CN104987845B - 一种环保型易撕保护胶带及其制备方法 - Google Patents

一种环保型易撕保护胶带及其制备方法 Download PDF

Info

Publication number
CN104987845B
CN104987845B CN201510419885.3A CN201510419885A CN104987845B CN 104987845 B CN104987845 B CN 104987845B CN 201510419885 A CN201510419885 A CN 201510419885A CN 104987845 B CN104987845 B CN 104987845B
Authority
CN
China
Prior art keywords
gauze
plastic
environment
cloth base
particle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510419885.3A
Other languages
English (en)
Other versions
CN104987845A (zh
Inventor
许金章
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Yongguan Zhongcheng new material science and Technology (Group) Limited by Share Ltd
Original Assignee
Shanghai Yongguan Adhesive Products CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Yongguan Adhesive Products CO Ltd filed Critical Shanghai Yongguan Adhesive Products CO Ltd
Priority to CN201510419885.3A priority Critical patent/CN104987845B/zh
Publication of CN104987845A publication Critical patent/CN104987845A/zh
Application granted granted Critical
Publication of CN104987845B publication Critical patent/CN104987845B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种环保型易撕保护胶带，包含布坯粒子、纱布、以及水性硅，其中布坯粒子包含PE塑料粒子和填充粒子。本发明还涉及保护胶带的制备方法，包括PE塑料粒子与填充料在260摄氏度‑300摄氏度高温下，以7：3重量比混合、熔化；与纱布复合成涂塑双面布坯；并在塑布胚的涂塑面，均匀地涂上一层环保型水性硅，在未涂硅面涂一层环保型高性能亚克力水胶。本发明的有益效果是采用双面淋膜加上特制易撕纱布与PE融为一体更能方便使用者，达到操作方便，可轻易撕断的效果；环保可达欧盟SVHC标准，无污染，提高产品的市场竞争力。

