CN104984385B - A kind of pre- stick of water soluble medical - Google Patents
A kind of pre- stick of water soluble medical Download PDFInfo
- Publication number
- CN104984385B CN104984385B CN201510436651.XA CN201510436651A CN104984385B CN 104984385 B CN104984385 B CN 104984385B CN 201510436651 A CN201510436651 A CN 201510436651A CN 104984385 B CN104984385 B CN 104984385B
- Authority
- CN
- China
- Prior art keywords
- parts
- stick
- water
- polyglycereol
- rosin ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provide it is a kind of be applied to injury gained in sports, surprisingly pull to wait and wrap up dressing, a kind of pre- stick of water soluble medical.The effect of water-soluble pre- stick is sprayed on the pars affecta skin of patient, quickly forms a kind of ventilative thin layer mucous membrane, is easy to bandage during wrapping not slipped with skin close adhesion, it is not loose be easy to remove.A kind of pre- stick of water soluble medical is by aqueous solvent（A）Constituted with polyglycereol rosin ester two parts.A agent raw material is the aqueous solution containing a small amount of medicinal alcohol；B agent is polyglycereol rosin ester thick liquid.Have the advantage that：Water-soluble pre- stick using the spraying of nuisanceless carbon dioxide propellant, can rapid film formation, it is easy to use, it is pollution-free to bad border.
Description
Technical field
The present invention relates to a kind of natural water-soluble pre- stick, specifically a kind of affected part for being sprayed at patient, favorably
In skin and bandage organic adhesion and be easy to what is removed, the material of referred to as a kind of pre- stick of water soluble medical.
Background technology
At present, at home, outside for the fixation of trauma skin surface bandage water-soluble pre- stick is undiscovered and remembers
Carry.The raw material based on polyglycereol rosin ester, the pre- stick of water-soluble bandage of exploitation will be opened for water-soluble pre- stick
Open up a new field.Due to the pre- stick water as solvent of this research project, the raw material based on natural glycerin modified rosin ester,
Auxiliary is antioxygen bactericide in the thymol extracted from the plants such as thyme, imparts natural, safe, the non-stimulated spy of pre- stick
Property.Because raw material is based on cheap and high security, thus it succeed in developing will for injury gained in sports, unexpected unexpected damage such as pull
New contribution is made in the fixation of bandage during the treatment of wound, meanwhile, the application of water-soluble pre- stick creates good warp for enterprise
Benefit of helping and social benefit.
The content of the invention
Pulled it is an object of the invention to provide one kind for human muscle, when injury gained in sports is treated, bandage is fixed necessary
A kind of water-soluble pre- stick.
The purpose of the present invention realizes that the pre- stick of water soluble medical is by the raw material of following weight proportion in the following manner
It is made, 70-90 parts of deionized water, 5-10 parts of medicinal alcohol, 2-6 parts of polyglycereol rosin ester, thymol bactericide 0.05-0.20
Part, preparation method is as follows：Individual raw material is added in reactor by proportioning, stirring is opened, is heated to 75 DEG C -- 90 DEG C, heating stirring
Homogeneous half an hour, it is finished product to be cooled to room temperature packaging.
The pre- stick of described water soluble medical, is to be prepared from the following raw materials in parts by weight, 75-85 parts of deionized water, doctor
With 6-9 parts of alcohol, 3-5 parts of polyglycereol rosin ester, 0.08-0.18 parts of thymol bactericide.
The pre- stick of described water soluble medical, is to be prepared from the following raw materials in parts by weight, 80 parts of deionized water, medical wine
Smart 7 parts, 4 parts of polyglycereol rosin ester, 0.15 part of thymol bactericide.
The excellent effect of the present invention is as follows：
Because polyglycerol rosin has certain emulsibility in itself, and contain multiple hydroxyls in molecule（—OH）And ether
Chain（-O-）Group, it is water-soluble good, can be mixed to the aqueous solution of uniformity in any proportion with water.Polyglycereol
The sticky feature group contained in rosin ester molecule, can be with the hydroxyl on gauze and skin（-0H）With amino (- NH2) formation
Faint hydrogen bond and realize bonding.Because pre- stick is that moisture on the aqueous solution, skin is easily locked without volatile, so not
Length is stopped by gauze to be all easy to remove.
Raw material aqueous solvent in formula, medical glycerine, polyglycereol rosin ester are natural, inexpensive, and raw material is easy to get.
