CN103602194A - Acrylate waterproof coating material - Google Patents
Acrylate waterproof coating material Download PDFInfo
- Publication number
- CN103602194A CN103602194A CN201310512441.5A CN201310512441A CN103602194A CN 103602194 A CN103602194 A CN 103602194A CN 201310512441 A CN201310512441 A CN 201310512441A CN 103602194 A CN103602194 A CN 103602194A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating material
- acrylate
- water
- acrylate waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses an acrylate waterproof coating material, which comprises, by weight, 10-20 parts of titanium dioxide powder, 20-30 parts of talc powder, 20-30 parts of heavy calcium carbonate, 1-2 parts of a dispersing agent, 50-70 parts of an emulsion, a proper amount of other auxiliary agents, and 10-20 parts of water. According to the acrylate waterproof coating material, an acrylate copolymerization emulsion is adopted as a film forming substance, and various pigments and fillers are added to prepare an aqueous, color-adjustable and rubber type coating material, wherein the coating material is the acrylate waterproof coating material; and after the coating film is dried, the continuous coating can be formed, wherein the coating has characteristics of good elongation, good breaking strength, good acid resistance, good alkali resistance, excellent weathering resistance, easy construction and no environment pollution, and is an ideal material used for roofing water resistance.
Description
Technical field
The present invention relates to a kind of water-miscible paint, be specifically related to a kind of acrylate waterproof paint.
Background technology
Along with people are to healthy understanding, more and more recognize the important of environmental protection, coating superior, functionalization, environmental protectionization is also accepted by market gradually, however Coating Market competition is always very fierce, along with the change of consumption structure, function and environmental protection coating material are ready to appear, are the focuses in market; As everyone knows, people 70% time tides over indoor, so the degree of cleaning of room air will directly have influence on people's health.In recent years, along with living standards of the people improve constantly, living environment is constantly improved, when upholstery is increasingly luxurious, attractive in appearance, the problem that affects HUMAN HEALTH because fitting up the indoor pollution causing gets more and more, investigation shows: 68% disease cause is relevant with the pollution of room air, and 80% cancer is relevant with living environment.Therefore, high-efficient and lasting ground purifies indoor harmful gas, the target that keeps life, the Working environment of pure and fresh health to become people more and more urgently to pursue.
Emulsion paint has good film-forming properties, abrasion resistance as coating, its membrane formation mechanism is that filming emulsion is under liquid state, face to be filled into row fully to grind coated, therefore latex particle is coated color stuffing particle completely, filming of obtaining becomes fine and close, and its film-forming properties, abrasion resistance, weathering resistance, anticreep mealiness can be improved greatly.
Summary of the invention
The object of the invention is to for the deficiencies in the prior art, provide that a kind of environmental pollution is little, easy construction and there is a kind of acrylate waterproof paint of superperformance.
Above-mentioned purpose of the present invention is achieved by the following scheme:
An acrylate waterproof paint, comprises the component of following weight part:
Titanium dioxide 10-20 part
Talcum powder 20-30 part
Water-ground limestone 20-30 part
Dispersion agent 1-2 part
Emulsion 50-70 part
Other auxiliary agents are appropriate
Water 10-20 part.
As improvement of the present invention, a kind of acrylate waterproof paint, comprises the component of following weight part:
15 parts of titanium dioxides
25 parts of talcum powder
25 parts of water-ground limestones
1.5 parts of dispersion agents
60 parts of emulsions
Other auxiliary agents are appropriate
Water 10-20 part.
Above-mentioned emulsion comprises the component of following weight part:
Methyl methacrylate 5-10 part
Vinylbenzene 10-20 part
2-EHA 10-20 part
Butyl acrylate 10-30 part
Reactive monomer 2-6 part
Vinyl unsaturated carboxylic acid 1-5 part
Tensio-active agent 2-3 part
Initiator 0.05-0.1 part
Water 40-60 part.
