%.
As further optimization: the color matching of described fabric is as follows: the deep blue C of the grass green B of extra white A:
Look, through circulation: 30A35B53A24C6B24C67A35C67A24C6B24C23A, amounts to 418, wherein extra white 240, grass green 47, deep blue 131;
Barry dyeing circulates: 32A25B32A14C4B14C41A24C41A14C4B14C, amounts to 259, wherein extra white 146, grass green 33, deep blue 80;
4260, extra white warp thread, 2310, deep blue warp thread, 840, grass green warp thread, extra white warp thread consumption 7.0666kg/100m, deep blue warp thread yarn-using amount 3.8319kg/100m, grass green warp thread yarn-using amount 1.3934kg/100m, limit yarn warp thread yarn-using amount 0.1991kg/100m, the total yarn-using amount of warp thread is 12.4910kg/100m, extra white weft yarn yarn-using amount 4.2898kg/100m, deep blue weft yarn yarn 2.3506kg/100m, grass green weft yarn yarn-using amount 0.9696kg/100m, the total yarn-using amount of weft yarn is 7.6100kg/100m.
Beneficial effect: the present invention produces 14.7/14.7512/315147 aloe fibre dobby on JAT710 type air-jet loom.The fabric warp produced through the present invention and weft yarn respectively with extra white, grass green, avy blue yarn for dominant hue, coordinate organization design, make it bright-colored, grid and decorative pattern clear, cloth cover is smooth, comfortable and easy to wear, has stronger third dimension, by consumer is favored, can be used for shirt, bedding, aviation interior trim etc.This fabric color is bright-coloured, grid and decorative pattern clear, cloth cover is smooth, comfortable and easy to wear, and after analyzing production technology aspect and optimizing, weaving efficiency, up to 93%, meets the demand that product specification improves in enterprise.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described.
Specific embodiment 1
As shown in Figure 1, a kind of weaving process of aloe fibre dobby, comprises the steps: winding process---warping technology---slashing technique---passes technique---weaving process;
Described winding process, adopt AUTOCONER338 type bobbin winder, each technological parameter is as follows:
Described warping technology, adopt Ben Ningge BENNINGER Sectional warping machines, the speed of a motor vehicle is 300m/min, and beaming speed is 350m/min, and rolling density is 0.51g/cm 3, every twisted flower number is 1 flower, and every twisted warp radical is 418, and warping hank number is 18 strands, and the 1st strand is 478, and the 2nd strand is 418 to 17 strands, and the 18th strand is 364.
Described slashing technique, formula of size is as follows: animal glue 25kg, carboxyl methyl cellulose 25kg, glycerine 0.5kg, saponification mineral oil 1kg, penetrant JFC0.5kg, 2-naphthols 0.5kg.
Described slashing technique: adopt field, Tianjin coltfoal HS20-II Sizing machines, slurry groove temperature 65 DEG C, stock tank viscosity is 8.5s, front and back squeezing roller pressure 5/9 (KN), and preliminary drying temperature is 115 DEG C, and bake out temperature is 100 DEG C, and the speed of a motor vehicle is 40m/min; The rate of sizing is 9.5%, and regain is 8.5%, percentage elongation < 3%, and slurry pH value is 6.5, and slurry temperature is 65 DEG C.
Describedly pass technique, technological parameter is as follows: heald frame 12 pages, method of wearing for (2,3,4,1) × 11,5,6,7,8,9,10,11,12,4, (1,2,3,4) × 91,1, each 60 of selvedge, the method for wearing is 2,3,4,1; 1st and each 1855 of 4 heald frame healds, the 2nd and each 1838 of 3 heald frame healds, the 5th, 6,7,8,9,10,11, each 18 of 12 heald frame healds; Porter is 120, and it is 2 to enter that every reed penetrates number.
Described weaving process, adopt JAT710 type air-jet loom, the speed of a motor vehicle is 650r/min, warp tension is 2000N, opening time is 285 °, back rest high and low position-1, warp stop frame high-low-position-1, main jet opening and closing time is 75 ° ~ 180 °, the opening and closing time of first group of pilot jet is 75 ° ~ 120 °, the opening and closing time of second group of pilot jet is 90 ° ~ 150 °, the opening and closing time of the 3rd group of pilot jet is 120 ° ~ 180 °, the opening and closing time of the 4th group of pilot jet is 150 ° ~ 220 °, the opening and closing time of the 5th group of pilot jet is 170 ° ~ 270 °, weft yarn reaches 240 °, angle, main jet air pressure 0.25MPa, pilot jet air pressure 0.3MPa.
