CN104746365A - 一种真丝织物的无盐染色工艺 - Google Patents

一种真丝织物的无盐染色工艺 Download PDF

Info

Publication number
CN104746365A
CN104746365A CN201510154318.XA CN201510154318A CN104746365A CN 104746365 A CN104746365 A CN 104746365A CN 201510154318 A CN201510154318 A CN 201510154318A CN 104746365 A CN104746365 A CN 104746365A
Authority
CN
China
Prior art keywords
silk fabric
real silk
temperature
dyeing
salt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510154318.XA
Other languages
English (en)
Inventor
顾晓平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TAICANG BAOMING CHEMICAL FIBER Co Ltd
Original Assignee
TAICANG BAOMING CHEMICAL FIBER Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TAICANG BAOMING CHEMICAL FIBER Co Ltd filed Critical TAICANG BAOMING CHEMICAL FIBER Co Ltd
Priority to CN201510154318.XA priority Critical patent/CN104746365A/zh
Publication of CN104746365A publication Critical patent/CN104746365A/zh
Pending legal-status Critical Current

Abstract

本发明提供给了一种真丝织物的无盐染色工艺,包括前处理、预定型、改性处理、染色、皂洗、固色、后整理、烘干、定型、轧光、收卷。本发明用阳离子改性剂预先对织物进行改性处理,增加了织物的上色率,降低了后续染色步骤的难度;染色工序中,没有使用元明粉或食盐等无机盐,降低了污染;加入了皂洗及固色工艺,使得染色牢固度好,固色工艺中采用了绿色环保无醛的TCD-R,固色后对纤维逐步进行干燥,使得纤维的牢固度大大提高;加入了后整理工艺,改善和提高了织物的色牢度、柔软度,减轻织物的粗糙感,使织物蓬松而富有弹性。

Description

—种真丝织物的无盐染色工艺
技术领域
[0001 ] 本发明涉及一种真丝织物的无盐染色工艺。
背景技术
[0002] 纤维分为化学纤维和天然纤维,其中化学纤维是用天然高分子化合物或人工合成的高分子化合物为原料,经过制备纺丝原液、纺丝和后处理等工序制得的具有纺织性能的纤维。具有耐光、耐磨、易洗易干、不霉烂、不被虫蛀等优点。广泛用于制造衣着织物、滤布、运输带、水龙带、绳索、渔网、电绝缘线、医疗缝线、轮胎帘子布和降落伞等。天然纤维是指自然界存在和生长的、具有纺织价值的纤维,真丝就属于一种天然纤维,确切的的说是一种天然的蛋白质纤维,由于其具有良好的吸湿、透气性能,有护肤保健作用等性能,因此也广泛的应用于衣物制造纺织领域。
