CN105088948A - 带有聚脲防护涂层的钢丝拉索的制作方法 - Google Patents
带有聚脲防护涂层的钢丝拉索的制作方法 Download PDFInfo
- Publication number
- CN105088948A CN105088948A CN201510084292.6A CN201510084292A CN105088948A CN 105088948 A CN105088948 A CN 105088948A CN 201510084292 A CN201510084292 A CN 201510084292A CN 105088948 A CN105088948 A CN 105088948A
- Authority
- CN
- China
- Prior art keywords
- polyurea
- protection coating
- coating
- wire
- polyurea protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种带有聚脲防护涂层的钢丝拉索的制作方法,它是先制作带聚脲防护涂层的钢丝,经过分丝将带聚脲防护涂层的钢丝经过聚脲材料填充工序,在各带聚脲防护涂层的钢丝之间填充聚脲材料后再经过聚并步骤构成带聚脲防护涂层的钢丝组合体、并在钢丝组合体的各带聚脲防护涂层的钢丝之间填充聚脲材料构成带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae?;以这两种结构的带有聚脲防护涂层的钢丝拉索为基本结构,再经过缠包成型,PE套挤塑工序Ⅰ、Ⅱ,聚脲材料涂覆工序Ⅱ、Ⅲ、Ⅳ等工序之中的一种或多种,构成具有多重保护层的带有聚脲防护涂层的钢丝拉索。本发明方法经济实用,制作出的带有聚脲防护涂层的钢丝拉索结构紧凑、防腐、减震,抗滑性、耐磨性好。
Description
技术领域
本发明涉及一种钢丝拉索的制作方法,特别是一种带有防护涂层的钢丝拉索的制作方法。
背景技术
预应力钢丝拉索是桥梁结构中一种关键的受力部件,要求具有较高的防腐耐久性;目前预应力用桥梁钢丝拉索通常参照国家标准GB/T18365-2001《斜拉桥热挤聚乙烯高强钢丝拉索技术条件》进行生产制造。
预应力钢丝的腐蚀是在应力和腐蚀复合作用下的应力腐蚀(属电化腐蚀范畴),其特点是在金属内部先形成裂纹,内裂纹发生后便形成应力集中,加速裂纹的发展,进而产生严重腐蚀。预应力钢丝的防腐镀(涂)层钢材总是在腐蚀介质的条件下服役,按保护层的种类,可分为非金属保护层(称为涂层),化学保护层和金属保护层(称为镀层)三类。1、非金属保护涂层预应力钢材的非金属涂层目前主要有塑料、环氧树脂和防腐油脂三种,但非金属涂层的抗老化问题尚未解决,且其力学性能较金属镀层低得多。因此,应用范围受到限制。2、化学保护层通过化学法,在金属表面形成保护层,如锌层的钝化、铝层的氧化、铁基的磷化等。该类保护层往往不是作为单一的钢材保护层,而是与金属镀层兼并使用。3、金属保护镀层在电化腐蚀中,处于阳极的金属首先被溶解,为此在钢丝表面镀以较铁活泼的金属,如锌、铝等。在腐蚀介质的环境中,使锌首先被溶解而保护铁基,称为阳极镀层保护。由于镀锌(或锌-铝合金)存在"氢脆"现象,降低钢丝的强度等级,一直备受争议。因此预应力钢丝的防腐是至关桥梁工程质量寿命的重大问题,对于预应力用钢丝必须加强确实可行的防腐措施,以减少预应力钢丝因腐蚀造成先期失效而带来的巨大损失。
聚脲材料是由异氰酸酯组份与氨基化合物组份反应生成的一种弹性体物质,分为纯聚脲和半聚脲,聚脲的最基本的特性就是防腐、防水、耐磨等,目前大多用在航天领域。
因此,如何将聚脲材料应用到钢丝拉索的防护中,制作一种带聚脲防护涂层的钢丝及带有聚脲防护涂层的钢丝拉索是预应力技术拉索技术领域人们目前急需解决的技术难题。
发明内容
本发明的目的在于提供一种带有聚脲防护涂层的钢丝拉索的制作方法,制作出带有聚脲防护涂层的钢丝拉索,该带有聚脲防护涂层的钢丝拉索利用聚脲材料的优异性能,能大大提高钢丝拉索的防腐、减震、抗滑性能,延迟拉索使用寿命,以解决已有技术存在的上述问题。
为解决上述问题,本发明采用的技术方案是:一种带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:它是先制作带聚脲防护涂层的钢丝、经过分丝后将带聚脲防护涂层的钢丝经过聚脲材料填充工序,在各带聚脲防护涂层的钢丝之间填充聚脲材料后再经过聚并步骤构成由n根带聚脲防护涂层的钢丝组成的钢丝组合体、并在各带聚脲防护涂层的钢丝之间填充有聚脲材料的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae;
其具体步骤包括:A、制作带聚脲防护涂层的钢丝;B、分丝;C、聚脲材料填充工序:将带聚脲防护涂层的钢丝之间填充聚脲材料;D、聚并成型;
其关键步骤是:A、制作带聚脲防护涂层的钢丝;C、聚脲材料填充工序:将带聚脲防护涂层的钢丝之间填充聚脲材料;
所述步骤A、制作带聚脲防护涂层的钢丝的步骤是:
A1:对钢丝进行预处理、干燥;
A2:防腐处理;
A3:成盘、包装;
所述的A2:防腐处理工序是将聚脲材料通过挤出涂覆、喷涂、浸泡抽涂或机器涂刷形式涂覆在单根光面钢丝上或单根钢丝表面附着有的环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层上,构成带聚脲防护涂层的钢丝;
该带聚脲防护涂层的钢丝或是由单根光面钢丝以及涂覆在单根光面钢丝外周的聚脲防护涂层Ⅰ构成的带聚脲防护涂层的钢丝;
该带聚脲防护涂层的钢丝或是由单根光面钢丝以及单根光面钢丝外的复合防护涂层构成的具有复合防护涂层的带聚脲防护涂层的钢丝,所述的复合防护涂层是在单根光面钢丝的外周附着有的环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层与涂覆在表面附着涂层或镀层上的聚脲防护涂层Ⅰ共同形成的复合防护涂层;
在A、制作带聚脲防护涂层的钢丝步骤:将聚脲材料通过挤出涂覆、喷涂、浸泡抽涂或机器涂刷形式涂覆的具体方法是:
将单根光面钢丝或已经附着有保护膜的单根钢丝-即在单根钢丝表面附着有环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层的钢丝,以下简称钢丝,通过聚脲材料涂覆工序Ⅰ,即通过以下方式之一:
①挤出涂覆:钢丝通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝上;
③浸泡抽涂:钢丝通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝上;
使单根光面钢丝的表面涂覆一层聚脲防护涂层Ⅰ或是在已经附着有保护膜的单根钢丝表面附着有的环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层上再涂覆一层聚脲防护涂层Ⅰ,形成由单根光面钢丝以及涂覆在单根光面钢丝外周的聚脲防护涂层Ⅰ构成的带聚脲防护涂层的钢丝、或是由单根光面钢丝以及单根光面钢丝外的复合防护涂层构成的具有复合防护涂层的带聚脲防护涂层的钢丝,以下统称为:带聚脲防护涂层的钢丝;
B、分丝:将带聚脲防护涂层的钢丝通过分丝板对应的孔位;
C、聚脲材料填充工序:在带聚脲防护涂层的钢丝之间填充聚脲材料的具体步骤是:
将带聚脲防护涂层的钢丝通过以下方式之一进行涂覆式填充:
①挤出涂覆填充:将带聚脲防护涂层的钢丝通过挤塑式设备热挤出的聚脲材料;
②喷涂填充:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到带聚脲防护涂层的钢丝上;
③浸泡抽涂填充:带聚脲防护涂层的钢丝通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式填充:利用机器涂刷使聚脲材料均匀涂覆在带聚脲防护涂层的钢丝上;