The trimmed size of the described aloe fibre dobby produced is as follows: Fabric width is 147cm, and grey cloth fabric width is 154cm, and upper machine reed width is 159.5cm, and total quantity of warps is 7530, wherein, and 60 × 2, limit yarn; Warp thread and weft yarn are the aloe fibre Pure Yarn of 14.7tex, finished product weft density is respectively 512/10cm and 315/10cm, grey cloth weft density is respectively 492/10cm and 303/10cm, machine upper warp and woof is close is respectively 472/10cm and 276/10cm, full width spends several+304,17 flower, warp-wise tightness 59%, broadwise tightness 36.3%, total tightness degree 73.9%.
The color matching of described fabric is as follows: the deep blue C of the grass green B of extra white A:
Look, through circulation: 30A35B53A24C6B24C67A35C67A24C6B24C23A, amounts to 418, wherein extra white 240, grass green 47, deep blue 131;
Barry dyeing circulates: 32A25B32A14C4B14C41A24C41A14C4B14C, amounts to 259, wherein extra white 146, grass green 33, deep blue 80;
4260, extra white warp thread, 2310, deep blue warp thread, 840, grass green warp thread, extra white warp thread consumption 7.0666kg/100m, deep blue warp thread yarn-using amount 3.8319kg/100m, grass green warp thread yarn-using amount 1.3934kg/100m, limit yarn warp thread yarn-using amount 0.1991kg/100m, the total yarn-using amount of warp thread is 12.4910kg/100m, extra white weft yarn yarn-using amount 4.2898kg/100m, deep blue weft yarn yarn 2.3506kg/100m, grass green weft yarn yarn-using amount 0.9696kg/100m, the total yarn-using amount of weft yarn is 7.6100kg/100m.
Specific embodiment 2
As shown in Figure 1, a kind of weaving process of aloe fibre dobby, comprises the steps: winding process---warping technology---slashing technique---passes technique---weaving process;
Described winding process, adopt AUTOCONER338 type bobbin winder, each technological parameter is as follows:
Described warping technology, adopt Ben Ningge BENNINGER Sectional warping machines, the speed of a motor vehicle is 400m/min, and beaming speed is 450m/min, and rolling density is 0.54g/cm 3, every twisted flower number is 1 flower, and every twisted warp radical is 418, and warping hank number is 18 strands, and the 1st strand is 478, and the 2nd strand is 418 to 17 strands, and the 18th strand is 364.
Described slashing technique, formula of size is as follows: animal glue 30kg, carboxyl methyl cellulose 30kg, glycerine 1kg, saponification mineral oil 1.5kg, penetrant JFC1kg, 2-naphthols 1kg.
Described slashing technique: adopt field, Tianjin coltfoal HS20-II Sizing machines, slurry groove temperature 80 DEG C, stock tank viscosity is 9.5s, front and back squeezing roller pressure 6/11 (KN), and preliminary drying temperature is 130 DEG C, and bake out temperature is 110 DEG C, and the speed of a motor vehicle is 50m/min; The rate of sizing is 10.5%, and regain is 9.5%, percentage elongation < 3%, and slurry pH value is 7.5, and slurry temperature is 80 DEG C.
Describedly pass technique, technological parameter is as follows: heald frame 12 pages, method of wearing for (2,3,4,1) × 11,5,6,7,8,9,10,11,12,4, (1,2,3,4) × 91,1, each 60 of selvedge, the method for wearing is 2,3,4,1; 1st and each 1855 of 4 heald frame healds, the 2nd and each 1838 of 3 heald frame healds, the 5th, 6,7,8,9,10,11, each 18 of 12 heald frame healds; Porter is 120, and it is 2 to enter that every reed penetrates number.