Compared with prior art, the beneficial effect that the present invention has is:
Acrylate waterproof paint of the present invention is to be the filmogen coating a kind of water-based color-adjustable, rubber-type that various pigment, filler are made in addition again by acrylate copolymer emulsion.After dried coating film, can form successional coating, coating has good unit elongation and breaking tenacity, acidproof, alkali resistance good, has excellent weather resistance, easy construction, non-environmental-pollution, and as roof waterproof, using is a kind of comparatively ideal material.
Embodiment
For ease of understanding the present invention, it is as follows that the present invention enumerates embodiment.Those skilled in the art should understand, described embodiment only, for helping to understand the present invention, should not be considered as concrete restriction of the present invention.
As no specific instructions, various raw material of the present invention all can obtain by commercially available; Or prepare according to the ordinary method of this area.Unless otherwise defined or described herein, all specialties used herein and scientific words and the art technology same meaning that skillfully person of entering is familiar.In addition any method similar or impartial to described content and material all can be applicable in the inventive method.
Unless otherwise indicated, the familiar same meaning of all specialties used herein and scientific words and those skilled in the art.
In addition any method similar or impartial to described content and material all can be applicable in the inventive method.
An acrylate waterproof paint, comprises the component of following weight part:
Titanium dioxide 10-20 part, talcum powder 20-30 part, water-ground limestone 20-30 part, dispersion agent 1-2 part, emulsion 50-70 part, other auxiliary agents are appropriate, water 10-20 part.
Above-mentioned emulsion comprises the component of following weight part:
Methyl methacrylate 5-10 part, vinylbenzene 10-20 part, 2-EHA 10-20 part, butyl acrylate 10-30 part, reactive monomer 2-6 part, vinyl unsaturated carboxylic acid 1-5 part, tensio-active agent 2-3 part, initiator 0.05-0.1 part, water 40-60 part.
The method for making of emulsion is as follows: monomer is carried out to suction header tank after pre-emulsification by the amount of formulating of recipe and tensio-active agent and water.Another header tank of suction after water dissolution for initiator.Both enter reactor in the mode dripping simultaneously and carry out polyreaction.Temperature of reaction is controlled at 70-85 degree, controls rate of addition, and reaction mass is dripped off at 3-3.5h.Last insulation reaction 1-1.5h, makes to react completely.Then cooling, with ammoniacal liquor, emulsion pH value is adjusted to 7-8.
Waterproof paint adopts conventional preparation method for coating: after water, dispersion agent, defoamer, pigment, filler and other auxiliary agents are weighed by formula, drop into high-speed dispersing kettle, the acrylate copolymer emulsion that simultaneously adds above-mentioned preparation obtains waterproof paint after fully stirring.Adoptable pigment, filler have titanium dioxide, talcum powder, water-ground limestone, process white, mica powder, china clay, zinc oxide etc.
Applicant's statement, person of ordinary skill in the field is on the basis of above-described embodiment, by the concrete content point value of above-described embodiment component, combined with the technical scheme of summary of the invention part, thereby the new numerical range producing, also be one of record scope of the present invention, the application, for making specification sheets simple and clear, is no longer enumerated these numerical ranges.
Claims (3)
1. an acrylate waterproof paint, is characterized in that, comprises the component of following weight part:
Titanium dioxide 10-20 part
Talcum powder 20-30 part
Water-ground limestone 20-30 part
Dispersion agent 1-2 part
Emulsion 50-70 part
Other auxiliary agents are appropriate
Water 10-20 part.
2. a kind of acrylate waterproof paint as claimed in claim 1, is characterized in that, comprises the component of following weight part:
15 parts of titanium dioxides
25 parts of talcum powder
25 parts of water-ground limestones
1.5 parts of dispersion agents
60 parts of emulsions
Other auxiliary agents are appropriate
Water 10-20 part.
3. a kind of acrylate waterproof paint as claimed in claim 1 or 2, is characterized in that, described emulsion comprises the component of following weight part: