CN105131832A - 一种冬季输电线防冰涂料及其制备方法 - Google Patents
一种冬季输电线防冰涂料及其制备方法 Download PDFInfo
- Publication number
- CN105131832A CN105131832A CN201510520429.8A CN201510520429A CN105131832A CN 105131832 A CN105131832 A CN 105131832A CN 201510520429 A CN201510520429 A CN 201510520429A CN 105131832 A CN105131832 A CN 105131832A
- Authority
- CN
- China
- Prior art keywords
- parts
- transmission line
- coating
- winter
- power transmission
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种冬季输电线防冰涂料及其制备方法，属于电力设备涂料领域。本发明是由以下重量份数的组分组成：端羟基聚二甲基硅氧烷40-55份、纳米氢氧化镁20-30份、十溴联苯乙烷10-15份、三氧化二锑3-6份、白炭黑15-20份、交联剂5-10份、催化剂0.5-1.5份、稀释剂45-60份、异丙醇铝10-15份、二甲苯10-15份、丙酮7-10份。本发明防冰涂料涂敷在电力设备上，实现了泄漏电流在需要防冰时通过损耗泄漏电流发热起作用，不需要防冰时大大降低损耗的效果。
Description
技术领域
本发明属于一种电力设备用涂料，具体地说，尤其涉及一种冬季输电线防冰涂料及其制备方法。
背景技术
冰灾和冰闪事故严重威胁电网安全，给电力系统和人们的生产生活带来巨大的经济损失。对目前输电线路绝缘子用的防污闪的涂料主要是室温硫化硅橡胶涂料，涂覆RTV涂料后，可提高绝缘子表面的憎水性，其表面积聚的污层也能获得不同程度的憎水性，具有很好的憎水迁移性，憎水性良好的涂层表面积聚水分比较少，不会形成连续的水膜，因此当气温下降到零度以下后表面覆冰量增加缓慢，然而当涂层被冰层完全覆盖时，失去憎水性后防冰性能就和普通的绝缘子一样了。而且RTV硅橡胶本身力学性能很差，很容易在恶劣天气下遭到破坏，阻燃性能、憎水性能、憎水迁恢复移性能还有待进一步提高。现有技术中亟需研制一种具有良好的防覆冰性能，且具有良好的阻燃性能、憎水性能和憎水恢复迁移性能的涂料。
发明内容
本发明目的是提供一种冬季输电线防冰涂料及其制备方法，以克服现有技术中输电线路防冰涂层力学性能差且阻燃性能、憎水性能、憎水迁恢复移性能一般的缺陷。
本发明是采用以下技术方案实现的：一种冬季输电线防冰涂料，是由以下重量份数的组分组成：
优选地，是由以下重量份数的组分组成：
一种冬季输电线防冰涂料的制备方法，包括以下步骤：
(1)将端羟基聚二甲基硅氧烷、十溴联苯乙烷、三氧化二锑、白炭黑、交联剂和催化剂在反应釜中按上述比例充分混合反应，然后加入稀释剂、纳米氢氧化镁充分混合，最终制得混合液；
(2)取上述比例的异丙醇铝、二甲苯和丙酮，将异丙醇铝溶解在二甲苯和丙酮混合液中，放入超声波清洗器中震荡40min，与步骤(1)中的混合液混合搅拌制成。
与现有技术相比，本发明的有益效果是：本发明防冰涂料通过设计绝缘子表面涂料喷涂方式，利用绝缘子表面冰水充当开关。在天气晴好时，由于普通RTV涂层的存在，表面涂层不形成导电通道，这时涂层无能耗；降雨量较小或起雾时，由于防覆冰涂层具有优良的憎水性，分散的水珠无法将导电通道贯通，因此，防覆冰涂层中流过的泄漏电流非常小，几乎没有损耗；覆冰天气时，在冰水共存情况下，普通RTV涂层隔离带被带有水膜的冰层桥接，这时候防冰涂层形成通路，整个绝缘子表面有电流流过，开始发挥电热效应，阻碍附着的降水凝结；覆冰天气结束后，导电通道又恢复切断状态，泄漏电流重新恢复极小值。基于这种涂刷方式带来的开关效应，实现了泄漏电流在需要防冰时通过损耗泄漏电流发热起作用，不需要防冰时大大降低损耗的效果。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1：一种冬季输电线防冰涂料，是由以下重量份数的组分组成：
实施例2：一种冬季输电线防冰涂料，是由以下重量份数的组分组成：
实施例3：一种冬季输电线防冰涂料，是由以下重量份数的组分组成：
一种冬季输电线防冰涂料的制备方法，包括以下步骤：
(1)将端羟基聚二甲基硅氧烷、十溴联苯乙烷、三氧化二锑、白炭黑、交联剂和催化剂在反应釜中按上述比例充分混合反应，然后加入稀释剂、纳米氢氧化镁充分混合，最终制得混合液；
(2)取上述比例的异丙醇铝、二甲苯和丙酮，将异丙醇铝溶解在二甲苯和丙酮混合液中，放入超声波清洗器中震荡40min，与步骤(1)中的混合液混合搅拌制得。
防冰效果对比实验：在模拟气候室内并排悬挂一串涂覆防冰涂料瓷绝缘子和相同型号清洁瓷绝缘子，两侧分别有喷头对两串绝缘子喷水。覆冰时均施加线路运行工作电压，覆冰2h后，清洁瓷绝缘子覆冰厚度3.06mm，而涂覆防冰涂料的绝缘子串表面几乎没有覆冰和冰凌，防冰效果显著。
Claims (3)
1.一种冬季输电线防冰涂料，其特征在于，是由以下重量份数的组分组成：
2.根据权利要求1所述的冬季输电线防冰涂料，其特征在于，是由以下重量份数的组分组成：
3.一种冬季输电线防冰涂料的制备方法，其特征在于：包括以下步骤：
(1)将端羟基聚二甲基硅氧烷、十溴联苯乙烷、三氧化二锑、白炭黑、交联剂和催化剂在反应釜中按上述比例充分混合反应，然后加入稀释剂、纳米氢氧化镁充分混合，最终制得混合剂；
(2)取上述比例的异丙醇铝、二甲苯和丙酮，将异丙醇铝溶解在二甲苯和丙酮混合液中，放入超声波清洗器中震荡40min，并与步骤(1)中的混合剂混合。