CN104975538A - 一种具有阻燃功能的fpi离型纸 - Google Patents
一种具有阻燃功能的fpi离型纸 Download PDFInfo
- Publication number
- CN104975538A CN104975538A CN201510307669.XA CN201510307669A CN104975538A CN 104975538 A CN104975538 A CN 104975538A CN 201510307669 A CN201510307669 A CN 201510307669A CN 104975538 A CN104975538 A CN 104975538A
- Authority
- CN
- China
- Prior art keywords
- parts
- fpi
- release paper
- membrane layer
- leaching membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种FPI专用离型纸，包括作为基材的白牛纸，所述白牛纸的两面均淋膜有均匀的淋膜层，而淋膜层上均匀的设有一层非硅离型层；所述淋膜层由以下重量份的原料组成：低密度PE30-40份、高密度PE30-40份、阻燃助剂6-8份、高流动性聚酰胺10-20份、润滑剂2-3份、起雾填料6-8份、增塑剂5-10份、无机填料1-2份、有机填料1-2份、功能助剂2-3份、交联剂1-2份、催化剂0-1份、溶剂40-50份。本发明离型纸的淋膜层具有阻燃功能，从而对离型纸整体进行保护，防止高温融化和燃烧的现象，提高了生产的安全性。
Description
技术领域
本发明涉及一种离型纸，具体是一种具有阻燃功能的FPI离型纸。
背景技术
离型纸又称隔离纸、防粘纸，主要用于贴覆在胶带的表面用于保护胶带表面的胶粘剂层。现有的离型纸一般是在离型纸底纸层的表面淋膜一层淋膜层（采用的材料主要有聚乙烯），然后在淋膜层的表面涂布一层离型剂层（采用的材料主要为硅油）得到离型纸。离型纸应用广泛，如电子、医疗等领域，现有的离型纸特性单一，无法满足各种特殊的工作环境，如高温环境下，离型纸上的淋膜层容易达到熔点和燃点，从而造成安全隐患。
发明内容
本发明的目的在于提供一种具有阻燃功能的FPI离型纸，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种FPI专用离型纸，包括作为基材的白牛纸，所述白牛纸的两面均淋膜有均匀的淋膜层，而淋膜层上均匀的设有一层非硅离型层；所述淋膜层由以下重量份的原料组成：低密度PE30-40份、高密度PE30-40份、阻燃助剂6-8份、高流动性聚酰胺10-20份、润滑剂2-3份、起雾填料6-8份、增塑剂5-10份、无机填料1-2份、有机填料1-2份、功能助剂2-3份、交联剂1-2份、催化剂0-1份、溶剂40-50份。
作为本发明进一步的方案：所述淋膜层由以下重量份的原料组成：低密度PE35份、高密度PE35份、阻燃助剂7份、高流动性聚酰胺15份、润滑剂1.5份、起雾填料7份、增塑剂7.5份、无机填料1.5份、有机填料1.5份、功能助剂2.5份、交联剂1.5份、催化剂0.5份、溶剂45份。
作为本发明进一步的方案：所述FPI专用离型纸具体制备方法如下：
（1）称取淋膜层所需的原料，混合均匀后送入淋膜机，用淋膜机在白牛纸两面均匀的淋膜一层淋膜层；
（2）等淋膜层冷却后，在淋膜层的表面涂抹非硅离型层，非硅离型层为氨基甲酸酯聚离型涂层，即可得到FPI专用离型纸。
作为本发明进一步的方案：所述阻燃助剂为磷酸三聚氰胺、倍半硅氧烷和有机钛螯合物的复配物，其中磷酸三聚氰胺：倍半硅氧烷∶有机钛螯合物为2-3：6-8：3。
作为本发明进一步的方案：所述起雾填料为粒径为20纳米的氧化铝、氧化镁、氧化钙中的一种。
作为本发明进一步的方案：所述润滑剂为石蜡、白油、硬脂酸、硬脂酸盐中的一种。
作为本发明进一步的方案：所述功能助剂为含异丙氧基偶联剂、多官能团酯类化合物的一种或其组合。
与现有技术相比，本发明的有益效果是：本发明离型纸的淋膜层具有阻燃功能，从而对离型纸整体进行保护，防止高温融化和燃烧的现象，提高了生产的安全性。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
本发明实施例中，一种FPI专用离型纸，包括作为基材的白牛纸，所述白牛纸的两面均淋膜有均匀的淋膜层，而淋膜层上均匀的设有一层非硅离型层；所述淋膜层由以下重量份的原料组成：低密度PE30份、高密度PE30份、阻燃助剂6份、高流动性聚酰胺10份、润滑剂2份、起雾填料6份、增塑剂5份、无机填料1份、有机填料1份、功能助剂2份、交联剂1份、催化剂0份、溶剂40份。
