CN106085191B - A kind of construction method of wood product surface paint - Google Patents
A kind of construction method of wood product surface paint Download PDFInfo
- Publication number
- CN106085191B CN106085191B CN201610395318.3A CN201610395318A CN106085191B CN 106085191 B CN106085191 B CN 106085191B CN 201610395318 A CN201610395318 A CN 201610395318A CN 106085191 B CN106085191 B CN 106085191B
- Authority
- CN
- China
- Prior art keywords
- wood
- parts
- paint
- drying
- middle level
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of construction methods of wood product surface paint, include the following steps：(1) sanding surface processing, (2) prime treatment and UV dryings, (3) colouring and drying, (4) sanding, dedusting, the processing of (5) middle level and (6) finishing coat are handled.In the wherein described step (2) UV wood crude oil paint by weight, including following components：Six 10 15 parts of official's polyurethane acrylic resins, 20 25 parts of two official's polyurethane acrylic resin, double officials are modified 30 35 parts of UV monomers, 35 parts of photosensitizer, 0.1 0.2 parts of levelling agent, 0.3 0.5 parts of antifoaming agent, 0.3 0.5 parts of wetting agent, 15 20 parts of nano silicon dioxide dispersion, 10 15 parts of gas phase nano silica dumb light powder.Embodiment through the invention, also obtaining one kind in wood surface has compared with thin protective layer, and waterproof antiwear is had excellent performance, while saving the texture and texture of timber essence again.
Description
Technical field
The present invention relates to painted surface treatment process fields, and in particular to a kind of construction method of wood product surface paint,
It is mainly used for the construction processing of the surface paint of timber floor, can be also used for the construction of the wood product surfaces such as furniture, timber paint
Processing.
Background technology
With national consumption level and to the raising of environmental requirement, people have when selecting woodwork it is more selection and
Higher requirement, such as require woodwork closer to the essential color and texture texture of timber.
The weatherability of traditional wood products, solid wooden floor board or solid wooden compound floor is poor, humidity and temperature change compared with
It is long-term in use, easy to produce deformation and cracking in big environment, poor dimensional stability.Especially timber floor, humidity compared with
In use, easy ting produce discoloration, rotten, stability is poor in high environment.Thus, one layer can be covered in traditional timber floor enough
The painting layer of thickness is also easy to produce discoloration, deformation, rotten when preventing timber floor from being used in the higher environment of humidity ratio to reach
Generation, improve the dimensional stability of timber floor.
Although current treatment process ensure that the waterproof corrosion resisting property of timber floor, still, also covered in wood floor surface
One layer of thicker protective film, is unable to the textural aesthetic and sense of touch of timber essence.And consumer is more desirable to when choosing timber floor
Selection wood surface has compared with thin protective layer, can embody the texture and sense of touch of timber essence.For this problem, there is one on the market
Product after a little improvement, such as protective layer is formed using wood wax oil dry vegetable oil, but since it is plant component, hard
The performance requirement of traditional paint is not achieved on degree, wear-resisting and high temperature resistant, resistance to acid and alkali.
Therefore, more and more wooden product enterprises are highly desirable can have a kind of product that can solve the above problems.
Invention content
In view of the above-mentioned problems, the present invention provides a kind of construction method of wood product surface paint, obtaining one kind has
Compared with thin protective layer, waterproof antiwear is had excellent performance, while saving the wooden floor of the texture and texture of timber essence again.
A kind of UV wood crude oil paint, includes the component of following parts by weight：
The present invention is added to nano silicon dioxide dispersion, and the anti-ultraviolet aging experimental performance of the micro- coating paint of UV can be with
600h or more is increased to by original 250h, scrub resistance improves 10 times or more, and the drying time of coating is greatly lowered, anti-pollution
Performance greatly improves, and has excellent self-cleaning property and adhesive force.If not adding nano silicon dioxide dispersion, coating
Resistant and ultraviolet-resistant performance will reduce.
The present invention is added to gas phase nano silica dumb light powder, can substantially reduce the glossiness of coating, makes coat side table
Face glossiness is at 5 degree or less.Surface gloss is not achieved if using normal dull powder in 5 degree of effects below.
