CN104084528A - 一种易剥离醇基铸造涂料及其制作方法 - Google Patents

一种易剥离醇基铸造涂料及其制作方法 Download PDF

Info

Publication number
CN104084528A
CN104084528A CN201410266637.5A CN201410266637A CN104084528A CN 104084528 A CN104084528 A CN 104084528A CN 201410266637 A CN201410266637 A CN 201410266637A CN 104084528 A CN104084528 A CN 104084528A
Authority
CN
China
Prior art keywords
stir
add
parts
minute
alcohol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410266637.5A
Other languages
English (en)
Other versions
CN104084528B (zh
Inventor
黄浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiaxing Ruyun Construction Technology Co.,Ltd.
Original Assignee
Wuhu Hongkun Auto Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Hongkun Auto Parts Co Ltd filed Critical Wuhu Hongkun Auto Parts Co Ltd
Priority to CN201410266637.5A priority Critical patent/CN104084528B/zh
Publication of CN104084528A publication Critical patent/CN104084528A/zh
Application granted granted Critical
Publication of CN104084528B publication Critical patent/CN104084528B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种易剥离醇基铸造涂料，其特征在于，由下列重量份的原料制成：耐火砖废料45-60、高铝矾土熟料55-70、凹凸棒土2-3、苯丙乳液3-5、氟硅酸钠0.5-0.8、氧化铝0.4-0.7、HES阻燃剂0.2-0.5、硫酸钡1-2、氧化锌1.2-3.2、麦秸秆12-16、聚乙烯醇羧丁醛5-9、乙醇40-60、助剂4-7；本发明提供的易剥离醇基铸造涂料，具有易剥离、强度高、透气性好、耐高温等性能；使用本发明的产品，在加工过程中模样不易变形，铸件表面几乎没有孔隙、粘砂，铸件质量大大提高。