D:聚并成型:将在带聚脲防护涂层的钢丝之间填充聚脲材料之间涂覆式填充有聚脲材料的带聚脲防护涂层的钢丝通过多组成型装置把带聚脲防护涂层的钢丝聚并成型;每个成型装置由2组3个互成120o角的滚压轮组成;通过调节每个滚压轮的相对位置和压紧力,使若干根钢丝索股整型为正六边形,索股内各带聚脲防护涂层的钢丝互相贴紧,使聚脲材料充分填充在带聚脲防护涂层的钢丝的索股间隙中,制成由n根带聚脲防护涂层的钢丝组成的钢丝组合体,各带聚脲防护涂层的钢丝之间填充有聚脲材料的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae;n为大于等于1小于等于1500的整数,所述的聚脲材料是纯聚脲材料或半聚脲材料。
其进一步技术方案是:将由n根带聚脲防护涂层的钢丝组成的钢丝组合体,并在各带聚脲防护涂层的钢丝之间填充有聚脲材料的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae再经过E:聚脲材料涂覆工序Ⅱ,即:通过以下方式之一:
①挤出涂覆:钢丝拉索Ⅰae或Ⅱae通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰae或Ⅱae上;
③浸泡抽涂:钢丝拉索Ⅰae或Ⅱae通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰae或Ⅱae上;
使带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae钢丝组合体的外周表面再附着一层聚脲防护涂层Ⅱ构成带有聚脲防护涂层的钢丝拉索Ⅰbe或带有聚脲防护涂层的钢丝拉索Ⅱbe,n为大于等于1小于等于1500的整数。
其更进一步的技术方案是:将上述各方案制作出的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae、Ⅰbe或Ⅱbe再通过PE套挤塑工序Ⅰ或是通过PE套挤塑工序Ⅰ和PE套挤塑工序Ⅱ,制作成外层有由HDPE护套构成的填充或涂覆有聚脲防护材料的钢丝拉索,或是由内层HDPE护套和外层HDPE护套组成的双层HDPE护套构成的带有聚脲防护涂层的钢丝拉索,包括:
(1)将各带聚脲防护涂层的钢丝之间填充有聚脲材料构成的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae;或是带有聚脲防护涂层的钢丝拉索Ⅰbe、Ⅱbe再经过PE套挤塑工序Ⅰ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在带有聚脲防护涂层的钢丝拉索索体外层形成HDPE护套,构成外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1或外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰbe1、Ⅱbe1。
(2)将外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1或带有聚脲防护涂层的钢丝拉索Ⅰbe1、Ⅱbe1再经过PE套挤塑工序Ⅱ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索索体外层,形成外层HDPE护套,构成具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2或带有聚脲防护涂层的钢丝拉索Ⅰbe2、Ⅱbe2。
其又更进一步的技术方案是:将采用其更进一步的技术方案制作的外层有由HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1,或是由内层HDPE护套和外层HDPE护套组成的双层HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2先经过对单层或双层PE护套表面处理后,再经过J:聚脲材料涂覆工序Ⅳ,包括:
(1)将外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1先经过对单层PE护套表面处理后,再经过J:聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1上;
③浸泡抽涂:将钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1上;
使外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1的单层HDPE护套外层再附着一层聚脲防护涂层Ⅳ,构成单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ的带有聚脲防护涂层的钢丝拉索Ⅰae1d、Ⅱae1d、Ⅰbe1d或Ⅱbe1d。
(2)将具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2经过对双层HDPE护套表面处理后,再经过J:聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2上;
③浸泡抽涂:将钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:由机器将聚脲材料涂刷到钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2上;
使具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2的外层HDPE护套外再附着一层聚脲防护涂层Ⅳ,构成双层HDPE护套外层涂覆有聚脲防护涂层Ⅳ的带有聚脲防护涂层的钢丝拉索Ⅰae2d、Ⅱae2d、Ⅰbe2d或Ⅱbe2d。
其再更进一步的技术方案是:将带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae、Ⅰbe或Ⅱbe的钢丝组合体外缠包一缠包带,构成带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo。
进一步:将钢丝组合体外缠包有一缠包带的带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo再经过聚脲材料涂覆工序Ⅲ,即:通过以下方式之一:
①挤出涂覆:将带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo上;
③浸泡抽涂:将钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:由机器将聚脲材料涂刷到钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo上;
使带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo的缠包带外周表面再附着一层聚脲防护涂层Ⅲ构成缠包带外层涂覆有聚脲防护涂层Ⅲ的带有聚脲防护涂层的钢丝拉索Ⅰaec、Ⅱaec、Ⅰbec和Ⅱbec。
更进一步:将缠包带外层涂覆有聚脲防护涂层Ⅲ的带有聚脲防护涂层的钢丝拉索Ⅰaec、Ⅱaec、Ⅰbec和带有聚脲防护涂层的钢丝拉索Ⅱbec再经过PE套挤塑工序Ⅰ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在带有聚脲防护涂层的钢丝拉索索体缠包带外层形成HDPE护套,构成外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1和带有聚脲防护涂层的钢丝拉索Ⅱbec1。
又更进一步:将外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1再经过PE套挤塑工序Ⅱ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索索体外层,形成外层HDPE护套,构成具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2。