Described weaving process, adopt JAT710 type air-jet loom, the speed of a motor vehicle is 700r/min, warp tension is 2300N, opening time is 315 °, back rest high and low position+1, warp stop frame high-low-position+1, main jet opening and closing time is 75 ° ~ 180 °, the opening and closing time of first group of pilot jet is 75 ° ~ 120 °, the opening and closing time of second group of pilot jet is 90 ° ~ 150 °, the opening and closing time of the 3rd group of pilot jet is 120 ° ~ 180 °, the opening and closing time of the 4th group of pilot jet is 150 ° ~ 220 °, the opening and closing time of the 5th group of pilot jet is 170 ° ~ 270 °, weft yarn reaches 230 °, angle, main jet air pressure 0.28MPa, pilot jet air pressure 0.33MPa.
The trimmed size of the described aloe fibre dobby produced is as follows: Fabric width is 147cm, and grey cloth fabric width is 154cm, and upper machine reed width is 159.5cm, and total quantity of warps is 7530, wherein, and 60 × 2, limit yarn; Warp thread and weft yarn are the aloe fibre Pure Yarn of 14.7tex, finished product weft density is respectively 512/10cm and 315/10cm, grey cloth weft density is respectively 492/10cm and 303/10cm, machine upper warp and woof is close is respectively 472/10cm and 276/10cm, full width spends several+304,17 flower, warp-wise tightness 59%, broadwise tightness 36.3%, total tightness degree 73.9%.
The color matching of described fabric is as follows: the deep blue C of the grass green B of extra white A:
Look, through circulation: 30A35B53A24C6B24C67A35C67A24C6B24C23A, amounts to 418, wherein extra white 240, grass green 47, deep blue 131;
Barry dyeing circulates: 32A25B32A14C4B14C41A24C41A14C4B14C, amounts to 259, wherein extra white 146, grass green 33, deep blue 80;
4260, extra white warp thread, 2310, deep blue warp thread, 840, grass green warp thread, extra white warp thread consumption 7.0666kg/100m, deep blue warp thread yarn-using amount 3.8319kg/100m, grass green warp thread yarn-using amount 1.3934kg/100m, limit yarn warp thread yarn-using amount 0.1991kg/100m, the total yarn-using amount of warp thread is 12.4910kg/100m, extra white weft yarn yarn-using amount 4.2898kg/100m, deep blue weft yarn yarn 2.3506kg/100m, grass green weft yarn yarn-using amount 0.9696kg/100m, the total yarn-using amount of weft yarn is 7.6100kg/100m.
Specific embodiment 3
As shown in Figure 1, a kind of weaving process of aloe fibre dobby, comprises the steps: winding process---warping technology---slashing technique---passes technique---weaving process;
Described winding process, adopt AUTOCONER338 type bobbin winder, each technological parameter is as follows:
Described warping technology, adopt Ben Ningge BENNINGER Sectional warping machines, the speed of a motor vehicle is 360m/min, and beaming speed is 420m/min, and rolling density is 0.53g/cm 3, every twisted flower number is 1 flower, and every twisted warp radical is 418, and warping hank number is 18 strands, and the 1st strand is 478, and the 2nd strand is 418 to 17 strands, and the 18th strand is 364.
Described slashing technique, formula of size is as follows: animal glue 29kg, carboxyl methyl cellulose 26kg, glycerine 0.8kg, saponification mineral oil 1.3kg, penetrant JFC0.7kg, 2-naphthols 0.6kg.
Described slashing technique: adopt field, Tianjin coltfoal HS20-II Sizing machines, slurry groove temperature 73 DEG C, stock tank viscosity is 9.0s, front and back squeezing roller pressure 5.5/10 (KN), and preliminary drying temperature is 120 DEG C, and bake out temperature is 105 DEG C, and the speed of a motor vehicle is 44m/min; The rate of sizing is 9.8%, and regain is 8.8%, percentage elongation < 3%, and slurry pH value is 6.9, and slurry temperature is 73 DEG C.
Describedly pass technique, technological parameter is as follows: heald frame 12 pages, method of wearing for (2,3,4,1) × 11,5,6,7,8,9,10,11,12,4, (1,2,3,4) × 91,1, each 60 of selvedge, the method for wearing is 2,3,4,1; 1st and each 1855 of 4 heald frame healds, the 2nd and each 1838 of 3 heald frame healds, the 5th, 6,7,8,9,10,11, each 18 of 12 heald frame healds; Porter is 120, and it is 2 to enter that every reed penetrates number.
