CN106009989A - Waterborne wood paint adhesive force enhancement undercoat and topcoat - Google Patents
Waterborne wood paint adhesive force enhancement undercoat and topcoat Download PDFInfo
- Publication number
- CN106009989A CN106009989A CN201610390484.4A CN201610390484A CN106009989A CN 106009989 A CN106009989 A CN 106009989A CN 201610390484 A CN201610390484 A CN 201610390484A CN 106009989 A CN106009989 A CN 106009989A
- Authority
- CN
- China
- Prior art keywords
- agent
- adhesive force
- undercoat
- topcoat
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a waterborne wood paint adhesive force enhancement undercoat and topcoat, and is characterized in that the waterborne wood paint adhesive force enhancement undercoat and topcoat comprise the following components: a film-forming auxiliary agent, a waterborne emulsion, other auxiliary agents, a pigment filler and deionized water. The film-forming auxiliary agent adopts a mixture of one or more of DPM, DPnB and DB. The other auxiliary agents adopt mixtures of one or more of a dispersing agent, a wetting agent, an anti-foaming agent, a leveling agent, a pH regulator, a thickener and an anti-settling agent. The pigment filler adopts a mixture of zero to more of heavy calcium carbonate, a talc powder and titanium dioxide. A preparation method of the waterborne wood paint adhesive force enhancement undercoat and topcoat comprises the steps of fully and uniformly dispersing the waterborne emulsion, the film-forming auxiliary agent, the other auxiliary agents, the pigment filler and deionized water, and packaging into a finished product. The waterborne wood paint adhesive force enhancement undercoat and topcoat have the advantages of good adhesive force in a traditional coating system, good water resistance, good staining resistance, excellent coating effect, environmental protection, safety, and simple and safe use, and can be widely used in furniture coating for families and factories.
Description
Technical field
The invention belongs to woodcare paint field, specifically, belong to for adhering to base material and ornamental priming paint and finish paint.
Technical background
Along with the raising of people's living standard, people are more and more higher to the environmental requirement of furniture item, and this is to Furniture Factory
Requirement, the requirement to our Paint manufacturers especially: environmental protection, safety, easy construction.
Factory uses solvent bottom paint or UV priming paint, does aqueous finish paint, and the common end, finish paint can not meet adhesive force etc. and execute
Work requirement, needs a kind of adhesive force good, the water paint of easy construction；Furniture renovation before family or factory, because in the past
The traditional solvent-borne finishing system used, common water paint cannot meet requirement, it is also desirable to a kind of adhesive force is good, construction party
Just water paint.Such finishing system is safe and environment-friendly, easy construction, reduces haze, meets the developing direction of furniture application.
Summary of the invention
It is an object of the invention to provide at the bottom of aqueous woodware paint Adhesion enhancement, finish paint, solve in traditional solvent-borne application
Adhesion problem in system, and tradition woodcare paint finishing system family and the renovation of factory.Make up " oil modify-water " now existing
The safety of real aqueous application, can meet again the cosmetic requirement of aqueous application.The present invention designs a kind of aqueous woodware paint attachment
Power strengthens the end, finish paint, it is characterised in that be made up of following constituent and percentage by weight:
It is characterized in that: coalescents uses one or more mixture of DPM, DPnB, DB.
It is characterized in that: water-based emulsion uses aqueous acrylic emulsion, aqueous acrylic modified polyaminoester emulsion, aqueous to gather
One or more mixture of urethane emulsion.
It is characterized in that: other auxiliary agent uses dispersant, wetting agent, defoamer, levelling agent, PH regulator, thickening agent, prevents
One or more mixture of heavy auxiliary agent.
It is characterized in that: color stuffing use 1500 mesh triple superphosphate, 800 mesh triple superphosphate, 1250 mesh Pulvis Talci, 3000 mesh Pulvis Talci,
Zero kind of titanium dioxide arrives multiple mixture.