再更进一步:将外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1先经过对单层PE护套表面处理后,再经过J:聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1上;
③浸泡抽涂:将钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1上;
使外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1的单层HDPE护套外层再附着一层聚脲防护涂层Ⅳ,构成单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ的带有聚脲防护涂层的钢丝拉索Ⅰaec1d、Ⅱaec1d、Ⅰbec1d或Ⅱbec1d。
或是将具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2先经过对双层PE护套表面处理后,再经过J:聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2上;
③浸泡抽涂:将钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2上;
使具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2的外层HDPE护套外再附着一层聚脲防护涂层Ⅳ,构成双层HDPE护套外层涂覆有聚脲防护涂层Ⅳ的带有聚脲防护涂层的钢丝拉索Ⅰaec2d、Ⅱaec2d、Ⅰbec2d或Ⅱbec2d。
由于采取以上技术方案,本发明之带有聚脲防护涂层的钢丝拉索的制作方法解决了如何将聚脲材料应用到钢丝拉索的防护中,制作带有聚脲防护涂层的钢丝拉索的技术难题,制造出的带有聚脲防护涂层的钢丝拉索具有以下特点和有益效果,具有很好的经济效益。
1.能大大提高钢丝拉索的防腐、减震、抗滑性能,延迟钢丝拉索的使用寿命:
由于本发明之带聚脲防护涂层钢丝拉索是由带聚脲防护涂层的钢丝组成的钢丝组合体组成,所述带聚脲防护涂层的钢丝是由单根光面钢丝及涂覆在单根光面钢丝外的防护涂层构成,该带聚脲防护涂层的钢丝外的防护涂层可以是涂覆在单根光面钢丝外周的聚脲防护涂层或是在单根光面钢丝的外周附着有的环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层与涂覆在表面附着涂层或镀层上的聚脲防护涂层共同形成的复合防护涂层,由于聚脲材料具有优良的耐磨性、抗冲击性和减震性,涂覆于钢丝拉索基体的钢丝表面,它涂层连续、致密,可以做到无接缝、无针孔,隔绝空气中的水份和氧气的渗入,能保护钢丝以及钢丝表面附着有的环氧涂层、塑料涂层或防腐油脂涂层不易老化,能减缓镀锌涂层易损耗、易受针孔等局部缺陷的影响,大大提高该类钢丝拉索的防腐能力,并增加其耐磨性能,延长钢丝拉索的使用寿命;同时聚脲材料具有优异的抗张强度、耐老化、耐磨损等特性,可减少生产制造及安装过程中因施工操作不当造成的损伤,由于聚脲涂层具有不易产生开裂、脱落现象,大大提高钢丝拉索的防腐能力、延长使用寿命。
2.结构紧凑、钢丝之间摩擦力大,增强其抗滑性能,抗疲劳强度提高:
本发明之带聚脲防护涂层钢丝拉索之钢丝最外表面及各带聚脲防护涂层的钢丝之间的间隙中均涂覆或填充有聚脲材料,由于聚脲材料具有高耐磨的物理性能,因此,聚脲涂层不必很厚,将他们组成预应力筋时,各根钢丝之间可以呈正六边形或缺角六边形紧密排列或其他形式排列,结构紧凑、能增强钢丝拉索的摩擦力,增强其抗滑性能;当其运用于索鞍结构时,更有利于在拉索在索塔两侧受不平衡力的工况下使用。
3.本发明能改善现有涂层或镀层钢丝的性能,因而也大大提高钢丝拉索的防腐能力,并增加其耐磨性,延长钢丝拉索的使用寿命。
4.制作方法合理,解决了如何将聚脲材料应用到钢丝拉索的防护中,制作一种带聚脲防护涂层的钢丝及带有聚脲防护涂层的钢丝拉索的技术难题;
目前用于涂刷聚脲的方式为手工涂刷及设备喷射,使用范围为较宽广的场地作业,因钢丝的外型轮廓较小,手工涂刷容易产生涂刷不均均匀及流挂现象,而常用的设备喷涂设备较大,喷射面积较大,对喷涂单根钢丝聚脲材料浪费较大,90%以上材料浪费掉。由于聚脲的成膜速度非常快,如果手工操作不当,喷涂掌握不准等则易造成涂层厚薄不均、表观不平整、色差大等问题。若施工经验缺乏,选择基层处理剂不当,基层未达到施工要求时,极易造成聚脲涂层起泡、针眼、分层、粘结不牢等现象。根据以上的涂刷方式不足现象。
本发明方法将聚脲材料通过挤出涂覆、喷涂、浸泡抽涂或机器涂刷的涂覆形式涂覆或涂覆式填充的具体方法是:
①挤出涂覆:将钢丝及钢丝拉索分别通过挤塑式设备热挤出的聚脲材料;通过挤塑式设备将已经配比好的聚脲材料颗粒进行加热,使聚脲材料在挤塑式设备熔融状态下充分反应,将钢丝或钢丝拉索通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝或钢丝拉索上;由机器喷嘴控制喷射量,均匀的挤塑到钢丝表面,可以有效的控制聚脲厚度层,可根据钢丝体积较小的特点,专门设计研发环型或小孔喷嘴的喷射设备,在流水线的生产线上均匀喷涂在钢丝表面,减少材料的浪费率;
③浸泡抽涂:将钢丝或钢丝拉索通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;通过牵引设备拉索将钢丝及钢丝拉索浸泡在聚脲涂料中,使其浸泡后通过出口环状结构成型,能均匀涂覆在钢丝及钢丝拉索上;
④机器涂刷方式:由机器将聚脲材料涂刷到钢丝或钢丝拉索上;利用机器设备自动化涂刷功能使聚脲材料均匀涂覆在钢丝及钢丝拉索上。
通过挤塑式设备挤出涂覆、环型或小孔喷涂、浸泡抽涂或机器涂刷的方式是目前市场上无出现过的涂覆方式,涂覆方式的改变,对体积较小的钢丝不但精确的控制聚脲的厚度,并且杜绝材料的浪费。
下面,结合附图和实施例对本发明之带有聚脲防护涂层的钢丝拉索的制作方法的技术特征作进一步的说明。
附图说明
图1-1~图1-2是本发明实施例一之带聚脲防护涂层的钢丝拉索的制作方法制作的带聚脲防护涂层的钢丝的结构示意图:
图1-1:由光面钢丝构成的带聚脲防护涂层的钢丝;
图1-2:带有复合防护涂层的带聚脲防护涂层的钢丝。
图2-1~图2-10是本发明实施例一之带有聚脲防护涂层的钢丝拉索的制作方法制作的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae及其变换的钢丝拉索结构示意图:
图2-1:带有聚脲防护涂层的钢丝组合体内各钢丝之间填充有聚脲材料构成的带有聚脲防护涂层的钢丝拉索Ⅰae;
图2-2:带有聚脲防护涂层的钢丝组合体内各钢丝之间填充有聚脲材料构成的带有聚脲防护涂层的钢丝拉索Ⅱae;
图2-3~图2-4:带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae外层有单层HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1;
图2-5~图2-6:带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae外层有双层HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2。
图2-7~图2-8:带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1的单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ构成的带有聚脲防护涂层的钢丝拉索Ⅰae1d、Ⅱae1d;
图2-9~图2-10:带有聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2的双层HDPE护套外层涂覆有聚脲防护涂层Ⅳ构成的带有聚脲防护涂层的钢丝拉索Ⅰae2d、Ⅱae2d。
