CN103305091A - Epoxy floor coating - Google Patents

Epoxy floor coating Download PDF

Info

Publication number
CN103305091A
CN103305091A CN2013101955706A CN201310195570A CN103305091A CN 103305091 A CN103305091 A CN 103305091A CN 2013101955706 A CN2013101955706 A CN 2013101955706A CN 201310195570 A CN201310195570 A CN 201310195570A CN 103305091 A CN103305091 A CN 103305091A
Authority
CN
China
Prior art keywords
parts
epoxy
host
agent
floor coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101955706A
Other languages
Chinese (zh)
Inventor
陆海龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HANGZHOU BAOLI MATERIAL REGENERATION UTILIZATION Co Ltd
Original Assignee
HANGZHOU BAOLI MATERIAL REGENERATION UTILIZATION Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANGZHOU BAOLI MATERIAL REGENERATION UTILIZATION Co Ltd filed Critical HANGZHOU BAOLI MATERIAL REGENERATION UTILIZATION Co Ltd
Priority to CN2013101955706A priority Critical patent/CN103305091A/en
Publication of CN103305091A publication Critical patent/CN103305091A/en
Pending legal-status Critical Current

Abstract

The invention discloses an epoxy floor coating, which is characterized by comprising a host and a curing agent, wherein the mixing ratio of the host to the curing agent is 2: 1, and wherein the host comprises the following components in parts by weight: 22-50 parts of epoxy resin, 10-30 parts of filler, 1-8 parts of thickener, 4-7 parts of auxiliaries, 18-35 parts of pigment or color cream and 6-20 parts of plasticizer, and wherein the curing agent is fatty amine and/or polyamide. The epoxy floor coating provided by the invention has excellent chemical corrosion resistance, high hardness, and excellent physical characteristics such as impact resistance, scrub resistance, abrasive resistance and the like; the epoxy floor coating is simple to prepare and convenient for construction; the epoxy floor coating is prepared from environment-friendly, solvent-free good-quality epoxy resin; the epoxy floor coating is wearproof and insulating, and hard and fine in surface; the epoxy floor coating is excellent in resistance to acid, to alkali, to salt, to oil, to esters, and to drugs; the epoxy floor coating is waterproof and non-absorbent, easy to flush, and simple and easy to clean and maintain; besides, the epoxy floor coating is bright and comfortable, smooth and beautiful in appearance with mirror face effect.

