CN104963193A - 一种苎麻织物的染整工艺 - Google Patents

一种苎麻织物的染整工艺 Download PDF

Info

Publication number
CN104963193A
CN104963193A CN201510450558.4A CN201510450558A CN104963193A CN 104963193 A CN104963193 A CN 104963193A CN 201510450558 A CN201510450558 A CN 201510450558A CN 104963193 A CN104963193 A CN 104963193A
Authority
CN
China
Prior art keywords
fabric
dyeing
ramie fabric
agent
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510450558.4A
Other languages
English (en)
Inventor
陈秀珍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang Cheng Le Chemical Fibre Co Ltd
Original Assignee
Taicang Cheng Le Chemical Fibre Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang Cheng Le Chemical Fibre Co Ltd filed Critical Taicang Cheng Le Chemical Fibre Co Ltd
Priority to CN201510450558.4A priority Critical patent/CN104963193A/zh
Publication of CN104963193A publication Critical patent/CN104963193A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种苎麻织物的染整工艺,包括前处理、预定型、改性处理、染色、皂洗、固色、后整理、烘干、定型、轧光、收卷。本发明采用超声波进行预处理,同时增加了改性处理步骤;染色工序中,没有使用大量的碱性物质和无机盐,采用了天然染料,同时加入了松香粉作为固色剂,增强了固色效果,同时避免了环境污染,符合绿色环保的要求;并且采用蒙脱土对织物进行改性处理和阻燃处理,使得织物的阻燃性高;本发明在预定型、定型中都使用了抗变黄试剂,使得最终的织物不容易变黄;后处理中,对织物进行低温等离子体处理,然后使用亲水整理剂和壳聚糖进行处理,使得织物的亲水性好,容易去污,并且具有抗菌性。

Description

一种苎麻织物的染整工艺
技术领域
[0001] 本发明涉及一种苎麻织物的染整工艺。
背景技术
[0002] 纤维分为化学纤维和天然纤维,化学纤维是用天然高分子化合物或人工合成的高分子化合物为原料,经过制备纺丝原液、纺丝和后处理等工序制得的具有纺织性能的纤维。化学纤维具有耐光、耐磨、易洗易干、不霉烂、不被虫蛀等优点,广泛用于制造衣着织物、滤布、运输带、水龙带、绳索、渔网、电绝缘线、医疗缝线、轮胎帘子布和降落伞等。天然纤维是指自然界存在和生长的、具有纺织价值的纤维。
[0003] 苎麻纤维是一种天然纤维,其中间有沟状空腔,管壁多孔隙,并且细长、坚韧、质地轻、吸湿散湿快,因而透气性比棉纤维高三倍左右,同时苎麻纤维含有叮咛、嘧啶、嘌呤等元素,对金黄色葡萄球菌、绿脓杆菌、大肠杆菌等都有不同程度的抑制效果,具有防腐、防菌、防霉等功能,适宜纺织各类卫生保健用品,苎麻纤维具有良好的穿着服用性能,是一种优良的纺织原料。
