CN107447329A - A kind of aloe modified viscose fiber interweaves with cotton takes the production technology of silver wire inlay cotton crepe - Google Patents

A kind of aloe modified viscose fiber interweaves with cotton takes the production technology of silver wire inlay cotton crepe Download PDF

Info

Publication number
CN107447329A
CN107447329A CN201710804929.3A CN201710804929A CN107447329A CN 107447329 A CN107447329 A CN 107447329A CN 201710804929 A CN201710804929 A CN 201710804929A CN 107447329 A CN107447329 A CN 107447329A
Authority
CN
China
Prior art keywords
yarn
white
light blue
opening
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710804929.3A
Other languages
Chinese (zh)
Inventor
马顺彬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Textile Vocational Technology College
Original Assignee
Nantong Textile Vocational Technology College
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Textile Vocational Technology College filed Critical Nantong Textile Vocational Technology College
Priority to CN201710804929.3A priority Critical patent/CN107447329A/en
Publication of CN107447329A publication Critical patent/CN107447329A/en
Pending legal-status Critical Current

Abstract

Interweave the invention discloses a kind of aloe modified viscose fiber and cotton and take the production technology of silver wire inlay cotton crepe.Present invention design produces a summer and is interweaved with aloe modified viscose fiber and cotton and take silver wire inlay cotton crepe, and after the fabric is collated, surface is creased, and concave-convex sense is strong, is equipped with a small amount of filamentary silver, makes color more dazzling, is preferable high-grade summer clothing fabric.The present invention is set for rational technique, is the basis for producing high-grade fabric.By optimizing each operation from technique, equipment, operation etc. so that effect is than more significant when producing the kind fabric, and loom efficiency reaches 94.2%, and First Grade Percentage Before Cloth Repairing 85.7%, storage top-quality product rate is 98%.

Description

A kind of aloe modified viscose fiber interweaves with cotton takes the production technology of silver wire inlay cotton crepe
Technical field
The invention belongs to fabric knitting field, and in particular to a kind of aloe modified viscose fiber interweaves with cotton takes silver wire inlay The production technology of cotton crepe.
Background technology
Currently, Textile and Clothing Industry of China is just marching toward the period of a high speed development, develops high-grade, personalized wearing fabric As the focus of current weaving face fabric research and development.Because the raw material for making garment material is a lot, how to meet consumer demand, Season needs are adapted to, such as summer clothes fabric requires comfortable, frivolous, ventilative, attractive in appearance.
The content of the invention
Goal of the invention:In order to solve the deficiencies in the prior art, the invention provides a kind of aloe modified viscose fiber and cotton Interweave and take the production technology of silver wire inlay cotton crepe.
Technical scheme:A kind of aloe modified viscose fiber interweaves with cotton takes the production technology of silver wire inlay cotton crepe, including such as Lower step:
(1) weft twisting
Weft yarn is C5.56tex compact spinning strong twisted yarns:2000 sth. made by twisting/m, set twist using wet bath method;By weft yarn at 35~37 DEG C 40~60s is soaked in hot water, is available for loom to use in 4~5h of weft yarn indoor storage after taking-up;Water for immersion should be protected Cleaning is held, water is changed once every 2~3h, in order to avoid pollution yarn;
(2) whole slurry process
Warping and sizing are carried out using LSG A600 types sizing warper, a flower warp thread number 123, are 6 flowers per twisted flower number, Per twisted warp radical 738, warping hank number twists for 7, and the 1st strand is 762, and the 2 to 6th twists as 738, and the 7th twists as 147;
Warp thread is aloe modified viscose silvalin, and the adhesion of the slurry of selection is eager to excel, and formula of size is water 100%, is gathered Acrylic acid 3.5%, PVA205MB 2.5%, penetrant 0.3%;
Sizing technique is:The rate of sizing 11%, regain 8.0%, elongation 2%, speed 50m/min, pH value 7, solid content 9%, slurry viscosity 7s, sizing temperature are 65 DEG C, are 0.3MPa close to bobbin cradle squeezing roller air pressure, close to the gas of drying room squeezing roller Press as 0.5MPa;