[0003] 染色是纤维织物的一个重要处理工艺,在染色工艺中需要用到各种染料。真丝织物传统的染色方法是采用酸性染料进行染色,随着国内外市场对真丝织物色牢度的要求愈来愈高,酸性染料染色往往达不到要求。活性染料色泽鲜艳、使用方便、色谱较全,是唯一的一类能与真丝纤维以共价键结合的反应性染料,用其染真丝织物色牢度可达4级以上。但是由于活性染料直接性较低,且活性基团较容易水解,导致固色率不高,尤其是在染色过程中必须加入大量的中性电解质如元明粉或食盐进行促染,这样不仅造成了大量资源浪费,而且增加了污水处理的成本。
[0004] 因此,为了经济的发展,也为了响应国家的节能、减排、绿色环保的号召,有必要开发出一种真丝织物的无盐染色工艺。
发明内容
[0005] 发明目的:本发明的目的是为了解决现有技术的不足,提供一种真丝织物的无盐染色工艺。
[0006] 技术方案:为了实现以上目的,本发明的一种真丝织物的无盐染色工艺,包括以下步骤:
(I)前处理:对真丝织物进行前处理,具体为:用尿素1-1.5g/L,无磷除油剂4.5-5.5g/L,十二烷基苯磺酸钠1-1.5 g/L,60%双氧水2-3 g/L,氧化退浆剂OS 0.8-1.2 g/L,在30°C水浴中处理2-3 min,浴比为20: 1,水浴然后升温,升温速度为2.5°C /min,当温度升至90°C后,在此温度下保持30-40min,然后水浴温度以1.5°C /min的速度降温,当温度降至60°C时,将处理后的废水排出,然后重新注入清水在室温下冲洗至洗液为中性,最后晾干;此步骤中采用了无磷除油剂进行除油,采用尿素这一碱性较温和的碱性物质,同时加入了双氧水、氧化退浆剂OS、表面活性剂十二烷基苯磺酸钠,其中氧化退浆剂OS和双氧水可以发生协同作用,改善预处理效果,在这些物质的协同作用下,对杂质的处理效果好,同时条件温和,对纤维织物的伤害较小,同时,环保无毒,产生的废水不含磷,不会造成富营养化等环境危害;其中,氧化退浆剂OS选自南通斯恩特纺织科技有限公司生产的氧化退浆剂OS ; (2)预定型:对真丝织物通过预定型机作预定型处理,预定型过程中定型温度为160-170°C,车速为 20-30m/min,超喂 5-10% ;
(3)改性处理:将定型后的真丝织物浸入到含有阳离子活性改性剂的改性液中进行改性处理,具体为使用的改性液为:改性剂3-8% (owf),碳酸钠3-9 g/L,浴比50:1,在50-70°C的水浴中浸泡处理30-60 min,然后水洗,最后在100°C烘干即可;改性剂CY-210是一种具有反应性官能团的阳离子型化合物,可以与真丝纤维上的羟基和氨基发生反应,降低真丝织物表面负电荷,减小真丝纤维与染料间的静电斥力,从而使得真丝的Κ/S值增大,使得经过改性处理后的真丝织物,其染色Κ/S值增大,使得染料的上染率和固色率大大提高,同时,改性剂CY-210也是一种环保的试剂,对环境无污染,在改性液中加入了碳酸钠,碳酸钠可以进一步增强改性剂与真丝纤维之间的反应活性,从而进一步增强改性效果,使得最终染料的上染率和固色率进一步提高,本发明使用的改性剂CY-210是广州创越化工有限公司生产的阳离子改性剂;
(4)染色:将改性处理后的真丝织物进行染色处理,具体为:室温下将纤维织物浸入染色机的清水中,然后向水浴中加入渗透剂1.5-2.5g/L,扩散剂DN 0.8-1.2g/L,硫酸钠6_8g/L,活性染料2-3% (owf),壳聚糖3-4% (owf ),浴比50:1,并通过pH缓冲剂醋酸-醋酸钠将染液的PH值调节为4-5,循环加料化料20min,然后染色机升温,升温速度为1°C /min,温度升至55-65°C时,保温染色40-60min,然后染色机降温,降温速度为2°C /min,当温度降至30°C时,将染料水排出并重新注入清水,用清水冲洗15min ;本步骤加入了壳聚糖,壳聚糖可以增加织物的上染率,使得染色效果好,同时,壳聚糖环保无毒,对环境无污染,降低了环境污染;加入的硫酸钠,可以起到固色的作用,无毒,同时也在一定程度上起到了媒染剂的作用,并且不含重金属离子;同时,在此步骤还加入了渗透剂和扩散剂等助剂,在这些助剂的作用下,进一步增强了染色效果及效率;另外,在此步骤中为了更好地控制染色需求的精确PH值,加入了 pH缓冲剂进行调节控制,这样可以精确控制pH值,使染色效果最佳;本步骤中可以发现,没有加入一些元明粉或食盐之类的无机盐电解质,这样,大大降低了环境污染,属于一种无盐染色工艺;
