CN103409024A - Regeneration-type sand maishi paint - Google Patents
Regeneration-type sand maishi paint Download PDFInfo
- Publication number
- CN103409024A CN103409024A CN2013103844430A CN201310384443A CN103409024A CN 103409024 A CN103409024 A CN 103409024A CN 2013103844430 A CN2013103844430 A CN 2013103844430A CN 201310384443 A CN201310384443 A CN 201310384443A CN 103409024 A CN103409024 A CN 103409024A
- Authority
- CN
- China
- Prior art keywords
- parts
- sand
- regeneration
- foundry sand
- maishi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a regeneration-type sand maishi paint which comprises the following component in parts by weight: 100 to 150 parts of pure acrylic emulsion, 80 to 130 parts of elastic emulsion, 8 to 13 parts of film-forming aid, 1 to 5 parts of thickening agent, 1 to 4 parts of corrosion remover, 0.5 to 3 parts of defoaming agent, 5 to 12 parts of hardening agent, 3 to 8 parts of ethylene glycol, 0 to 750 parts of color sand, 0 to 750 parts of regeneration-type sand and 3 to 10 parts of water. The regeneration-type sand maishi paint not only has the stone imitation effect of a maishi paint but also can be used for consuming and utilizing a large amount of the regeneration-type sand. The regeneration-type sand maishi paint is stable in performance and low in production cost, and has the dual effects of beautifying the environment and preventing the environment pollution. Thus, the regeneration-type sand maishi paint has the strong market competitiveness.
Description
Technical field
The present invention relates to the building coating technical field, be specifically related to the true mineral varnish of a kind of regenerated foundry sand.
Background technology
True mineral varnish is the new coating of the real stone material of a kind of ornamental emulation, mainly adopts emulsion and the preparation of colored sand, is widely used at present the decoration of exterior wall of buildings, deeply welcomed by the people.But the place of production of highly purified colorful quartz sands is limited, and output is little, and cost is high, the production competitive power descends.Although the regenerated foundry sand color and luster has a bit dark, it is a kind of highly purified quartz sand, is ostracised outside true mineral varnish always.The present invention attempts regenerated foundry sand and colorful quartz sands reasonably combined, produces the true mineral varnish that can meet decorative effect, can dissolve and utilize regenerated foundry sand again.
Summary of the invention
The present invention is intended to overcome the deficiency that current true mineral varnish can not utilize regenerated foundry sand, invents the true mineral varnish of regenerated foundry sand always, can meet decorative effect, stable performance, can dissolve and utilize a large amount of regenerated foundry sands again, realize recycling economy, reach and beautify the environment and the purpose that prevents that contaminate environment from developing simultaneously.
Technical scheme of the present invention is achieved in that the true mineral varnish of a kind of regenerated foundry sand, comprises following component and weight part:
Pure-acrylic emulsion 100-150,
Elastic emulsion 80-130,
Film coalescence aid 8-13,
Thickening material 1-5,
Sanitas 1-4,
Defoamer 0.5-3,
Hardening agent 5-12,
Ethylene glycol 3-8,
Color sand 0-750,
Regenerated foundry sand 0-750,
Water 3-10.
Described elastic emulsion is commercially available polyacrylic ester elastic emulsion; Described film coalescence aid is commercially available propandiol butyl ether; Described thickening material is commercially available ASE60 thickening material; Described sanitas is commercially available HY608 sanitas; Described Hardening agent is commercially available silicon sol; Described defoamer is commercially available SP202 defoamer.
Described regenerated foundry sand for discarded foundry sand through oven dry, impurity elimination, dedusting, washing, dry and the art breading such as sieve after glass sand.
The present invention is with respect to prior art, its beneficial effect had is: the present invention is reasonably combined by regenerated foundry sand and colorful quartz sands, produce the true mineral varnish effect that can meet decorative effect, can dissolve again and utilize a large amount of regenerated foundry sands, realize recycling economy, reach and beautify the environment and the purpose that prevents that contaminate environment from developing simultaneously.