The appropriate tension force for increasing side yarn, avoids forming slack list in weaving process;The inspection of reinforcement yarn passage, prevent from scraping Hinder warp thread;It is strict to strengthen production management, carry out the examination of the sizing qualities such as regain, the rate of sizing, elongation, good axial ratio;Beam of a loom Disc is vertical, avoids the occurrence of the defect axle such as rabbet;
(3) process is passed
Porter is 138.5 teeth/10cm, and ground tissue and Selvage Stitch enter using 2, and filamentary silver 1 enters, and it is 63 teeth often to spend dent number, entirely Width dent number is 2355 teeth, and upper machine reed width is 170cm;Comprehensive number of pages uses page 5, and page 1,2,3,4 be comprehensive to be organized and Selvage Stitch with wearing, Wherein it is organized in page 1,2,3,4 and comprehensive middle uses straight arrangement, i.e., 1,2,3,4;Menopause tablet is 4 row, using 1,1,2,2,3,3, 4,4 threading methods;Due to filamentary silver non-refractory, and starching is not required to, therefore 111 filamentary silver bobbins are individually placed to two rows and make simple bobbin by oneself On frame, and default some tension, without the starching of sizing warper and baking apparatus etc., combine by the arranged requirement of color in whole slurry Inserted at locomotive head in expansion reed, so as to meet to produce needs;Filamentary silver penetrate page 5 it is comprehensive in;
(4) weaving process
Weaved using ZAX-e-190 type air-jet looms, for ensure it is woven be smoothed out, mainly from warp tension, Opening process weft insertion techniques etc. are configured;
The size of warp tension, there is direct influence to Fabric Style and loom efficiency, warp tension is big, is advantageous to out Clear shed open;Because warp thread is thin special aloe modified viscose fiber, strongly than relatively low, warp tension should be smaller, will by debugging Warp tension is adjusted to 1200N;
Opening process relates generally to opening time and amount of opening, back rest height, warp stop frame height are low, because fabric is plain weave Tissue, to be advantageous to urgent weft yarn and eliminating open reed, early opening and the high back rest should be used, opening time is 285 °, back beam height For 90mm, depth 50mm, warp stop frame is highly 70mm, depth 15mm, amount of opening 90mm, 80mm, 70mm, 65mm, 60mm;
To ensure that weft yarn can smoothly introduce shed open, the faults such as looped weft are reduced, answer reasonable adjusting weft insertion technique parameter, main jet opens The time is closed as 60 ° -195 °, the opening and closing time of the 1st group of pilot jet is 60 ° -120 °, and the opening and closing time of the 2nd group of pilot jet is 80 ° -150 °, the opening and closing time of the 3rd group of pilot jet is 110 ° -180 °, the opening and closing time of the 4th group of pilot jet for 150 ° - 220 °, the opening and closing time of the 5th group of pilot jet is 180 ° -270 °, and the opening and closing time of the 6th group of pilot jet is 200 ° -300 °;It is main The pressure of nozzle is arranged to 0.35MPa, and the pressure of pilot jet is arranged to 0.38MPa, while to prevent weft yarn retraction from skidding off master Nozzle, the gentle breeze of main burner should tune up, and be arranged to 0.1MPa;In addition, spinner answers running check wefting insertion passage, flyings etc. are prevented Debris blocks wefting insertion passage, causes to stop platform.
As optimization:The finished textile product specifications design is as follows:Fabric width 146cm, fabric breadth are 156cm, total warp Radical 4599, wherein 24 × 2, side yarn;Warp thread is 5.56tex aloe modified viscose silvalins and embedded filamentary silver, weft yarn are C5.56tex compact spinnings strong twisted yarn (2000 sth. made by twisting/m), finished product weft density are respectively 315/10cm and 291/10cm, and fabric passes through Filling density is respectively 277/10cm and 272/10cm, and full width spends number 37 to spend.
As optimization:The fabric warp-wise respectively to add white yarn, light blue yarn and blue yarn as main tone, and Embedded filamentary silver is as auxiliary;Weft yarn uses white yarn;2 Z that weft yarn uses are twisted with the fingers and 2 S twist with the fingers C5.56tex compact spinning heavy twists Yarn (2000 sth. made by twisting/m) is spaced;The fabric tissue is plain weave.