Description

Epoxy flooring coating
Technical field
The present invention relates to a kind of coating, specifically, relate in particular to a kind of epoxy flooring coating.
Background technology
Epoxy flooring coating is used for functional terrace from the outset: wear-resisting as anticorrosion, anti-skidding, develop into general general industry terrace; Except having functional requirement, also has ornamental effect.Obtain at industry ground slab on the basis of widespread use, along with improving constantly of people's living standard, now in family decoratees, applied.The epoxy industry ground slab has become one of China's industry with the fastest developing speed, causes everybody's attention.It can resemble realizes batch production production the cement products, and prospect is more considerable! But all there is certain deficiency in existing epoxy flooring coating on the market, and erosion resistance is inadequate, anti-stampability, and the physical propertys such as abrasion resistance, wear resistance are relatively poor, and preparation process is complicated, inadequate environmental protection etc.
Granted publication number discloses a kind of epoxy flooring coating in the patent of CN1923931, its technical scheme that adopts is: a kind of epoxy flooring coating, be comprised of host and solidifying agent, it is characterized in that by weight, described host is comprised of following component: E-44 Resins, epoxy 20-25 part; E-20 Resins, epoxy 10-12 part; Color stuffing 40-50 part; Nano aluminium oxide 2-10 part; Auxiliary agent 2-10 part; Solvent 15-20 part.But still there is above-mentioned deficiency in disclosed epoxy flooring coating in this patent.
Summary of the invention
The problems referred to above for prior art exists the invention provides a kind of epoxy flooring coating, and it is inadequate that purpose is to solve existing epoxy flooring coating erosion resistance, anti-stampability, the physical property such as abrasion resistance, wear resistance is relatively poor, and preparation process is complicated, not the problem of environmental protection.
To achieve these goals, the present invention adopts following technical scheme:
Epoxy flooring coating is characterized in that, it comprises host and solidifying agent, and the mixing match of described host and solidifying agent is 2:1;
Wherein, this host comprises following component by weight:
Resins, epoxy 22-50 part;
Filler 10-30 part;
Thickening material 1-8 part;
Auxiliary agent 4-7 part;
Pigment or color 18-35 part;
Softening agent 6-20 part;
Wherein, solidifying agent is selected fatty amine and/or polymeric amide.
Wherein, filler is the nanometer calcium carbonate superfine powder.
Wherein, auxiliary agent is one of dispersion agent, flow agent, defoamer or combination.
This host comprises following component by weight:
22 parts of Resins, epoxy;
15 parts of nanometer calcium carbonate superfine powders;
1 part of thickening material;
0.7 part of dispersion agent;
5 parts of flow agents;
1 part of defoamer;
18 parts of colors;
6 parts in softening agent;
Wherein, solidifying agent is selected fatty amine and/or polymeric amide.
Epoxy flooring coating, it comprises host and solidifying agent, the mixing match of described host and solidifying agent is 2:1;
Wherein, this host comprises following component by weight:
Resins, epoxy 30-50 part;
Filler 10-30 part;
Thickening material 3-8 part;
Auxiliary agent 4-7 part;
Pigment or color 20-35 part;
Softening agent 12-20 part;
Wherein, solidifying agent is selected fatty amine and/or polymeric amide.
Compared to existing technology, the present invention has following beneficial effect:
(1) epoxy flooring coating of the present invention has good chemicals-resistant corrosive nature, has higher hardness and good anti-stampability, the physical propertys such as abrasion resistance, wear resistance, and preparation is simple, easy construction.
(2) environmental protection, solvent-free high-quality Resins, epoxy is made.
(3) wear-resisting, insulation, the surface is hard fine and closely woven.
(4) acid-and base-resisting, salt, oil, ester class, resistance to chemical reagents is good.
(5) waterproof, do not absorb water, easily the flushing, cleaning is simply easy.
(6) outward appearance is beautiful comfortable, level and smooth, attractive in appearance, tool mirror effect.
Embodiment
For technique means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with specific embodiment, further set forth the present invention.
Embodiment 1: epoxy flooring coating, and it comprises host and solidifying agent, the mixing match of described host and solidifying agent is 2:1; Wherein, this host comprises following component by weight: Resins, epoxy 22-50 part; Filler 10-30 part; Thickening material 1-8 part; Auxiliary agent 4-7 part; Pigment or color 18-35 part; Softening agent 6-20 part; Wherein, solidifying agent is selected fatty amine and/or polymeric amide.
Wherein, filler is the nanometer calcium carbonate superfine powder.
Wherein, auxiliary agent is one of dispersion agent, flow agent, defoamer or combination.
Particularly, this host comprises following component by weight: 22 parts of Resins, epoxy; 15 parts of nanometer calcium carbonate superfine powders; 1 part of thickening material; 0.7 part of dispersion agent; 5 parts of flow agents; 1 part of defoamer; 18 parts of colors; 6 parts in softening agent; Wherein, solidifying agent is selected fatty amine and/or polymeric amide.
Embodiment 2: epoxy flooring coating, and it comprises host and solidifying agent, the mixing match of described host and solidifying agent is 2:1; Wherein, this host comprises following component by weight: Resins, epoxy 30-50 part; Filler 10-30 part; Thickening material 3-8 part; Auxiliary agent 4-7 part; Pigment or color 20-35 part; Softening agent 12-20 part; Wherein, solidifying agent is selected fatty amine and/or polymeric amide.
Embodiment 3: a kind of epoxy flooring coating, formed by host and solidifying agent, and by weight, described host is comprised of following component: 30 parts of Resins, epoxy; 10 parts of fillers; 3 parts of thickening materials; 4 parts of auxiliary agents; 20 parts of pigment; 12 parts in softening agent, solidifying agent is selected fatty amine.
Embodiment 4: a kind of epoxy flooring coating, formed by host and solidifying agent, and by weight, described host is comprised of following component: 50 parts of Resins, epoxy; 30 parts of fillers; 8 parts of thickening materials; 7 parts of auxiliary agents; 35 parts of pigment; 20 parts in softening agent, solidifying agent is selected polymeric amide.
Embodiment 5: a kind of epoxy flooring coating, formed by host and solidifying agent, and by weight, described host is comprised of following component: 39 parts of Resins, epoxy; 22 parts of fillers; 5 parts of thickening materials; 5.5 parts of auxiliary agents; 26.5 parts of pigment; 16 parts in softening agent, solidifying agent is selected fatty amine.
This product mainly is the groundbed material, road, garage usefulness, scumbling finish paint, acid and alkali-resistance coating, surperficial ornaments.
The above only is preferred implementation of the present invention, and protection scope of the present invention is not limited in above-mentioned embodiment, and every technical scheme that belongs to the principle of the invention all belongs to protection scope of the present invention.For a person skilled in the art, some improvement of under the prerequisite that does not break away from principle of the present invention, carrying out, these improvement also should be considered as protection scope of the present invention.

Claims (5)

1. epoxy flooring coating is characterized in that, it comprises host and solidifying agent, and the mixing match of described host and solidifying agent is 2:1;
Wherein, this host comprises following component by weight:
Resins, epoxy 22-50 part;
Filler 10-30 part;
Thickening material 1-8 part;
Auxiliary agent 4-7 part;
Pigment or color 18-35 part;
Softening agent 6-20 part;
Wherein, solidifying agent is selected fatty amine and/or polymeric amide.
2. epoxy flooring coating as claimed in claim 1 is characterized in that, wherein, filler is the nanometer calcium carbonate superfine powder.
3. epoxy flooring coating as claimed in claim 1 is characterized in that, wherein, auxiliary agent is one of dispersion agent, flow agent, defoamer or combination.
4. such as the described epoxy flooring coating of claim 1~3, it is characterized in that, this host comprises following component by weight:
22 parts of Resins, epoxy;
15 parts of nanometer calcium carbonate superfine powders;
1 part of thickening material;
0.7 part of dispersion agent;
5 parts of flow agents;
1 part of defoamer;
18 parts of colors;
6 parts in softening agent;
Wherein, solidifying agent is selected fatty amine and/or polymeric amide.
5. epoxy flooring coating as claimed in claim 1 is characterized in that, it comprises host and solidifying agent, and the mixing match of described host and solidifying agent is 2:1;
Wherein, this host comprises following component by weight:
Resins, epoxy 30-50 part;
Filler 10-30 part;
Thickening material 3-8 part;
Auxiliary agent 4-7 part;
Pigment or color 20-35 part;
Softening agent 12-20 part;
Wherein, solidifying agent is selected fatty amine and/or polymeric amide.
CN2013101955706A 2013-05-23 2013-05-23 Epoxy floor coating Pending CN103305091A (en)