[0004] 苎麻在染色过程中,为了降低环境污染,目前开始研宄采用天然染料进行染色,但是天然染料通常需要在较低温度下进行染色,并且天然染料的染色效果较差,染出的织物其固色度较低,为了提高固色度通常在染色过程中加入了大量的纯碱和无机盐,这给高含盐量的印染废水处理带来较大难度,如直接排放会破坏生态环境,导致土壤盐碱化,同时使用天然染料通常还会用到一些重金属离子作为媒染剂,不符合当前生态纺织品的要求,且重金属离子媒染后织物的色光大多变得暗淡,影响染色织物的鲜艳度和美观性。为了降低后续染色工艺的染色难度,通常在染色之前需要对纤维织物进行预处理,但是目前的预处理基本上都是采用保险粉、碳酸钠等碱性溶液进行高温预处理,对纤维的损伤较大。
发明内容
[0005] 发明目的:针对现有技术存在的上述问题,本发明的目的是提供一种苎麻织物的染整工艺。
[0006] 技术方案:为实现上述发明目的,本发明采用的技术方案如下:
一种苎麻织物的染整工艺,包括以下步骤:
(I)前处理:对苎麻织物进行前处理,具体为:用尿素1-1.5g/L,无磷除油剂4.5-5.5g/L,精练剂1-1.5 g/L,30%双氧水8-10 g/L,中温退浆酶4-6 g/L,在40°C的超声波水浴中进行超声处理1-2 min,浴比为30:1,超声波频率为45Hz,处理结束后重新注入清水洗涤2次,然后晾干;精练剂为广州庄杰化工有限公司生产的ZJ-CH58低温精炼剂。
[0007] (2)预定型:对芒麻织物进行预定型处理,定型时加入抗热变黄剂8-10 g/L,定型温度为150-160°C,车速为20-30m/min,超喂5-10% ;北京中纺化工股份有限公司生产的抗热黄变剂FK-161 ;
(3)改性处理:将定型后的苎麻织物放入水浴中进行改性处理,2,3-环氧丙基三甲基氯化铵20-30 g/L,蒙脱土 3-5 g/L,乙醇20-30 g/L,浴比为50:1,在50°C下改性处理60-80min,处理结束后重新注入清水洗涤2次,然后晾干;
(4)染色:将苎麻织物进行染色处理,具体为:室温下将纤维织物浸入染色机的清水中,然后向水浴中加入渗透剂1.5-2.5g/L,扩散剂DN 0.8-1.2g/L,高粱红色素1.5-2.5%(owf ),松香粉8-10% (owf ),蒙脱土 3-5 g/L,浴比40:1,并通过pH缓冲剂醋酸-醋酸钠将染液的PH值调节为7-7.5,循环加料化料20min,然后染色机升温,升温速度为1°C /min,温度升至85°C时,保温染色60-80min,然后染色机降温,降温速度为2V /min,当温度降至40°C时,将染料水排出并重新注入清水,用清水冲洗15min ;
(5)皂洗:将染色后的苎麻织物经过室温清水冲洗1min后,再用十二烷基硫酸钠Ig/L,聚乙烯吡咯烷酮 4.5 g/L, AE0-9 4.5 g/L,乙醇 10-20 g/L,浴比为 40:1,在 50_60°C下冲洗30 min,最后再用40_50°C的清水冲洗15min ;
(6)固色:将清洗后的苎麻织物放入固色液中进行固色,所述固色液含有食盐3-5g/L,松香粉3-5g/L,乙醇10-20 g/L,浴比为20:1,固色温度50_60°C,固色时间为30_40min,然后温度降低,40-50°C用清水冲洗15min,然后通过烘干机在80°C预烘4 min,然后在110°C焙烘3 min ;
(7)后整理:将苎麻织物进行后整理,具体为:
Ca)亲水性整理:将苎麻织物放入等离子体设备中进行等离子体处理,放电功率为100W,放电频率为13.56MHz,处理时间3min ;然后将处理后的织物浸入到处理液中进行亲水除菌处理,用亲水整理剂5-7 g/L,壳聚糖3-5 g/L,在30-40°C的水浴中处理20-30 min,浴比为20:1 ;亲水整理剂选用东莞市涵峰化工科技有限公司生产的亲水整理剂CF400 ;
(b)混合整理:将苎麻织物放入混合处理液中进行处理,用防缩防皱整理剂GFR-8 2-4g/L,柔软剂1-2 g/L,防紫外整理剂UV-BS 3-4 g/L,在30-40°C的水浴中处理20-30 min,浴比为20:1 ;防缩防皱整理剂GFR-8为南通斯恩特纺织科技有限公司生产;防紫外整理剂UV-BS为南通斯恩特纺织科技有限公司生产;
