CN105237043A - 一种水性高性能低温陶瓷釉及其制备方法 - Google Patents

一种水性高性能低温陶瓷釉及其制备方法 Download PDF

Info

Publication number
CN105237043A
CN105237043A CN201510781434.4A CN201510781434A CN105237043A CN 105237043 A CN105237043 A CN 105237043A CN 201510781434 A CN201510781434 A CN 201510781434A CN 105237043 A CN105237043 A CN 105237043A
Authority
CN
China
Prior art keywords
water
aqueous
glaze
ceramic glaze
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510781434.4A
Other languages
English (en)
Inventor
张里艺
潘财亮
卢成堆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WENZHOU CIJUESHI TECHNOLOGY Co Ltd
Original Assignee
WENZHOU CIJUESHI TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WENZHOU CIJUESHI TECHNOLOGY Co Ltd filed Critical WENZHOU CIJUESHI TECHNOLOGY Co Ltd
Priority to CN201510781434.4A priority Critical patent/CN105237043A/zh
Publication of CN105237043A publication Critical patent/CN105237043A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种水性高性能低温陶瓷釉。其组分及所占质量分数比例如下:水15-40份;水性树脂30-70份;水性助剂5-15份;有机硅改性固化剂5-9份;水性硅溶胶2-4份;所述水性树脂为有机硅改性树脂;所述水性助剂包括水性分散剂、水性消泡剂、水性流变助剂、水性附着力促进剂、水性防流挂助剂、水性PH调节剂中的一种或两种及以上的组合。该发明简单易行,由于加入的助剂的辅助作用,水釉成膜后釉膜光泽可达120以上,硬度可达8H,耐刮檫性能优异,耐高温、耐水、耐酸碱性能很好。

Description

-种水性高性能低溫陶瓷釉及其制备方法
技术领域
[0001] 本发明设及陶瓷表面涂装领域,具体设及一种水性高性能低溫陶瓷釉及其制备方 法。
背景技术
[0002] 一般陶瓷都必须经过高溫烧制,才能得到瓷釉高光泽、高硬度、高耐酸碱性等优异 性能。陶瓷烧制上釉整体工艺复杂,而且烧制过程溫度必须在1000摄氏度W上,严重耗能, 与环保节能相违背。本专利提出一种水性高性能低溫陶瓷釉及其制备方法。
[0003] 水性陶瓷釉是一种使用水为稀释剂的涂装用釉,由于其使用水性成膜物质和水性 助剂为原料,经过低溫烘烤即可达到高性能要求,节能环保,运对传统陶瓷工艺的升级是一 种质的飞跃。
发明内容
[0004] 本发明提供一种可在陶瓷表面代替陶瓷釉的水性釉,各种性能最大限度接近陶瓷 釉,并且拥有环保无毒节能等特点。
[0005] 所述水性釉至少包括W下组分,各组分及组分的质量分数比重范围分别为: 水:15-40 水性陶瓷树脂:30-70 水性助剂:5-15 有机娃改性固化剂:5-9 水性娃溶胶:2-4 优选为,所述水性树脂为有机娃改性树脂; 优选为,所述水性助剂包括水性分散剂、水性消泡剂、水性流变助剂、水性附着力促进 剂、水性防流挂助剂、水性PH调节剂中的一种或两种及W上的组合。
[0006] 一种水性陶瓷釉的制备方法,其特征包括: 制备A组分水性陶瓷树脂分散液; 先将水性树脂、水和Kl调节剂加入分散设备揽拌均匀的混合液一; 在混合液一中加入水性助剂,高速分散半小时,得到混合液二; 再混合液二中加入水性娃溶胶,高速分散半小时,即得水性陶瓷树脂分散液。
[0007] 制备水性陶瓷釉; 取10公斤水性陶瓷树脂分散液,加入2. 5公斤有机娃改性固化剂,高速分散10分钟并 过滤即得水性陶瓷釉; 优选为,该陶瓷釉使用有时间限制,必须在制备完后4小时内使用完毕。
[000引本发明提供了一种水性透明陶瓷釉,由水性树脂、水性助剂、水性固化剂、水性娃 溶胶组成。本发明还提供了一种水性陶瓷釉的制备方法,首先制备A组分水性陶瓷釉树脂 分散液,再加入有机娃改性固化剂,高速分散均匀,最后制得水性陶瓷釉。本发明所述制备 方法简单易行,由于加入的助剂的辅助作用,水釉成膜后釉膜光泽可达120W上,硬度可达 細,耐刮擦性能优异,耐高溫、耐水、耐酸碱性能很好。
具体实施方式
[0009] 为了能更好的解决本发明的技术方案,一下将举例具体实施案例来说明,但运些 具体案例不应限制本发明的保护范围。
[0010] 案例一;
Figure CN105237043AD00041
优选为,案例一具体操作步骤如下: 步骤一:先将水性树脂、水和PH调节剂加入分散设备揽拌均匀; 步骤二:在混合液中按表格依次加入水性助剂,高速分散半小时; 步骤=:加入水性娃溶胶,高速分散半小时,即得水性陶瓷树脂分散液; 步骤四:在100公斤分散液中加入2. 5公斤有机娃改性固化剂,高速分散10分钟并过 滤即得水性陶瓷釉。
[0011] 本发明实施,具有如下优势: 本发明的水性金属涂装烤釉不含甲苯、二甲苯、甲醒、游离TDI有毒重金属等成分,无 毒无刺激性气味,对人体无害,不污染环境; 本发明的水性金属涂装烤釉不燃不爆,釉膜光泽可达120W上,硬度可达細,耐刮擦性 能优异,耐高溫、耐水、耐酸碱性能很好。
[0012] 本发明的水性陶瓷釉适合喷涂、刷涂、淋涂、浸涂,釉膜固化只需90度烘烤一小 时,性能可替代传统工艺的上釉烧制工艺,环保节能。
[0013] 本发明的水性釉能达到W下指标:
Figure CN105237043AD00042
[0014] W上对本发明提供的一种水性高性能低溫陶瓷釉及其制备方法进行了详细的介 绍,本文中应用的具体案例对发明及实施方式进行了阐述,案例仅用于帮助理解本发明技 术方案及其核屯、思想,应当指出,对于本技术领域的普通人员来说,在不脱离本发明原理的 前提下,还可W对本发明进行若干改进和修饰,运些改进和修饰也在本发明权利要求范围 内。

Claims (2)

1. 一种水性高性能低温陶瓷釉,特征在于,其组分及所占质量分数比例如下:水15-40 份;水性树脂30-70份;水性助剂5-15份;有机硅改性固化剂5-9份;水性硅溶胶2-4份; 所述水性树脂为有机硅改性树脂;所述水性助剂包括水性分散剂、水性消泡剂、水性流变助 剂、水性附着力促进剂、水性防流挂助剂、水性PH调节剂中的一种或两种及以上的组合。
2. 权利要求1所述水性高性能低温陶瓷釉的制备方法,特征在于,包括:在树脂中加入 水、PH调节剂分散后加入水性助剂,再加入水性硅溶胶得到低温水性陶瓷釉分散液;将所 述分散液中加入质量比为4:1的有机硅改性固化剂,搅拌均匀,即得到低温水性陶瓷釉。
CN201510781434.4A 2015-11-16 2015-11-16 一种水性高性能低温陶瓷釉及其制备方法 Pending CN105237043A (zh)