Embodiment
The formula that below further illustrates the embodiment of the present invention forms.
Embodiment 1:
Pure-acrylic emulsion 150, elastic emulsion 80, film coalescence aid 8, thickening material 1, sanitas 1, defoamer 0.5, Hardening agent 5, ethylene glycol 3, color sand 0, regenerated foundry sand 750, water 5.
Embodiment 2:
Pure-acrylic emulsion 140, elastic emulsion 90, film coalescence aid 9, thickening material 2, sanitas 2, defoamer 1, Hardening agent 7, ethylene glycol 4, color sand 750, regenerated foundry sand 0, water 6.
Embodiment 3:
Pure-acrylic emulsion 130, elastic emulsion 100, film coalescence aid 10, thickening material 3, sanitas 2.5, defoamer 1.5, Hardening agent 8, ethylene glycol 5, color sand 300, regenerated foundry sand 450, water 7.
Embodiment 4:
Pure-acrylic emulsion 120, elastic emulsion 110, film coalescence aid 10.5, thickening material 4, sanitas 3, defoamer 2, Hardening agent 9, ethylene glycol 6, color sand 500, regenerated foundry sand 250, water 3.
Embodiment 5:
Pure-acrylic emulsion 110, elastic emulsion 120, film coalescence aid 11, thickening material 5, sanitas 3.5, defoamer 2.5, Hardening agent 10, ethylene glycol 7, color sand 650, regenerated foundry sand 100, water 4.
Embodiment 6:
Pure-acrylic emulsion 100, elastic emulsion 130, film coalescence aid 12, thickening material 5, sanitas 4, defoamer 3, Hardening agent 12, ethylene glycol 8, color sand 200, regenerated foundry sand 550, water 9.
Embodiment 7:
Pure-acrylic emulsion 150, elastic emulsion 80, film coalescence aid 12, thickening material 4.5, sanitas 3, defoamer 3, Hardening agent 11, ethylene glycol 6.5, color sand 100, regenerated foundry sand 650, water 10.
Embodiment 8:
Pure-acrylic emulsion 105, elastic emulsion 125, film coalescence aid 12, thickening material 3.5, sanitas 3, defoamer 2.5, Hardening agent 10, ethylene glycol 5.5, color sand 400, regenerated foundry sand 350, water 8.
Embodiment 9:
Pure-acrylic emulsion 135, elastic emulsion 95, film coalescence aid 11.5, thickening material 3, sanitas 2.5, defoamer 2, Hardening agent 9.5, ethylene glycol 4.5, color sand 50, regenerated foundry sand 700, water 7.5.
Embodiment 10:
Pure-acrylic emulsion 145, elastic emulsion 85, film coalescence aid 10, thickening material 3.5, sanitas 3, defoamer 3, Hardening agent 11, ethylene glycol 7.5, color sand 150, regenerated foundry sand 600, water 7.5.
Claims (3)
1. true mineral varnish of regenerated foundry sand is characterized in that the component contained and parts by weight are:
Pure-acrylic emulsion 100-150,
Elastic emulsion 80-130,
Film coalescence aid 8-13,
Thickening material 1-5,
Sanitas 1-4,
Defoamer 0.5-3,
Hardening agent 5-12,
Ethylene glycol 3-8,
Color sand 0-750,
Regenerated foundry sand 0-750,
Water 3-10.
2. the true mineral varnish of a kind of regenerated foundry sand according to claim 1, it is characterized in that: described elastic emulsion is the polyacrylic ester elastic emulsion; Described film coalescence aid is propandiol butyl ether; Described thickening material is the ASE60 thickening material; Described sanitas is the HY608 sanitas; Described Hardening agent is silicon sol; Described defoamer is the SP202 defoamer.
3. the true mineral varnish of a kind of regenerated foundry sand according to claim 1 is characterized in that: described regenerated foundry sand for discarded foundry sand through oven dry, impurity elimination, dedusting, washing, dry and the glass sand of the art breading such as sieve.