CN104194533A - Waterborne non-slip floor coating based on inorganic magnesium salt and preparation method of waterborne non-slip floor coating - Google Patents
Waterborne non-slip floor coating based on inorganic magnesium salt and preparation method of waterborne non-slip floor coating Download PDFInfo
- Publication number
- CN104194533A CN104194533A CN201410461790.3A CN201410461790A CN104194533A CN 104194533 A CN104194533 A CN 104194533A CN 201410461790 A CN201410461790 A CN 201410461790A CN 104194533 A CN104194533 A CN 104194533A
- Authority
- CN
- China
- Prior art keywords
- magnesium salt
- water
- magnesium
- inorganic
- inorganic magnesium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a waterborne non-slip floor coating based on inorganic magnesium salt and a preparation method of the waterborne non-slip floor coating. The coating comprises the following components in percentage by weight: 15-30% of inorganic magnesium salt, 5-60% of synthetic resin, 5-40% of a filler, 1-15% of an additive, 0-3% of a color pigment and the balance of water, wherein the total weight is 100%, the inorganic magnesium salt refers to at least one of magnesium carbonate, magnesium silicate, magnesium chloride, magnesium hydroxide, magnesium sulfate, or magnesium oxide, and the weight content of the magnesium is 1-40%. The inorganic magnesium salt, the synthetic resin, the filler, the additive, the color pigment and water are added to a container proportionally, and the stirred for 0.5-3 hours to obtain the required product. According to the invention, the inorganic magnesium salt is introduced into a polymer coating, so that the production cost is greatly lowered, and the coating further is better in skid resistance, wear resistance, weather resistance, pressure resistance and impact resistance. The product preparation and production process is simple, and the raw materials are easy to obtain, so that the waterborne non-slip surface coating is suitable for large-scale production.
Description
Technical field
The present invention relates to a kind of water-based anti-slip floor paint, particularly a kind of water-based anti-slip floor paint based on inorganic magnesium salt and preparation method thereof.
Background technology
Along with improving gradually and environmental regulation increasingly strict of people's environmental consciousness, water-borne coatings will become the focus that 21 century studies.Along with the continuous application of achievement in research, current water-based inner, external wall coating, the research of the domestic environments coating such as aqueous woodware paint reaches its maturity, and also has comparatively ripe product to circulate on market.Comparatively speaking, people are less to the environmental-protecting performance research of the paint product using under outdoor environment, add outdoor products and be subject to the impact of weather environment factor complicated and changeable, more strict to the requirement of product performance, make the research and development of outdoor aqueous coating obviously lag behind indoor article.And paint out of doors in paint field, for the coating on ground because it is at sticking power, wear resistance, crushing resistance, hardness, has many special requirements in many-sided index such as weathering resistance, make the research of domestic this series products at present face larger difficulty.
Floor line and coating on China's road is base-material mainly with petroleum resin and modified rosin resin greatly at present, exists energy consumption high larger with pollution, and operating efficiency is low, graticule is repaired the shortcomings such as difficulty.Develop in recent years performance better and more the water-borne coatings of environmental protection become the main development direction of coatings industry, on market, emerging floor coating is mainly epoxy resin or polyurethane material, mostly has complex process, and cost is higher, wear resistance and weathering resistance are poor, the shortcomings such as poor stability.
Summary of the invention
The object of the invention is to provide a kind of water-based anti-slip floor paint based on inorganic magnesium salt and preparation method thereof.
The water-based anti-slip floor paint based on inorganic magnesium salt that the present invention proposes, described coating is comprised of inorganic magnesium salt, synthetic resins, weighting agent, additive, tinting pigment and water, and its weight percent is:
Inorganic magnesium salt: 15-30%
Synthetic resins: 5-60%
Weighting agent: 5%-40%
Additive: 1%-15%
Tinting pigment: 0%-3%
All the other are water, and its gross weight meets 100%;
Wherein: described inorganic magnesium salt refers at least one in magnesiumcarbonate, Magnesium Silicate q-agent, magnesium chloride, magnesium hydroxide, magnesium sulfate or magnesium oxide, its magnesium elements weight content is 1%-40%.
The preparation method of the aqueous ground coating based on inorganic magnesium salt that the present invention proposes, is added into inorganic magnesium salt, synthetic resins, weighting agent, additive, tinting pigment and water in container in proportion, stirs and within 0.5-3 hour, obtains desired product.
In the present invention, described in state synthetic resins and refer at least one in acrylic resin, aqueous epoxy resins, epoxy resin or urethane.
In the present invention, described weighting agent refers at least one in flyash, kaolin, silicon-dioxide or glass fibre.
In the present invention, described additive refers at least one in film coalescence aid, sanitas, tackifier, dispersion agent or thickening material.
In the present invention, described tinting pigment is titanium dioxide, red iron oxide or iron oxide green etc.
