CN104693926B - A kind of preparation method of aqueous floor paint and the construction technology of aqueous terrace - Google Patents
A kind of preparation method of aqueous floor paint and the construction technology of aqueous terrace Download PDFInfo
- Publication number
- CN104693926B CN104693926B CN201510081891.2A CN201510081891A CN104693926B CN 104693926 B CN104693926 B CN 104693926B CN 201510081891 A CN201510081891 A CN 201510081891A CN 104693926 B CN104693926 B CN 104693926B
- Authority
- CN
- China
- Prior art keywords
- parts
- aqueous
- preparation
- defoamers
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of preparation method and its construction technology of aqueous floor paint, belong to floor material field, its preparation method comprises the following steps：By 10 30 parts of deionized waters, 15 40 parts of titanium dioxides, 0.4 0.8 parts of dispersants, 0.2 0.5 parts of defoamers, disperse 30 50 minutes at a high speed；30 60 parts of water-based acrylic resins, 13 parts of mill bases, 0.3 0.6 parts of defoamers, 0.5 1 parts of levelling agents, 0.5 1 parts of wetting agents, 25 parts of thickeners are added, middling speed is scattered 10 30 minutes；Stop disperseing, produce this material.Compared with prior art, the present invention is mixed with hydroxyl acrylic emulsion with hydroxyl acrylic aqueous dispersion with arbitrary proportion, and can obtain more preferable brightness, abrasion resistance, suppleness and color retention rate, there is provided more longlasting color retention rate and weatherability；Aqueous terrace is nontoxic, environmental protection, it is to avoid harm of the organic solvent to health, and the complete feature of environmental protection of construction and application can be achieved.
Description
Technical field
The present invention relates to a kind of preparation method of aqueous floor paint and the construction technology of aqueous terrace, belong to floor material field.
Background technology
Terrace is the part that bottom room is in contact with soil layer, and it bears the load in bottom room, it is desirable to certain
Strength and stiffness, and with protection against the tide, waterproof, warming, wear-resisting performance.Chemical industry and war industry's industry, field of aerospace, medicine and food
Product manufacturing industry, auto manufacturing, hospital, airport, school, sports buildings, office building, Venue, underground parking or garage,
Freight yard, freight house, oil depot etc., are intended to floor coatings and carry out coating protection and decoration.
Traditional floor structure is masonry, wood floor structure.The structure that modern age is commonly used is cement concrete, reinforced concrete
Soil, floor ceramic tile, granite and marble, glued board and plastic plate.
Masonry and cement concrete are carbonate material, porous in alkalescence, easily broken and corrosion, timber also genus polyporus material
Material, is also easily corroded, matter is not soft wear-resisting, though floor ceramic tile and marble are hard, matter is just broken, not acid and alkali-resistance by other medium osmosis
Corrode.Traditional floor construction is complicated, and curing at low temperatures speed is slow, is generally required from constructing to coming into operation for a long time.Plastic cement
Plate is attractive in appearance smooth, but low intensity, puncture resistance it is poor, without wearability.
Conventional floor coatings mainly include：Epoxy floor coating, polyurethane resin floor coatings, unsaturated polyester (UP)
Cold coating etc..Except with it is necessary it is ornamental in addition to, floor paint also have excellent wearability, skid resistance, elasticity, it is corrosion-resistant and
Antistatic behaviour.But the use of traditional floor paint must have corresponding solvent, these solvents are usually to have certain murder by poisoning, no
Only environment is polluted, the health of constructor and user is also had a strong impact on.
The content of the invention
One of the object of the invention is to provide a kind of preparation method of aqueous floor paint, for replace traditional floor paint (have solvent, it is non-
Environmental protection), the construction of terrace under normal temperature and pressure conditionses is may be implemented in, there is higher cost performance, better performance index and more ring
The product quality of guarantor.
Another object of the present invention is to provide a kind of construction technology of aqueous terrace.
The technical solution adopted in the present invention is：
A kind of preparation method of aqueous floor paint, it is characterised in that comprise the following steps：
(1) it is high by 10-30 parts of deionized waters, 15-40 parts of titanium dioxides, 0.4-0.8 parts of dispersants, 0.2-0.5 parts of defoamers
Speed is scattered 30-50 minutes；
(2) 30-60 parts of water-based acrylic resins, 1-3 parts of mill bases, 0.3-0.6 parts of defoamers, and 0.5-1 parts of streams are added
Flat agent, 0.5-1 parts of wetting agents, 2-5 parts of thickeners, middling speed are scattered 10-30 minutes；
(3) stop disperseing, produce this material.
Described water-based acrylic resin is that hydroxyl acrylic emulsion is mixed with hydroxyl acrylic aqueous dispersion with arbitrary proportion.
Described titanium dioxide is rutile type titanium white.
Described thickener is synthesized polymer species thickener.
Described defoamer is the polysiloxane-based defoamer of hydrophobic type.
Described mill base is aqueous organic environmental-protection or the inorganic mill base of aqueous, environmental protective.
