CN105038337B - A kind of diatom ooze coating component and the diatom ooze paste paint including the coating composition - Google Patents
A kind of diatom ooze coating component and the diatom ooze paste paint including the coating composition Download PDFInfo
- Publication number
- CN105038337B CN105038337B CN201510410248.XA CN201510410248A CN105038337B CN 105038337 B CN105038337 B CN 105038337B CN 201510410248 A CN201510410248 A CN 201510410248A CN 105038337 B CN105038337 B CN 105038337B
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- coating
- coating component
- ooze coating
- calcium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of diatom ooze coating component and the diatom ooze paste paint including the coating composition, by adding calcium sulfate crystal whiskers, make coating that there is enhancing, toughness reinforcing, thickening, it is heat-resisting, it is wear-resisting, oil resistant and the function such as thixotropy is high, addition aluminium hydroxide, improved diatom ooze coating color, uprise painting color brightness, color is whiter, and this diatom ooze coating acid-base value partial neutral, it is difficult the accumulation of salt in the surface soil, and this paint viscosity is high, adhesive effect is strong, slippery is high, be not in the phenomenons such as dry linting, and low cost, it is cheap, environmental protection, firmly, and compared to like product, weight is lighter.
Description
Technical field
The present invention relates to paint field, and in particular to a kind of diatom ooze coating component and the diatom ooze including the coating composition
Paste paint.
Background technology
With the improvement of people ' s living standards, requirement of the people to indoor environment also more and more higher, diatom ooze coating conduct
A kind of emerging coating, is increasingly paid attention to by people, and diatom ooze coating is not only environmentally friendly, without harmful chemical, except
With non-ignitable, sound insulation, fire prevention, it is lightweight and heat-insulated the features such as outside, also dehumidifying, the deodorant, effect of purifying the air of a room etc. is
Excellent environment-friendly type indoor and outdoor decoration material, however, for the performance of coating in existing diatom ooze coating, often with the addition of big
Other additives are measured, causes to be provided with toxicity in originally pure natural diatom ooze, and existing diatom ooze coating color is inclined
Secretly, color is not bright enough.
The content of the invention
It is of the invention there is provided a kind of diatom ooze coating component and its including the component in order to solve the deficiencies in the prior art
Diatom ooze paste paint.
The present invention use technical solution be：A kind of diatom ooze coating component, including following mass percent component：
35-50% diatomite, 0.05-0.3% calcium sulfate crystal whiskers, 3-10% dispersants, 2-8% aluminium hydroxides, 0.05-1% titanium dioxide, 1-
8% nanomete talc powder, 0.03-0.8% calcium hydroxides, 0.5-3% coarse whitings, 0.5-10% calcium sulfate, 0.3-2% mica powders.
Described calcium sulfate is food grade calcium sulfate.
Described calcium hydroxide is lightweight calcium hydroxide.
A kind of diatom ooze paste paint comprising diatom ooze coating component, including diatom ooze coating component and water, described silicon
Algae slime paint component is 1 with the mass ratio of water：0.85-1：0.95.
Described diatom ooze coating component is 1 with the mass ratio of water：0.9.
The beneficial effects of the invention are as follows：The invention provides a kind of diatom ooze coating component and its diatom including the component
Mud coating, by adding calcium sulfate crystal whiskers, makes coating have enhancing, toughness reinforcing, thickening, heat-resisting, wear-resisting, oil resistant and thixotropy high
Etc. function, aluminium hydroxide is added, improved diatom ooze coating color, uprise painting color brightness, color is whiter, and this
Diatom ooze coating acid-base value partial neutral, is difficult the accumulation of salt in the surface soil, and this paint viscosity is high, and adhesive effect is strong, and slippery is high, is not in dry linting
It is cheap etc. phenomenon, and low cost, and compared to like product, weight is lighter.
Specific embodiment
With reference to some specific embodiments, to a kind of diatom ooze coating component of the invention and its silicon including the component
Algae mud coating is further described.
Embodiment 1
A kind of diatom ooze coating component, including following mass percent component：35% diatomite, 0.3% calcium sulfate crystal whiskers,
10% dispersant, 2% aluminium hydroxide, 1% titanium dioxide, 1% nanomete talc powder, 0.8% lightweight calcium hydroxide, 2% coarse whiting, 0.5% food
Use level calcium sulfate, 2% mica powder.
By above-mentioned diatom ooze coating component and water 1：0.85 is mixed to prepare diatom ooze paste paint.
Embodiment 2
A kind of diatom ooze coating component, including following mass percent component：50% diatomite, 0.1% calcium sulfate crystal whiskers,
3% dispersant, 5% aluminium hydroxide, 0.05% titanium dioxide, 2% nanomete talc powder, 0.03% lightweight calcium hydroxide, 0.5% coarse whiting,
10% food grade calcium sulfate, 1% mica powder.
By above-mentioned diatom ooze coating component and water 1：0.9 is mixed to prepare the painting of diatom mud.
Embodiment 3
A kind of diatom ooze coating component, including following mass percent component：40% diatomite, 0.05-0.3% calcium sulfate is brilliant
Must, 7% dispersant, 8% aluminium hydroxide, 0.7% titanium dioxide, 8% nanomete talc powder, 0.5% lightweight calcium hydroxide, 3% coarse whiting,
8% food grade calcium sulfate, 0.3% mica powder.
By above-mentioned diatom ooze coating component and water 1：0.95 is mixed to prepare diatom ooze paste paint.
Experiment detection
Calcium sulfate crystal whiskers make coating have enhancing, toughness reinforcing, thickening, heat-resisting, wear-resisting, oil resistant and thixotropy high in the present invention
Performance, and its is nontoxic, it is pollution-free；
Aluminium hydroxide makes to have adjusted the color of coating, makes it whiter, and increased the viscosity of product；
Nanomete talc powder increased the slippery of coating；And replace the expensive titanium dioxide in part by adding nanomete talc powder
Titanium, saves cost；
Calcium hydroxide and coarse whiting increased the bond strength of coating；
Food grade calcium sulfate increased the viscosity of product, and food grade, safety non-pollution；
Mica powder increased the density of product.
The above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications
Should be regarded as protection scope of the present invention.
Claims (5)
1. a kind of diatom ooze coating component, it is characterised in that including following mass percent component：35-50% diatomite, 0.05-
0.3% calcium sulfate crystal whiskers, 3-10% dispersants, 2-8% aluminium hydroxides, 0.05-1% titanium dioxide, 1-8% nanomete talc powders, 0.03-
0.8% calcium hydroxide, 0.5-3% coarse whitings, 0.5-10% calcium sulfate, 0.3-2% mica powders.
2. a kind of diatom ooze coating component according to claim 1, it is characterised in that described calcium sulfate is food grade sulphur
Sour calcium.
3. a kind of diatom ooze coating component according to claim 1, it is characterised in that described calcium hydroxide is lightweight hydrogen
Calcium oxide.
4. a kind of diatom ooze paste paint comprising diatom ooze coating component according to claim 1, it is characterised in that including
Diatom ooze coating component and water, described diatom ooze coating component and the mass ratio of water is 1：0.85-1：0.95.
5. diatom ooze paste paint according to claim 4, it is characterised in that the matter of described diatom ooze coating component and water
Amount is than being 1：0.9.