CN104278410A - Acrylic and Richcel fiber florescent denim and weaving method thereof - Google Patents
Acrylic and Richcel fiber florescent denim and weaving method thereof Download PDFInfo
- Publication number
- CN104278410A CN104278410A CN201410399943.6A CN201410399943A CN104278410A CN 104278410 A CN104278410 A CN 104278410A CN 201410399943 A CN201410399943 A CN 201410399943A CN 104278410 A CN104278410 A CN 104278410A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- denim
- fluorescent
- fluorescence
- acrylic fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides acrylic and Richcel fiber florescent denim and a weaving method thereof. The denim brings the characteristics of acrylic and Richcel fiber into full play, so that the fluffiness, the thermal insulation and the light fastness of the denim in autumn and winter are improved, and the cloth cover has a fluorescent colorful effect.
Description
Technical field:
The invention belongs to garment production technical field, be specifically related to a kind of acrylic fibers and richcel fiber fluorescence denim and weaving method thereof.
Background technology
Jean is a kind of fashion, the dark clothes by people's favor, and along with the raising of people's living standard, require also improving constantly to dress ornament, it is just progressively to aspect development such as functionalization, personalization, variations.Current garment material is advocated comfortable, goodlooking and have functional, require that fabric has frivolous comfortable, high resilience, attractive in appearance and health care, and traditional denim quality is stiffening, solid wear-resisting, thick and heavy warming, obviously, the thick and heavy denim of tradition is unfavorable for embodying arbitrarily, comfortableness, leads wet, gas permeability and also will be a greater impact.Existing jean is a lot, but the defect that most jean exists due to link of selecting materials, prepare, cause the clothes elasticity of processing not good enough, nice and cool not, stiff not fashion.In recent years, continuing to bring out of tencel material, brings tremendous increase space to the exploitation of jean, by using tencel, give jeans functional, comfortableness, meet people to jeans conformability, stretching, functional etc. in demand.
Acrylic fibers are a kind of synthetic fiber, and its performance pole is like wool, and elasticity is better, and when extending 20%, rebound degree still can keep 65%, and fluffy curling and soft, warmth retention property is higher than wool by 15%, has the title of synthetic wool; Intensity 22.1 ~ 48.5cN/dtex is higher than wool 1 ~ 2.5 times; Sun-proof function admirable.
Richcel fiber (Richcel) is polynosic (Polynosic) fiber adopting Japanese Japan to spin proprietary technology and material system production.Richcel fiber raw material is that natural coniferous tree refines wood pulp, and resource is renewable, and discarded object can natural degradation, safety and environmental protection.Richcel fiber has high strength, high wet modulus, high polymerization degree and suitable degree of stretching, good hygroscopicity, its performance and sky silk (Tencel) fiber close; The market price is significantly less than tencel fiber, comparatively close with model (Modal).Producing pure Richcel fabric DIMENSIONAL STABILITY is better, and shrinkage factor is less, more washable, endurable; Lovely luster, the features such as drapability is good.
Have no acrylic fibers and richcel fiber at present simultaneously for the production of fluorescence denim.Due to acrylic fibers and richcel fiber nature difference larger, in sizing process, greatly fluorescent effect can be reduced after needing Fluorescent Acrylic Fiber to dye, for the fluorescent effect making the Fluorescent Acrylic Fiber after dyeing can keep good, comparatively complete chromatogram can be reached again, need to consider to select applicable coloring agent and dyeing.
Summary of the invention:
The object of this invention is to provide a kind of acrylic fibers and richcel fiber fluorescence denim.
Be specifically related to a kind of fluorescence denim, described fluorescent denim fabric warp thread is acrylic fibers and beautiful match blended yarn, and weft yarn is cotton yarn.Acrylic fibers described in above-mentioned fluorescence denim account for the 20%-30% of acrylic fibers and beautiful match blended yarn, and Li Sai accounts for the 70%-80% of acrylic fibers and beautiful match blended yarn.Further preferably acrylic fibers account for 25%, Li Sai of acrylic fibers and beautiful match blended yarn and account for 75% of acrylic fibers and beautiful match blended yarn.
Another object of the present invention carries the weaving method of a kind of acrylic fibers and richcel fiber fluorescence denim and weaving method thereof.Comprise following steps: 1. winder
2. warping batch warping;
3. pulp cationic fluorescent dyestuff dyes with the cation dyes with fluorescent effect, and the technical recipe of dyeing is dye strength 0.3%-2.0%; Dye bath pH value 3.5-5.5; Bath raio bath raio 1-1.5:100; For the fluorescent effect making the Fluorescent Acrylic Fiber after dyeing can keep good, comparatively complete chromatogram can be reached again, select three primary colors cation dyes to carry out combination dyeing to Fluorescent Acrylic Fiber; Dyeing is be incubated-naturally cool-washing-oven dry under 70 DEG C of yarns enter to contaminate-be warmed up to uniform temperature;
4. employing 12 of gaiting is combined, and gaits along the method for wearing;
5. weaving warp yarns and weft yarns;
6. singe.
