CN104693926A - Preparation method of water-based floor paint and construction process of water-based floor paint - Google Patents
Preparation method of water-based floor paint and construction process of water-based floor paint Download PDFInfo
- Publication number
- CN104693926A CN104693926A CN201510081891.2A CN201510081891A CN104693926A CN 104693926 A CN104693926 A CN 104693926A CN 201510081891 A CN201510081891 A CN 201510081891A CN 104693926 A CN104693926 A CN 104693926A
- Authority
- CN
- China
- Prior art keywords
- water
- floor paint
- based floor
- agent
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a preparation method of water-based floor paint and a construction process of the water-based floor paint and belongs to the field of floor materials. The preparation method of the water-based floor paint comprises the following steps: adding 10-30 parts of deionized water, 15-40 parts of titanium dioxide, 0.4-0.8 part of a dispersing agent and 0.2-0.5 part of a defoaming agent, and dispersing for 30-50 minutes at a high speed; adding 30-60 parts of waterborne acrylic resin, 1-3 parts of color paste, 0.3-0.6 part of a defoaming agent, 0.5-1 part of a flattening agent, 0.5-1 part of a wetting agent and 2-5 parts of a thickening agent and dispersing for 10-30 minutes at a middle speed; and stopping dispersing to prepare the water-based floor paint. Compared with the prior art, a hydroxyl acrylic emulsion is mixed with hydroxyl acrylic dispersion according to any ratio, so that the water-based floor paint is relatively high in brightness, abradability, flexibility and color retaining rate; the relatively high color retaining rate and the weather resistance are achieved; the water-based floor paint is non-toxic, harmless and environmentally friendly; the harm to the human health caused by organic solvents is avoided; the complete environmental protection effect of construction and application can be implemented.
Description
Technical field
The present invention relates to a kind of method for making of water-based floor paint and the construction technology of water-based terrace, belong to floor material field.
Background technology
Terrace is the part that bottom room contacts with soil layer, and it bears the load in bottom room, requires to have certain strength and stiffness, and has protection against the tide, waterproof, warming, wear-resisting performance.Chemical industry and war industry's industry, field of aerospace, medicine and foodstuff manufacturing, automobile industry, hospital, airport, school, sports buildings, office building, Venue, underground parking or garage, freight yard, freight house, oil depot etc., all want terrace paint to carry out coating protection and decoration.
Traditional floor structure is masonry, wood floor structure.The structure that modern age is commonly used is cement concrete, Steel Concrete, floor ceramic tile, granite and marble, glued board and plastic plate.
Masonry and cement concrete are carbonate material, porous in alkalescence, easily broken and corrosion, timber is genus polyporus material also, is also easily corroded by other medium osmosis, and matter is soft not wear-resisting, though floor ceramic tile and marble hard, matter is just easily broken, and acid and alkali-resistance does not corrode.Tradition floor construction is complicated, and curing at low temperatures speed is slow, comes into operation often need for a long time from constructing to.Plastic plate is attractive in appearance smooth, but intensity is low, puncture resistance is poor, without wear resistance.
Conventional terrace paint mainly comprises: epoxy floor coating, urethane resin terrace paint, unsaturated polyester resin coating etc.Except have necessary ornamental except, floor paint also has excellent wear resistance, anti-skid, elasticity, corrosion-resistant and static resistance.But the use of traditional floor paint must have corresponding solvent, these solvents are generally have certain murder by poisoning, not only to environment, also have a strong impact on the health of constructor and user.
Summary of the invention
One of the object of the invention is to provide a kind of method for making of water-based floor paint, be used for replacing traditional floor paint (having solvent, non-environmental protection), the construction of terrace under normal temperature and pressure conditions can be realized, have the product quality of higher cost performance, better properties index and more environmental protection.
Another object of the present invention is to provide a kind of construction technology of water-based terrace.
The technical solution adopted in the present invention is:
A preparation method for water-based floor paint, is characterized in that, comprises the steps:
(1) by 10-30 part deionized water, 15-40 part titanium dioxide, 0.4-0.8 part dispersion agent, 0.2-0.5 part defoamer, high speed dispersion 30-50 minute;
(2) 30-60 part water-borne acrylic resin, 1-3 part mill base, 0.3-0.6 part defoamer is added, and 0.5-1 part flow agent, 0.5-1 part wetting agent, 2-5 part thickening material, middling speed dispersion 10-30 minute;
(3) stop dispersion, obtain this material.
Described water-borne acrylic resin is that hydroxyl acrylic emulsion mixes with arbitrary proportion with hydroxyl acrylic aqueous dispersion.
Described titanium dioxide is Rutile type Titanium Dioxide.
Described thickening material is synthetic polymer class thickening material.
Described defoamer is hydrophobic type polysiloxane defoamer.
Described mill base is water-based organic environmental-protection or the inorganic mill base of aqueous, environmental protective.
Described dispersion agent is polypropylene ester class dispersion agent; Described flow agent is organic silicon surfactant; Described wetting agent is polyacrylate(s) wetting agent.
