CN105033571A - 一种螺栓加工工艺 - Google Patents
一种螺栓加工工艺 Download PDFInfo
- Publication number
- CN105033571A CN105033571A CN201510301678.8A CN201510301678A CN105033571A CN 105033571 A CN105033571 A CN 105033571A CN 201510301678 A CN201510301678 A CN 201510301678A CN 105033571 A CN105033571 A CN 105033571A
- Authority
- CN
- China
- Prior art keywords
- bolt
- machining process
- hour
- hours
- per hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种螺栓加工工艺,包括如下步骤:1)用冷镦机将原料冷镦成形,使螺栓本体的角部饱满一致;2)用攻丝机在螺栓本体上加工出外螺纹,形成螺栓;3)将螺栓放入到高温入内,入炉温度控制在500℃以下,然后以每小时升温50-100℃的速率升温至800摄氏度,并保持3-4小时;4)自然冷却2-3小时。本发明生产的螺母抗压耐磨,使用寿命长。
Description
技术领域
本发明属于机械加工技术领域,特别涉及一种螺栓加工工艺。
背景技术
螺栓属于五金类标准件,常用于各种精密零件、机箱、机柜、汽车构件等,焊接螺栓的一个端面上设有多个焊接点,各焊接点的高度一致。现有的焊接螺栓的加工工艺存在螺母抗压耐磨性能不足的缺陷。
发明内容
本发明的技术方案是这样实现的:一种螺栓加工工艺,包括如下步骤:
1)用冷镦机将原料冷镦成形,使螺栓本体的角部饱满一致;
2)用攻丝机在螺栓本体上加工出外螺纹,形成螺栓;
3)将螺栓放入到高温入内,入炉温度控制在500℃以下,然后以每小时升温50-100℃的速率升温至800摄氏度,并保持3-4小时;
4)自然冷却2-3小时。
优选地,所述步骤3)的最佳升温速率为每小时升温70摄氏度。
优选地,所述步骤4)的最佳冷却时间为2.5小时。
本发明的有益效果:本发明生产的螺母抗压耐磨,使用寿命长。
具体实施方式
对本发明提供的实施方式作进一步详细的说明:
一种螺栓加工工艺,包括如下步骤:
1)用冷镦机将原料冷镦成形,使螺栓本体的角部饱满一致;
2)用攻丝机在螺栓本体上加工出外螺纹,形成螺栓;
3)将螺栓放入到高温入内,入炉温度控制在500℃以下,然后以每小时升温50-100℃的速率升温至800摄氏度,并保持3-4小时;
4)自然冷却2-3小时。
优选地,所述步骤3)的最佳升温速率为每小时升温70摄氏度。
优选地,所述步骤4)的最佳冷却时间为2.5小时。
本发明的有益效果:本发明生产的螺母抗压耐磨,使用寿命长。
在此说明书中,本发明已参照其特定的实施例作了描述。但是,很显然仍可以做出各种修改和变换而不背离本发明的精神和范围。因此,说明书应被认为是说明性的而非限制性的。
Claims (3)
1.一种螺栓加工工艺,其特征在于,包括如下步骤:
1)用冷镦机将原料冷镦成形,使螺栓本体的角部饱满一致;
2)用攻丝机在螺栓本体上加工出外螺纹,形成螺栓;
3)将螺栓放入到高温入内,入炉温度控制在500℃以下,然后以每小时升温50-100℃的速率升温至800摄氏度,并保持3-4小时;
4)自然冷却2-3小时。
2.根据权利要求1所述的螺栓加工工艺,其特征在于,所述步骤3)的最佳升温速率为每小时升温70摄氏度。
3.根据权利要求1所述的螺栓加工工艺,其特征在于,所述步骤4)的最佳冷却时间为2.5小时。