Above-mentioned weaving method step 3. in the technical recipe of dyeing be dye strength 0.5%, dyeing temperature 85 DEG C, dyeing time 75min, Value in Dyeing Process 3.5, bath raio is 1:100.Described three primary colors cation dyes are selected from one or more in fluorescein 10GFF, bright red X-5GN, blue X-GRRL and red X-GRL.While dyeing, fluorescent whitening agent TF-920 can be added.In the weaving process of above-mentioned weaving method, enter the sword time 55 °-60 °, move back the sword time 275 °-285 °, ancestor is 310 ° at ordinary times, and shed opening is 32mm, ancestor at ordinary times between frame top be 132mm. loom rotating speed apart from the distance of heald frame side rails upper limb be 400r/min, opening time 310 °, back beam height+4, open height 30mm, 100mm, up and down 80mm before and after warp stop frame, warp tension position is 3 holes.
Above-mentioned weaving method singe in operation, process conditions are flame temperature 800 DEG C, fabric speed of a motor vehicle 90m/min, and number of times two positive two of singing is anti-, flame and cloth distance 0.6-1.0 centimetre
The specification requirements of acrylic fibers richcel fiber fluorescence denim
Institutional framework: 3/1 right tiltedly fabric width: 148 centimetres
Through weft yarn 9
s+ RSB8
sx R8
s
Thread count: 284 × 210/10cm
Warp-wise Suo≤-2.0% broadwise Suo≤-1.0%
Process chart is as shown in Figure 1:
Due to greatly fluorescent effect can be reduced after Fluorescent Acrylic Fiber dyeing in the present invention, need the cation dyes selected some cationic fluorescent dyestuffs He there is fluorescent effect, for the fluorescent effect making the Fluorescent Acrylic Fiber after dyeing can keep good, comparatively complete chromatogram can be reached again, select three primary colors cation dyes fluorescein 10GFF, bright red X-5GN and blue X-GRRL, under optimum dyeing process conditions, combination dyeing is carried out to Fluorescent Acrylic Fiber.Some fluorescent whitening agents and cation dyes are adopted to carry out brightening dyeing with bath.Experimental result shows: when the combination dyeing of tricolor dye, takes suitable dyestuff proportioning that Fluorescent Acrylic Fiber can be made to obtain comparatively complete chromatogram; When fluorescent whitening agent and cation dyes brighten dyeing with bath, fluorescent whitening agent TF-920 can further improve the fluorescent effect of Fluorescent Acrylic Fiber.
The invention provides a kind of acrylic fibers and richcel fiber fluorescence denim and weaving method thereof, this cloth gives full play to the characteristic of acrylic fibers and richcel fiber, improves fluffy, the warming and light resistance of autumn and winter season denim, makes again cloth cover have the effect of fluorescent magic color.
accompanying drawing illustrates:
Fig. 1: acrylic fibers and richcel fiber fluorescence denim weaving process flow chart
specific embodiment:
Hereafter the preferred embodiment of the inventive method is described in more detail.It will be appreciated by those skilled in the art that these preferred embodiments are only used to example the present invention instead of form limitation ot it.
Embodiment 1:
Warp thread adopts acrylic fibers and beautiful match blended yarn, and weft yarn adopts cotton yarn; Wherein acrylic fibers account for 20%, Li Sai of acrylic fibers and beautiful match blended yarn proportion and account for 80% of acrylic fibers and beautiful match blended yarn proportion.Thread count: 284 × 210/10cm; Fabric width: 148 centimetres.Warp-wise Suo≤-2.0% broadwise Suo≤-1.0%.
The acrylic fibers of the present embodiment and the weaving method of richcel fiber fluorescence denim, described weaving process is formed by warp thread and weft yarns, warp thread through winder, warping, pulp, pass, tying-in, weave, grey cloth inspection process, weft yarn through cylinder yarn through dead twist after enter weaving process with warp thread;
Main production process main points are:
In winding procedure, slack winder generally adopts the linear velocity of 800-1000m/min to be advisable.Pine formula package arm pressure selection, at 2-3N overfeeding, compensate for the tension variation caused by the annoying unwinding of feeding package.Before the last drawing-off of overfeeding roller in winding process, yarn is carried out.General yarn is selected at about 20-25% as well.Tension force arranges 5g-10g.Temperature and Humidity Control is about 60-70%.