(5)皂洗:将染色后的真丝织物经过室温清水冲洗1min后,再用低温皂洗剂lg/L,浴比为20:1,在60-70 °C下冲洗15 min,最后再用40-50 °C的清水冲洗15min ;
(6)固色:将清洗后的真丝织物放入固色液中进行固色,所述固色液含有食盐3-5g/L,固色剂2-4g/L,50%的冰醋酸lg/L,浴比为20:1,固色温度60-70 °C,固色时间为30-40min,然后温度降低,40-50°C用清水冲洗15min,然后通过烘干机在80°C预烘4 min,然后在110 °C焙烘3 min ;
(7)后整理:将真丝织物放入柔软处理液中进行柔软处理,分两步进行,具体为:
(a)用含有纤维素酶2% (owf),通过pH缓冲剂醋酸-醋酸钠将pH值调节为4.8-5时,浴比为20:1的处理液中进行处理,温度为45-55°C,反应20-30min,然后水洗;该纤维素酶为北京双螺旋微生物培养基制品厂生产的纤维素酶;
(b)经过步骤a后,再将真丝织物放入防紫外线处理液中进行处理,用防紫外整理剂UV-BS 3-4 g/L,在30-40°C的水浴中处理20-30 min,浴比为20:1 ;增加了真丝织物的防紫外线性,显著降低整理织物的紫外线透过率,提高紫外遮挡系数,此整理剂为南通斯恩特纺织科技有限公司生产; (C)经过步骤b后,再将真丝织物放入混合处理液中进行处理,用柔软剂1-2 g/L,抗菌整理剂1-2 g/L,防缩防皱整理剂GFR-8 0.8-1.2 g/L,在30-40°C的水浴中处理20-30min,浴比为20:1 ;经过三步后整理,使得真丝织物织物的整体性能更好;防缩防皱整理剂GFR-8为南通斯恩特纺织科技有限公司生产,可以与其他整理剂如柔软剂等拼混使用,
(8)烘干:将柔软处理后的真丝织物放入烘干机中进行烘干处理,烘干温度100-110 °C,机车速为 65-70m/min ;
(9)定型:将烘干的真丝织物放入定型机中进行定型处理,定型温度155-165Ό,机车速为 25-30m/min,超喂 5-8% ;
(10)轧光:将定型后的真丝织物放入轧光机进行轧光处理,乳光温度115-125°C,机车速为 20-25m/min ;
(11)收卷:将真丝织物进行收卷。
[0007] 所述步骤I中的无磷除油剂为无磷中性去油灵TF-104M。本发明采用的无磷中性去油灵TF-104M为浙江传化股份有限公司生产的传化牌去油灵TF-104M,分散、乳化、润湿、渗透性好,泡沫低、去污力强,同时兼有退浆、增白、防止染料凝聚,确保染色匀艳等独特功能,并且不损伤纤维,对真丝织物织物无伤害性。
[0008] 所述步骤3中的改性剂为阳离子改性剂CY-210。该改性剂是一种具有反应性官能团的化合物,可以增加织物的固色性,同时还可以使得织物具有柔和的手感和鲜艳的色光,使得染色效果更好。
[0009] 所述步骤4中的渗透剂为渗透剂JFC。
[0010] 所述步骤4中的活性染料为活性红L-S、活性黄L-3R、活性艳蓝L-R中的一种。该活性染料可以使用市售的上述常规活性染料即可。