Description

一种易剥离醇基铸造涂料及其制作方法
技术领域
本发明涉及铸造涂料领域，具体涉及一种易剥离醇基铸造涂料及其制作方法。
背景技术
铸造涂料是指用来涂敷在型腔或砂芯表面，以改变其表面耐火度、化学稳定性、抗金属冲刷性、抗粘砂性等性能的铸造辅助材料，它是由多种性质不同的材料组成的分散系，其组成主要包括耐火材料、悬浮剂、载体、粘结剂及特殊添加剂等组成。作用于铸件时要求涂料有良好的工艺性能、工作性能、质量稳定性以及施涂重现性，一方面可以起到隔热，均衡温度，免除金属液的冲击腐蚀性的目的，另一方面可以防止铸件产品因局部冷却过快而造成的开裂、砂眼、白口铁形成等缺陷。铸造涂料种类繁多，大体可以分为两类：水基涂料和醇基涂料。其中醇基涂料在涂覆后经点燃既可固化，不需烘干，能缩短生产周期，简化工艺，减少烘干设备投资，是被铸造界广为使用的一种快干涂料，已广泛应用于钢、铁、有色铸件的生产中。
然而现有技术中醇基铸造涂料有诸多缺陷，比如：悬浮稳定性较差、在长途运输和存放过程中易分层、耐高温性能较差、硬度低、化学稳定性差、抗金属冲刷性能低、抗粘砂性弱等，使得醇基铸造涂料功能单一，无法满足大规模的工业化生产。
发明内容
本发明的目的就是提供一种易剥离醇基铸造涂料及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种易剥离醇基铸造涂料，其特征在于，由下列重量份的原料制成：耐火砖废料45-60、高铝矾土熟料55-70、凹凸棒土2-3、苯丙乳液3-5、氟硅酸钠0.5-0.8、氧化铝0.4-0.7、HES阻燃剂0.2-0.5、硫酸钡1-2、氧化锌1.2-3.2、麦秸秆12-16、聚乙烯醇羧丁醛5-9、乙醇40-60、助剂4-7。
所述的助剂由下列重量份原料制成：建筑垃圾21-30、凹凸棒粘土6-9、高岭土75-95、硅烷偶联剂KH-5701.2-3.5、纳米碳化硅0.5-1.1、氧化铁粉2-5、羧甲基纤维素3-6、纳米二氧化锌0.6-1.3、玻璃微珠2-6、硅灰石6-9、聚醋酸乙烯乳液2.5-4.1、适量水，其制备方法是将建筑垃圾、凹凸棒粘土、高岭土放入煅烧炉中在550-680℃下煅烧2-3小时，取出，放入8-12%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干粉碎，加水搅拌成浆，同时，加入纳米二氧化锌、氧化铁粉研磨，喷雾干燥制得干燥粉；将硅烷偶联剂KH-570加热到200-230℃，搅拌10-20分钟，冷却至60-80℃加入纳米碳化硅、玻璃微珠高速搅拌20-30分钟制得混合物；将硅灰石研磨成粉，加入聚醋酸乙烯乳液搅拌5-10分钟，再加入上述制得的干燥粉、混合物及其他剩余成分研磨造粒，烘干即得。
所述的一种易剥离醇基铸造涂料的制备方法，其特征在于包括以下步骤：
（1）将麦秸秆放入炭化炉中在450-550℃下煅烧处理3-4小时，取出，放入10-12%的盐酸溶液中浸泡3-6小时，过滤取出，用清水反复洗涤，烘干粉碎，喷洒苯丙乳液搅拌混匀制得改性的麦秸秆灰烬；
（2）将上述步骤制得的改性麦秸秆灰烬与凹凸棒土、1/4重量的乙醇一起搅拌成浆并加热至95-120℃，保持温度搅拌1-2小时，冷却至50-60℃加入硫酸钡研磨30-40分钟，喷雾干燥制得干燥粉；
（3）将耐火砖废料高温煅烧处理后粉碎，加入氧化铝、氧化锌继续搅拌20-30分钟，再与1/5重量的乙醇搅拌均匀，然后加入聚乙烯醇羧丁醛加热至70-80℃搅拌30-40分钟；
（4）将高铝矾土熟料投入反应釜中，加入氟硅酸钠和剩余量的乙醇搅拌研磨10-15分钟，再加入步骤（2）、（3）产物、HES阻燃剂、助剂，将反应釜温度缓慢升至75-85℃，保持温度搅拌20-40分钟，研磨直至细度达到50μm以下即可。
本发明有以下有益效果：本发明提供的易剥离醇基铸造涂料，具有易剥离、强度高、透气性好、耐高温等性能；使用本发明的产品，在加工过程中模样不易变形，铸件表面几乎没有孔隙、粘砂，铸件质量大大提高；涂料的涂层易于从铸件表面剥离，后续处理简单，节省大量的人工，节约成本。
具体实施方式
所述的一种易剥离醇基铸造涂料，其特征在于，由下列重量份的原料制成：耐火砖废料47、高铝矾土熟料59、凹凸棒土2、苯丙乳液3、氟硅酸钠0.5、氧化铝0.4、HES阻燃剂0.2、硫酸钡1、氧化锌1.2、麦秸秆16、聚乙烯醇羧丁醛5、乙醇40、助剂4。
所述的助剂由下列重量份原料制成：建筑垃圾26、凹凸棒粘土6、高岭土79、硅烷偶联剂KH-5701.5、纳米碳化硅0.5、氧化铁粉2、羧甲基纤维素3、纳米二氧化锌0.6、玻璃微珠2、硅灰石9、聚醋酸乙烯乳液2.5、适量水，其制备方法是将建筑垃圾、凹凸棒粘土、高岭土放入煅烧炉中在550-680℃下煅烧2-3小时，取出，放入8-12%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干粉碎，加水搅拌成浆，同时，加入纳米二氧化锌、氧化铁粉研磨，喷雾干燥制得干燥粉；将硅烷偶联剂KH-570加热到200-230℃，搅拌10-20分钟，冷却至60-80℃加入纳米碳化硅、玻璃微珠高速搅拌20-30分钟制得混合物；将硅灰石研磨成粉，加入聚醋酸乙烯乳液搅拌5-10分钟，再加入上述制得的干燥粉、混合物及其他剩余成分研磨造粒，烘干即得。
制作方法包括以下步骤：
（1）将麦秸秆放入炭化炉中在450-550℃下煅烧处理3-4小时，取出，放入10-12%的盐酸溶液中浸泡3-6小时，过滤取出，用清水反复洗涤，烘干粉碎，喷洒苯丙乳液搅拌混匀制得改性的麦秸秆灰烬；
（2）将上述步骤制得的改性麦秸秆灰烬与凹凸棒土、1/4重量的乙醇一起搅拌成浆并加热至95-120℃，保持温度搅拌1-2小时，冷却至50-60℃加入硫酸钡研磨30-40分钟，喷雾干燥制得干燥粉；
（3）将耐火砖废料高温煅烧处理后粉碎，加入氧化铝、氧化锌继续搅拌20-30分钟，再与1/5重量的乙醇搅拌均匀，然后加入聚乙烯醇羧丁醛加热至70-80℃搅拌30-40分钟；
（4）将高铝矾土熟料投入反应釜中，加入氟硅酸钠和剩余量的乙醇搅拌研磨10-15分钟，再加入步骤（2）、（3）产物、HES阻燃剂、助剂，将反应釜温度缓慢升至75-85℃，保持温度搅拌20-40分钟，研磨直至细度达到50μm以下即可。
通过上述实施例加工得到的铸造涂料的技术指标如下：
（1）涂层耐磨性：0.68；
（2）发气量：12.5 mL/g；
（3）涂层的常温强度高于700g/mm；
（4）经过1200℃焙烧后涂料涂层的强度：570g/mm；
（5）涂敷、烘干、冷却后涂层外观：无裂纹、无起泡和肉眼可见的针孔的均匀涂层。