It is characterized in that: deionized water uses zero kind of the self-produced deionized water of factory to one.Its mixed proportion is:
(1-5) %:(10-90) %:(0.1-10%) %:(0-70) %:(0-50) %
At the bottom of a kind of aqueous woodware paint Adhesion enhancement, the preparation method of finish paint, it is characterised in that: its step be by aqueous breast
Liquid, coalescents, other auxiliary agent, color stuffing, deionized water are fully dispersed uniformly, and packaging is to finished product.
Owing to using technique scheme, the present invention has following good effect: described aqueous woodware paint adhesive force increases
The water-based emulsion of the strong end, finish paint and preparation method thereof uses water-based emulsion, and particle diameter is thin, and adhesive force is strong, and hardness is high, and film property is good,
Pliability is fine, has load, stripper-resistance very well to powder body simultaneously.At the bottom of described aqueous woodware paint Adhesion enhancement,
Finish paint and preparation method thereof, owing to inside adding color stuffing, meets individual demand, meets practice of construction demand simultaneously.Institute
At the bottom of the aqueous woodware paint Adhesion enhancement stated, finish paint is being owing to filling out inside agent addition coalescents, dry rate and film forming efficiency
It is greatly reinforced.At the bottom of described aqueous woodware paint Adhesion enhancement, finish paint and preparation method thereof owing to inside adding other auxiliary agent,
It is readily produced manufacture, meets the actual demands such as scratch resistance, fast package, bin stability.Described aqueous woodware paint adhesive force
Strengthen the end, finish paint and preparation method thereof, on tradition finishing system, there is good adhesive force, there is good water resistance, resistance to simultaneously
Contaminative and excellent painting effect, environmental protection, safety, use are simple and safe；The furniture that can be widely used in family and factory is coated with
Dress.
Specific construction mode:
Embodiment 1
Preparing this based white primer, by all components by dispersion machine, after being uniformly dispersed, packaging gets product.The present embodiment paint can
It is used as Adhesion enhancement based white primer to use.
Embodiment 2:
Preparing this white finish paint, by all components by dispersion machine, after being uniformly dispersed, packaging gets product.The present embodiment paint can
It is used as Adhesion enhancement white finish paint to use.
Embodiment 3:
Preparing this clear priming paint, by all components by dispersion machine, after being uniformly dispersed, packaging gets product.
The present embodiment paint can be used as the clear priming paint of Adhesion enhancement and uses.
Embodiment 4:
Preparing this clear finish, by all components by dispersion machine, after being uniformly dispersed, packaging gets product.The present embodiment paint can
It is used as Adhesion enhancement clear finish to use.
Claims (6)
1. at the bottom of an aqueous woodware paint Adhesion enhancement, finish paint, it is characterised in that by following constituent and percentage by weight group
Become:
Coalescents 1-5%,
Water-based emulsion 10-90%,
Other auxiliary agent 0.1-10%
Color stuffing 0-70%
Deionized water 0-50%.
2. at the bottom of a kind of aqueous woodware paint Adhesion enhancement as described in claim 1, finish paint, it is characterised in that: coalescents is adopted
With one or more mixture of DPM, DPnB, DB.
3. at the bottom of a kind of aqueous woodware paint Adhesion enhancement as described in claim 1, finish paint, it is characterised in that: water-based emulsion is adopted
With aqueous acrylic emulsion, aqueous acrylic modified polyaminoester emulsion, one or more mixture of aqueous polyurethane emulsion.
4. at the bottom of a kind of aqueous woodware paint Adhesion enhancement as described in claim 1, finish paint, it is characterised in that: other auxiliary agent is adopted
With dispersant, wetting agent, defoamer, levelling agent, PH regulator, thickening agent, one or more mixture of anti-settling auxiliary agent.
5. at the bottom of a kind of aqueous woodware paint Adhesion enhancement as described in claim 1, finish paint, it is characterised in that: color stuffing uses
1500 mesh triple superphosphate, 800 mesh triple superphosphate, 1250 mesh Pulvis Talci, 3000 mesh Pulvis Talci, zero kind of titanium dioxide to multiple mixture.
6. at the bottom of a kind of aqueous woodware paint Adhesion enhancement as described in claim 1, finish paint, it is characterised in that: deionization hydromining
With zero kind of the self-produced deionized water of factory to one.