[0011] 所述步骤5中的低温皂洗剂为JY-1103D皂洗剂。低温皂洗剂JY-1103D是丙烯酸-乙烯吡络烷酮-马来酸酐三元共聚产物,产品具有良好的胶体特性。采用此皂洗剂进行皂洗时,在60-700C条件下,聚乙烯吡络烷酮结构中的内酰胺结构使其与染料分子中的羟基、氨基和羧基有很强的结合力,与染料形成络合物,防止染料反沾到织物上。
[0012] 所述步骤6中的固色剂为T⑶-R。本发明采用的固色剂为广东德美精细化工股份有限公司生产的无醛固色剂T⑶-R,环保无害,固色效果好。
[0013] 所述步骤7中的柔软剂为酯基季铵盐柔软剂,抗菌整理剂为抗菌整理剂GQ-100。本发明采用的酯基季铵盐柔软剂可以选用韩国LG化学的EQ400或EQ200等柔软剂,对皮肤温和无害,使得真丝织物织物具有柔软性和抗静电性,环保无害,柔软效果好。抗菌整理剂GQ-100是南通斯恩特纺织科技有限公司生产的抗菌整理剂,该试剂比仅仅环保无毒、无刺激、无过敏反应,在抗菌的作用之外还兼具柔软、抗静电等作用,与柔软剂合用,进一步增强了柔软效果。
[0014] 有益效果:本发明提供的真丝织物的无盐染色工艺与现有技术相比,具有以下优占.V.1、本发明在前处理过程中严格控制了温度、时间及助剂的用量,同时没有加入纯碱的碱性较强的物质,使得前处理液的PH值最终保持在中性左右,处理环境温和,对真丝织物的损伤小,同时采用的去油剂为中心环保无磷除油剂,对环境的污染小,更为环保;
2、本发明在染色工序之前,增加了改性处理步骤,通过改性剂的使用从根本上对真丝织物的性能进行改性处理,增加了织物的上色率,降低了后续染色步骤的难度;
3、本发明在染色工序中,加入了壳聚糖,无毒环保,增强了染色效果及效率;染色过程中PH值的控制通过pH值缓冲剂进行控制,使得染色的酸碱度环境可以进一步优化,染色效果好;染色过程中温度没有超过70°C,属于较低温度的染色工艺,节约了能源,降低了能耗;
4、本发明在染色工序中,严格控制了升温降温速率,以及染色时间,使得纤维织物染色牢固度高、染色均匀、染色稳定性好;
5、本发明在在染色后进行皂洗,除去纤维织物表面的浮色,使其色光纯正,同时还确保染色牢度;
6、本发明在染色后加入了固色工艺,固色工艺中采用了绿色环保无醛的T⑶-R,固色后对真丝织物逐步进行干燥,使得真丝织物的牢固度大大提高;
7、本发明加入了后整理理工艺,改善和提高了织物的色牢度、柔软度、抗紫外线性、抗菌性等性能,同时在处理中采用先用纤维素酶进行处理,再用整理剂进行整理,比起通常的一步处理,其处理效果更为优越,同时在整理过程中,多种整理剂混合时候,各种选用的整理剂在发挥各自的作用的同时,还可以起到互相增强的作用,协同效应好;
8、本发明进一步采用了轧光处理,使纤维织物的光洁平整,可进一步改善手感,使手感更柔软蓬松,同时保证缩水率满足要求;
9、本发明的预处理、染色、定型等几个工序的温度比较平稳,这样工艺条件跳跃性较小,工艺比较平稳,使得织物的最终性能比较稳定;
10、本发明的染色工艺高效、绿色环保、工艺简单,操作便捷,可推广使用。
具体实施方式
[0015] 以下结合具体的实施例对本发明进行详细说明,但同时说明本发明的保护范围并不局限于本实施例的具体范围,基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
[0016] 实施例1
一种真丝织物的无盐染色工艺,包括以下步骤:
(1)前处理:对真丝织物进行前处理,具体为:用尿素lg/L,无磷中性去油灵TF-104M
4.5 g/L,十二烷基苯磺酸钠I g/L,60%双氧水2 g/L,氧化退浆剂OS 0.8 g/L,在30°C水浴中处理2-3 min,浴比为20:1,水浴然后升温,升温速度为2.5°C /min,当温度升至90°C后,在此温度下保持30-40min,然后水浴温度以1.5 °C /min的速度降温,当温度降至60°C时,将处理后的废水排出,然后重新注入清水在室温下冲洗至洗液为中性,最后晾干;