图3-1~图3-10是本发明实施例二之带有聚脲防护涂层的钢丝拉索的制作方法制作的带有聚脲防护涂层的钢丝拉索Ⅰbe、Ⅱbe及其变换的钢丝拉索结构示意图:
图3-1:带有聚脲防护涂层的钢丝拉索Ⅰae的钢丝组合体外周有一聚脲防护涂层Ⅱ的带有聚脲防护涂层的钢丝拉索Ⅰbe;
图3-2:带有聚脲防护涂层的钢丝拉索Ⅱae的钢丝组合体外周有一聚脲防护涂层Ⅱ的带有聚脲防护涂层的钢丝拉索Ⅱbe;
图3-3~图3-4:带有聚脲防护涂层的钢丝拉索Ⅰbe、Ⅱbe外层有单层HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰbe1、Ⅱbe1;
图3-5~图3-6:带有聚脲防护涂层的钢丝拉索Ⅰbe、Ⅱbe外层有双层HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰbe2、Ⅱbe2。
图3-7~图3-8:带有聚脲防护涂层的钢丝拉索Ⅰbe1、Ⅱbe1的单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ构成的带有聚脲防护涂层的钢丝拉索Ⅰbe1d、Ⅱbe1d;
图3-9~图3-10:带有聚脲防护涂层的钢丝拉索Ⅰbe2、Ⅱbe2的双层HDPE护套外层涂覆有聚脲防护涂层Ⅳ构成的带有聚脲防护涂层的钢丝拉索Ⅰbe2d、Ⅱbe2d。
图4-1~图4-16是是本发明实施例三之带有聚脲防护涂层的钢丝拉索的制作方法制作的钢丝组合体外有一缠包带或是缠包带外层涂覆有聚脲防护涂层Ⅲ31c的带有聚脲防护涂层的钢丝拉索的结构示意图:
图4-1~图4-4:带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae、Ⅰbe、Ⅱbe的钢丝组合体外有一缠包带构成的带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo、Ⅱbeo;
图4-5:带有聚脲防护涂层的钢丝拉索Ⅰaeo缠包带外层涂覆有聚脲防护涂层Ⅲ构成的带有聚脲防护涂层的钢丝拉索Ⅰaec;
图4-6:带有聚脲防护涂层的钢丝拉索Ⅱaeo缠包带外层涂覆有聚脲防护涂层Ⅲ构成的带有聚脲防护涂层的钢丝拉索Ⅱaec;
图4-7:带有聚脲防护涂层的钢丝拉索Ⅰbeo缠包带外层涂覆有聚脲防护涂层Ⅲ的带有聚脲防护涂层的钢丝拉索Ⅰbec;
图4-8:带有聚脲防护涂层的钢丝拉索Ⅱbeo缠包带外层涂覆有聚脲防护涂层Ⅲ的带有聚脲防护涂层的钢丝拉索Ⅱbec;
图4-9~图4-10:带有聚脲防护涂层的钢丝拉索Ⅰaec、Ⅱaec外层有单层HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1;
图4-11~图4-12:带有聚脲防护涂层的钢丝拉索Ⅰbec、Ⅱbec外层有单层HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰbec1、Ⅱbec1;
图4-13~图4-14:带有聚脲防护涂层的钢丝拉索Ⅰaec、Ⅱaec外层有双层HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰaec2、Ⅱaec2;
图4-15~图4-16:带有聚脲防护涂层的钢丝拉索Ⅰbec、Ⅱbec外层有双层HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰbec2、Ⅱbec2。
图5-1~图5-4是本发明实施例四之单层HDPE护套外层涂覆有聚脲防护涂层的具有多重保护层的带有聚脲防护涂层的钢丝拉索的制作方法制作的带有聚脲防护涂层的钢丝拉索的结构示意图:
图5-1~图5-2:带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1的单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ的带有聚脲防护涂层的钢丝拉索Ⅰaec1d、Ⅱaec1d;
图5-3~图5-4:带有聚脲防护涂层的钢丝拉索Ⅰbec1、Ⅱbec1的单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ的带有聚脲防护涂层的钢丝拉索Ⅰbec1d、Ⅱbec1d。
图6-1~图6-4是本发明实施例五之双层HDPE护套的外层涂覆有聚脲防护涂层的具有多重保护层的带有聚脲防护涂层的钢丝拉索的制作方法制作的带有聚脲防护涂层的钢丝拉索的结构示意图:
图6-1~图6-2:带有聚脲防护涂层的钢丝拉索Ⅰaec2、Ⅱaec2的双层HDPE护套的外层还涂覆有一层聚脲防护涂层Ⅳ构成的带有聚脲防护涂层的钢丝拉索Ⅰaec2d、Ⅱaec2d;
图6-3~图6-4:带有聚脲防护涂层的钢丝拉索Ⅰbec2、Ⅱbec2的双层HDPE护套的外层还涂覆有一层聚脲防护涂层Ⅳ构成的带有聚脲防护涂层的钢丝拉索Ⅰbec2d、Ⅱbec2d。
1-单根光面钢丝;2-表面附着涂层或镀层;5-缠包带;6-单层或内层HDPE护套;7-外层HDPE护套;
31a-聚脲防护涂层Ⅰ;31b-聚脲防护涂层Ⅱ;31c-聚脲防护涂层Ⅲ;31d-聚脲防护涂层Ⅳ;32-聚脲材料;
41-带聚脲防护涂层的钢丝;42-由单根光面钢丝以及单根光面钢丝外的复合防护涂层构成的带聚脲防护涂层的钢丝;
81ae:带有聚脲防护涂层的钢丝拉索Ⅰae;
82ae:带有聚脲防护涂层的钢丝拉索Ⅱae;
81ae1:带有聚脲防护涂层的钢丝拉索Ⅰae1;
82ae1:带有聚脲防护涂层的钢丝拉索Ⅱae1;
81ae2:带有聚脲防护涂层的钢丝拉索Ⅰae2;
82ae2:带有聚脲防护涂层的钢丝拉索Ⅱae2;
81ae1d:带有聚脲防护涂层的钢丝拉索Ⅰae1d;
82ae1d:带有聚脲防护涂层的钢丝拉索Ⅱae1d;
81ae2d:带有聚脲防护涂层的钢丝拉索Ⅰae2d;
82ae2d:带有聚脲防护涂层的钢丝拉索Ⅱae2d;
81be:带有聚脲防护涂层的钢丝拉索Ⅰbe;
82be:带有聚脲防护涂层的钢丝拉索Ⅱbe;
81be1:带有聚脲防护涂层的钢丝拉索Ⅰbe1;
82be1:带有聚脲防护涂层的钢丝拉索Ⅱbe1;
81be2:带有聚脲防护涂层的钢丝拉索Ⅰbe2;
82be2:带有聚脲防护涂层的钢丝拉索Ⅱbe2;
81be1d:带有聚脲防护涂层的钢丝拉索Ⅰbe1d;
82be1d:带有聚脲防护涂层的钢丝拉索Ⅱbe1d;
81be2d:带有聚脲防护涂层的钢丝拉索Ⅰbe2d;
82be2d:带有聚脲防护涂层的钢丝拉索Ⅱbe2d。
81aeo:带有聚脲防护涂层的钢丝拉索Ⅰaeo;
82aeo:带有聚脲防护涂层的钢丝拉索Ⅱaeo;
81beo:带有聚脲防护涂层的钢丝拉索Ⅰbeo;
82beo:带有聚脲防护涂层的钢丝拉索Ⅱbeo;
81aec:带有聚脲防护涂层的钢丝拉索Ⅰaec;
82aec:带有聚脲防护涂层的钢丝拉索Ⅱaec;
81bec:带有聚脲防护涂层的钢丝拉索Ⅰbec;
82bec:带有聚脲防护涂层的钢丝拉索Ⅱbec;
81aec1:带有聚脲防护涂层的钢丝拉索Ⅰaec1;
82aec1:带有聚脲防护涂层的钢丝拉索Ⅱaec1;
81bec1:带有聚脲防护涂层的钢丝拉索Ⅰbec1;
82bec1:带有聚脲防护涂层的钢丝拉索Ⅱbec1;
81aec2:带有聚脲防护涂层的钢丝拉索Ⅰaec2;
82aec2:带有聚脲防护涂层的钢丝拉索Ⅱaec2;
81bec2:带有聚脲防护涂层的钢丝拉索Ⅰbec2;
82bec2:带有聚脲防护涂层的钢丝拉索Ⅱbec2。
81aec1d:带有聚脲防护涂层的钢丝拉索Ⅰaec1d;
82aec1d:带有聚脲防护涂层的钢丝拉索Ⅱaec1d;
81bec1d:带有聚脲防护涂层的钢丝拉索Ⅰbec1d;
82bec1d:带有聚脲防护涂层的钢丝拉索Ⅱbec1d;
81aec2d:带有聚脲防护涂层的钢丝拉索Ⅰaec2d;
82aec2d:带有聚脲防护涂层的钢丝拉索Ⅱaec2d;
