CN105170890A - 一种可提高铸件光洁度的铸造涂料 - Google Patents
一种可提高铸件光洁度的铸造涂料 Download PDFInfo
- Publication number
- CN105170890A CN105170890A CN201510603529.7A CN201510603529A CN105170890A CN 105170890 A CN105170890 A CN 105170890A CN 201510603529 A CN201510603529 A CN 201510603529A CN 105170890 A CN105170890 A CN 105170890A
- Authority
- CN
- China
- Prior art keywords
- parts
- casting
- modified straw
- straw ash
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及铸造领域,更具体的说涉及一种可提高铸件光洁度的铸造涂料,其特征在于包括下列重量份的组分:15-20份硅藻土、2-5份二氧化钛、2-3份硫酸铝、5-7份硅溶胶、1-2份水性交联剂、0.5-1份水性增稠剂、1-2份有机粘连剂、70-80份乙醇、1-2份膨润土悬浮剂、10-15份正辛醇、1-3份马来酸酐、20-25份改性秸秆灰分,本发明采用的原材料种类少,易于配置,价格低廉,另外加入的改性秸秆灰分有助于提高本发明的强度和稳定性,在涂层中大量高度分散,进一步的提高了涂层的致密性、粘稠性及高温耐磨性,对提高抗粘砂性和抗夹砂性起着重要的作用,本发明可以提高铸件表面的光洁度。
Description
技术领域:
本发明涉及铸造领域,更具体的说涉及一种可提高铸件光洁度的铸造涂料。
背景技术:
砂型铸造用的涂料,主要为了屏蔽砂型和金属液体之间相互作用,在浇铸温度下形成致密耐火涂层,放置金属液体渗入到砂型中,同时由于砂型的材料在高温下分解产生气体,涂料可以防止进入金属液体中,影响铸件的表面光洁度。随着铸造业的快速发展,对铸造工件表面质量的要求越来越高,对砂型表面涂料的要求也随之增强,一般都必须要求质量均一、粘结性优良、耐水耐热性强,且在常温和高压下性质稳定,易于涂刷,在浇铸时能达到防止粘砂、夹砂等缺陷,从而得到表面光洁的铸件。
发明内容:
本发明所要解决的技术问题在于克服现有的技术缺陷提供一种可提高铸件光洁度的铸造涂料。
本发明所要解决的技术问题采用以下的技术方案来实现:
一种可提高铸件光洁度的铸造涂料,其特征在于包括下列重量份的组分:15-20份硅藻土、2-5份二氧化钛、2-3份硫酸铝、5-7份硅溶胶、1-2份水性交联剂、0.5-1份水性增稠剂、1-2份有机粘连剂、70-80份乙醇、1-2份膨润土悬浮剂、10-15份正辛醇、1-3份马来酸酐、20-25份改性秸秆灰分。
进一步的,所述的改性秸秆灰分包括下列重量份的组分:90-100份灰分、2-3份增韧剂、5-8份钛白粉、2-4份乳化剂、6-9份六偏磷酸钠、1-2份二甲基有机硅油、2-4份云母粉、3-5份气相二氧化硅、1-2份助剂。
进一步的,所述的改性秸秆灰分的制备方法为:将各原料加入高速捏合机中,升温至200-230℃,保温搅拌8-11min后,出料得成品。
一种可提高铸件光洁度的铸造涂料的制备方法,其特征在于包括下列步骤:
(1)将硅溶胶、硅藻土、二氧化钛、硫酸铝投入到带搅拌器的反应釜中,启动搅拌并缓慢升温到80-90℃,加入水性交联剂、水性增稠剂、膨润土悬浮剂,溶解反应两个小时,然后冷却至常温;
(2)将有机粘连剂、正辛醇、马来酸酐和改性秸秆灰分放入乙醇中均匀混合,然后加入步骤(1)得到的混合物,均匀搅拌;
(3)将步骤(2)得到的混合物在胶体磨中研磨8-12分钟,即得到成品。