Preferably, the photosensitizer is cracking type photosensitizer.
Preferably, the levelling agent is fluorine richness carbonic ether acrylate.
Preferably, the antifoaming agent is organosilicon antifoaming agent.
Preferably, the wetting agent is polyether-modified poly- silica siloxane copolymers class wetting agent.
A kind of preparation method of UV wood crude oil paint, includes the following steps：
1) six official's polyurethane acrylic resins, two official polyurethane acroleic acid trees are put into successively by weight in dispersion cylinder
Fat, double officials are modified UV monomers, photosensitizer, levelling agent, antifoaming agent, wetting agent, and stirring makes to be uniformly mixed, and obtains the group of clear
Divide A；
2) component A is stirred, nano silicon dioxide dispersion is added into, is uniformly mixed, obtains component B；
3) component B is stirred, gas phase nano silica dumb light powder is added into, is uniformly mixed, the UV wood crude oil is obtained
Paint.
Preferably, in step 1), mixing speed is 2000RPM, and mixing time is 20 minutes.
Preferably, in step 2), mixing speed is 400RPM, and mixing time is 10 minutes.
Preferably, in step 3), mixing speed is 800RPM, and mixing time is 20 minutes.
The UV wood crude oil paints of the present invention may penetrate into lumber fibre, after ultraviolet light, be sent out with lumber fibre rapidly
Raw cross-linking reaction reinforces lumber fibre, and forms one layer of very thin protective layer in wood surface, has wear-resisting, the effect of waterproof,
Remain the texture texture of timber again simultaneously；Nano silicon dioxide dispersion is added, the anti-ultraviolet aging of the coating is improved
Performance and pollution resistance, are greatly lowered drying time；Gas phase nano silica dumb light powder is added, the gloss of coating is reduced
Degree；For the paint without formaldehyde, benzene and heavy metal etc., safety and environmental protection, VOC content are low.
In order to realize that the technical purpose of the present invention, the present invention adopt the following technical scheme that.
A kind of construction method of wood product surface paint, includes the following steps：
(1) sanding surface is handled, and ensures plain plate surface Glabrous thorn；
(2) prime treatment is dried with UV：It will be dried with UV drying machines after the former paint of the plain plate UV handled well wood；
(3) colouring and drying：Plain plate after drying is coated with Waterborne wood original paint and is painted, Waterborne wood original paint is made to enter fiber
In pore, then plain plate is placed in 10-20 meters long of infrared levelling channel dried；
(4) sanding, dedusting：After plain plate sanding after will be dry in step (3) is pierced to Waterborne wood original paint surface Glabrous
It is dusted processing；
(5) middle level processing one：Step (2) is repeated, and is dusted after gained element plate sanding to surface Glabrous is pierced
Processing；
(6) middle level processing two：After the plain plate of gained in step (5) the former paint of UV wood, dried with UV drying machines, sand
Light carries out dust removal process after being pierced to surface Glabrous；
(7) finishing coat is handled：Step (2) is repeated, finished product is obtained.
Preferably, the UV wood crude oil paint by weight, including following components：Six official's polyurethane acrylic resins：10-
15 parts, two official's polyurethane acrylic resins：20-25 parts, double officials modification UV monomers：30-35 parts, photosensitizer：3-5 parts, levelling agent：
0.1-0.2 parts, antifoaming agent：0.3-0.5 parts, wetting agent：0.3-0.5 parts, nano silicon dioxide dispersion：15-20 parts, gas phase receives
Rice silica dumb light powder：10-15 parts.
Preferably, UV wood crude oil paint coating weights are 5-8g/m in the step (2)2, UV drying conditions are 100-120mJ/
cm2。
Preferably, Waterborne wood original paint coating weight is 10-15g/m in the step (3)2, drying condition is to be done at 55-60 DEG C
It is 1-2 minutes dry.