81bec2d:带有聚脲防护涂层的钢丝拉索Ⅰbec2d;
82bec2d:带有聚脲防护涂层的钢丝拉索Ⅱbec2d。
具体实施方式
实施例一:
一种带有聚脲防护涂层的钢丝拉索的制作方法,它是先制作带聚脲防护涂层的钢丝、经过分丝将带聚脲防护涂层的钢丝经过聚脲材料填充工序,在各带聚脲防护涂层的钢丝之间填充聚脲材料32后再经过聚并步骤构成由n根带聚脲防护涂层的钢丝组成的钢丝组合体,构成由带聚脲防护涂层的钢丝组成、并在各带聚脲防护涂层的钢丝之间填充有聚脲材料32的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae;
其具体步骤包括:A、制作带聚脲防护涂层的钢丝;B、分丝C、聚脲材料填充工序:将带聚脲防护涂层的钢丝之间填充聚脲材料32;D、聚并成型;
其关键步骤是:A、制作带聚脲防护涂层的钢丝;C、聚脲材料填充工序:将带聚脲防护涂层的钢丝之间填充聚脲材料32,以下分述如下:
A、制作带聚脲防护涂层的钢丝:
以由单根光面钢丝1以及单根光面钢丝外的复合护涂层构成的具有复合防护涂层的带聚脲防护涂层的钢丝42为例,说明制作带聚脲防护涂层的钢丝42的具体步骤:
A11:对于原料钢丝进行严格检验,且其外表面不应有油、脂、漆等污染物,通过放线盘对钢丝进行解盘;
A12:表面处理:采用磷酸和超声波对钢丝表面进行处理,除掉钢丝表面的油污、灰尘、锈迹,并在单根钢丝表面生成一层均匀不容易腐蚀的灰色磷化膜;
A13:干燥:对钢丝进行加热干燥,去除表面水份;
A14:涂覆:将涂料微粒吸附在钢丝表面,使得钢丝表面附着环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层2;
A15:固化:涂覆后的单根钢丝,经过表面固结处理,在单根钢丝表面单独形成致密涂层保护膜:
A2:聚脲材料涂覆工序Ⅰ,即通过以下方式之一:
①挤出涂覆:钢丝通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝上;
③浸泡抽涂:钢丝通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝上;
使已经附着有保护膜的单根钢丝表面附着有的环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层上再涂覆一层聚脲防护涂层Ⅰ31a,形成由单根光面钢丝1以及单根光面钢丝外的复合防护涂层构成的具有复合防护涂层的带聚脲防护涂层的钢丝42(参见图1-2);
A3:成盘、包装:合格的具有复合防护涂层的带聚脲防护涂层的钢丝42经履带式牵引机定速牵引,并通过缠盘机同步卷制成盘,制作完成。
作为本发明实施例的一种变换,当制作由单根光面钢丝1以及单根光面钢丝外的聚脲防护涂层构成的带聚脲防护涂层的钢丝41时,可以省略步骤A14、A15,直接将加热干燥后的单根光面钢丝经过A2:聚脲材料涂覆工序Ⅰ使单根光面钢丝的表面涂覆一层聚脲防护涂层Ⅰ-31a构成由单根光面钢丝1以及涂覆在单根光面钢丝1外周的聚脲防护涂层Ⅰ31a构成的带聚脲防护涂层的钢丝41(参见图1-1)。
由于A11~A15为公知技术,在权利要求中,为叙述方便,将所述步骤A、制作带聚脲防护涂层的钢丝的步骤简化为:
A1:对钢丝进行预处理、干燥;
A2:聚脲材料涂覆工序Ⅰ;
A3:成盘、包装。
B:分丝:将带聚脲防护涂层的钢丝通过分丝板对应的孔位;C、聚脲材料填充工序:在带聚脲防护涂层的钢丝41、42之间填充聚脲材料32:
将带聚脲防护涂层的钢丝41、42通过以下方式之一进行涂覆式填充:
①挤出涂覆填充:将带聚脲防护涂层的钢丝41或42通过挤塑式设备热挤出的聚脲材料;
②喷涂填充:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到带聚脲防护涂层的钢丝41或42上;
③浸泡抽涂填充:带聚脲防护涂层的钢丝41或42通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式填充:利用机器涂刷使聚脲材料均匀涂覆在带聚脲防护涂层的钢丝41或42上;
D:聚并成型成钢丝组合体:将在带聚脲防护涂层的钢丝之间涂敷式填充有聚脲材料的带聚脲防护涂层的钢丝41、42在未干燥前通过多组成型装置把带聚脲防护涂层的钢丝41、42聚并成型;每个成型装置由2组3个互成120o角的滚压轮组成;通过调节每个滚压轮的相对位置和压紧力,使若干根钢丝索股整型为正六边形,索股内各带聚脲防护涂层的钢丝互相贴紧,使聚脲材料充分填充在带聚脲防护涂层的钢丝的索股间隙中,制成由n根带聚脲防护涂层的钢丝组成的钢丝组合体,各带聚脲防护涂层的钢丝之间填充有聚脲材料32的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae(参见图2-1、图2-2);图2-1、图2-2中,所述的带聚脲防护涂层的钢丝有19根,作为本发明实施例的一种变换,构成带聚脲防护涂层的钢丝拉索的带聚脲防护涂层的钢丝(41\42)的根数n根据实际需要可以增加或减少,至少为1根,用的比较多的是7-685根,一般n的取值范围是:1≤n≤1500,即:n为大于等于1小于等于1500的整数,所述的聚脲材料是纯聚脲材料或半聚脲材料。
作为本发明实施例的又一种变换,将制作成的带有聚脲防护涂层的钢丝拉索Ⅰae或带有聚脲防护涂层的钢丝拉索Ⅱae再经过PE套挤塑工序Ⅰ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在带有聚脲防护涂层的钢丝拉索索体外层,形成HDPE护套,构成外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae1或带有聚脲防护涂层的钢丝拉索Ⅱae1(参见图2-3~图2-4)。
作为本发明实施例的又一种变换,将外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae1或带有聚脲防护涂层的钢丝拉索Ⅱae1再经过PE套挤塑工序Ⅱ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索索体外层,形成外层HDPE护套,构成由内层HDPE护套6和外层HDPE护套7组成的双层HDPE护套构成的带有聚脲防护涂层的钢丝拉索Ⅰae2或带有聚脲防护涂层的钢丝拉索Ⅱae2(参见图2-5~图2-6)。
实施例二:
在钢丝组合体内部各带聚脲防护涂层的钢丝之间填充有聚脲材料的带聚脲防护涂层的钢丝拉索的钢丝组合体外周有一聚脲防护涂层Ⅱ构成的带有聚脲防护涂层的钢丝拉索的制作方法:
将实施例一制作的由n根带聚脲防护涂层的钢丝组成的钢丝组合体、并在各带聚脲防护涂层的钢丝之间填充有聚脲材料的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae再经过E:聚脲材料涂覆工序Ⅱ,即:通过以下方式之一:
①挤出涂覆:钢丝拉索Ⅰae或Ⅱae通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰae或Ⅱae上;
③浸泡抽涂:钢丝拉索Ⅰae或Ⅱae通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰae或Ⅱae上;
使带有聚脲防护涂层的钢丝拉索Ⅰae或带有聚脲防护涂层的钢丝拉索Ⅱae钢丝组合体的外周表面再附着一层聚脲防护涂层Ⅱ31b构成带有聚脲防护涂层的钢丝拉索Ⅰbe-81be或带有聚脲防护涂层的钢丝拉索Ⅱb-82be(参见图3-1、3-2)。
作为本发明实施例二的一种变换,将钢丝组合体内部各带聚脲防护涂层的钢丝之间填充有聚脲材料的带聚脲防护涂层的钢丝拉索Ⅰbe或Ⅱbe经过H:PE套挤塑工序Ⅰ制作成外层有单层HDPE护套的带聚脲防护涂层的钢丝拉索Ⅰbe1或Ⅱbe1(参见图3-3~图3-4);