Described weaving process, adopt JAT710 type air-jet loom, the speed of a motor vehicle is 680r/min, warp tension is 2200N, opening time is 305 °, back rest high and low position 0, warp stop frame high-low-position 0, main jet opening and closing time is 75 ° ~ 180 °, the opening and closing time of first group of pilot jet is 75 ° ~ 120 °, the opening and closing time of second group of pilot jet is 90 ° ~ 150 °, the opening and closing time of the 3rd group of pilot jet is 120 ° ~ 180 °, the opening and closing time of the 4th group of pilot jet is 150 ° ~ 220 °, the opening and closing time of the 5th group of pilot jet is 170 ° ~ 270 °, weft yarn reaches 235 °, angle, main jet air pressure 0.27MPa, pilot jet air pressure 0.31MPa.
The trimmed size of the described aloe fibre dobby produced is as follows: Fabric width is 147cm, and grey cloth fabric width is 154cm, and upper machine reed width is 159.5cm, and total quantity of warps is 7530, wherein, and 60 × 2, limit yarn; Warp thread and weft yarn are the aloe fibre Pure Yarn of 14.7tex, finished product weft density is respectively 512/10cm and 315/10cm, grey cloth weft density is respectively 492/10cm and 303/10cm, machine upper warp and woof is close is respectively 472/10cm and 276/10cm, full width spends several+304,17 flower, warp-wise tightness 59%, broadwise tightness 36.3%, total tightness degree 73.9%.
The color matching of described fabric is as follows: the deep blue C of the grass green B of extra white A:
Look, through circulation: 30A35B53A24C6B24C67A35C67A24C6B24C23A, amounts to 418, wherein extra white 240, grass green 47, deep blue 131;
Barry dyeing circulates: 32A25B32A14C4B14C41A24C41A14C4B14C, amounts to 259, wherein extra white 146, grass green 33, deep blue 80;
4260, extra white warp thread, 2310, deep blue warp thread, 840, grass green warp thread, extra white warp thread consumption 7.0666kg/100m, deep blue warp thread yarn-using amount 3.8319kg/100m, grass green warp thread yarn-using amount 1.3934kg/100m, limit yarn warp thread yarn-using amount 0.1991kg/100m, the total yarn-using amount of warp thread is 12.4910kg/100m, extra white weft yarn yarn-using amount 4.2898kg/100m, deep blue weft yarn yarn 2.3506kg/100m, grass green weft yarn yarn-using amount 0.9696kg/100m, the total yarn-using amount of weft yarn is 7.6100kg/100m.
The present invention is not limited to above-mentioned preferred forms; anyone can draw other various forms of products under enlightenment of the present invention; no matter but any change is done in its shape or structure; every have identical with the application or akin technical scheme, all drops within protection scope of the present invention.

Claims (8)

1. a weaving process for aloe fibre dobby, is characterized in that: comprise the steps: winding process---warping technology---slashing technique---passes technique---weaving process;
Described slashing technique, formula of size is as follows: animal glue 25kg ~ 30kg, carboxyl methyl cellulose 25kg ~ 30kg, glycerine 0.5kg ~ 1kg, saponification mineral oil 1kg ~ 1.5kg, penetrant JFC0.5kg ~ 1kg, 2-naphthols 0.5kg ~ 1kg.
2. the weaving process of aloe fibre dobby according to claim 1, is characterized in that: described winding process, and adopt AUTOCONER338 type bobbin winder, each technological parameter is as follows:
3. the weaving process of aloe fibre dobby according to claim 1, it is characterized in that: described warping technology, adopt Ben Ningge BENNINGER Sectional warping machines, the speed of a motor vehicle is 300m/min ~ 400m/min, beaming speed is 350m/min ~ 450m/min, and rolling density is 0.51g/cm 3~ 0.54g/cm 3, every twisted flower number is 1 flower, and every twisted warp radical is 418, and warping hank number is 18 strands, and the 1st strand is 478, and the 2nd strand is 418 to 17 strands, and the 18th strand is 364.