Preferably, UV wood crude oil paint coating weights are 3-5g/m in the step (6)2, UV drying conditions are 100-120mJ/
cm2。
The beneficial effects of the invention are as follows：The present invention provides a kind of construction methods of wood product surface paint, and pass through this
The UV wood crude oil paints provided in invention are used in combination, and further embody advantages of the present invention, compared with prior art, have
Following advantages：
1, guarantee this texture of timber and sense of touch and timber paint film that existing woodwork or timber floor enterprise frustrate are solved
The problem of cannot having both of waterproof antiwear performance；
2, timber floor stability of the invention is good, water resistance is excellent, and wear-resisting property is good；
3, surface paint used in the present invention is without the harmful substances such as formaldehyde, benzene, heavy metal, Environmental Safety；
4, simple production process, equipment requirement is low, be suitble to large-scale promotion use, can be widely used in timber floor, timber,
Paint treatment process in the surfaces such as furniture, woodwork workpiece.
Specific implementation mode
In order to better understand the present invention, invention is described in detail with reference to specific embodiment, such as nothing is especially said
Bright, the group of UV wood crude oil paint is divided into following embodiment, by weight, including following components：Six official polyurethane acroleic acid trees
Fat：10-15 parts, two official's polyurethane acrylic resins：20-25 parts, double officials modification UV monomers：30-35 parts, photosensitizer：3-5 parts,
Levelling agent：0.1-0.2 parts, antifoaming agent：0.3-0.5 parts, wetting agent：0.3-0.5 parts, nano silicon dioxide dispersion：15-20
Part, gas phase nano silica dumb light powder：10-15 parts.
The 6145-100 of Changxing company can be selected in six official's polyurethane acrylic resins of the present invention；
The EB-264 of Qing Te companies can be selected in two official's polyurethane acrylic resins of the present invention；
The EM222 in Changxing can be selected in double official UV monomers of the present invention；
The cracking type photosensitizer 1173 of Hua Tai high molecular materials company production can be used in the photosensitizer of the present invention；
The BYK-3510 of Bi Ke companies can be selected in the levelling agent of the present invention；
The BYK-055 of Bi Ke companies can be selected in the antifoaming agent of the present invention；
The BYK-306 of Bi Ke companies can be selected in the wetting agent agent of the present invention；
The VK-S01A of Jing Rui companies can be selected in the nano silicon dioxide dispersion of the present invention；
The R972 of goldschmidt chemical corporation can be selected in the gas phase nano silica dumb light powder of the present invention.
Embodiment 1：
A kind of UV wood crude oil paint, includes the component of following parts by weight：
UV wood crude oil paint preparation methods：(1) 15 part of six official's polyurethane acroleic acid is put into successively by weight in dispersion cylinder
Resin, 25 part of two official's polyurethane acrylic resin, 30 parts of double officials be modified UV monomers, 4 parts of photosensitizers, 0.2 part of levelling agent, 0.3 part
Antifoaming agent, 0.5 part of wetting agent stir 20 minutes in the case where blender rotating speed is 2000RPM, make to be uniformly mixed, obtain clear
Component A；(2) in the case where blender rotating speed is 400RPM, component A is stirred, while being added into 15 parts of nano silicon dioxide dispersions,
Stirring 10 minutes is uniformly mixed, obtains component B；(3) in the case where blender rotating speed is transferred to 800PRM, component B is stirred, is added simultaneously
Enter 10 parts of gas phase nano silica dumb light powders, stir 20 minutes, is uniformly mixed to get to the UV wood crude oil paints of the present invention.
A kind of construction method of wood product surface paint, includes the following steps：
(1) sanding surface is handled, and ensures plain plate surface Glabrous thorn；
(2) prime treatment is dried with UV：By the former paint of the plain plate UV handled well wood, guarantee coating weight is 8g/m2,
Then UV drying machines are used to dry, drying energy 120mJ/cm2；
(3) colouring and drying：Plain plate after drying is coated with Waterborne wood original paint and is painted, guarantee coating weight is 15g/m2,
So that Waterborne wood original paint is entered in fiber pore, then plain plate is placed in 10-20 meters long of levelling channel dried, drying condition is
It is 1-2 minutes dry at 55-60 DEG C；
(4) sanding, dedusting：After plain plate sanding after will be dry in step (3) is pierced to Waterborne wood original paint surface Glabrous
It is dusted processing；
(5) middle level processing one：Step (2) is repeated, and is dusted after gained element plate sanding to surface Glabrous is pierced
Processing；
(6) middle level processing two：By the plain plate of gained in step (5) the former paint of UV wood, guarantee coating weight is 5g/m2,
Then UV drying machines are used to dry, drying energy 120mJ/cm2；Sanding carries out dust removal process after being pierced to surface Glabrous again；
(7) finishing coat is handled：Step (2) is repeated, finished product is obtained.