作为本发明实施例的又一种变换,将外层有单层HDPE护套的带聚脲防护涂层的钢丝拉索Ⅰbe1或Ⅱbe1再经过I:PE套挤塑工序Ⅱ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在外层有单层HDPE护套的带聚脲防护涂层的钢丝拉索索体外层,形成外层HDPE护套,构成由内层HDPE护套6和外层HDPE护套7组成的双层HDPE护套构成的带聚脲防护涂层的钢丝拉索Ⅰbe2或Ⅱbe2(参见图3-5~图3-6)。
作为本发明实施例一或实施例二的又一种变换,将外层有单层HDPE护套的带聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1再经过聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1上;
③浸泡抽涂:将钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1上;
使外层有单层HDPE护套的带聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1的单层HDPE护套6外层再附着一层聚脲防护涂层Ⅳ31d,构成单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ31d的带聚脲防护涂层的钢丝拉索Ⅰae1d、Ⅱae1d(参见图2-7~图2-8)、Ⅰbe1d或Ⅱbe1d(参见图3-7~图3-8)。
作为本发明实施例一或实施例二的又一种变换,将外层有双层HDPE护套构成的带聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2经过对双层HDPE护套表面处理后,再经过J:聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2上;
③浸泡抽涂:将钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:由机器将聚脲材料涂刷到钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2上;
使具有双层HDPE护套的带聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2的外层HDPE护套外再附着一层聚脲防护涂层Ⅳ31d,构成双层HDPE护套外层涂覆有聚脲防护涂层Ⅳ31d的带聚脲防护涂层的钢丝拉索Ⅰae2d、Ⅱae2d(参见图2-9~图2-10)、Ⅰbe2d或Ⅱbe2d(参见图3-9~图3-10)。
实施例三:
带有聚脲防护涂层的钢丝拉索的钢丝组合体外有一缠包带、其缠包带的外层涂覆有一层聚脲防护涂层的带有聚脲防护涂层的钢丝拉索的制作方法:
将实施例一制作的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae以及实施例二制作出的带有聚脲防护涂层的钢丝拉索Ⅰbe、Ⅱbe经过F:缠包成型步骤,缠上一缠包带5,构成带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo(参见图4-1~图4-4)。
再将钢丝组合体外缠包有一缠包带的带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo再经过G:聚脲材料涂覆工序Ⅲ,即:通过以下方式之一:
①挤出涂覆:将带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae、Ⅰbe或Ⅱbe分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰae、Ⅱae、Ⅰbe或Ⅱbe上;
③浸泡抽涂:将钢丝拉索Ⅰae、Ⅱae、Ⅰbe或Ⅱbe通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:由机器将聚脲材料涂刷到钢丝拉索Ⅰae、Ⅱae、Ⅰbe或Ⅱbe上;
使带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo的缠包带外周表面再附着一层聚脲防护涂层Ⅲ31c构成缠包带外层涂覆有聚脲防护涂层Ⅲ31c的带有聚脲防护涂层的钢丝拉索钢丝拉索Ⅰaec、Ⅱaec、Ⅰbec、Ⅱbec;(参见图4-5、图4-6,图4-7、图4-8)。
作为本发明实施例三的一种变换,再将缠包带外层涂覆有聚脲防护涂层Ⅲ的带有聚脲防护涂层的钢丝拉索Ⅰaec、Ⅱaec、Ⅰbec和Ⅱbec经过H:PE套挤塑工序Ⅰ或I:PE套挤塑工序Ⅱ,制作成具有多重保护层的带有聚脲防护涂层的钢丝拉索。
H:PE套挤塑工序Ⅰ或I:PE套挤塑工序Ⅱ的具体内容如下:
H:PE套挤塑工序Ⅰ:将缠包带外层涂覆有聚脲防护涂层Ⅲ的带有聚脲防护涂层的钢丝拉索Ⅰaec、Ⅱaec、Ⅰbec或Ⅱbec再经过PE套挤塑工序Ⅰ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在带有聚脲防护涂层的钢丝拉索索体外层形成HDPE护套,构成外层有单层HDPE护套6的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1(参见图4-9~图4-12)
I:PE套挤塑工序Ⅱ:将外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1、Ⅱbec1再经过PE套挤塑工序Ⅱ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索索体外层,形成外层HDPE护套7,构成具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2、Ⅱbec2。(参见图4-13~图4-16)。
实施例四:
单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ的具有多重保护层的带有聚脲防护涂层的钢丝拉索的制作方法:
将实施例三制作出的外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1先经过对单层PE护套表面处理后,再经过J:聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1上;
③浸泡抽涂:将钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1上;
使外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1的单层HDPE护套6外层再附着一层聚脲防护涂层Ⅳ31d,构成单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ31d的带有聚脲防护涂层的钢丝拉索Ⅰaec1d、Ⅱaec1d、Ⅰbec1d或Ⅱbec1d;(参见图5-1~图5-4)。
实施例五:
双层HDPE护套的外层涂覆有聚脲防护涂层的具有多重保护层的带有聚脲防护涂层的钢丝拉索的制作方法:
将实施例三制作出的双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰbc2、Ⅱbc2、Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2先经过对双层PE护套表面处理后,再经过J:聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2上;
③浸泡抽涂:将钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2上;
使具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2的外层HDPE护套外再附着一层聚脲防护涂层Ⅳ31d,构成双层HDPE护套外层涂覆有聚脲防护涂层Ⅳ31d的带有聚脲防护涂层的钢丝拉索Ⅰaec2d、Ⅱaec2d、Ⅰbec2d或Ⅱbec2d(参见图6-1~图6-4)。