本发明采用的原材料种类少,易于配置,价格低廉,另外加入的改性秸秆灰分有助于提高本发明的强度和稳定性,在涂层中大量高度分散,进一步的提高了涂层的致密性、粘稠性及高温耐磨性,对提高抗粘砂性和抗夹砂性起着重要的作用,本发明可以提高铸件表面的光洁度。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1:一种可提高铸件光洁度的铸造涂料,其特征在于包括下列重量份的组分:15份硅藻土、2份二氧化钛、2份硫酸铝、5份硅溶胶、1份水性交联剂、0.5份水性增稠剂、1份有机粘连剂、70份乙醇、1份膨润土悬浮剂、10份正辛醇、1份马来酸酐、20份改性秸秆灰分。
改性秸秆灰分包括下列重量份的组分:90份灰分、2份增韧剂、5份钛白粉、2份乳化剂、6份六偏磷酸钠、1份二甲基有机硅油、2份云母粉、3份气相二氧化硅、1份助剂。
改性秸秆灰分的制备方法为:将各原料加入高速捏合机中,升温至200℃,保温搅拌8min后,出料得成品。
一种可提高铸件光洁度的铸造涂料,其特征在于包括下列步骤:
(1)将硅溶胶、硅藻土、二氧化钛、硫酸铝投入到带搅拌器的反应釜中,启动搅拌并缓慢升温到80℃,加入水性交联剂、水性增稠剂、膨润土悬浮剂,溶解反应两个小时,然后冷却至常温;
(2)将有机粘连剂、正辛醇、马来酸酐和改性秸秆灰分放入乙醇中均匀混合,然后加入步骤(1)得到的混合物,均匀搅拌;
(3)将步骤(2)得到的混合物在胶体磨中研磨8分钟,即得到成品。
实施例2:一种可提高铸件光洁度的铸造涂料,其特征在于包括下列重量份的组分:20份硅藻土、5份份二氧化钛、3份硫酸铝、7份硅溶胶、2份水性交联剂、1份水性增稠剂、2份有机粘连剂、80份乙醇、2份膨润土悬浮剂、15份正辛醇、3份马来酸酐、25份改性秸秆灰分。
改性秸秆灰分包括下列重量份的组分:100份灰分、3份增韧剂、8份钛白粉、4份乳化剂、9份六偏磷酸钠、2份二甲基有机硅油、4份云母粉、5份气相二氧化硅、2份助剂。
改性秸秆灰分的制备方法为:将各原料加入高速捏合机中,升温至230℃,保温搅拌11min后,出料得成品。
一种可提高铸件光洁度的铸造涂料,其特征在于包括下列步骤:
(1)将硅溶胶、硅藻土、二氧化钛、硫酸铝投入到带搅拌器的反应釜中,启动搅拌并缓慢升温到90℃,加入水性交联剂、水性增稠剂、膨润土悬浮剂,溶解反应两个小时,然后冷却至常温;
(2)将有机粘连剂、正辛醇、马来酸酐和改性秸秆灰分放入乙醇中均匀混合,然后加入步骤(1)得到的混合物,均匀搅拌;
(3)将步骤(2)得到的混合物在胶体磨中研磨12分钟,即得到成品。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种可提高铸件光洁度的铸造涂料,其特征在于包括下列重量份的组分:15-20份硅藻土、2-5份二氧化钛、2-3份硫酸铝、5-7份硅溶胶、1-2份水性交联剂、0.5-1份水性增稠剂、1-2份有机粘连剂、70-80份乙醇、1-2份膨润土悬浮剂、10-15份正辛醇、1-3份马来酸酐、20-25份改性秸秆灰分。
2.根据权利要求1所述的一种可提高铸件光洁度的铸造涂料,其特征在于所述的改性秸秆灰分包括下列重量份的组分:90-100份灰分、2-3份增韧剂、5-8份钛白粉、2-4份乳化剂、6-9份六偏磷酸钠、1-2份二甲基有机硅油、2-4份云母粉、3-5份气相二氧化硅、1-2份助剂。
3.根据权利要求2所述的一种可提高铸件光洁度的铸造涂料,其特征在于所述的改性秸秆灰分的制备方法为:将各原料加入高速捏合机中,升温至200-230℃,保温搅拌8-11min后,出料得成品。
4.一种可提高铸件光洁度的铸造涂料的制备方法,其特征在于包括下列步骤:
(1)将硅溶胶、硅藻土、二氧化钛、硫酸铝投入到带搅拌器的反应釜中,启动搅拌并缓慢升温到80-90℃,加入水性交联剂、水性增稠剂、膨润土悬浮剂,溶解反应两个小时,然后冷却至常温;
(2)将有机粘连剂、正辛醇、马来酸酐和改性秸秆灰分放入乙醇中均匀混合,然后加入步骤(1)得到的混合物,均匀搅拌;
(3)将步骤(2)得到的混合物在胶体磨中研磨8-12分钟,即得到成品。