In warping process, warping is being weaved cotton cloth on axle by the warp thread of certain radical by the length and width close wind of regulation, and general warping technology is divided into section warping and batch warping.In use batch warping situation, one is walk yarn distance, and two is that batch warping is generally suitable for needing sizing, and namely yam surface wraps up one deck sizing, facilitates woven situation.Batch warping production efficiency is high, and sheet thread tension is relatively more even, and warp quality is better, is suitable for producing in enormous quantities.In warping process, warp tension should be even, and keep constant tension in warping process, thus in minimizing rear road processing, warp end break and float reduce the frictionally damage to yarn body simultaneously as far as possible.Tension force control range 70-80CN; Package size impact yarn unwinding tension, we adopt collective's creeling; Adopt staged and layered configuration weight of tension ring: front row overweights rear row, and middle level overweights upper and lower layer; Adopt point row's denting method speed of beaming to improve, Yarn break will increase, and affects warping efficiency, is advisable with middling speed 450-500m/min; Trim-beam number and warping radical determination principle: the few axle of bull as far as possible.
In sizing operation, if sizing quality does not reach requirement, easily cause warp end break, " three jump " fault increases.Sizing adopts tandem sizing box, should be powerful to improve warp thread.Designing sizing technology follow soak into be main, be coated to be auxiliary, strengthen the principle of protecting and stretching, adopt " two high one low " sizing technique.First dye with cationic fluorescent dyestuff and the cation dyes with fluorescent effect, the technical recipe of dyeing is dye strength 0.5%, dyeing temperature 85 DEG C, dyeing time 75min, Value in Dyeing Process 3.5, bath raio 1:100.Dyeing: 70 DEG C of yarns are incubated-naturally cool-washing-oven dry under entering to contaminate-be warmed up to uniform temperature.For the fluorescent effect making the Fluorescent Acrylic Fiber after dyeing can keep good, comparatively complete chromatogram can be reached again, select three primary colors cation dyes fluorescein 10GFF, bright red X-5GN and blue X-GRRL, combination dyeing is carried out to Fluorescent Acrylic Fiber.When fluorescent whitening agent and cation dyes brighten dyeing with bath, add the fluorescent effect that fluorescent whitening agent TF-920 can further improve Fluorescent Acrylic Fiber.
Gait in operation, adopt 12 to combine, gait along the method for wearing, institutional framework of gaiting: 3/1 is tiltedly right
In weaving process, enter the sword time 55 °-60 °, move back the sword time 275 °-285 °, ancestor is 310 ° at ordinary times, and shed opening is 32mm, ancestor at ordinary times between frame top be 132mm. loom rotating speed apart from the distance of heald frame side rails upper limb be 400r/min, opening time 310 °, back beam height+4, open height 30mm, 100mm, up and down 80mm before and after warp stop frame, warp tension position is 3 holes.
In running repair operation, by cloth inspecting machine, perching is carried out to the grey cloth woven, defectively knit flaw point by manually to repair.
Singe in operation, process conditions: flame temperature 800 DEG C, fabric speed of a motor vehicle 90m/min, number of times two positive two of singing is anti-, flame and cloth distance 0.8 centimetre
Fixed grade can will be put in storage after finished product package, warp-wise Suo≤-2.0% broadwise Suo≤-1.0%
Embodiment 2:
Weaving method is except slashing technique, and other step is with embodiment 1, and warp thread adopts acrylic fibers and beautiful match blended yarn, and weft yarn adopts cotton yarn; Wherein acrylic fibers account for 30%, Li Sai of acrylic fibers and beautiful match blended yarn proportion and account for 70% of acrylic fibers and beautiful match blended yarn proportion.。Thread count: 284 × 210/10cm; Fabric width: 148 centimetres.Warp-wise Suo≤-2.0% broadwise Suo≤-1.0%.
In sizing operation, if sizing quality does not reach requirement, easily cause warp end break, " three jump " fault increases.Sizing adopts tandem sizing box, should be powerful to improve warp thread.Designing sizing technology follow soak into be main, be coated to be auxiliary, strengthen the principle of protecting and stretching, adopt " two high one low " sizing technique.First dye with cationic fluorescent dyestuff and the cation dyes with fluorescent effect, the process conditions of dyeing are dye strength 2.0%, dyeing temperature 85 DEG C, dyeing time 75min, Value in Dyeing Process 5.5, bath raio 1:100; .Dyeing: 70 DEG C of yarns are incubated-naturally cool-washing-oven dry under entering to contaminate-be warmed up to uniform temperature; For the fluorescent effect making the Fluorescent Acrylic Fiber after dyeing can keep good, comparatively complete chromatogram can be reached again, select three primary colors cation dyes fluorescein 10GFF, bright red X-5GN and blue X-GRRL, combination dyeing is carried out to Fluorescent Acrylic Fiber.When fluorescent whitening agent and cation dyes brighten dyeing with bath, add the fluorescent effect that fluorescent whitening agent TF-920 can further improve Fluorescent Acrylic Fiber.