As optimization:The fabric color matching design is as follows:Weft yarn arrangement:It is of the same colour white;Warp Tension Test:White 3, light blue 1, white 1, Indigo plant 1, light blue 3, white 3, filamentary silver 1, white 5, indigo plant 1, light blue 3, indigo plant 2, white 7, light blue 3, indigo plant 1, light blue 3, white 16, light blue 3, blue 1, it is light blue 3, white 21, light blue 3, indigo plant 1, light blue 3, indigo plant 1, light blue 3, white 7, indigo plant 2, light blue 3, indigo plant 2, light blue 3, white 4, filamentary silver 1, white 4, indigo plant 1 is shallow Indigo plant 3, white 3, filamentary silver 1;Warp thread circulation is 123, wherein, white 74, light blue 34, blue 12, filamentary silver 3.
Beneficial effect:Present invention design produces a summer and is interweaved with aloe modified viscose fiber and cotton and take silver wire inlay Cotton crepe, after the fabric is collated, surface is creased, and concave-convex sense is strong, is equipped with a small amount of filamentary silver, makes color more dazzling, is preferable height Shelves summer clothing fabric.The present invention is set for rational technique, is the basis for producing high-grade fabric.By from technique, equipment, behaviour Make etc. optimization each operation so that effect is than more significant when producing the kind fabric, and loom efficiency reaches 94.2%, lower machine one It is 85.7% Deng product rate, storage top-quality product rate is 98%.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, so that the technology of this area Personnel can be better understood from advantages and features of the invention, so as to make apparent boundary to protection scope of the present invention It is fixed.Embodiment described in the invention is only part of the embodiment of the present invention, rather than whole embodiments, based on the present invention In embodiment, the every other implementation that those of ordinary skill in the art are obtained on the premise of creative work is not made Example, belongs to the scope of protection of the invention.
Specific embodiment
1st, product design
1.1 fabric specifications design:
Trimmed size design is as follows:Fabric width 146cm, fabric breadth are 156cm, total quantity of warps 4599, wherein side 24 × 2, yarn.Warp thread is 5.56tex aloe modified viscose silvalins and embedded filamentary silver, and weft yarn is C5.56tex compact spinning heavy twists Yarn (2000 sth. made by twisting/m), finished product weft density are respectively 315/10cm and 291/10cm, and fabric weft density is respectively 277/ 10cm and 272/10cm, full width spends number 37 to spend.
1.2 Fabric Styles and feature design:
Warp-wise is respectively to add white yarn, light blue yarn and blue yarn as main tone, and embedded filamentary silver is as auxiliary. Weft yarn uses white yarn.Because the color of filamentary silver is different from dominant hue, so as to form the filler rod line of light along fabric warp-wise Effect.Simultaneously because 2 Z that weft yarn uses are twisted with the fingers and 2 S twist with the fingers C5.56tex compact spinnings strong twisted yarn (2000 sth. made by twisting/m) and are spaced, After final finishing, because weft yarn shrinks, crape effect is presented in fabric face, there is stronger third dimension.The fabric tissue is flat Line.
The color matching design of 1.3 fabrics:
Warp Tension Test:White 3, light blue 1, white 1, indigo plant 1, light blue 3, white 3, filamentary silver 1, white 5, indigo plant 1, light blue 3, blue 2, white 7, it is light blue 3, indigo plant 1, light blue 3, white 16, light blue 3, indigo plant 1, light blue 3, white 21, light blue 3, indigo plant 1, light blue 3, indigo plant 1, light blue 3, white 7, blue 2, it is light blue 3, indigo plant 2, light blue 3, white 4, filamentary silver 1, white 4, indigo plant 1, light blue 3, white 3, filamentary silver 1.Warp thread circulation is 123, wherein white 74, it is light blue It is 34, blue 12, filamentary silver 3.
Weft yarn arrangement:It is of the same colour white.
2nd, weft twisting
The reinforced sth. made by twisting of yarn, fiber is stretched the internal stress that anti-twisting can be produced after effect in yarn body, so that yarn The twist it is unstable, and using air-jet loom weaving when, air-flow to yarn controling power deficiency, looping of easily twisting together, produce latitude The faults such as contracting, therefore, strong twisted yarn must set twist before weaving.Because weft yarn is C5.56tex compact spinnings strong twisted yarn (2000 sth. made by twisting/m) Requirement can be reached using wet bath method dead twist.Weft yarn is soaked into 40~60s in 35~37 DEG C of hot water, in weft yarn room after taking-up 4~5h of interior storage is available for loom to use.Water for immersion should be kept cleaning, and water is changed once every 2~3h, in order to avoid pollution Yarn.