(2)预定型:对真丝织物通过预定型机作预定型处理,预定型过程中定型温度为160 0C,车速为 20m/min,超喂 5% ;
(3)改性处理:将定型后的真丝织物浸入到含有阳离子活性改性剂的改性液中进行改性处理,具体为使用的改性液为:改性剂CY-210 3% (owf ),碳酸钠3 g/L,浴比50:1,在50°C的水浴中浸泡处理30 min,然后水洗,最后在100°C烘干即可;
(4)染色:将改性处理后的真丝织物进行染色处理,具体为:室温下将纤维织物浸入染色机的清水中,然后向水浴中加入渗透剂JFC 1.5g/L,扩散剂DN 0.8g/L,硫酸钠6g/L,活性染料活性红L-S 2% (owf),壳聚糖3% (owf),浴比50:1,并通过pH缓冲剂醋酸-醋酸钠将染液的PH值调节为4,循环加料化料20min,然后染色机升温,升温速度为1°C /min,温度升至55°C时,保温染色40min,然后染色机降温,降温速度为2 V /min,当温度降至30°C时,将染料水排出并重新注入清水,用清水冲洗15min ;
(5)皂洗:将染色后的真丝织物经过室温清水冲洗1min后,再用低温皂洗剂JY-1103D lg/L,浴比为20:1,在601下冲洗15 min,最后再用40°C的清水冲洗15min ;
(6)固色:将清洗后的真丝织物放入固色液中进行固色,所述固色液含有食盐3g/L,固色剂TCD-R 2g/L,50%的冰醋酸lg/L,浴比为20:1,固色温度60°C,固色时间为30min,然后温度降低,40-°C用清水冲洗15min,然后通过烘干机在80°C预烘4 min,然后在110°C焙烘 3 min ;
(7)后整理:将真丝织物放入柔软处理液中进行柔软处理,分两步进行,具体为:
(a)用含有纤维素酶2% (owf),通过pH缓冲剂醋酸-醋酸钠将pH值调节为4.8时,浴比为20:1的处理液中进行处理,温度为45°C,反应20min,然后水洗;
(b)经过步骤a后,再将真丝织物放入防紫外线处理液中进行处理,用防紫外整理剂UV-BS 3g/L,在30°C的水浴中处理20min,浴比为20:1 ;
(c)经过步骤b后,再将真丝织物放入混合处理液中进行处理,用柔软剂EQ200 I g/L,抗菌整理剂GQ-100 I g/L,防缩防皱整理剂GFR-8 0.8 g/L,在30°C的水浴中处理20 min,浴比为20:1 ;
(8)烘干:将柔软处理后的真丝织物放入烘干机中进行烘干处理,烘干温度100°C,机车速为65m/min ;
(9)定型:将烘干的真丝织物放入定型机中进行定型处理,定型温度155°C,机车速为25m/min,超喂 5% ;
(10)轧光:将定型后的真丝织物放入轧光机进行轧光处理,乳光温度115°C,机车速为20m/min ;
(11)收卷:将真丝织物进行收卷。
[0017] 实施例2
一种真丝织物的无盐染色工艺,包括以下步骤:
(1)前处理:对真丝织物进行前处理,具体为:用尿素1.2g/L,无磷中性去油灵TF-104M 5 g/L,十二烷基苯磺酸钠1.2 g/L,60%双氧水2.5 g/L,氧化退浆剂OS lg/L,在30°C水浴中处理2-3 min,浴比为20: 1,水浴然后升温,升温速度为2.5°C /min,当温度升至90°C后,在此温度下保持35min,然后水浴温度以1.5°C /min的速度降温,当温度降至60°C时,将处理后的废水排出,然后重新注入清水在室温下冲洗至洗液为中性,最后晾干;
(2)预定型:对真丝织物通过预定型机作预定型处理,预定型过程中定型温度为165 0C,车速为 25m/min,超喂 8% ;