Embodiment 2：
A kind of UV wood crude oil paint, includes the component of following parts by weight：
Weight more than raw material use prepares UV wood crude oil paints using 1 method of embodiment.
A kind of construction method of wood product surface paint, includes the following steps：
(1) sanding surface is handled, and ensures plain plate surface Glabrous thorn；
(2) prime treatment is dried with UV：By the former paint of the plain plate UV handled well wood, guarantee coating weight is 6g/m2,
Then UV drying machines are used to dry, drying energy 110mJ/cm2；
(3) colouring and drying：Plain plate after drying is coated with Waterborne wood original paint and is painted, guarantee coating weight is 12g/m2,
So that Waterborne wood original paint is entered in fiber pore, then plain plate is placed in 10-20 meters long of infrared levelling channel dried, drying condition
It is 1-2 minutes dry at 55-60 DEG C；
(4) sanding, dedusting：After plain plate sanding after will be dry in step (3) is pierced to Waterborne wood original paint surface Glabrous
It is dusted processing；
(5) middle level processing one：Step (2) is repeated, and is dusted after gained element plate sanding to surface Glabrous is pierced
Processing；
(6) middle level processing two：By the plain plate of gained in step (5) the former paint of UV wood, guarantee coating weight is 4g/m2,
Then UV drying machines are used to dry, drying energy 110mJ/cm2；Sanding carries out dust removal process after being pierced to surface Glabrous again；
(7) finishing coat is handled：Step (2) is repeated, finished product is obtained.
Embodiment 3：
A kind of UV wood crude oil paint, includes the component of following parts by weight：
Weight more than raw material use prepares UV wood crude oil paints using the method for embodiment 1.
A kind of construction method of wood product surface paint, includes the following steps：
(1) sanding surface is handled, and ensures plain plate surface Glabrous thorn；
(2) prime treatment is dried with UV：By the former paint of the plain plate UV handled well wood, guarantee coating weight is 5g/m2,
Then UV drying machines are used to dry, drying energy 100mJ/cm2；
(3) colouring and drying：Plain plate after drying is coated with Waterborne wood original paint and is painted, guarantee coating weight is 10g/m2,
So that Waterborne wood original paint is entered in fiber pore, then plain plate is placed in 10-20 meters long of infrared levelling channel dried, drying condition
It is 1-2 minutes dry at 55-60 DEG C；
(4) sanding, dedusting：After plain plate sanding after will be dry in step (3) is pierced to Waterborne wood original paint surface Glabrous
It is dusted processing；
(5) middle level processing one：Step (2) is repeated, and is dusted after gained element plate sanding to surface Glabrous is pierced
Processing；
(6) middle level processing two：By the plain plate of gained in step (5) the former paint of UV wood, guarantee coating weight is 3g/m2,
Then UV drying machines are used to dry, drying energy 100mJ/cm2；Sanding carries out dust removal process after being pierced to surface Glabrous again；
(7) finishing coat is handled：Step (2) is repeated, finished product is obtained.
Embodiment 4
A kind of UV wood crude oil paint, includes the component of following parts by weight：
Weight more than raw material use prepares UV wood crude oil paints, using embodiment 1 using the method for embodiment 1
Method by the UV wood crude oil paints of preparation be coated in wood product surface on.