3rd, whole slurry process
Due to the arranged complexity of fabric color, warping and sizing are carried out using LSG A600 types sizing warper.One flower warp Yarn number 123, it is 6 flowers per twisted flower number, per twisted warp radical 738, warping hank number twists for 7, and the 1st strand is 762, and the 2 to 6th twists For 738, the 7th twists as 147.
Because warp thread is aloe modified viscose silvalin, therefore the adhesion for the slurry selected is eager to excel, and formula of size is water 100%, polyacrylic acid 3.5%, PVA205MB 2.5%, penetrant 0.3%.
Sizing technique is:The rate of sizing 11%, regain 8.0%, elongation 2%, speed 50m/min, pH value 7, solid content 9%, slurry viscosity 7s, sizing temperature are 65 DEG C, are 0.3MPa close to bobbin cradle squeezing roller air pressure, close to the gas of drying room squeezing roller Press as 0.5MPa.
The appropriate tension force for increasing side yarn, avoids forming slack list in weaving process;The inspection of reinforcement yarn passage, prevent from scraping Hinder warp thread;It is strict to strengthen production management, carry out the examination of the sizing qualities such as regain, the rate of sizing, elongation, good axial ratio;Beam of a loom Disc is vertical, avoids the occurrence of the defect axle such as rabbet.
4th, process is passed
Porter is 138.5 teeth/10cm, and ground tissue and Selvage Stitch enter using 2, and filamentary silver 1 enters, and it is 63 teeth often to spend dent number, entirely Width dent number is 2355 teeth, and upper machine reed width is 170cm.Comprehensive number of pages uses page 5, and page 1,2,3,4 be comprehensive to be organized and Selvage Stitch with wearing, Wherein it is organized in page 1,2,3,4 and comprehensive middle uses straight arrangement, i.e., 1,2,3,4.Menopause tablet is 4 row, using 1,1,2,2,3,3, 4,4 threading methods.Due to filamentary silver non-refractory, and starching is not required to, therefore 111 filamentary silver bobbins are individually placed to two rows and make simple bobbin by oneself On frame, and default some tension, without the starching of sizing warper and baking apparatus etc., combine by the arranged requirement of color in whole slurry Inserted at locomotive head in expansion reed, so as to meet to produce needs.Filamentary silver penetrate page 5 it is comprehensive in.
5th, weaving process
Weaved using ZAX-e-190 type air-jet looms.For ensure it is woven be smoothed out, mainly from warp tension, Opening process weft insertion techniques etc. are configured.
The size of warp tension, there is direct influence to Fabric Style and loom efficiency.Warp tension is big, is advantageous to out Clear shed open.Because warp thread is thin special aloe modified viscose fiber, strongly than relatively low, warp tension should be smaller, will by debugging Warp tension is adjusted to 1200N.
Opening process relates generally to opening time and amount of opening, back rest height, warp stop frame height are low, because fabric is plain weave Tissue, to be advantageous to urgent weft yarn and eliminating open reed, early opening and the high back rest should be used, opening time is 285 °, back beam height For 90mm, depth 50mm, warp stop frame is highly 70mm, depth 15mm, amount of opening 90mm, 80mm, 70mm, 65mm, 60mm。
To ensure that weft yarn can smoothly introduce shed open, the faults such as looped weft are reduced, answer reasonable adjusting weft insertion technique parameter, main jet opens The time is closed as 60 ° -195 °, the opening and closing time of the 1st group of pilot jet is 60 ° -120 °, and the opening and closing time of the 2nd group of pilot jet is 80 ° -150 °, the opening and closing time of the 3rd group of pilot jet is 110 ° -180 °, the opening and closing time of the 4th group of pilot jet for 150 ° - 220 °, the opening and closing time of the 5th group of pilot jet is 180 ° -270 °, and the opening and closing time of the 6th group of pilot jet is 200 ° -300 °.By It is the strong twisted yarn of two kinds of different twist directions in weft yarn, to prevent its untwisting, produces broken end or form looped weft fault, it is main and auxiliary to help nozzle Pressure requirements suitably heighten, the pressure of main burner is arranged to 0.35MPa, and the pressure of pilot jet is arranged to 0.38MPa, simultaneously To prevent weft yarn retraction from skidding off main burner, the gentle breeze of main burner should tune up, and be arranged to 0.1MPa.
