CN1051339A - 绿彩金星釉料 - Google Patents
绿彩金星釉料 Download PDFInfo
- Publication number
- CN1051339A CN1051339A CN 90108654 CN90108654A CN1051339A CN 1051339 A CN1051339 A CN 1051339A CN 90108654 CN90108654 CN 90108654 CN 90108654 A CN90108654 A CN 90108654A CN 1051339 A CN1051339 A CN 1051339A
- Authority
- CN
- China
- Prior art keywords
- glaze
- green
- venus
- add
- golden
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
绿彩金星釉料属于一种可用于景泰蓝和料器制
造的装饰用高温釉料。
本发明的特征是在以SiO2、Al2O3、CaCO3、
K2CO3和NaNO3为主的基料中再加入Na2B4O7·
10H2O或Na2CO3，另外还有兼起着色作用的成核剂
Cr2O3、TiO2和ZrO2。有时为了使金星细密而均匀，
还可加入成核促进WO3。与现有的金星釉料相比，
它是一种绿底五彩金星釉料，在阳光下可显示出红、
蓝、绿、黄和紫色，其晶粒可大可小，直径在0.1～
1mm之间，可作装饰材料使用。
Description
绿彩金星釉料是一种用于景泰蓝和料器工业的高温釉料，也可作砌面材料使用。
绿彩金星釉料一般由基料和兼起着色作用的成核剂组成。苏联专利967973在1982年10月23日公开了一种用于建筑砌面材料的金星玻璃，其配方及重量组成为（%）：
SiO240.3～51.6;B2O318.2～23;Al2O309～25;CaO 1.8～4.2;Na2o 15～24.1;K2O 1～4;Cr2O31.4～5.1;CoO 0.9～6。另一份苏联专利783251在1980年12月3日也公开了一种作同样用途的金星玻璃，其配方及重量组成为（%）：
SiO252.0～57.0;Al2O37.0～8.75;CaO 210～245;MgO 2.51～4.51;MnO 0.1～0.5;TiO20.1～0.5 FeO 0.01～2.0;Na2O 2.51～4.49;S＝0.1～1.7 Cr2O3001～20;Fe2O3202～7.2。它们的共同缺点是，都是绿色或深绿色，色彩单调，无法用作景泰蓝和料器等对金星色彩要求多一些的工业部门作装饰品用，而且晶粒大小未见报导。
为了解决可用于景泰蓝和料器工业使用的绿底五彩金星釉料的配方组成及工艺问题，本发明提出了一种绿彩金星釉料，其配方及重量比如下：
基料由下列成份组成：
SiO2（26.5～41.5），Al2O3（0.5～4.5），CaCO3（9.0～16.5）K2Co3（4.0～14.5），NaNO3（9.0～13.5），
另外还要加入
Na2B4O7·10H2o（32.5～36.5）或Na2Co3（21.5～28.0）;
成核剂由下列成份组成：
Cr2O3（0.5～2.0），TiO2（1.0～3.5），ZrO2（0.5～2.5），
有时为了得到细而均匀的晶粒，还可加入成核促进剂WO3（0.5～1.8）。如为了使景泰蓝衬底不显出铜质来，需要用乳浊状的细金星，可以加入重量比为2.1的P2O5。
在制备时，先把用硅碳棒加热的电炉升温到1000℃，再将釉料按上述配方重量比称重，研磨，用100目筛子过筛，混合均匀后放入电炉中，以70～80℃/h的速率升温至1300～1350℃，熔化2～3小时，然后以120℃/h的速率降温至1000～1280℃，保温6～12小时，断电，自然降温至室温。
本发明生产的绿彩金星釉料是一种高温釉料，它能产生绿彩金星，在阳光下可见到绿色、蓝色、黄色、红色和紫色星光散布在玻璃体内，晶体直径可大可小，在0.1～1mm之间，大金星反射光能力强，小金星细密而均匀，其膨胀系数为17～23×10-6，使用温度在700～1100℃之间，在此范围内均可保持金星不变。它可用作装饰用金星釉料、星光玻璃雕刻、日用陶瓷装饰、工艺品装饰釉料、发卡、领带卡、纪念章、头饰及景泰蓝釉彩中。
实施例：见表1。
Claims (2)
1、一种绿彩金星釉料，包括基料和兼起着色作用的成核剂，其特征在于，
(1)、配方及重量比(%)
基料由下列成份组成，
SiO2(26.5～41.5)，Al2O3(0.5～4.5)，CaCO3(9.0～16.5)K2CO3(4.0～14.5)NaNO3(9.0～13.5)，
另外还要加入
Na2B4O7·10H2O(32.5～36.5)或Na2CO3(21.5～28.0)；
成核剂由下列成份组成，
Cr2O3(0.5～4.0)，TiO2(1.0～3.5)，ZrO2(0.5～2.5)；
(2)、工艺过程如下：
先把用硅碳棒加热的电炉升温到1000℃，再将釉料按上述配方重量比称重，研磨，用100目筛子过筛，混合均匀后放入炉中，以70～80℃/h的速率快速升温至1300℃～1350℃熔化2～3小时，然后以120℃/h的速率降温到1000～1280℃保温6～12小时，断电，自然降至室温。
2、根据权利要求1的绿彩金星釉料，其特征在于，所述的配方中还可加入成核促进剂WO3（0.5～1.8）。