CN108355940A - The closed coating process of woodenware aqueous priming paint, preparation method and woodenware - Google Patents
The closed coating process of woodenware aqueous priming paint, preparation method and woodenware Download PDFInfo
- Publication number
- CN108355940A CN108355940A CN201810160914.2A CN201810160914A CN108355940A CN 108355940 A CN108355940 A CN 108355940A CN 201810160914 A CN201810160914 A CN 201810160914A CN 108355940 A CN108355940 A CN 108355940A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- woodenware
- priming paint
- coating
- preset time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the closed coating process of a kind of woodenware aqueous priming paint, preparation method and woodenware.The woodenware aqueous priming paint includes following component：Polyurethane acroleic acid lotion 58~65%, aqueous dispersion 7~10%, aqueous levelling agent 1~3%, aqueous defoamer 2~4%, remaining be water；It is wherein in terms of 100% by the priming paint gross weight, the percentage is weight percentage.Woodenware aqueous priming paint provided by the invention does not include aqueous necessary coalescents, it is not necessarily to limit blender rotating speed in process, it can be operated by the production technology of oil paint, crude oil coating material production producer can be produced without rearranging production line according to the formula, improvement cost is small, and production environment can substantially improve.
Description
Technical field
The present invention relates to woodwork coatings, and in particular to a kind of woodenware aqueous priming paint, woodenware aqueous priming paint preparation method and
The closed coating process of woodenware.
Background technology
In Coating Market now, based on oiliness polyurethane PU coating, since polyurethane PU coating has, hardness is high, gloss
It is good, the advantages that service life is long and non-discolouring and be widely used.But oil paint produces big during production and application
The exhaust gas of amount, waste water, give up the substance for having pollution to environment such as solid.Simultaneously because oiliness, so it is inflammable and explosive, to the people and public affairs
Property safety generates threat altogether.Country also pays much attention to problems, so country is guided by various laws and regulations in recent years
Coating is gradually turned to aqueous by oiliness.Because there is pollution in oil paint and serious danger, aqueous future are bound to
Instead of oiliness.
Because of the distinctive loose speciality of timber, as in pine and the medium density fibre board (MDF) moisture absorption, wood fibre are easy expansion, and
Tannic acid present in solid wood and the readily permeable surface to paint film of grease make paint film turn to be yellow or spit oil.All kinds of markets at this stage
On water-borne wood coating be painted on woodenware, some are oil primers, aqueous finish paint, and such is false aqueous；And some priming paint
All it is aqueous with finishing coat, sprays on woodenware after a period of use, whole bulging tendons and discoloration, the not bulging tendons of oil paint can not be replaced
With the characteristic of color inhibition.
Therefore, it is really necessary to provide the improved wood paint aqueous priming paint of one kind to solve the above technical problems.
Invention content
In order to overcome above-mentioned technical problem, the present invention to provide the wood paint aqueous priming paint of a kind of color inhibition and anti-bulging tendons.
Technical scheme is as follows：
A kind of woodenware aqueous priming paint, the priming paint include following component：Polyurethane acroleic acid lotion 58~65%, aqueous point
Powder 7~10%, aqueous levelling agent 1~3%, aqueous defoamer 2~4%, remaining be water；Wherein it is with the priming paint gross weight
100% meter, the percentage are weight percentage.
Preferably, the priming paint includes following component：Polyurethane acroleic acid lotion 60%, aqueous dispersion 8%, aqueous flow
Flat agent 2%, aqueous defoamer 2% and water 28%；It is wherein in terms of 100% by the priming paint gross weight, the percentage is weight hundred
Divide ratio.
Preferably, the aqueous dispersion is TEGO Dispers 655.
Preferably, the aqueous levelling agent is EFKA3580.
Preferably, the aqueous defoamer is TEG0902W.