In addition, spinner answers running check wefting insertion passage, prevent the debris such as flyings from blocking wefting insertion passage, cause to stop platform.
Present invention design produces a summer and is interweaved with aloe modified viscose fiber and cotton and take silver wire inlay cotton crepe, and this is knitted After thing is collated, surface is creased, and concave-convex sense is strong, is equipped with a small amount of filamentary silver, makes color more dazzling, is to take preferable high-grade summer Fabric.The present invention is set for rational technique, is the basis for producing high-grade fabric.By excellent from technique, equipment, operation etc. Change each operation so that for effect than more significant, loom efficiency reaches 94.2% when producing the kind fabric, and First Grade Percentage Before Cloth Repairing is 85.7%, storage top-quality product rate is 98%.

Claims (4)

1. a kind of aloe modified viscose fiber interweaves with cotton takes the production technology of silver wire inlay cotton crepe, it is characterised in that:Including such as Lower step:
(1) weft twisting
Weft yarn is C5.56tex compact spinning strong twisted yarns:2000 sth. made by twisting/m, set twist using wet bath method;By hot water of the weft yarn at 35~37 DEG C 40~60s of middle immersion, it is available for loom to use in 4~5h of weft yarn indoor storage after taking-up;Water for immersion should keep clear It is clean, change water once every 2~3h, in order to avoid pollution yarn;
(2) whole slurry process
Warping and sizing are carried out using LSG A600 types sizing warper, a flower warp thread number 123, is 6 flowers per twisted flower number, often twists Warp thread radical 738, warping hank number are 7 strands, and the 1st twists as 762, and the 2 to 6th strand is 738, and the 7th strand is 147;
Warp thread is aloe modified viscose silvalin, and the adhesion of the slurry of selection is eager to excel, and formula of size is water 100%, polypropylene Acid 3.5%, PVA205MB 2.5%, penetrant 0.3%;
Sizing technique is:The rate of sizing 11%, regain 8.0%, elongation 2%, speed 50m/min, pH value 7, solid content 9%, Slurry viscosity 7s, sizing temperature are 65 DEG C, are 0.3MPa close to bobbin cradle squeezing roller air pressure, and the air pressure close to drying room squeezing roller is 0.5MPa;
The appropriate tension force for increasing side yarn, avoids forming slack list in weaving process;The inspection of reinforcement yarn passage, prevents scratch from passing through Yarn;It is strict to strengthen production management, carry out the examination of the sizing qualities such as regain, the rate of sizing, elongation, good axial ratio;Beam disc for weaving It is vertical, avoid the occurrence of the defect axle such as rabbet;
(3) process is passed
Porter is 138.5 teeth/10cm, and ground tissue and Selvage Stitch enter using 2, and filamentary silver 1 enters, and it is 63 teeth often to spend dent number, full width reed The number of teeth is 2355 teeth, and upper machine reed width is 170cm;Comprehensive number of pages uses page 5, and page 1,2,3,4 be comprehensive to be organized and Selvage Stitch with wearing, wherein Ground is organized in page 1,2,3,4 and comprehensive middle uses straight arrangement, i.e., 1,2,3,4;Menopause tablet is 4 row, is worn using 1,1,2,2,3,3,4,4 Method;Due to filamentary silver non-refractory, and starching is not required to, therefore 111 filamentary silver bobbins is individually placed to two rows and made by oneself on simple bobbin cradle, And default some tension, without the starching of sizing warper and baking apparatus etc., by the arranged requirement of color in sizing warper car Inserted at head in expansion reed, so as to meet to produce needs;Filamentary silver penetrate page 5 it is comprehensive in;
(4) weaving process
Weaved using ZAX-e-190 type air-jet looms, for ensure it is woven be smoothed out, mainly from warp tension, opening Technique weft insertion techniques etc. are configured;