A construction technology for water-based terrace, is characterized in that comprising the steps:
(1) concrete pedestal is processed;
(2) blade coating aqueous priming paint;
(3) levelling to the basic use epoxy-based lacquers processed;
(4) blade coating or spraying water-based floor paint colored paint layer;
(5) blade coating or spraying water varnish finishing coat.
In above-mentioned construction technology, raw materials used except water-based floor paint, other are the commodity of prior art, are commercially easy to obtain; Whole system is made to realize the construction of Water-borne modification to utilization of the present invention.
Compared with prior art, the invention has the beneficial effects as follows:
(1) water-borne acrylic resin of the present invention is that hydroxyl acrylic emulsion mixes with arbitrary proportion with hydroxyl acrylic aqueous dispersion, can obtain better luminance brightness, fastness to rubbing, suppleness and Bao Se and lead, and provides more lasting guarantor's look rate and weathering resistance.
(2) water-based terrace take water as solvent, nontoxic, and environmental protection avoids the harm of organic solvent to HUMAN HEALTH, can realize the complete feature of environmental protection of constructing and applying.
(3) titanium dioxide of the present invention adopts rutile-type, has the feature of good water tolerance, weather resistance, hiding rare, high tinting strength, color inhibition.
(4) defoamer that the present invention adopts is hydrophobic type polysiloxane defoamer, and easily broken bubble, easily eliminates mechanical bubble, can make that coatingsurface brightness is higher, color and luster is vivider, physicals is better.
(5) thickening material that the present invention adopts is synthetic polymer class thickening material, can provide the rheological property that product is desirable, be conducive to the stability in storage of system.
(6) product processes of the present invention is simple, easy to operate, the raw materials used commodity being prior art, is commercially easy to obtain, and has very strong practicality and generalization.
Embodiment
Embodiment 1-4: formula (unit: Kg)
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | |
| Deionized water | 15 | 20 | 25 | 25 |
| Titanium dioxide | 20 | 15 | 25 | 30 |
| Dispersion agent | 0.4 | 0.4 | 0.6 | 0.7 |
| Defoamer | 0.4 | 0.4 | 0.5 | 0.6 |
| Water-borne acrylic resin | 30 | 35 | 40 | 50 |
| Aqueous color paste | 1 | 1 | 2 | 2 |
| Thickening material | 2 | 2 | 3 | 3 |
| Wetting agent | 0.5 | 0.5 | 0.7 | 0.7 |
| Flow agent | 0.5 | 0.5 | 0.5 | 0.5 |
Wherein, water-borne acrylic resin is that hydroxyl acrylic emulsion mixes with arbitrary proportion with hydroxyl acrylic aqueous dispersion.
The titanium dioxide selected is Rutile type Titanium Dioxide; Thickening material is synthetic polymer class thickening material; Defoamer is hydrophobic type polysiloxane defoamer; Select water-based organic environmental-protection or the inorganic mill base of aqueous, environmental protective.
Described dispersion agent is polypropylene ester class dispersion agent; Described flow agent is organic silicon surfactant; Described wetting agent is polyacrylate(s) wetting agent.
Embodiment 5: optimum embodiment
A preparation method for water-based terrace, comprises the steps:
(1) by 14 parts of deionized waters, 30 parts of titanium dioxides, 0.5 part of dispersion agent, 0.3 part of defoamer, high speed dispersion 30-50 minute;
(2) 50 parts of water-borne acrylic resins, 1 part of mill base, 0.5 part of defoamer and 0.5 part of flow agent, 0.7 part of wetting agent, 2.5 parts of thickening materials are added, middling speed dispersion 10-30 minute;
(3) stop dispersion, obtain this material.
Claims (5)
1. a method for making for water-based floor paint, is characterized in that, comprises the steps:
(1) by 10-30 part deionized water, 15-40 part titanium dioxide, 0.4-0.8 part dispersion agent, 0.2-0.5 part defoamer, high speed dispersion 30-50 minute;
(2) 30-60 part water-borne acrylic resin, 1-3 part mill base, 0.3-0.6 part defoamer is added, and 0.5-1 part flow agent, 0.5-1 part wetting agent, 2-5 part thickening material, middling speed dispersion 10-30 minute;
(3) stop dispersion, obtain this material.
2. the preparation method of a kind of water-based floor paint according to claim 1, is characterized in that, described water-borne acrylic resin is that hydroxyl acrylic emulsion mixes with arbitrary proportion with hydroxyl acrylic aqueous dispersion.
3. the preparation method of a kind of water-based floor paint according to claim 1, is characterized in that, described titanium dioxide is Rutile type Titanium Dioxide.
4. the preparation method of a kind of water-based floor paint according to claim 1, is characterized in that, described mill base is water-based organic environmental-protection or the inorganic mill base of aqueous, environmental protective.
5. the preparation method of a kind of water-based floor paint according to claim 1, is characterized in that, described dispersion agent is polypropylene ester class dispersion agent; Described flow agent is organic silicon surfactant; Described wetting agent is polyacrylate(s) wetting agent.