Present invention simultaneously provides a kind of preparation method of woodenware aqueous priming paint described above, the preparation method includes such as
Lower step：
Polyurethane acroleic acid lotion is put into blender and stirs the first preset time, aqueous dispersion stirring is then added
Second preset time, the sum of first preset time and second preset time are 10min；
Then aqueous levelling agent is added and stirs 5min；
Add aqueous defoamer stirring 5min；
It is eventually adding tap water stirring 5min；
Woodenware aqueous priming paint finished product is packaged to be after standing.
The present invention also provides a kind of closed coating process of woodenware, the coating process includes the following steps：
Step 1: the surface for the woodenware for waiting for application is carried out sanding processing, woodenware external coating then after treatment is wooden
Device aqueous priming paint forms first coating, to prevent the tannic acid in woodenware from oozing out；The woodenware aqueous priming paint is in accordance with the following methods
It prepares：
(1) each component is weighed according to the dosage in formula, wherein the woodenware aqueous priming paint includes following component：Poly- ammonia
Ester acrylic emulsion 58~65%, aqueous wetting dispersing agent 7~10%, aqueous levelling agent 1~3%, aqueous defoamer 2~4%,
Remaining is water；It is wherein in terms of 100% by the priming paint gross weight, the percentage is weight percentage；
(2) polyurethane acroleic acid lotion is put into blender and stirs the first preset time, aqueous dispersion is then added
The second preset time is stirred, the sum of first preset time and second preset time are 10min；
(3) and then addition aqueous levelling agent stirs 5min；
(4) aqueous defoamer stirring 5min is added；
(5) it is eventually adding tap water stirring 5min；
(6) woodenware aqueous priming paint finished product is obtained after standing；
Step 2: in the aqueous wood grain treasured of the first coating external coating to form second coating, the second coating and
The first coating combines, and keeps the back cover of the woodenware more secured；
Step 3: in the aqueous dressing agent of the second coating external coating and varnish to form third coating, so that described
It woodenware high temperature resistance and prevents from permeating.
Preferably, in the step 1, the woodenware aqueous priming paint includes following component：Polyurethane acroleic acid lotion
60%, aqueous wetting dispersing agent 8%, aqueous levelling agent 2%, aqueous defoamer 2% and water 28%；Wherein with the priming paint gross weight
For 100% meter, the percentage is weight percentage.
Compared to the prior art, the closed application of woodenware aqueous priming paint provided by the invention, preparation method and woodenware
Method has the advantages that：
One, woodenware aqueous priming paint provided by the invention does not include aqueous necessary coalescents, is not necessarily in process
Blender rotating speed is limited, can be operated by the production technology of oil paint, crude oil coating material production producer does not have to
Rearranging production line can be produced according to the formula, and improvement cost is small, and production environment can substantially improve.
Two, the preparation method of woodenware aqueous priming paint is easy to operate, and operating condition is not harsh, and production efficiency is high, and priming paint at
Quality is good.
Three, application is carried out according to the closed coating process of woodenware provided by the invention, in sanding treated woodenware table
Application woodenware aqueous priming paint in face forms first coating, can prevent the tannic acid in woodenware from oozing out；Then on first coating surface
The aqueous wood grain treasured of application forms second coating, and aqueous wood grain is precious, and on the one hand material to be made to be more clear transparent, and with first coating knot
It is more secured that conjunction can make first coating close bottom；In the third coating of second coating external coating for repairing color, and high temperature resistance, energy
It prevents from permeating, makes woodenware color inhibition not bulging tendons, reached the non-discolouring technique effect of woodwork coating.
Specific implementation mode
Technical scheme of the present invention is clearly and completely described below in conjunction in the embodiment of the present invention, it is clear that institute
The embodiment of description is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention,
All other embodiment obtained by those of ordinary skill in the art without making creative efforts, belongs to this hair
The range of bright protection.
The present invention provides a kind of woodenware aqueous priming paint, and the priming paint includes following component：Polyurethane acroleic acid lotion 58~
65%, aqueous dispersion 7~10%, aqueous levelling agent 1~3%, aqueous defoamer 2~4%, remaining be water；Wherein with described
Priming paint gross weight is 100% meter, and the percentage is weight percentage.