Preservative in formula is thymol, is the thymol solution extracted from natural thyme, frequently as external application
One kind of bactericide, with medical value.With very strong bactericidal action and very strong acaricidal action, effect is rapid reliable.
Make solvent with alcohol water blend, wrap up pre-bonding when being treated applied to patient's local damage, pre- stick being had in itself
Some bioaffinities, it is nontoxic to skin, non-stimulated and with certain protective effect.
Pre- stick function admirable, it is easy to use, after spraying can effectively, a thin layer of glue is promptly formed on skin
Film, and the wrapping and adhesion of bandage are realized, thus it is pre- anti-slip and loose, and be easy to release and change.
The chemical stability of water-soluble pre- stick is good, and heat-resisting, cold tolerance is good, and physical property is good, there is enough glue
Property, no volume contraction, rheology is small, is non-thermal, electric conductor.
Embodiment
Embodiment 1：
The pre- stick of water soluble medical is to be prepared from the following raw materials in parts by weight, 90 parts of deionized water, 10 parts of medicinal alcohol,
6 parts of polyglycereol rosin ester, 0.20 part of thymol bactericide：
Preparation method is as follows：Individual raw material is added in reactor by proportioning, stirring is opened, 75 DEG C -90 DEG C, heating are heated to
Homogeneous half an hour is stirred, it is finished product to be cooled to room temperature packaging.
Embodiment 2
The pre- stick of water soluble medical is to be prepared from the following raw materials in parts by weight, 70 parts of deionized water, 5 parts of medicinal alcohol,
2 parts of polyglycereol rosin ester, 0.05 part of thymol bactericide.
Preparation method is same as Example 1.
Embodiment 3
The pre- stick of described water soluble medical, is to be prepared from the following raw materials in parts by weight, 75 parts of deionized water, medical wine
Smart 6 parts, 3 parts of polyglycereol rosin ester, 0.08 part of thymol bactericide.
Preparation method is same as Example 1.
Embodiment 4
The pre- stick of described water soluble medical, is to be prepared from the following raw materials in parts by weight, 85 parts of deionized water, medical wine
Smart 9 parts, 5 parts of polyglycereol rosin ester, 0.18 part of thymol bactericide.
Preparation method is same as Example 1.
Embodiment 5
The pre- stick of described water soluble medical, is to be prepared from the following raw materials in parts by weight, 80 parts of deionized water, medical wine
Smart 7 parts, 4 parts of polyglycereol rosin ester, 0.15 part of thymol bactericide.
Preparation method is same as Example 1.
This water soluble medical pre-bonding agent producing process is relatively simple, and the key of technical process is polyglycereol rosin ester in water
Dissolving.
Embodiment 6
The pre- stick of water soluble medical is sprayed on pars affecta skin when using, then wrapped up using bandage, bandage i.e. with
Skin is brought into close contact, and is difficult to slip, convenient to be applicable, with safety, it is natural, efficiently, biological property is good the characteristics of.The pre- stick
Succeed in developing, and the application in wound auxiliary treatment rehabilitation, it will the security of increase wound wrapping and the pre- stick of reduction
Cost, the physiotherapy and rehabilitation for injury gained in sports and accident trauma is made new contribution, at the same create good economic benefit and
Social benefit.
It is the known technology of those skilled in the art in addition to the technical characteristic described in specification.
Claims (3)
1. a kind of pre- stick of water soluble medical, it is characterised in that be to be prepared from the following raw materials in parts by weight, deionized water 70-90
Part, 5-10 parts of medicinal alcohol, 2-6 parts of polyglycereol rosin ester, 0.05-0.20 parts of thymol bactericide, preparation method is as follows：Will be each
Raw material is added in reactor by proportioning, is opened stirring, is heated to 75 DEG C -- 90 DEG C, heating stirring homogeneous half an hour, it is cooled to room
Thermometer bulb dress is finished product.
2. the pre- stick of water soluble medical according to claim 1, it is characterised in that be by the raw material system of following weight proportion
Into 75-85 parts of deionized water, 6-9 parts of medicinal alcohol, 3-5 parts of polyglycereol rosin ester, 0.08-0.18 parts of thymol bactericide.
3. the pre- stick of water soluble medical according to claim 1, it is characterised in that be by the raw material system of following weight proportion
Into 80 parts of deionized water, 7 parts of medicinal alcohol, 4 parts of polyglycereol rosin ester, 0.15 part of thymol bactericide.