Described dispersant is polypropylene esters dispersant；Described levelling agent is organic silicon surfactant；Described
Wetting agent is polyacrylate wetting agent.
A kind of construction technology of aqueous terrace, it is characterised in that comprise the following steps：
(1) concrete pedestal is handled；
(2) aqueous priming paint is scratched；
(3) it is levelling with water-base epoxy paint to the basis treated；
(4) scratch or spray aqueous floor paint colored paint layer；
(5) scratch or spray water varnish finishing coat.
Raw materials used in addition to aqueous floor paint in above-mentioned construction technology, other are the commodity of prior art, commercially
It is readily available；Utilization to the present invention causes whole system to realize the construction of Water-borne modification.
Compared with prior art, the beneficial effects of the invention are as follows：
(1) water-based acrylic resin of the present invention is that hydroxyl acrylic emulsion and hydroxyl acrylic aqueous dispersion are mixed with arbitrary proportion
Close, can obtain more preferable brightness, abrasion resistance, suppleness and color retention rate, there is provided more longlasting color retention rate and weatherability.
(2) aqueous terrace is nontoxic using water as solvent, environmental protection, it is to avoid danger of the organic solvent to health
Evil, can be achieved the complete feature of environmental protection of construction and application.
(3) titanium dioxide of the invention uses rutile-type, with preferable water resistance, weather resistance, hiding rare, high coloring
The characteristics of power, color inhibition.
(4) defoamer that the present invention is used is the polysiloxane-based defoamer of hydrophobic type, easy brokenly bubble, easily eliminates mechanical bubble,
Can make that coating surface brightness is higher, color and luster is vivider, physical property more preferably.
(5) thickener that the present invention is used is synthesized polymer species thickener, it is possible to provide the preferable rheological property of product, has
Beneficial to the storage stability of system.
(6) product processes of the invention are simple, and easy to operate, raw materials used is the commodity of prior art, in market
On be readily available, with very strong practicality and generalization.
Embodiment
Embodiment 1-4：It is formulated (unit：Kg)
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | |
| Deionized water | 15 | 20 | 25 | 25 |
| Titanium dioxide | 20 | 15 | 25 | 30 |
| Dispersant | 0.4 | 0.4 | 0.6 | 0.7 |
| Defoamer | 0.4 | 0.4 | 0.5 | 0.6 |
| Water-based acrylic resin | 30 | 35 | 40 | 50 |
| Aqueous color paste | 1 | 1 | 2 | 2 |
| Thickener | 2 | 2 | 3 | 3 |
| Wetting agent | 0.5 | 0.5 | 0.7 | 0.7 |
| Levelling agent | 0.5 | 0.5 | 0.5 | 0.5 |
Wherein, water-based acrylic resin is that hydroxyl acrylic emulsion is mixed with hydroxyl acrylic aqueous dispersion with arbitrary proportion.
The titanium dioxide of selection is rutile type titanium white；Thickener is synthesized polymer species thickener；Defoamer is hydrophobic
The polysiloxane-based defoamer of type；From aqueous organic environmental-protection or the inorganic mill base of aqueous, environmental protective.
Described dispersant is polypropylene esters dispersant；Described levelling agent is organic silicon surfactant；Described
Wetting agent is polyacrylate wetting agent.
Embodiment 5：Optimum embodiment
A kind of preparation method of aqueous terrace, comprises the following steps：
(1) by 14 parts of deionized waters, 30 parts of titanium dioxides, 0.5 part of dispersant, 0.3 part of defoamer, scattered 30-50 points at a high speed
Clock；
(2) 50 parts of water-based acrylic resins, 1 part of mill base, 0.5 part of defoamer and 0.5 part of levelling agent, 0.7 part of profit are added
Humectant, 2.5 parts of thickeners, middling speed are scattered 10-30 minutes；
(3) stop disperseing, produce this material.
Claims (1)
1. a kind of preparation method of aqueous floor paint, it is characterised in that comprise the following steps：
(1) by 10-30 parts of deionized waters, 15-40 parts of titanium dioxides, 0.4-0.8 parts of dispersants, 0.2-0.5 parts of defoamers, divide at a high speed
Dissipate 30-50 minutes；
(2) 30-60 parts of water-based acrylic resins, 1-3 parts of mill bases, 0.3-0.6 parts of defoamers are added, and 0.5-1 parts of levelling agents,
0.5-1 parts of wetting agents, 2-5 parts of thickeners, middling speed are scattered 10-30 minutes；
(3) stop disperseing, produce this material；
Described water-based acrylic resin is that hydroxyl acrylic emulsion is mixed with hydroxyl acrylic aqueous dispersion with arbitrary proportion；It is described
Titanium dioxide be rutile type titanium white；Described mill base is aqueous organic environmental-protection or the inorganic mill base of aqueous, environmental protective；Described point
Powder is polypropylene esters dispersant；Described levelling agent is organic silicon surfactant；Described wetting agent is polyacrylic acid
Esters wetting agent.