CN105017870A - High-temperature resistant paint for decoration - Google Patents
High-temperature resistant paint for decoration Download PDFInfo
- Publication number
- CN105017870A CN105017870A CN201410598943.9A CN201410598943A CN105017870A CN 105017870 A CN105017870 A CN 105017870A CN 201410598943 A CN201410598943 A CN 201410598943A CN 105017870 A CN105017870 A CN 105017870A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature resistant
- water
- emulsion
- decoration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-temperature resistant paint for decoration. The high-temperature resistant paint for the decoration is composed, by weight, of 60-70 parts of modified styrene acrylic latex, 20-30 parts of VAE latex, 10-12 parts of ethyl cellulose, 2-4 parts of arachidic acid, 2-4 parts of gel amorphous silica, 0.4-0.6 part of a flatting agent, 11-13 parts of titanium dioxide powder, 3-5 parts of a titanate coupling agent, 4-6 parts of ethylene glycol butyl ether, 0.5-0.8 part of an antiseptic agent, 2.5-3.5 parts of thickening agents, 0.5-0.9 part of an antifoaming agent and 30-40 parts of water. According to the high-temperature resistant paint for the decoration, the raw materials do not contain hazardous substances such as formaldehyde and formaldehyde; according to the paint which takes the acrylic latex modified through organosilicone as the base material, due to the fact that chain structures contain siloxane bonds and groups which are prone to being oxidized and hydrolyzed, the gloss retention, the high-temperature resistance, the water resistance and the weather resistance of the paint are better.
Description
Technical field
The present invention relates to decorative paint field, specifically belong to a kind of high temperature resistant decorative paints.
Background technology
Paint is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes.Paint is thickness oil colour, inflammable in not dry situation, water insoluble, is slightly soluble in fat, dissolves in alcohol, aldehyde, ether, benzene, alkane, be soluble in gasoline, kerosene, diesel oil.
Kind is painted much in present market, but various paint is all made up of filmogen (various resin), solvent, pigment, siccative, additive.Common paint makes solvent with gasoline usually, and epoxy iron red shop primer is containing a small amount of dimethylbenzene, and dipping lacquer mainly containing toluene, also has a small amount of benzene, very large on human body impact.
Summary of the invention
The object of this invention is to provide a kind of high temperature resistant decorative paints, not containing the objectionable impurities such as formaldehyde and trimethylbenzene in starting material, with the paint that organic-silicon-modified ACRYLIC EMULSION is base-material, due to silicone-containing key in chain structure, not containing group that is oxidizable and hydrolysis, the gloss retention thus painted, high thermal resistance, water tolerance and weathering resistance are better.
The technical solution used in the present invention is as follows:
A kind of high temperature resistant decorative paints, by weight, is made up of following raw material:
Modifying cinepazid emulsion 60-70, VAE emulsion 20-30, ethyl cellulose 10-12, eicosanoic acid 2-4, aerosil 2-4, flow agent 0.4-0.6, titanium dioxide 11-13, organo-siloxane 4-6, titanate coupling agent 3-5, butyl glycol ether 4-6, sanitas 0.5-0.8, thickening material 2.5-3.5, defoamer 0.5-0.9, water 30-40;
Its concrete preparation method is as follows:
By above-mentioned weight part, by modifying cinepazid emulsion and VAE emulsion, titanate coupling agent and 1/3rd water carry out suction header tank after pre-emulsification, ethyl cellulose, titanium dioxide, butyl glycol ether another header tank of suction after the water dissolution of 2/3rds, two header tanks enter steel basin in the mode dripped simultaneously, in steel basin, temperature controls at 80-90 DEG C, control rate of addition, reaction mass is dripped off at 1.5-2.5h, then 1-1.5h is incubated, then cool, cool rear and the abundant mix and blend of all the other raw materials, to obtain final product.
A kind of high temperature resistant decorative paints, is made up of following raw material: modifying cinepazid emulsion 65, VAE emulsion 25, ethyl cellulose 11, eicosanoic acid 3, aerosil 3, flow agent 0.5, titanium dioxide 12, organo-siloxane 5, titanate coupling agent 4, butyl glycol ether 5, sanitas 0.6, thickening material 3, defoamer 0.7, water 35.
Not containing the objectionable impurities such as formaldehyde and trimethylbenzene in starting material of the present invention, with the paint that organic-silicon-modified ACRYLIC EMULSION is base-material, due to silicone-containing key in chain structure, not containing group that is oxidizable and hydrolysis, the gloss retention thus painted, high thermal resistance, water tolerance and weathering resistance are better.
Embodiment
A kind of high temperature resistant decorative paints, by weight, is made up of following raw material:
Modifying cinepazid emulsion 65, VAE emulsion 25, ethyl cellulose 11, eicosanoic acid 3, aerosil 3, flow agent 0.5, titanium dioxide 12, organo-siloxane 5, titanate coupling agent 4, butyl glycol ether 5, sanitas 0.6, thickening material 3, defoamer 0.7, water 35;
Its concrete preparation method is as follows:
By above-mentioned weight part, by modifying cinepazid emulsion and VAE emulsion, titanate coupling agent and 1/3rd water carry out suction header tank after pre-emulsification, ethyl cellulose, titanium dioxide, butyl glycol ether another header tank of suction after the water dissolution of 2/3rds, two header tanks enter steel basin in the mode dripped simultaneously, in steel basin, temperature controls at 80-90 DEG C, control rate of addition, reaction mass is dripped off at 1.5-2.5h, then 1-1.5h is incubated, then cool, cool rear and the abundant mix and blend of all the other raw materials, to obtain final product.
Claims (2)
1. a high temperature resistant decorative paints, by weight, is characterized in that, is made up of following raw material:
Modifying cinepazid emulsion 60-70, VAE emulsion 20-30, ethyl cellulose 10-12, eicosanoic acid 2-4, aerosil 2-4, flow agent 0.4-0.6, titanium dioxide 11-13, organo-siloxane 4-6, titanate coupling agent 3-5, butyl glycol ether 4-6, sanitas 0.5-0.8, thickening material 2.5-3.5, defoamer 0.5-0.9, water 30-40;
Its concrete preparation method is as follows:
By above-mentioned weight part, by modifying cinepazid emulsion and VAE emulsion, titanate coupling agent and 1/3rd water carry out suction header tank after pre-emulsification, ethyl cellulose, titanium dioxide, butyl glycol ether another header tank of suction after the water dissolution of 2/3rds, two header tanks enter steel basin in the mode dripped simultaneously, in steel basin, temperature controls at 80-90 DEG C, control rate of addition, reaction mass is dripped off at 1.5-2.5h, then 1-1.5h is incubated, then cool, cool rear and the abundant mix and blend of all the other raw materials, to obtain final product.
2. high temperature resistant decorative paints according to claim 1, it is characterized in that, be made up of following raw material: modifying cinepazid emulsion 65, VAE emulsion 25, ethyl cellulose 11, eicosanoic acid 3, aerosil 3, flow agent 0.5, titanium dioxide 12, organo-siloxane 5, titanate coupling agent 4, butyl glycol ether 5, sanitas 0.6, thickening material 3, defoamer 0.7, water 35.