(c)阻燃整理:将苎麻织物放入阻燃处理液中进行处理,用2,3-环氧丙基三甲基氯化铵20-30 g/L,蒙脱土 3-5 g/L,异丙醇15-20 g/L,在50-70°C的水浴中处理40-60 min,浴比为30:1 ;
(8)烘干:将后整理后的苎麻织物放入烘干机中进行烘干处理,烘干温度100-110°C,机车速为65-70m/min ;
(9)定型:将烘干的苎麻织物进行定型处理,定型时加入抗热变黄剂8-10 g/L,抗酚变黄剂8-10 g/L,定型温度155-165°C,机车速为25_30m/min,超喂5_8% ;北京中纺化工股份有限公司生产的抗热黄变剂FK-161以及抗酚黄变剂FK-162 ;
(10)轧光:将定型后的苎麻织物放入轧光机进行轧光处理,乳光温度115-125°C,机车速为 20-25m/min ;
(11)收卷:将苎麻织物进行收卷。
[0008] 所述步骤I中的无磷除油剂为无磷中性去油灵TF-104M,中温退浆酶为中温退浆酶BF-7658。无磷中性去油灵TF-104M为浙江传化股份有限公司生产的传化牌去油灵TF-104M。
[0009] 所述步骤4中的渗透剂为渗透剂JFC,天然染料为高粱红色素。
[0010] 所述步骤7中的柔软剂为酯基季铵盐柔软剂。酯基季铵盐柔软剂可以选用韩国LG化学的EQ400或EQ200等柔软剂,对皮肤温和无害,使得苎麻织物织物具有柔软性和抗静电性,环保无害,柔软效果好。
[0011] 有益效果:与现有技术相比,本发明具有如下显著性有益效果:
1、本发明在前处理时采用超声波进行前处理,相较于常规的前处理,处理温度变低、时间变短,同时退浆率提高,白度提高,综合前处理效果更好,同时没有加入纯碱的碱性较强的物质,使得前处理液的PH值最终保持在中性左右,处理环境温和,对苎麻织物的损伤小,同时采用的去油剂为中心环保无磷除油剂,对环境的污染小,更为环保;
2、本发明在染色工序之前,采用2,3-环氧丙基三甲基氯化铵对纤维织物进行改性处理,从根本上对苎麻织物织物的性能进行改性处理,克服了其自身存在的一些缺陷,同时还增加了织物的上色率,降低了后续染色步骤的难度;经过该步骤处理后,其织物的上染率和固色率都大大提高;同时还加入了蒙脱土,起到阻燃作用,2,3-环氧丙基三甲基氯化铵也可以对蒙脱土进行改性,进一步提高阻燃性;
3、本发明在染色工序中,没有使用大量的碱性物质和无机盐,采用了天然染料,同时加入了松香粉作为固色剂,增强了固色效果,同时避免了环境污染,符合绿色环保的要求;染色过程中加入了壳聚糖,提高了抗菌性;同时还加入了蒙脱土,起到阻燃作用;
4、本发明在染色工序中,严格控制了升温降温速率,以及染色时间,使得纤维织物染色牢固度高、染色均匀、染色稳定性好;
5、本发明在染色后加入了固色工艺,固色工艺中采用了绿色环保的天然固色剂松香粉,避免了环境污染,进一步提高了苎麻织物的固色度;固色之前采用的皂洗工艺中,采用了十二烷基硫酸钠、聚乙烯吡咯烷酮以及AEO-9进行复配,防沾色、去浮色效果好,同时使得皂洗后染色织物耐洗色牢度、耐摩擦色牢度,尤其湿摩擦牢度都大幅度增强,同时还降低了 ;
6、本发明加入了后整理理工艺,改善和提高了织物的防缩防皱性能、色牢度、柔软度、抗紫外线性、抗菌性、抗阻燃等性能;同时在整理过程中,多种整理剂混合时候,各种选用的整理剂在发挥各自的作用的同时,还可以起到互相增强的作用,协同效应好;选用蒙脱土作为阻燃剂,同时加入了季铵盐对蒙脱土进行改性,使得阻燃效果更好,无环境污染;
7、本发明在预定型、定型中都使用了抗变黄试剂,使得最终的织物不容易变黄;本发明在后处理中,对织物进行低温等离子体处理,然后使用亲水整理剂和壳聚糖进行处理,使得织物的亲水性好,容易去污,并且具有抗菌性;
8、本发明进一步采用了轧光处理,使纤维织物的光洁平整,可进一步改善手感,使手感更柔软蓬松,同时保证缩水率满足要求;
9、本发明的预处理、染色、定型等几个工序的温度比较平稳,这样工艺条件跳跃性较小,工艺比较平稳,使得织物的最终性能比较稳定;
10、本发明的染色工艺高效、绿色环保、工艺简单,操作便捷,可推广使用。
具体实施方式
