CN105155078A - 一种维涤勾子线的生产工艺 - Google Patents
一种维涤勾子线的生产工艺 Download PDFInfo
- Publication number
- CN105155078A CN105155078A CN201510467955.2A CN201510467955A CN105155078A CN 105155078 A CN105155078 A CN 105155078A CN 201510467955 A CN201510467955 A CN 201510467955A CN 105155078 A CN105155078 A CN 105155078A
- Authority
- CN
- China
- Prior art keywords
- wire
- twist
- polyester
- polyvinyl
- good
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种维涤勾子线的生产工艺。该生产工艺,包括以下步骤:1)倂线;2)初捻;3)复捻;4)以复捻好的捻度为180-270的股线,由摇纱机卷绕成绞线;5)浆池调浆;6)绞线放入已调好的浆液里;7)上浆好的涤/维绞线,由脱水机脱去60-70%浆液;8)上浆好的绞线上蜡线机进行牵伸定形,时间为15-25分钟,当涤/维通丝线干度达到70%-80%,进行手工上蜡2-3分钟,下蜡线机后进行风干,湿度低于3%,制作成维涤勾子线。本发明所提供的维涤勾子线,断裂强度显著增强。伸缩率下降。摩擦系数提高30%-60%。
Description
技术领域
本发明属于纺织技术领域,具体的涉及一种维涤勾子线的生产工艺。
背景技术
目前,提花织机的织造幅宽增大,对通丝提出了更高的要求,为此研制高强度、低伸缩率的的通丝线已经是保证提花织机开口时梭口清晰、顺利织造的亟不可待的需求。同时高强度、低伸缩率的的通丝能够有效的减少织物经向瑕疵点。
目前,常用方法制得的维涤勾子线,拉伸断裂强度低。小负荷下通丝的伸缩量较大。产品在织造厂,由于通丝的伸缩变化量大,影响正常生产。尤其在空气湿度较大的季节,此通丝的伸缩量变得较大,严重降低织机织造的效率,比较容易造成织物的经向疵点,甚至发生该通丝的断裂现象。
发明内容
针对现有技术的缺陷,本发明提出了一种维涤勾子线的生产工艺,从加工工艺上来克服上述缺陷。
本发明解决技术问题的方案如下:
一种维涤勾子线的生产工艺,包括以下步骤:
1)倂线,以2根333dtex-420dtex高强低伸涤纶长丝与2根29.5tex维纶牵切纱进行合併为1股;2)初捻,捻向Z,股线数捻度为捻/100㎝,以合併好的1股进行加捻,捻度为360-466;
3)复捻,捻向S,股线数捻度为捻/100㎝,以初捻好的合成3股,再进行加捻,捻度为180-270;
4)以复捻好的捻度为180-270的股线,由摇纱机卷绕成绞线;
5)浆池调浆、染色,浆液浓度为10-20%,染料为总浆液0.0010-0.0020%,放在一起调浆;
6)绞线放入已调好的浆液里,浸泡时间为40分钟-70分钟;
7)上浆好的涤/维绞线,由脱水机脱去60-70%浆液;
8)上浆好的绞线上蜡线机进行牵伸定形,时间为15-25分钟,当涤/维通丝线干度达到70%-80%,进行手工上蜡2-3分钟,下蜡线机后进行风干,湿度低于3%,制作成维涤勾子线。
优选,所述浆液由以下重量份的原料组成:PVA179920-70份,PVA178810-30份,聚酯10-30份,淀粉10-30%。
优选,所述染料是黄色或直接冻黄或兰色或翠兰。
本发明的另一个目的是生产工艺制备得到的维涤勾子线。本发明所提供的维涤勾子线,断裂强度显著增强。伸缩率下降。摩擦系数提高30%-60%。
具体实施方式
下面结合具体实施例对本发明做出进一步说明。
实施例1
一种维涤勾子线的生产工艺,包括以下步骤:
1)倂线,以2根333dtex-420dtex高强低伸涤纶长丝与2根29.5tex维纶牵切纱进行合併为1股;
2)初捻,捻向Z,股线数捻度为捻/100㎝,以合併好的1股进行加捻,捻度为360-466;
3)复捻,捻向S,股线数捻度为捻/100㎝,以初捻好的合成3股,再进行加捻,捻度为180-270;
4)以复捻好的捻度为180-270的股线,由摇纱机卷绕成绞线;
5)浆池调浆、染色,浆液浓度为10-20%,染料为总浆液0.0010-0.0020%,放在一起调浆;
6)绞线放入已调好的浆液里,浸泡时间为40分钟-70分钟;
7)上浆好的涤/维绞线,由脱水机脱去60-70%浆液;
8)上浆好的绞线上蜡线机进行牵伸定形,时间为15-25分钟,当涤/维通丝线干度达到70%-80%,进行手工上蜡2-3分钟,下蜡线机后进行风干,湿度低于3%,制作成维涤勾子线。
本实施中,所述浆液由以下重量份的原料组成:PVA179920-70份,PVA178810-30份,聚酯10-30份,淀粉10-30%。
本实施中,染料是黄色。
Claims (3)
1.一种维涤勾子线的生产工艺,其特征在于,包括以下步骤:
1)倂线,以2根333dtex-420dtex高强低伸涤纶长丝与2根29.5tex维纶牵切纱进行合併为1股;
2)初捻,捻向Z,股线数捻度为捻/100㎝,以合併好的1股进行加捻,捻度为360-466;
3)复捻,捻向S,股线数捻度为捻/100㎝,以初捻好的合成3股,再进行加捻,捻度为180-270;
4)以复捻好的捻度为180-270的股线,由摇纱机卷绕成绞线;
5)浆池调浆、染色,浆液浓度为10-20%,染料为总浆液0.0010-0.0020%,放在一起调浆;
6)绞线放入已调好的浆液里,浸泡时间为40分钟-70分钟;
7)上浆好的涤/维绞线,由脱水机脱去60-70%浆液;
8)上浆好的绞线上蜡线机进行牵伸定形,时间为15-25分钟,当涤/维通丝线干度达到70%-80%,进行手工上蜡2-3分钟,下蜡线机后进行风干,湿度低于3%,制作成维涤勾子线。
2.根据权利要求1所述的维涤勾子线的生产工艺,其特征在于,所述浆液由以下重量份的原料组成:PVA179920-70份,PVA178810-30份,聚酯10-30份,淀粉10-30%。
3.根据权利要求1或2所述的生产工艺,其特征在于,所述染料是黄色或直接冻黄或兰色或翠兰。