Claims (2)

1.一种易剥离醇基铸造涂料，其特征在于，由下列重量份的原料制成：耐火砖废料45-60、高铝矾土熟料55-70、凹凸棒土2-3、苯丙乳液3-5、氟硅酸钠0.5-0.8、氧化铝0.4-0.7、HES阻燃剂0.2-0.5、硫酸钡1-2、氧化锌1.2-3.2、麦秸秆12-16、聚乙烯醇羧丁醛5-9、乙醇40-60、助剂4-7；所述的助剂由下列重量份原料制成：建筑垃圾21-30、凹凸棒粘土6-9、高岭土75-95、硅烷偶联剂KH-5701.2-3.5、纳米碳化硅0.5-1.1、氧化铁粉2-5、羧甲基纤维素3-6、纳米二氧化锌0.6-1.3、玻璃微珠2-6、硅灰石6-9、聚醋酸乙烯乳液2.5-4.1、适量水，其制备方法是将建筑垃圾、凹凸棒粘土、高岭土放入煅烧炉中在550-680℃下煅烧2-3小时，取出，放入8-12%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干粉碎，加水搅拌成浆，同时，加入纳米二氧化锌、氧化铁粉研磨，喷雾干燥制得干燥粉；将硅烷偶联剂KH-570加热到200-230℃，搅拌10-20分钟，冷却至60-80℃加入纳米碳化硅、玻璃微珠高速搅拌20-30分钟制得混合物；将硅灰石研磨成粉，加入聚醋酸乙烯乳液搅拌5-10分钟，再加入上述制得的干燥粉、混合物及其他剩余成分研磨造粒，烘干即得。
2.根据权利要求1所述的一种易剥离醇基铸造涂料的制作方法，其特征在于包括以下步骤：
（1）将麦秸秆放入炭化炉中在450-550℃下煅烧处理3-4小时，取出，放入10-12%的盐酸溶液中浸泡3-6小时，过滤取出，用清水反复洗涤，烘干粉碎，喷洒苯丙乳液搅拌混匀制得改性的麦秸秆灰烬；
（2）将上述步骤制得的改性麦秸秆灰烬与凹凸棒土、1/4重量的乙醇一起搅拌成浆并加热至95-120℃，保持温度搅拌1-2小时，冷却至50-60℃加入硫酸钡研磨30-40分钟，喷雾干燥制得干燥粉；
（3）将耐火砖废料高温煅烧处理后粉碎，加入氧化铝、氧化锌继续搅拌20-30分钟，再与1/5重量的乙醇搅拌均匀，然后加入聚乙烯醇羧丁醛加热至70-80℃搅拌30-40分钟；
（4）将高铝矾土熟料投入反应釜中，加入氟硅酸钠和剩余量的乙醇搅拌研磨10-15分钟，再加入步骤（2）、（3）产物、HES阻燃剂、助剂，将反应釜温度缓慢升至75-85℃，保持温度搅拌20-40分钟，研磨直至细度达到50μm以下即可。
CN201410266637.5A 2014-06-16 2014-06-16 一种易剥离醇基铸造涂料及其制作方法 Active CN104084528B (zh)