[0012] 下面结合实施例对本发明技术方案做进一步详细、完整地说明。
[0013] 实施例1 一种苎麻织物的染整工艺,包括以下步骤:
(1)前处理:对苎麻织物进行前处理,具体为:用尿素lg/L,无磷除油剂TF-104M 4.5g/L,精练剂I g/L,30%双氧水8 g/L,中温退浆酶BF-7658 4 g/L,在40°C的超声波水浴中进行超声处理I min,浴比为30:1,超声波频率为45Hz,处理结束后重新注入清水洗涤2次,然后晾干;
(2)预定型:对芒麻织物进行预定型处理,定型时加入抗热变黄剂FK-161 8 g/L,定型温度为150°C,车速为20m/min,超喂5% ;
(3)改性处理:将定型后的苎麻织物放入水浴中进行改性处理,2,3-环氧丙基三甲基氯化铵20 g/L,蒙脱土 3 g/L,乙醇20 g/L,浴比为50:1,在50°C下改性处理60min,处理结束后重新注入清水洗涤2次,然后晾干;
(4)染色:将苎麻织物进行染色处理,具体为:室温下将纤维织物浸入染色机的清水中,然后向水浴中加入渗透剂JFC 1.5g/L,扩散剂DN 0.8g/L,天然染料高粱红色素1.5%(owf ),松香粉8%(owf ),蒙脱土 3 g/L,浴比40:1,并通过pH缓冲剂醋酸-醋酸钠将染液的PH值调节为7-7.5,循环加料化料20min,然后染色机升温,升温速度为1°C /min,温度升至85°C时,保温染色60min,然后染色机降温,降温速度为2V /min,当温度降至40°C时,将染料水排出并重新注入清水,用清水冲洗15min ;
(5)皂洗:将染色后的苎麻织物经过室温清水冲洗1min后,再用十二烷基硫酸钠Ig/L,聚乙烯吡咯烷酮4.5 g/L, AE0-9 4.5 g/L,乙醇10 g/L,浴比为40:1,在50°C下冲洗30 min,最后再用40 °C的清水冲洗15min ;
(6)固色:将清洗后的苎麻织物放入固色液中进行固色,所述固色液含有食盐3g/L,松香粉3g/L,乙醇10 g/L,浴比为20:1,固色温度50 °C,固色时间为30min,然后温度降低,40°C用清水冲洗15min,然后通过烘干机在80°C预烘4 min,然后在110°C焙烘3 min ;
(7)后整理:将苎麻织物进行后整理,具体为:
Ca)亲水性整理:将苎麻织物放入等离子体设备中进行等离子体处理,放电功率为100W,放电频率为13.56MHz,处理时间3min ;然后将处理后的织物浸入到处理液中进行亲水除菌处理,用亲水整理剂CF400 5 g/L,壳聚糖3 g/L,在30°C的水浴中处理20 min,浴比为 20:1 ;
(b)混合整理:将苎麻织物放入混合处理液中进行处理,用防缩防皱整理剂GFR-8 2 g/L,柔软剂EQ200 lg/L,防紫外整理剂UV-BS 3 g/L,在30°C的水浴中处理20 min,浴比为20:1 ;
(c)阻燃整理:将苎麻织物放入阻燃处理液中进行处理,用2,3-环氧丙基三甲基氯化铵20 g/L,蒙脱土 3 g/L,异丙醇15 g/L,在50°C的水浴中处理40 min,浴比为30:1 ;
(8)烘干:将后整理后的苎麻织物放入烘干机中进行烘干处理,烘干温度100°C,机车速为 65m/min ;
(9)定型:将烘干的苎麻织物进行定型处理,定型时加入抗热变黄剂FK-161 8 g/L,抗酚变黄剂FK-162 8 g/L,定型温度155°C,机车速为25m/min,超喂5% ;
(10)轧光:将定型后的苎麻织物放入轧光机进行轧光处理,乳光温度115°C,机车速为20m/min ;
(11)收卷:将苎麻织物进行收卷。
[0014] 实施例2
一种苎麻织物的染整工艺,包括以下步骤:
(1)前处理:对苎麻织物进行前处理,具体为:用尿素1.2g/L,无磷除油剂TF-104M 5g/L,精练剂1.2 g/L,30%双氧水9 g/L,中温退浆酶BF-7658 5 g/L,在40°C的超声波水浴中进行超声处理1.5 min,浴比为30:1,超声波频率为45Hz,处理结束后重新注入清水洗涤2次,然后晾干;