This coating can be preserved more than 6 months under airtight normal temperature condition.
In the present invention, inorganic magnesium salt generally has good hardness and ultimate compression strength, synthetic resins can be adsorbed on inorganic magnesium salt particle surface securely, and form three dimensional polymeric at its pore space, with inorganic magnesium salt external phase each other, thereby guaranteed firmly cohering between inorganic magnesium salt and synthetic resins, such structure can improve hardness and the snappiness after coating dehydration simultaneously, therefore coating of the present invention has good wear resistance and weathering resistance.
In the present invention, described weighting agent cost is lower, after adding, can when keeping described invention coating anti-skid, wear resistance and sticking power, effectively reduce production costs.
In the present invention, described additive is at aspect of performances such as film-forming properties, dispersiveness and viscosity, optionally to add one or more to improve its deficiency for described coating.
The present invention is incorporated into inorganic magnesium salt in high-molecular coating first, has not only significantly reduced production cost, also makes its coating have good anti-skid and wear resistance.Of the present invention except thering is good wear resistance and weathering resistance, also there is the advantages such as easy construction, closely zero organic volatile (VOC) discharges, cost is lower.This product preparation and production technique are simple, and raw material is easy to get, and is applicable to large-scale production.
Embodiment
Below in conjunction with some embodiment, technical scheme of the present invention is described further, but should limit by any way the present invention, claimed scope of the present invention embodies in claims.
Embodiment 1: in 5 kg epoxy resin, add 2 kg Magnesium Silicate q-agents, and 1.8 kg silicon-dioxide, 1 kg water, 0.3 kg thickening material, 0.2 kg titanium dioxide, mixes at the uniform velocity to stir within 2 hours, obtaining water-based skid-resistant coating sample 1.
Embodiment 2: in 40 kg epoxy resin, add 25 kg magnesium oxide, and 5 kg silicon-dioxide, 7kg kaolin, 10 kg aqueous polyurethanes, 10 kg water, 0.2 kg dispersion agent, 2 kg titanium dioxides, mix at the uniform velocity to stir within 0.5 hour, obtaining water-based skid-resistant coating sample 2.
Embodiment 3: in 5 kg urethane, add 2.5kg magnesium hydroxide, and 0.8 kg silicon-dioxide, 2 kg water, 0.3 kg thickening material, 0.02kg red iron oxide, 0.01kg dispersion agent, mixes at the uniform velocity to stir within 1 hour, obtaining the red skid-resistant coating sample 3 of water-based.
Embodiment 4: in 2 kg urethane, add 1.6 kg magnesium chlorides, and 0.7 kg magnesium oxide, 1.8 kg silicon-dioxide, 3 kg water, 0.1kg dispersion agent, mixes at the uniform velocity to stir within 2.5 hours, obtaining water-based skid-resistant coating sample 4.
Embodiment 5: in 6 kg acrylic resins, add 2 kg magnesium sulfate, and 1.8 kg silicon-dioxide, 1kg aqueous epoxy resins, 2 kg water, 0.15 kg dispersion agent, 0.2 kg iron oxide green, mixes at the uniform velocity to stir within 2.5 hours, obtaining water-based skid-resistant coating sample 5.
The performance test results of each sample is as follows:
Claims (5)
1. the water-based anti-slip floor paint based on inorganic magnesium salt, is characterized in that described coating is comprised of inorganic magnesium salt, synthetic resins, weighting agent, additive, tinting pigment and water, and its weight percent is:
Inorganic magnesium salt: 15-30%
Synthetic resins: 5-60%
Weighting agent: 5%-40%
Additive: 1%-15%
Tinting pigment: 0%-3%
All the other are water, and its gross weight meets 100%;
Wherein: described inorganic magnesium salt refers at least one in magnesiumcarbonate, Magnesium Silicate q-agent, magnesium chloride, magnesium hydroxide, magnesium sulfate or magnesium oxide, its magnesium elements weight content is 1%-40%.
2. the preparation method of the aqueous ground coating based on inorganic magnesium salt as claimed in claim 1, it is characterized in that inorganic magnesium salt, synthetic resins, weighting agent, additive, tinting pigment and water to be added in proportion in container, stir and within 0.5-3 hour, obtain desired product.
3. the water-based anti-slip floor paint based on inorganic magnesium salt according to claim 1, states synthetic resins and refers at least one in acrylic resin, aqueous epoxy resins, epoxy resin or urethane described in it is characterized in that.
4. the water-based anti-slip floor paint based on inorganic magnesium salt according to claim 1, is characterized in that described weighting agent refers at least one in flyash, kaolin, silicon-dioxide or glass fibre.
5. the water-based anti-slip floor paint based on inorganic magnesium salt according to claim 1, is characterized in that described additive refers at least one in film coalescence aid, sanitas, tackifier, dispersion agent or thickening material.