Embodiment 3:
Weaving method is except slashing technique, and other step is with embodiment 1, and warp thread adopts acrylic fibers and beautiful match blended yarn, and weft yarn adopts cotton yarn; Wherein acrylic fibers account for 25%, Li Sai of acrylic fibers and beautiful match blended yarn proportion and account for 75% of acrylic fibers and beautiful match blended yarn proportion.。Thread count: 284 × 210/10cm; Fabric width: 148 centimetres.Warp-wise Suo≤-2.0% broadwise Suo≤-1.0%.
In sizing operation, if sizing quality does not reach requirement, easily cause warp end break, " three jump " fault increases.Sizing adopts tandem sizing box, should be powerful to improve warp thread.Designing sizing technology follow soak into be main, be coated to be auxiliary, strengthen the principle of protecting and stretching, adopt " two high one low " sizing technique.First dye with cationic fluorescent dyestuff and the cation dyes with fluorescent effect, the process conditions of dyeing are dye strength 0.3%, dyeing temperature 85 DEG C, dyeing time 75min, Value in Dyeing Process 4.5.Dyeing: 70 DEG C of yarns are incubated-naturally cool-washing-oven dry under entering to contaminate-be warmed up to uniform temperature; For the fluorescent effect making the Fluorescent Acrylic Fiber after dyeing can keep good, comparatively complete chromatogram can be reached again, select three primary colors cation dyes fluorescein 10GFF, bright red X-5GN and blue X-GRRL, combination dyeing is carried out to Fluorescent Acrylic Fiber.When fluorescent whitening agent and cation dyes brighten dyeing with bath, add the fluorescent effect that fluorescent whitening agent TF-920 can further improve Fluorescent Acrylic Fiber.
Claims (9)
1. a fluorescence denim, is characterized in that, described fluorescent denim fabric warp thread is acrylic fibers and beautiful match blended yarn, and weft yarn is cotton yarn.
2. fluorescence denim according to claim 1, is characterized in that, described acrylic fibers account for the 20%-30% of acrylic fibers and beautiful match blended yarn, and Li Sai accounts for the 70%-80% of acrylic fibers and beautiful match blended yarn.
3. fluorescence denim according to claim 2, is characterized in that, described 25%, Li Sai of acrylic fibers and the beautiful match blended yarn that account for accounts for 75% of acrylic fibers and beautiful match blended yarn.
4. a weaving method for the fluorescence denim as described in as arbitrary in claims 1 to 3, is characterized in that, comprise following steps:
1) winder;
2) warping batch warping;
3) pulp cationic fluorescent dyestuff dyes with the cation dyes with fluorescent effect, and the technical recipe of dyeing is dye strength 0.3%-2.0%; Dye bath pH value 3.5-5.5; Bath raio bath raio 1-1.5:100; For the fluorescent effect making the Fluorescent Acrylic Fiber after dyeing can keep good, comparatively complete chromatogram can be reached again, select three primary colors cation dyes to carry out combination dyeing to Fluorescent Acrylic Fiber; Dyeing is be incubated-naturally cool-washing-oven dry under 70 DEG C of yarns enter to contaminate-be warmed up to uniform temperature;
4) employing 12 of gaiting is combined, and gaits along the method for wearing;
5) weaving warp yarns and weft yarns;
6) singe.
5. the weaving method of fluorescence denim according to claim 4, is characterized in that: the technical recipe of the dyeing in described step 3 is dye strength 0.5%, dyeing temperature 85 DEG C, dyeing time 75min, Value in Dyeing Process 3.5, and bath raio is 1:100.
6. the weaving method of fluorescence denim according to claim 4, is characterized in that: described three primary colors cation dyes are selected from one or more in fluorescein 10GFF, bright red X-5GN, blue X-GRRL or red X-GRL.
7. according to the weaving method of the arbitrary described fluorescence denim of claim 4 to 7, it is characterized in that: while dyeing, add fluorescent whitening agent TF-920.
8. the weaving method of fluorescence denim according to claim 4, it is characterized in that: in described weaving process, enter the sword time 55 °-60 °, move back the sword time 275 °-285 °, ancestor is 310 ° at ordinary times, shed opening is 32mm, ancestor at ordinary times between frame top be 132mm. loom rotating speed apart from the distance of heald frame side rails upper limb be 400r/min, opening time 310 °, back beam height+4, open height 30mm, 100mm, up and down 80mm before and after warp stop frame, warp tension position is 3 holes.
9. the weaving method of fluorescence denim according to claim 4, is characterized in that: described singes in operation, and process conditions are flame temperature 800 DEG C, fabric speed of a motor vehicle 90m/min, and number of times two positive two of singing is anti-, flame and cloth distance 0.6-1.0 centimetre.