(2)预定型:对芒麻织物进行预定型处理,定型时加入抗热变黄剂FK-161 9 g/L,定型温度为155°C,车速为25m/min,超喂8% ;
(3)改性处理:将定型后的苎麻织物放入水浴中进行改性处理,2,3-环氧丙基三甲基氯化铵25 g/L,蒙脱土 4g/L,乙醇25 g/L,浴比为50: 1,在50°C下改性处理70min,处理结束后重新注入清水洗涤2次,然后晾干;
(4)染色:将苎麻织物进行染色处理,具体为:室温下将纤维织物浸入染色机的清水中,然后向水浴中加入渗透剂JFC 2g/L,扩散剂DN lg/L,天然染料高粱红色素2% (owf),松香粉9% (owf),蒙脱土 4g/L,浴比40:1,并通过pH缓冲剂醋酸-醋酸钠将染液的pH值调节为7-7.5,循环加料化料20min,然后染色机升温,升温速度为1°C /min,温度升至85°C时,保温染色70min,然后染色机降温,降温速度为2°C /min,当温度降至40°C时,将染料水排出并重新注入清水,用清水冲洗15min ;
(5)皂洗:将染色后的苎麻织物经过室温清水冲洗1min后,再用十二烷基硫酸钠Ig/L,聚乙烯吡咯烷酮4.5 g/L, AE0-9 4.5 g/L,乙醇15 g/L,浴比为40:1,在55°C下冲洗30 min,最后再用45°C的清水冲洗15min ;
(6)固色:将清洗后的苎麻织物放入固色液中进行固色,所述固色液含有食盐4g/L,松香粉4g/L,乙醇15 g/L,浴比为20:1,固色温度55 °C,固色时间为35min,然后温度降低,45°C用清水冲洗15min,然后通过烘干机在80°C预烘4 min,然后在110°C焙烘3 min ;
(7)后整理:将苎麻织物进行后整理,具体为:
Ca)亲水性整理:将苎麻织物放入等离子体设备中进行等离子体处理,放电功率为100W,放电频率为13.56MHz,处理时间3min ;然后将处理后的织物浸入到处理液中进行亲水除菌处理,用亲水整理剂CF400 6 g/L,壳聚糖4 g/L,在35°C的水浴中处理25 min,浴比为20:1 ;
(b)混合整理:将苎麻织物放入混合处理液中进行处理,用防缩防皱整理剂GFR-8 3g/L,柔软剂EQ200 1.5g/L,防紫外整理剂UV-BS 3.5 g/L,在35°C的水浴中处理25 min,浴比为 20:1 ;
(c)阻燃整理:将苎麻织物放入阻燃处理液中进行处理,用2,3-环氧丙基三甲基氯化铵25g/L,蒙脱土 4 g/L,异丙醇18 g/L,在60°C的水浴中处理50 min,浴比为30:1 ;
(8)烘干:将后整理后的苎麻织物放入烘干机中进行烘干处理,烘干温度105°C,机车速为 68m/min ;
(9)定型:将烘干的苎麻织物进行定型处理,定型时加入抗热变黄剂FK-161 9 g/L,抗酚变黄剂FK-162 9 g/L,定型温度160°C,机车速为28m/min,超喂5-8% ;
(10)轧光:将定型后的苎麻织物放入轧光机进行轧光处理,乳光温度120°C,机车速为28m/min ; (11)收卷:将苎麻织物进行收卷。
[0015] 实施例3
一种苎麻织物的染整工艺,包括以下步骤:
(1)前处理:对苎麻织物进行前处理,具体为:用尿素1.5g/L,无磷除油剂TF-104M 5.5区/1,精练剂1.5 g/L,30%双氧水10 g/L,中温退浆酶BF-7658 6 g/L,在40°C的超声波水浴中进行超声处理2 min,浴比为30:1,超声波频率为45Hz,处理结束后重新注入清水洗涤2次,然后晾干;
(2)预定型:对芒麻织物进行预定型处理,定型时加入抗热变黄剂FK-161 10 g/L,定型温度为160°C,车速为30m/min,超喂10% ;
(3)改性处理:将定型后的苎麻织物放入水浴中进行改性处理,2,3-环氧丙基三甲基氯化钱30 g/L,蒙脱土5 g/L,乙醇30 g/L,浴比为50:1,在50°C下改性处理80min,处理结束后重新注入清水洗涤2次,然后晾干;