Preferably, the priming paint includes following component：Polyurethane acroleic acid lotion 60%, aqueous dispersion 8%, aqueous flow
Flat agent 2%, aqueous defoamer 2% and water 28%；It is wherein in terms of 100% by the priming paint gross weight, the percentage is weight hundred
Divide ratio.
Preferably, the aqueous dispersion is TEGO Dispers 655.
Preferably, the aqueous levelling agent is EFKA3580.
Preferably, the aqueous defoamer is TEG0902W.
Embodiment one
It weighs and is stirred 4 minutes in 580 grams of watersoluble polyurethane acrylic acid lotions addition blenders, be then added 70 grams aqueous point
Powder TEGO Dispers 655, are stirred for obtaining the first mixed solution in 6 minutes, and 10 grams of addition is aqueous in the first mixed solution
Levelling agent EFKA3580, stirring obtains the second mixed solution for 5 minutes, then 40 grams of antifoaming agent are added into the second mixed solution
TEG0902W, and be stirred for 5 minutes, it finally adds 300 grams of water and stirs 5 minutes, woodenware aqueous priming paint A is made.
Embodiment two
It weighs and is stirred 4 minutes in 600 grams of watersoluble polyurethane acrylic acid lotions addition blenders, be then added 80 grams aqueous point
Powder TEGO Dispers 655, are stirred for obtaining the first mixed solution in 6 minutes, and 20 grams of addition is aqueous in the first mixed solution
Levelling agent EFKA3580, stirring obtains the second mixed solution for 5 minutes, then 20 grams of antifoaming agent are added into the second mixed solution
TEG0902W, and be stirred for 5 minutes, it finally adds 280 grams of water and stirs 5 minutes, woodenware aqueous priming paint B is made.
Embodiment three
It weighs and is stirred 4 minutes in 650 grams of watersoluble polyurethane acrylic acid lotions addition blenders, be then added 70 grams aqueous point
Powder TEGO Dispers 655, are stirred for obtaining the first mixed solution in 6 minutes, and 30 grams of addition is aqueous in the first mixed solution
Levelling agent EFKA3580, stirring obtains the second mixed solution for 5 minutes, then 30 grams of antifoaming agent are added into the second mixed solution
TEG0902W, and be stirred for 5 minutes, it finally adds 220 grams of water and stirs 5 minutes, woodenware aqueous priming paint C is made.
Example IV
It will wait for that the surface of the woodenware of application carries out sanding processing, then woodenware external coating embodiment one after treatment is made
The either aqueous bottoms of woodenware made from woodenware aqueous priming paint B made from embodiment two or embodiment two woodenware aqueous priming paint A
It paints C and forms first coating, to prevent the tannic acid in woodenware from oozing out；Then precious in the aqueous wood grain of the first coating external coating
To form second coating, the second coating and the first coating combine, and keep the back cover of the woodenware more secured；Finally in institute
The aqueous dressing agent of second coating external coating and varnish are stated to form third coating, so as to the woodenware high temperature resistance and prevent from oozing
Thoroughly.
The closed coating process of woodenware aqueous priming paint provided by the invention, preparation method and woodenware has beneficial below
Effect：
One, woodenware aqueous priming paint provided by the invention does not include aqueous necessary coalescents, is not necessarily in process
Blender rotating speed is limited, can be operated by the production technology of oil paint, crude oil coating material production producer does not have to
Rearranging production line can be produced according to the formula, and improvement cost is small, and production environment can substantially improve.
Two, the preparation method of woodenware aqueous priming paint is easy to operate, and operating condition is not harsh, and production efficiency is high, and priming paint at
Quality is good.