Comparative example 1
A kind of UV wood crude oil paint, includes the component of following parts by weight：
The UV wood crude oil paint preparation methods：(1) 25 part of six official's polyurethane propylene is put into successively by weight in dispersion cylinder
Acid resin, 32 part of two official's polyurethane acrylic resin, 37 parts of double officials are modified UV monomers, 5 parts of photosensitizers, 0.2 part of levelling agent, 0.4
Part antifoaming agent, 0.4 part of wetting agent stir 20 minutes in the case where blender rotating speed is 2000RPM, make to be uniformly mixed to get to the UV
The wooden crude oil paint.
The UV wood crude oil paints of preparation are coated on wood product surface using the method for embodiment 1.
Paint film property after the former paint application of UV wood prepared by embodiment 1-4 and comparative example 1 is measured, gained knot
Fruit is as shown in table 1.
1 performance detection table of 1 embodiment 1-4 of table and comparative example
Can be seen that the UV wood crude oil paints that prepare of the present invention from upper table data and be coated on wood product surface, gained it is wooden
Product meet indices, and use the UV wood without containing nano silicon dioxide dispersion and gas phase nano silicon dioxide dumb light powder
Crude oil paint is coated on wood product surface, and the woodwork rub resistance and stain resistance of gained substantially reduce, and do not meet indices
Regulation.By the coating UV wood crude oil paint on woodwork, it is made to penetrate into lumber fibre, after ultraviolet light, rapidly with
Lumber fibre crosslinks reaction, reinforces lumber fibre.On the other hand it is also obtained in wood surface a kind of with relatively thin protection
Layer, waterproof antiwear is had excellent performance, while saving the texture and texture of timber essence again.
The basic principles, main features and advantages of the invention have been shown and described above.The technical staff of the industry should
Understand, the invention is not limited in any way above-described embodiment, all to be obtained by the way of equivalent substitution or equivalent transformation
Technical solution is all fallen in protection scope of the present invention.
Claims (4)
1. a kind of construction method of wood product surface paint, which is characterized in that include the following steps：
(1) it is surface-treated, ensures plain plate surface Glabrous thorn；
(2) prime treatment is dried with UV：It will be dried with UV drying machines after the former paint of the plain plate UV handled well wood；
(3) colouring and drying：Plain plate after drying Waterborne wood original paint is coated with dry after painting；
(4) sanding, dedusting：Plain plate sanding after will be dry in step (3) carries out after being pierced to Waterborne wood original paint surface Glabrous
Dust removal process；
(5) middle level is handled：It is coated processing with UV wood crude oil paints；
(6) finishing coat is handled：It will be dried with UV drying machines after the former paint of the plain plate UV handled well wood, obtain finished product；
The middle level processing includes middle level processing one and middle level processing two, wherein middle level handles one and is：The plain plate handled well is used
It is dried with UV drying machines after the former paint of UV wood, and place is dusted after gained element plate sanding to surface Glabrous is pierced
Reason；Middle level handles two：It is dry with UV drying machines after the plain plate of gained after middle level processing one is coated with again with UV wood crude oil paints
Dry, sanding to surface Glabrous carries out dust removal process after piercing；
The UV wood crude oil paint by weight, including following components：Six official's polyurethane acrylic resins：10-15 parts, two officials it is poly-
Urethane acrylate resin：20-25 parts, double officials modification UV monomers：30-35 parts, photosensitizer：3-5 parts, levelling agent：0.1-0.2 parts,
Antifoaming agent：0.3-0.5 parts, wetting agent：0.3-0.5 parts, nano silicon dioxide dispersion：15-20 parts, gas phase nano silica
Dumb light powder：10-15 parts.
2. a kind of construction method of wood product surface paint according to claim 1, it is characterised in that：The middle level processing
UV wood crude oil paint coating weight is 3-5g/m in two2, UV drying conditions are 100-120mJ/cm2。
3. a kind of construction method of wood product surface paint according to claim 1, it is characterised in that：The step (2)
Middle UV wood crude oil paint coating weight is 5-8g/m2, UV drying conditions are 100-120mJ/cm2。
4. a kind of construction method of wood product surface paint according to claim 1, it is characterised in that：The step (3)
Middle Waterborne wood original paint coating weight is 10-15g/m2, drying condition is 1-2 minutes dry at 55-60 DEG C.