(4)染色:将苎麻织物进行染色处理,具体为:室温下将纤维织物浸入染色机的清水中,然后向水浴中加入渗透剂JFC 2.5g/L,扩散剂DN 1.2g/L,天然染料高粱红色素2.5%(owf),松香粉10% (owf),蒙脱土 5 g/L,浴比40:1,并通过pH缓冲剂醋酸-醋酸钠将染液的PH值调节为7-7.5,循环加料化料20min,然后染色机升温,升温速度为1°C /min,温度升至85°C时,保温染色60-80min,然后染色机降温,降温速度为2°C /min,当温度降至40°C时,将染料水排出并重新注入清水,用清水冲洗15min ;
(5)皂洗:将染色后的苎麻织物经过室温清水冲洗1min后,再用十二烷基硫酸钠Ig/L,聚乙烯吡咯烷酮4.5 g/L, AE0-9 4.5 g/L,乙醇20 g/L,浴比为40:1,在60°C下冲洗30 min,最后再用50°C的清水冲洗15min ;
(6)固色:将清洗后的苎麻织物放入固色液中进行固色,所述固色液含有食盐5g/L,松香粉5g/L,乙醇20 g/L,浴比为20:1,固色温度60 °C,固色时间为40min,然后温度降低,50°C用清水冲洗15min,然后通过烘干机在80°C预烘4 min,然后在110°C焙烘3 min ;
(7)后整理:将苎麻织物进行后整理,具体为:
Ca)亲水性整理:将苎麻织物放入等离子体设备中进行等离子体处理,放电功率为100W,放电频率为13.56MHz,处理时间3min ;然后将处理后的织物浸入到处理液中进行亲水除菌处理,用亲水整理剂CF400 7 g/L,壳聚糖5 g/L,在40°C的水浴中处理30 min,浴比为 20:1 ;
(b)混合整理:将苎麻织物放入混合处理液中进行处理,用防缩防皱整理剂GFR-8 4 g/L,柔软剂EQ200 2 g/L,防紫外整理剂UV-BS 4 g/L,在40°C的水浴中处理30 min,浴比为20:1 ;
(c)阻燃整理:将苎麻织物放入阻燃处理液中进行处理,用2,3-环氧丙基三甲基氯化铵30 g/L,蒙脱土 5 g/L,异丙醇20 g/L,在70°C的水浴中处理60 min,浴比为30:1;
(8)烘干:将后整理后的苎麻织物放入烘干机中进行烘干处理,烘干温度110°C,机车速为 70m/min ;
(9)定型:将烘干的苎麻织物进行定型处理,定型时加入抗热变黄剂FK-161 10 g/L,抗酚变黄剂FK-162 10 g/L,定型温度165°C,机车速为30m/min,超喂8% ;
(10)轧光:将定型后的苎麻织物放入轧光机进行轧光处理,乳光温度125°C,机车速为25m/min ;
(11)收卷:将苎麻织物进行收卷。
[0016] 本发明采用上述实施例的技术方案,在染色过程中,没有使用大量的碱性物质和无机盐,采用了天然染料,同时加入了松香粉作为固色剂,增强了固色效果,同时避免了环境污染,符合绿色环保的要求,最终使得染色后的苎麻织物织物其上染率在95%以上,大大超过了同类产品的上染率,其固色率也可以达到95%左右,固色效果好,同时染色后得到的纤维织物,还对其进行固色度和耐摩擦色牢度的测试,测试结果显示,其干、湿摩擦牢度达到4级以上,固色度达5级以上,同时在改性处理、染色工序中都加入了蒙脱土,起到阻燃作用,最后还增加了阻燃整理工序,使得最终织物的氧指数LOI为36%,这表明其阻燃性能高,并且本发明在预定型、定型中都使用了抗变黄试剂,使得最终的织物不容易变黄,同时还增加了防缩防皱处理,使得织物不易起皱;后处理中,对织物进行低温等离子体处理,然后使用亲水整理剂和壳聚糖进行处理,使得织物的亲水性好,容易去污,并且具有抗菌性;同时柔软性、抗紫外线性等性能都较好。
[0017] 最后需要在此指出的是:以上仅是本发明的部分优选实施例,不能理解为对本发明保护范围的限制,本领域的技术人员根据本发明的上述内容作出的一些非本质的改进和调整均属于本发明的保护范围。

Claims (4)