Three, application is carried out according to the closed coating process of woodenware provided by the invention, in sanding treated woodenware table
Application woodenware aqueous priming paint in face forms first coating, can prevent the tannic acid in woodenware from oozing out；Then on first coating surface
The aqueous wood grain treasured of application forms second coating, and aqueous wood grain is precious, and on the one hand material to be made to be more clear transparent, and with first coating knot
It is more secured that conjunction can make first coating close bottom；In the third coating of second coating external coating for repairing color, and high temperature resistance, energy
It prevents from permeating, makes woodenware color inhibition not bulging tendons, reached the non-discolouring technique effect of woodwork coating.
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (8)
1. a kind of woodenware aqueous priming paint, which is characterized in that the priming paint includes following component：Polyurethane acroleic acid lotion 58~
65%, aqueous dispersion 7~10%, aqueous levelling agent 1~3%, aqueous defoamer 2~4%, remaining be water；Wherein with described
Priming paint gross weight is 100% meter, and the percentage is weight percentage.
2. a kind of woodenware aqueous priming paint according to claim 1, which is characterized in that the priming paint includes following component：It is poly-
Urethane acrylic emulsion 60%, aqueous dispersion 8%, aqueous levelling agent 2%, aqueous defoamer 2% and water 28%；Wherein with institute
It is 100% meter to state priming paint gross weight, and the percentage is weight percentage.
3. a kind of woodenware aqueous priming paint according to claim 1 or 2, which is characterized in that the aqueous dispersion is TEGO
Dispers 655。
4. a kind of woodenware aqueous priming paint according to claim 1 or 2, the aqueous levelling agent is EFKA3580.
5. a kind of woodenware aqueous priming paint according to claim 1 or 2, the aqueous defoamer is TEG0902W.
6. a kind of preparation method of woodenware aqueous priming paint according to any one of claims 1 to 5, which is characterized in that including
Following steps：
Polyurethane acroleic acid lotion is put into blender and stirs the first preset time, aqueous dispersion stirring second is then added
Preset time, the sum of first preset time and second preset time are 10min；
Then aqueous levelling agent is added and stirs 5min；
Add aqueous defoamer stirring 5min；
It is eventually adding water stirring 5min；
Woodenware aqueous priming paint finished product is packaged to be after standing.
7. the closed coating process of woodenware, which is characterized in that include the following steps：
Step 1: the surface of the woodenware for waiting for application is carried out sanding processing, then woodenware external coating woodenware water after treatment
Property priming paint formed first coating, to prevent the tannic acid in woodenware from oozing out；The woodenware aqueous priming paint is prepared in accordance with the following methods：
(1) each component is weighed according to the dosage in formula, wherein the woodenware aqueous priming paint includes following component：Polyurethane third
Olefin(e) acid lotion 58~65%, aqueous dispersion 7~10%, aqueous levelling agent 1~3%, aqueous defoamer 2~4%, remaining be
Water；It is wherein in terms of 100% by the priming paint gross weight, the percentage is weight percentage；
(2) watersoluble polyurethane acrylic acid lotion is put into blender and stirs the first preset time, aqueous dispersion is then added
The second preset time is stirred, the sum of first preset time and second preset time are 10min；
(3) and then addition aqueous levelling agent stirs 5min；
(4) aqueous defoamer stirring 5min is added；
(5) it is eventually adding tap water stirring 5min；
(6) woodenware aqueous priming paint finished product is obtained after standing；
Step 2: in the aqueous wood grain treasured of the first coating external coating to form second coating, the second coating and described
First coating combines, and keeps the back cover of the woodenware more secured；
Step 3: in the aqueous dressing agent of the second coating external coating and varnish to form third coating, so that the woodenware
It high temperature resistance and prevents from permeating.
8. the closed coating process of woodenware according to claim 7, which is characterized in that in the step 1, the woodenware
Aqueous priming paint includes following component：Polyurethane acroleic acid lotion 60%, aqueous wetting dispersing agent 8%, aqueous levelling agent 2%, water
Property antifoaming agent 2% and water 28%；It is wherein in terms of 100% by the priming paint gross weight, the percentage is weight percentage.