本发明各实施例中,所述的聚脲防护涂层的材料是纯聚脲材料或半聚脲材料;包括以下三种类型:
1)芳香族聚脲,该聚脲是利用芳香族异氰酸酯(如MDI、液化MDI、PAPI等)与氨基聚醚、氨基扩链剂反应而成,具有强度高,价格较合理等优点,适用在防腐、耐磨等的材料防护。
2)脂肪族聚脲,该聚脲是利用脂肪族异氰酸酯(如HDI、HDI的三聚体、HMDI、TMXDI等)与氨基聚醚、脂环胺类扩链剂反应制备的,具有耐黄变、良好的抗腐性能、优异的保色性能等,用于室外建筑的装饰面漆,也可以用作芳香族聚脲涂料的表面保护层。
3)聚天门冬氨酸酯聚脲,该聚脲是利用脂肪族异氰酸酯和聚天门冬氨酸酯反应制备,涂料的反应速度可调,凝胶时间可以从几分钟到几小时不等。可使用在高温高压撞击式混合环境中,具有低温固化、涂层不泛黄、固化过程中不易发泡、可厚涂施工、对底材的附着力好等优点。
聚脲涂料的选择根据施工的需要而定,所涉及到的聚脲涂料可以是聚脲防水涂料、聚脲防腐涂料、聚脲减震涂料、聚脲表面涂料、聚脲底层涂料、聚脲填充涂料、聚脲耐磨涂料、聚脲抗滑涂料等。
本发明各实施例中,是以高密度聚乙烯制作的HDPE护套为例,作为本发明实施例的一种变换,所述HDPE护套也可以是采用普通的低密度聚乙烯、中密度聚乙烯制作的PE护套或其他适于制作建筑用桥梁拉索护套的材料例如橡胶等制作的护套,这些都是等同置换,也是本专利的保护范围。
Claims (12)
1.一种带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:它是先制作带聚脲防护涂层的钢丝,经过分丝将带聚脲防护涂层的钢丝经过聚脲材料填充工序,在各带聚脲防护涂层的钢丝之间填充聚脲材料(32)后再经过聚并步骤构成由n根带聚脲防护涂层的钢丝组成的钢丝组合体、并在各带聚脲防护涂层的钢丝之间填充有聚脲材料(32)的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae;
其具体步骤包括:A、制作带聚脲防护涂层的钢丝;B、分丝、C、聚脲材料填充工序:将带聚脲防护涂层的钢丝之间填充聚脲材料(32);D、聚并成型;
其关键步骤是:A、制作带聚脲防护涂层的钢丝;C、聚脲材料填充工序:将带聚脲防护涂层的钢丝之间填充聚脲材料(32);
所述步骤A、制作带聚脲防护涂层的钢丝的步骤是:
A1:对钢丝进行预处理、干燥;
A2:防腐处理;
A3:成盘、包装;
所述的A2:防腐处理工序是将聚脲材料通过挤出涂覆、喷涂、浸泡抽涂或机器涂刷形式涂覆在单根光面钢丝上或单根钢丝表面附着有的环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层上,构成带聚脲防护涂层的钢丝;
该带聚脲防护涂层的钢丝或是由单根光面钢丝(1)以及涂覆在单根光面钢丝(1)外周的聚脲防护涂层Ⅰ(31a)构成的带聚脲防护涂层的钢丝(41);
该带聚脲防护涂层的钢丝或是由单根光面钢丝(1)以及单根光面钢丝外的复合防护涂层构成的具有复合防护涂层的带聚脲防护涂层的钢丝(42),所述的复合防护涂层是在单根光面钢丝(1)的外周附着有的环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层(2)与涂覆在表面附着涂层或镀层(2)上的聚脲防护涂层Ⅰ(31a)共同形成的复合防护涂层;
在A、制作带聚脲防护涂层的钢丝步骤:将聚脲材料通过挤出涂覆、喷涂、浸泡抽涂或机器涂刷形式涂覆的具体方法是:
将单根光面钢丝或已经附着有保护膜的单根钢丝-即在单根钢丝表面附着有环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层的钢丝,以下简称钢丝,通过聚脲材料涂覆工序Ⅰ,即通过以下方式之一:
①挤出涂覆:钢丝通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝上;
③浸泡抽涂:钢丝通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝上;
使单根光面钢丝的表面涂覆一层聚脲防护涂层Ⅰ(31a)或是在已经附着有保护膜的单根钢丝表面附着有的环氧涂层、镀锌涂层、塑料涂层、防腐油脂涂层、油性蜡或金属镀层之表面附着涂层或镀层上再涂覆一层聚脲防护涂层Ⅰ(31a),形成由单根光面钢丝(1)以及涂覆在单根光面钢丝(1)外周的聚脲防护涂层Ⅰ(31a)构成的带聚脲防护涂层的钢丝(41)、或是由单根光面钢丝(1)以及单根光面钢丝外的复合防护涂层构成的具有复合防护涂层的带聚脲防护涂层的钢丝(42),以下统称为:带聚脲防护涂层的钢丝(41、42);
B:分丝:将带聚脲防护涂层的钢丝通过分丝板对应的孔位;
C、聚脲材料填充工序:在带聚脲防护涂层的钢丝(41、42)之间填充聚脲材料(32):
将带聚脲防护涂层的钢丝(41、42)通过以下方式之一进行涂覆式填充:
①挤出涂覆填充:将带聚脲防护涂层的钢丝(41、42)通过挤塑式设备热挤出的聚脲材料;
②喷涂填充:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到带聚脲防护涂层的钢丝(41、42)上;
③浸泡抽涂填充:带聚脲防护涂层的钢丝(41、42)通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式填充:利用机器涂刷使聚脲材料均匀涂覆在带聚脲防护涂层的钢丝(41、42)上;
D:聚并成型:将在带聚脲防护涂层的钢丝之间填充聚脲材料(32)之间涂覆式填充有聚脲材料的带聚脲防护涂层的钢丝(41、42)通过多组成型装置把带聚脲防护涂层的钢丝(41、42)聚并成型;每个成型装置由2组3个互成120o角的滚压轮组成;通过调节每个滚压轮的相对位置和压紧力,使若干根钢丝索股整型为正六边形,索股内各带聚脲防护涂层的钢丝互相贴紧,使聚脲材料充分填充在带聚脲防护涂层的钢丝的索股间隙中,制成由n根带聚脲防护涂层的钢丝组成的钢丝组合体,各带聚脲防护涂层的钢丝之间填充有聚脲材料(32)的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae;n为大于等于1小于等于1500的整数,所述的聚脲材料是纯聚脲材料或半聚脲材料。
2.根据权利要求1所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将由n根带聚脲防护涂层的钢丝组成的钢丝组合体,并在各带聚脲防护涂层的钢丝之间填充有聚脲材料(32)的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae再经过E:聚脲材料涂覆工序Ⅱ,即:通过以下方式之一:
①挤出涂覆:钢丝拉索Ⅰae或Ⅱae通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰae或Ⅱae上;
③浸泡抽涂:钢丝拉索Ⅰae或Ⅱae通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰae或Ⅱae上;
使带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae钢丝组合体的外周表面再附着一层聚脲防护涂层Ⅱ(31b)构成带有聚脲防护涂层的钢丝拉索Ⅰbe(81be)或带有聚脲防护涂层的钢丝拉索Ⅱbe(82be),n为大于等于1小于等于1500的整数。
3.根据权利要求1或2所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将各带聚脲防护涂层的钢丝之间填充有聚脲材料(32)构成的带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae;或是带有聚脲防护涂层的钢丝拉索Ⅰbe、Ⅱbe再经过PE套挤塑工序Ⅰ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在带有聚脲防护涂层的钢丝拉索索体外层形成HDPE护套,构成外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1或外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰbe1、Ⅱbe1。