Description

一种环保型易撕保护胶带及其制备方法
技术领域
本发明涉及胶带领域，具体涉及一种环保型易撕保护胶带及其制备方法。
背景技术
现有保护胶带以纯PE膜为基材，涂油性胶水，可基本达到保护作用但缺点有很多：
1.纯PE膜使用不方便：难撕要借助剪刀、刀片及其它利器工具操作，存在一定的安全隐患。
2.采用油胶：油胶是以甲苯、醋酸乙酯为溶剂即不环保又对环境及使用者身体有一定的危害。
3.耐磨性差，在贴物体表面保护使用过程中难免有物体之间摩擦，耐磨性差从而把胶带磨破，损坏物品起不到保护作用。
4.耐温性差：在高温环境使用下现有胶带会老化胶水变质，产生掉胶在物体表面造成污染，不易清除。
5.持粘力差：胶带与物体表面保护相贴使用的过程中，持粘力差，一段时间后会自动脱落，保护功能失效。
发明内容
本发明的目的是为了克服现有技术中的不足，针对因实际操作不便，及不环保带来的安全隐患及环境污染，提供一种环保型易撕保护胶带。
具体的，本发明一方面提供一种环保型易撕保护胶带，包含布坯粒子、纱布、以及水性硅，其中布坯粒子包含PE塑料粒子和塑料填充粒子。
优选地，PE塑料粒子为高密度LDPE。
优选地，其中布坯粒子百分比为：粒子高密度LDPE 60％、塑料填充粒子40％(6:4)。
优选地，其中布坯粒子百分比为：粒子高密度LDPE 70％、塑料填充粒子30％(7:3)。
优选地，PE塑料粒子与塑料填充粒子的重量比为7:3。
在本发明的一个具体实施方式中，还包含亚克力胶水(含固量为50％)。
在本发明的一个具体实施方式中，所述塑料填充粒子为CH-808
在本发明的一个具体实施方式中，纱布重量百分比为：经线30％-50％，纬线40％-60％。
优选地，其中纱布百分比为：经线40％，纬线60％；
在本发明的一个具体实施方式中，其中：布坯粒子中PE塑料粒子的重量百分比为70％、塑料填充粒子CH-808的重量百分比为30％。
在本发明的一个具体实施方式中，其中PE塑料粒子38％，塑料填充料粒子CH-80816％，纱布经线2.4％，纱布纬线3.6％，水性硅(其中，水1.2﹪,硅0.8﹪)，亚克力胶水(其中，水19％,胶19％)。
在本发明的一个具体实施方式中，布坯(塑料粒子+纱布+水性硅)与胶水百分比为布坯(塑料粒子+纱布+水性硅)62％，涂胶(水+胶)38％。
本发明另一方面的目的是提供一种环保型易撕保护胶带的制备方法，包括将(1)PE塑料粒子与塑料填充粒子搅拌均匀后加入螺杆以260℃-300℃高温下混合、熔化与纱布复合成涂塑双面布坯；(2)将水性硅加入料槽中，通过料槽中网纹辊带动布坯的转动，在涂布胚的涂塑面，均匀地涂抹上一层环保型水性硅，经过90℃-100℃烘道烘干，使环保型水性硅稳定地固化再布胚的表面。
在本发明的一个具体实施方式中，还包括(3)按含固量百分比，将亚克力胶水通过直涂方法涂湿胶70-80g/㎡与布坯上，经过100℃-110℃烘道烘干。
优选地，PE塑料粒子为高密度LDPE。
优选地，其中布坯粒子百分比为：粒子高密度LDPE 60％、填充粒子40％。
优选地，其中布坯粒子百分比为：粒子高密度LDPE 70％、填充粒子30％。
优选地，PE塑料粒子与塑料填充粒子的重量比为7:3。
在本发明的一个具体实施方式中，所述填充粒子为塑料CH-808；
在本发明的一个具体实施方式中，纱布重量百分比为：经线30％-50％，纬线40％-60％。
优选地，其中纱布百分比为：经线40％，纬线60％；
在本发明的一个具体实施方式中，其中：布坯粒子中PE塑料粒子的重量百分比为70％、塑料填充粒子CH-808的重量百分比为30％。
在本发明的一个具体实施方式中，其中PE塑料粒子38％，塑料填充料粒子CH-80816％，纱布经线2.4％，纱布纬线3.6％，水性硅(水1.2％,硅0.8％)，亚克力胶水(水19％,胶19％)。
在本发明的一个具体实施方式中，布坯(塑料粒子+纱布+水性硅)与胶水百分比为布坯(塑料粒子+纱布+水性硅)62％，涂胶(水+胶)38％。
本发明的有益效果在于，本发明采用PE塑料粒、填充粒子混合融化，通过一次双面淋膜复膜的方法，把纱布夹在中间合为一体，其达到易撕效果。
纱布采用优质网络丝交织而成，材料搭配方面采用更合理的搭配方法，由塑料粒子LDPE、填充粒子；耐磨性、柔韧性、可塑性好。
胶水采用环保型高性能亚克力水胶，更能达到耐温性、持粘力、环保无污染的效果。
本发明采用双面淋膜加上特制易撕纱布与PE融为一体更能方便使用者无需借助利器及其它工具，易撕可轻易撕断到达操作方便安全的效果；环保可达欧盟SVHC标准，充分达到了环保，无污染，使用方便安全的效果，提高产品的市场竞争。
附图说明
图1：本发明工艺流程图
具体实施方式
下面结合具体实施方式对本发明作进一步详细描述：
实施例1
一种环保型易撕保护胶带，
配方：PE塑料粒子、塑料填充料粒子CH-808、纱布、水性硅、胶水，其中PE塑料粒子38％，塑料填充料粒子CH-80816％，纱布经线2.4％，纱布纬线3.6％，水性硅(水1.2％,硅0.8％)，亚克力胶水(水19％,胶19％)。
制备过程如下：
(1)将PE塑料粒子与塑料填充料粒子CH-808搅拌均匀后加入螺杆以260℃-300℃高温下混合、熔化与纱布复合成涂塑双面布胚；
(2)将用于表面离型处理的环保型水性硅加入料槽中，通过料槽中网纹辊带动布坯的转动，在涂布胚的涂塑面，均匀地涂抹上一层环保型水性硅，经过90℃-100℃烘道烘干，使环保型水性硅稳定地固化再布胚的表面；
(3)环保型高性能亚克力胶水的涂胶，按含固量百分比，将胶水通过直涂方法涂湿胶70-80g/㎡于布坯上，经过100℃-110℃烘道烘干。
保护胶带的性能测试见表1。
表1

Claims (2)

1.一种环保型易撕保护胶带，其特征在于，原料包含布坯粒子、纱布、含固量为40％的水性硅以及含固量为50％的亚克力胶水，其中布坯粒子包含PE塑料粒子和塑料填充粒子CH-808，PE塑料粒子的重量百分比为70％、塑料填充粒子CH-808的重量百分比为30％；纱布重量百分比为：经线30％-50％，纬线40％-60％。
2.一种环保型易撕保护胶带的制备方法，包括将(1)PE塑料粒子与塑料填充粒CH-808子搅拌均匀后加入螺杆以260℃-300℃高温下混合、熔化与纱布复合成涂塑双面布坯；(2)将水性硅加入料槽中，通过料槽中网纹辊带动布坯的转动，在涂布胚的涂塑面，均匀地涂抹上一层环保型水性硅，经过90℃-100℃烘道烘干，使环保型水性硅稳定地固化再布胚的表面；(3)按含固量百分比，将亚克力胶水通过直涂方法涂湿胶70-80g/㎡于布坯上，经过100℃-110℃烘道烘干；所述纱布重量百分比为：经线30％-50％，纬线40％-60％。
CN201510419885.3A 2015-07-17 2015-07-17 一种环保型易撕保护胶带及其制备方法 Active CN104987845B (zh)