4. the weaving process of aloe fibre dobby according to claim 1, it is characterized in that: described slashing technique: adopt field, Tianjin coltfoal HS20-II Sizing machines, slurry groove temperature 65 DEG C ~ 80 DEG C, stock tank viscosity is 8.5s ~ 9.5s, front and back squeezing roller pressure 5 ~ 6/9 ~ 11 (KN), preliminary drying temperature is 115 DEG C ~ 130 DEG C, and bake out temperature is 100 DEG C ~ 110 DEG C, and the speed of a motor vehicle is 40m/min ~ 50m/min; The rate of sizing is 9.5% ~ 10.5%, and regain is 8.5% ~ 9.5%, percentage elongation < 3%, and slurry pH value is 6.5 ~ 7.5, and slurry temperature is 65 DEG C ~ 80 DEG C.
5. the weaving process of aloe fibre dobby according to claim 1, is characterized in that: described in pass technique, technological parameter is as follows: heald frame 12 pages, and method of wearing is (2,3,4,1) × 11,5,6,7,8,9,10,11,12,4, (1,2,3,4) × 91,1, each 60 of selvedge, the method of wearing is 2,3,4,1; 1st and each 1855 of 4 heald frame healds, the 2nd and each 1838 of 3 heald frame healds, the 5th, 6,7,8,9,10,11, each 18 of 12 heald frame healds; Porter is 120, and it is 2 to enter that every reed penetrates number.
6. the weaving process of aloe fibre dobby according to claim 1, it is characterized in that: described weaving process, adopt JAT710 type air-jet loom, the speed of a motor vehicle is 650r/min ~ 700r/min, warp tension is 2000N ~ 2300N, opening time is 285 ° ~ 315 °, back rest high and low position-1 ~+1, warp stop frame high-low-position-1 ~+1, main jet opening and closing time is 75 ° ~ 180 °, the opening and closing time of first group of pilot jet is 75 ° ~ 120 °, the opening and closing time of second group of pilot jet is 90 ° ~ 150 °, the opening and closing time of the 3rd group of pilot jet is 120 ° ~ 180 °, the opening and closing time of the 4th group of pilot jet is 150 ° ~ 220 °, the opening and closing time of the 5th group of pilot jet is 170 ° ~ 270 °, weft yarn reaches 230 ° ~ 240 °, angle, main jet air pressure 0.25MPa ~ 0.28MPa, pilot jet air pressure 0.3MPa ~ 0.33MPa.
7. the weaving process of aloe fibre dobby according to claim 1, it is characterized in that: described in the trimmed size of aloe fibre dobby produced as follows: Fabric width is 147cm, grey cloth fabric width is 154cm, upper machine reed width is 159.5cm, total quantity of warps is 7530, wherein, 60 × 2, limit yarn; Warp thread and weft yarn are the aloe fibre Pure Yarn of 14.7tex, finished product weft density is respectively 512/10cm and 315/10cm, grey cloth weft density is respectively 492/10cm and 303/10cm, machine upper warp and woof is close is respectively 472/10cm and 276/10cm, full width spends several+304,17 flower, warp-wise tightness 59%, broadwise tightness 36.3%, total tightness degree 73.9%.
8. the weaving process of aloe fibre dobby according to claim 1, is characterized in that: the color matching of described fabric is as follows: the deep blue C of the grass green B of extra white A:
Look, through circulation: 30A35B53A24C6B24C67A35C67A24C6B24C23A, amounts to 418, wherein extra white 240, grass green 47, deep blue 131;
Barry dyeing circulates: 32A25B32A14C4B14C41A24C41A14C4B14C, amounts to 259, wherein extra white 146, grass green 33, deep blue 80;
4260, extra white warp thread, 2310, deep blue warp thread, 840, grass green warp thread, extra white warp thread consumption 7.0666kg/100m, deep blue warp thread yarn-using amount 3.8319kg/100m, grass green warp thread yarn-using amount 1.3934kg/100m, limit yarn warp thread yarn-using amount 0.1991kg/100m, the total yarn-using amount of warp thread is 12.4910kg/100m, extra white weft yarn yarn-using amount 4.2898kg/100m, deep blue weft yarn yarn 2.3506kg/100m, grass green weft yarn yarn-using amount 0.9696kg/100m, the total yarn-using amount of weft yarn is 7.6100kg/100m.
CN201510557901.5A 2015-09-02 2015-09-02 Weaving process for aloe fiber small jacquard fabric CN105239249A (en)