4.根据权利要求3所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1或带有聚脲防护涂层的钢丝拉索Ⅰbe1、Ⅱbe1再经过PE套挤塑工序Ⅱ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索索体外层,形成外层HDPE护套,构成具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2或带有聚脲防护涂层的钢丝拉索Ⅰbe2、Ⅱbe2。
5.根据权利要求3所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1先经过对单层PE护套表面处理后,再经过聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1上;
③浸泡抽涂:将钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1上;
使外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae1、Ⅱae1、Ⅰbe1或Ⅱbe1的单层HDPE护套(6)外层再附着一层聚脲防护涂层Ⅳ(31d),构成单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ(31d)的带有聚脲防护涂层的钢丝拉索Ⅰae1d、Ⅱae1d、Ⅰbe1d或Ⅱbe1d。
6.根据权利要求4所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2经过对双层HDPE护套表面处理后,再经过聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2上;
③浸泡抽涂:将钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:由机器将聚脲材料涂刷到钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2上;
使具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰae2、Ⅱae2、Ⅰbe2或Ⅱbe2的外层HDPE护套外再附着一层聚脲防护涂层Ⅳ(31d),构成双层HDPE护套外层涂覆有聚脲防护涂层Ⅳ(31d)的带有聚脲防护涂层的钢丝拉索Ⅰae2d、Ⅱae2d、Ⅰbe2d或Ⅱbe2d。
7.根据权利要求1或2所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将带有聚脲防护涂层的钢丝拉索Ⅰae、Ⅱae、Ⅰbe或Ⅱbe的钢丝组合体外缠包一缠包带(5),构成带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo。
8.根据权利要求7所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将钢丝组合体外缠包有一缠包带(5)的带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo再经过聚脲材料涂覆工序Ⅲ,即:通过以下方式之一:
①挤出涂覆:将带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo上;
③浸泡抽涂:将钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:由机器将聚脲材料涂刷到钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo上;
使带有聚脲防护涂层的钢丝拉索Ⅰaeo、Ⅱaeo、Ⅰbeo或Ⅱbeo的缠包带外周表面再附着一层聚脲防护涂层Ⅲ(31c)构成缠包带外层涂覆有聚脲防护涂层Ⅲ(31c)的带有聚脲防护涂层的钢丝拉索Ⅰaec、Ⅱaec、Ⅰbec或Ⅱbec。
9.根据权利要求8所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将缠包带外带有聚脲防护涂层的钢丝拉索Ⅰaec、Ⅱaec、Ⅰbec或Ⅱbec再经过PE套挤塑工序Ⅰ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在带有聚脲防护涂层的钢丝拉索索体缠包带外层形成HDPE护套,构成外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1。
10.根据权利要求9所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1或带有聚脲防护涂层的钢丝拉索Ⅰbec1、Ⅱbec1再经过PE套挤塑工序Ⅱ,即通过挤塑式设备将高密度聚乙烯塑料挤塑在外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索索体外层,形成外层HDPE护套(7),构成具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2和Ⅱbec2。
11.根据权利要求9所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1先经过对单层PE护套表面处理后,再经过聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1上;
③浸泡抽涂:将钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1上;
使外层有单层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec1、Ⅱaec1、Ⅰbec1或Ⅱbec1的单层HDPE护套(6)外层再附着一层聚脲防护涂层Ⅳ(31d),构成单层HDPE护套外层涂覆有聚脲防护涂层Ⅳ(31d)的带有聚脲防护涂层的钢丝拉索Ⅰaec1d、Ⅱaec1d、Ⅰbec1d或Ⅱbec1d。
12.根据权利要求10所述的带有聚脲防护涂层的钢丝拉索的制作方法,其特征在于:将具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2经过对双层HDPE护套表面处理后,再经过聚脲材料涂覆工序Ⅳ,即:通过以下方式之一:
①挤出涂覆:将钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2分别通过挤塑式设备热挤出的聚脲材料;
②喷涂:通过设备加温加压,原料在喷嘴处混合后由喷枪喷射聚脲材料到钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2上;
③浸泡抽涂:将钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2通过牵引设备浸泡在聚脲涂料中,浸泡后通过出口环状结构成型;
④机器涂刷方式:利用机器涂刷使聚脲材料均匀涂覆在钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2上;
使具有双层HDPE护套的带有聚脲防护涂层的钢丝拉索Ⅰaec2、Ⅱaec2、Ⅰbec2或Ⅱbec2的外层HDPE护套外再附着一层聚脲防护涂层Ⅳ(31d),构成双层HDPE护套外层涂覆有聚脲防护涂层Ⅳ(31d)的带有聚脲防护涂层的钢丝拉索Ⅰaec2d、Ⅱaec2d、Ⅰbec2d或Ⅱbec2d。