The size of warp tension, there is direct influence to Fabric Style and loom efficiency, warp tension is big, is advantageous to opening or cleaning shuttle Mouthful;Because warp thread is thin special aloe modified viscose fiber, strongly than relatively low, warp tension should be smaller, by debugging, by upper machine Tension adjustment is 1200N;
Opening process relates generally to opening time and amount of opening, back rest height, warp stop frame height are low, because fabric is plain weave group Knit, to be advantageous to urgent weft yarn and eliminating open reed, early opening and the high back rest should be used, opening time is 285 °, and back beam height is 90mm, depth 50mm, warp stop frame are highly 70mm, depth 15mm, amount of opening 90mm, 80mm, 70mm, 65mm, 60mm;
To ensure that weft yarn can smoothly introduce shed open, the faults such as looped weft are reduced, reasonable adjusting weft insertion technique parameter are answered, when main jet opens and closes Between be 60 ° -195 °, the opening and closing time of the 1st group of pilot jet is 60 ° -120 °, the opening and closing time of the 2nd group of pilot jet for 80 ° - 150 °, the opening and closing time of the 3rd group of pilot jet is 110 ° -180 °, and the opening and closing time of the 4th group of pilot jet is 150 ° -220 °, the The opening and closing time of 5 groups of pilot jets is 180 ° -270 °, and the opening and closing time of the 6th group of pilot jet is 200 ° -300 °;Main burner Pressure is arranged to 0.35MPa, and the pressure of pilot jet is arranged to 0.38MPa, while to prevent weft yarn retraction from skidding off main burner, it is main The gentle breeze of nozzle should tune up, and be arranged to 0.1MPa;In addition, spinner answers running check wefting insertion passage, prevent the debris such as flyings from blocking up Wefting insertion passage is filled in, causes to stop platform.
2. aloe modified viscose fiber according to claim 1 interweaves with cotton takes the production technology of silver wire inlay cotton crepe, its It is characterised by:The finished textile product specifications design is as follows:Fabric width 146cm, fabric breadth are 156cm, total quantity of warps 4599 Root, wherein 24 × 2, side yarn;Warp thread is 5.56tex aloe modified viscose silvalins and embedded filamentary silver, and weft yarn is that C5.56tex is tight Close spinning strong twisted yarn (2000 sth. made by twisting/m), finished product weft density is respectively 315/10cm and 291/10cm, and fabric weft density is respectively 277/10cm and 272/10cm, full width spends number 37 to spend.
3. aloe modified viscose fiber according to claim 1 interweaves with cotton takes the production technology of silver wire inlay cotton crepe, its It is characterised by:The fabric warp-wise is respectively to add white yarn, light blue yarn and blue yarn as main tone, and embedded filamentary silver As auxiliary;Weft yarn uses white yarn;2 Z that weft yarn uses are twisted with the fingers and 2 S twist with the fingers C5.56tex compact spinnings strong twisted yarn (2000 Sth. made by twisting/m) it is spaced;The fabric tissue is plain weave.
4. aloe modified viscose fiber according to claim 1 interweaves with cotton takes the production technology of silver wire inlay cotton crepe, its It is characterised by:The fabric color matching design is as follows:Weft yarn arrangement:It is of the same colour white;Warp Tension Test:White 3, light blue 1, white 1, indigo plant 1 is light blue 3, white 3, filamentary silver 1, white 5, indigo plant 1, light blue 3, indigo plant 2, white 7, light blue 3, indigo plant 1, light blue 3, white 16, light blue 3, indigo plant 1, light blue 3, white 21, Light blue 3, indigo plant 1, light blue 3, indigo plant 1, light blue 3, white 7, indigo plant 2, light blue 3, indigo plant 2, light blue 3, white 4, filamentary silver 1, white 4, indigo plant 1, light blue 3, in vain 3, filamentary silver 1;Warp thread circulation is 123, wherein, white 74, light blue 34, blue 12, filamentary silver 3.
CN201710804929.3A 2017-09-08 2017-09-08 A kind of aloe modified viscose fiber interweaves with cotton takes the production technology of silver wire inlay cotton crepe Pending CN107447329A (en)