所述阻燃助剂为磷酸三聚氰胺、倍半硅氧烷和有机钛螯合物的复配物，其中磷酸三聚氰胺：倍半硅氧烷∶有机钛螯合物为2：6：3。
所述起雾填料为粒径为20纳米的氧化铝、氧化镁、氧化钙中的一种；
所述润滑剂为石蜡、白油、硬脂酸、硬脂酸盐中的一种；
所述功能助剂为含异丙氧基偶联剂、多官能团酯类化合物的一种或其组合。
所述FPI专用离型纸具体制备方法如下：
（1）称取淋膜层所需的原料，混合均匀后送入淋膜机，用淋膜机在白牛纸两面均匀的淋膜一层淋膜层；
（2）等淋膜层冷却后，在淋膜层的表面涂抹非硅离型层，非硅离型层为氨基甲酸酯聚离型涂层，即可得到FPI专用离型纸。
实施例2
本发明实施例中，一种FPI专用离型纸，包括作为基材的白牛纸，所述白牛纸的两面均淋膜有均匀的淋膜层，而淋膜层上均匀的设有一层非硅离型层；所述淋膜层由以下重量份的原料组成：低密度PE35份、高密度PE35份、阻燃助剂7份、高流动性聚酰胺15份、润滑剂1.5份、起雾填料7份、增塑剂7.5份、无机填料1.5份、有机填料1.5份、功能助剂2.5份、交联剂1.5份、催化剂0.5份、溶剂45份。
所述阻燃助剂为磷酸三聚氰胺、倍半硅氧烷和有机钛螯合物的复配物，其中磷酸三聚氰胺：倍半硅氧烷∶有机钛螯合物为1.5：7：3。
所述起雾填料为粒径为20纳米的氧化铝、氧化镁、氧化钙中的一种；
所述润滑剂为石蜡、白油、硬脂酸、硬脂酸盐中的一种；
所述功能助剂为含异丙氧基偶联剂、多官能团酯类化合物的一种或其组合。
所述FPI专用离型纸具体制备方法如下：
（1）称取淋膜层所需的原料，混合均匀后送入淋膜机，用淋膜机在白牛纸两面均匀的淋膜一层淋膜层；
（2）等淋膜层冷却后，在淋膜层的表面涂抹非硅离型层，非硅离型层为氨基甲酸酯聚离型涂层，即可得到FPI专用离型纸。
实施例3
本发明实施例中，一种FPI专用离型纸，包括作为基材的白牛纸，所述白牛纸的两面均淋膜有均匀的淋膜层，而淋膜层上均匀的设有一层非硅离型层；所述淋膜层由以下重量份的原料组成：低密度PE40份、高密度PE40份、阻燃助剂8份、高流动性聚酰胺20份、润滑剂3份、起雾填料8份、增塑剂10份、无机填料2份、有机填料2份、功能助剂3份、交联剂2份、催化剂1份、溶剂50份。
所述阻燃助剂为磷酸三聚氰胺、倍半硅氧烷和有机钛螯合物的复配物，其中磷酸三聚氰胺：倍半硅氧烷∶有机钛螯合物为3：8：3。
所述起雾填料为粒径为20纳米的氧化铝、氧化镁、氧化钙中的一种；
所述润滑剂为石蜡、白油、硬脂酸、硬脂酸盐中的一种；
所述功能助剂为含异丙氧基偶联剂、多官能团酯类化合物的一种或其组合。
所述FPI专用离型纸具体制备方法如下：
（1）称取淋膜层所需的原料，混合均匀后送入淋膜机，用淋膜机在白牛纸两面均匀的淋膜一层淋膜层；
（2）等淋膜层冷却后，在淋膜层的表面涂抹非硅离型层，非硅离型层为氨基甲酸酯聚离型涂层，即可得到FPI专用离型纸。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (7)
1.一种FPI专用离型纸，包括作为基材的白牛纸，所述白牛纸的两面均淋膜有均匀的淋膜层，而淋膜层上均匀的设有一层非硅离型层，其特征在于；所述淋膜层由以下重量份的原料组成：低密度PE30-40份、高密度PE30-40份、阻燃助剂6-8份、高流动性聚酰胺10-20份、润滑剂2-3份、起雾填料6-8份、增塑剂5-10份、无机填料1-2份、有机填料1-2份、功能助剂2-3份、交联剂1-2份、催化剂0-1份、溶剂40-50份。
2.根据权利要求1所述的一种FPI专用离型纸，其特征在于，所述淋膜层由以下重量份的原料组成：低密度PE35份、高密度PE35份、阻燃助剂7份、高流动性聚酰胺15份、润滑剂1.5份、起雾填料7份、增塑剂7.5份、无机填料1.5份、有机填料1.5份、功能助剂2.5份、交联剂1.5份、催化剂0.5份、溶剂45份。
3.一种如权利要求1-2任一所述的FPI专用离型纸的制备方法，其特征在于，所述FPI专用离型纸具体制备方法如下：
（1）称取淋膜层所需的原料，混合均匀后送入淋膜机，用淋膜机在白牛纸两面均匀的淋膜一层淋膜层；
（2）等淋膜层冷却后，在淋膜层的表面涂抹非硅离型层，非硅离型层为氨基甲酸酯聚离型涂层，即可得到FPI专用离型纸。
4.根据权利要求1或2所述的一种FPI专用离型纸，其特征在于，所述阻燃助剂为磷酸三聚氰胺、倍半硅氧烷和有机钛螯合物的复配物，其中磷酸三聚氰胺：倍半硅氧烷∶有机钛螯合物为2-3：6-8：3。
5.根据权利要求1或2所述的一种FPI专用离型纸，其特征在于，所述起雾填料为粒径为20纳米的氧化铝、氧化镁、氧化钙中的一种。
6.根据权利要求1或2所述的一种FPI专用离型纸，其特征在于，所述润滑剂为石蜡、白油、硬脂酸、硬脂酸盐中的一种。
7.根据权利要求1或2所述的一种FPI专用离型纸，其特征在于，所述功能助剂为含异丙氧基偶联剂、多官能团酯类化合物的一种或其组合。