1.一种苎麻织物的染整工艺,其特征在于:包括以下步骤: (1)前处理:对苎麻织物进行前处理,具体为:用尿素1-1.5g/L,无磷除油剂4.5-5.5g/L,精练剂1-1.5 g/L,30%双氧水8-10 g/L,中温退浆酶4-6 g/L,在40°C的超声波水浴中进行超声处理1-2 min,浴比为30:1,超声波频率为45Hz,处理结束后重新注入清水洗涤2次,然后晾干; (2)预定型:对芒麻织物进行预定型处理,定型时加入抗热变黄剂8-10 g/L,定型温度为 150-160°C,车速为 20-30m/min,超喂 5-10% ; (3)改性处理:将定型后的苎麻织物放入水浴中进行改性处理,2,3-环氧丙基三甲基氯化铵20-30 g/L,蒙脱土 3-5 g/L,乙醇20-30 g/L,浴比为50:1,在50°C下改性处理60-80min,处理结束后重新注入清水洗涤2次,然后晾干; (4)染色:将苎麻织物进行染色处理,具体为:室温下将纤维织物浸入染色机的清水中,然后向水浴中加入渗透剂1.5-2.5g/L,扩散剂DN 0.8-1.2g/L,高粱红色素1.5-2.5%(owf ),松香粉8-10% (owf ),蒙脱土 3-5 g/L,浴比40:1,并通过pH缓冲剂醋酸-醋酸钠将染液的PH值调节为7-7.5,循环加料化料20min,然后染色机升温,升温速度为1°C /min,温度升至85°C时,保温染色60-80min,然后染色机降温,降温速度为2V /min,当温度降至40°C时,将染料水排出并重新注入清水,用清水冲洗15min ; (5)皂洗:将染色后的苎麻织物经过室温清水冲洗1min后,再用十二烷基硫酸钠Ig/L,聚乙烯吡咯烷酮 4.5 g/L, AE0-9 4.5 g/L,乙醇 10-20 g/L,浴比为 40:1,在 50_60°C下冲洗30 min,最后再用40_50°C的清水冲洗15min ; (6)固色:将清洗后的苎麻织物放入固色液中进行固色,所述固色液含有食盐3-5g/L,松香粉3-5g/L,乙醇10-20 g/L,浴比为20:1,固色温度50_60°C,固色时间为30_40min,然后温度降低,40-50°C用清水冲洗15min,然后通过烘干机在80°C预烘4 min,然后在110°C焙烘3 min ; (7)后整理:将苎麻织物进行后整理,具体为: Ca)亲水性整理:将苎麻织物放入等离子体设备中进行等离子体处理,放电功率为100W,放电频率为13.56MHz,处理时间3min ;然后将处理后的织物浸入到处理液中进行亲水除菌处理,用亲水整理剂5-7 g/L,壳聚糖3-5 g/L,在30-40°C的水浴中处理20-30 min,浴比为20:1 ; (b)混合整理:将苎麻织物放入混合处理液中进行处理,用防缩防皱整理剂GFR-8 2-4g/L,柔软剂1-2 g/L,防紫外整理剂UV-BS 3-4 g/L,在30-40°C的水浴中处理20-30 min,浴比为20:1 ; (c)阻燃整理:将苎麻织物放入阻燃处理液中进行处理,用2,3-环氧丙基三甲基氯化铵20-30 g/L,蒙脱土 3-5 g/L,异丙醇15-20 g/L,在50-70°C的水浴中处理40-60 min,浴比为30:1 ; (8)烘干:将后整理后的苎麻织物放入烘干机中进行烘干处理,烘干温度100-110°C,机车速为65-70m/min ; (9)定型:将烘干的苎麻织物进行定型处理,定型时加入抗热变黄剂8-10 g/L,抗酚变黄剂8-10 g/L,定型温度155-165°C,机车速为25_30m/min,超喂5_8% ; (10)轧光:将定型后的苎麻织物放入轧光机进行轧光处理,乳光温度115-125°C,机车速为 20-25m/min ; (11)收卷:将苎麻织物进行收卷。
2.根据权利要求1所述的苎麻织物的染整工艺,其特征在于:所述步骤I中的无磷除油剂为无磷中性去油灵TF-104M,中温退浆酶为中温退浆酶BF-7658。
3.根据权利要求1所述的苎麻织物的染整工艺,其特征在于:所述步骤4中的渗透剂为渗透剂JFC。
4.根据权利要求1所述的苎麻织物的染整工艺,其特征在于:所述步骤7中的柔软剂为酯基季铵盐柔软剂。
CN201510450558.4A 2015-07-28 2015-07-28 一种苎麻织物的染整工艺 Pending CN104963193A (zh)