(3)改性处理:将定型后的真丝织物浸入到含有阳离子活性改性剂的改性液中进行改性处理,具体为使用的改性液为:改性剂CY-210 5.5% (owf),碳酸钠6 g/L,浴比50:1,在60°C的水浴中浸泡处理45 min,然后水洗,最后在100°C烘干即可;
(4)染色:将改性处理后的真丝织物进行染色处理,具体为:室温下将纤维织物浸入染色机的清水中,然后向水浴中加入渗透剂JFC 2g/L,扩散剂DN lg/L,硫酸钠7 g/L,活性染料活性黄L-3R 2.5%(owf),壳聚糖3.5%(owf),浴比50:1,并通过pH缓冲剂醋酸-醋酸钠将染液的PH值调节为4.5,循环加料化料20min,然后染色机升温,升温速度为1°C /min,温度升至60°C时,保温染色50min,然后染色机降温,降温速度为2°C/min,当温度降至30°C时,将染料水排出并重新注入清水,用清水冲洗15min ;
(5)皂洗:将染色后的真丝织物经过室温清水冲洗1min后,再用低温皂洗剂JY-1103D lg/L,浴比为20:1,在651下冲洗15 min,最后再用45°C的清水冲洗15min ;
(6)固色:将清洗后的真丝织物放入固色液中进行固色,所述固色液含有食盐4g/L,固色剂TCD-R 3g/L,50%的冰醋酸lg/L,浴比为20:1,固色温度65°C,固色时间为35min,然后温度降低,45°C用清水冲洗15min,然后通过烘干机在80°C预烘4 min,然后在110°C焙烘
3 min ;
(7)后整理:将真丝织物放入柔软处理液中进行柔软处理,分两步进行,具体为:
(a)用含有纤维素酶2% (owf),通过pH缓冲剂醋酸-醋酸钠将pH值调节为4.9时,浴比为20:1的处理液中进行处理,温度为50°C,反应25min,然后水洗;
(b)经过步骤a后,再将真丝织物放入防紫外线处理液中进行处理,用防紫外整理剂UV-BS 3.5 g/L,在35°C的水浴中处理25 min,浴比为20:1;
(c)经过步骤b后,再将真丝织物放入混合处理液中进行处理,用柔软剂EQ200 1.5 g/L,抗菌整理剂GQ-100 1.5 g/L,防缩防皱整理剂GFR-8 lg/L,在35°C的水浴中处理25min,浴比为20:1 ;
(8)烘干:将柔软处理后的真丝织物放入烘干机中进行烘干处理,烘干温度105°C,机车速为68m/min ;
(9)定型:将烘干的真丝织物放入定型机中进行定型处理,定型温度160°C,机车速为28m/min,超喂 6% ;
(10)轧光:将定型后的真丝织物放入轧光机进行轧光处理,乳光温度115-125°C,机车速为 22m/min ;
(11)收卷:将真丝织物进行收卷。
[0018] 实施例3
一种真丝织物的无盐染色工艺,包括以下步骤:
(1)前处理:对真丝织物进行前处理,具体为:用尿素1.5g/L,无磷中性去油灵TF-104M 5.5 g/L,十二烷基苯磺酸钠1.5 g/L,60%双氧水3 g/L,氧化退浆剂OS 1.2 g/L,在30°C水浴中处理2-3 min,浴比为20:1,水浴然后升温,升温速度为2.5°C /min,当温度升至90°C后,在此温度下保持40min,然后水浴温度以1.5°C /min的速度降温,当温度降至60°C时,将处理后的废水排出,然后重新注入清水在室温下冲洗至洗液为中性,最后晾干;
(2)预定型:对真丝织物通过预定型机作预定型处理,预定型过程中定型温度为170 0C,车速为 30m/min,超喂 10% ;
(3)改性处理:将定型后的真丝织物浸入到含有阳离子活性改性剂的改性液中进行改性处理,具体为使用的改性液为:改性剂CY-210 8% (owf ),碳酸钠9 g/L,浴比50:1,在70°C的水浴中浸泡处理60 min,然后水洗,最后在100°C烘干即可;
(4)染色:将改性处理后的真丝织物进行染色处理,具体为:室温下将纤维织物浸入染色机的清水中,然后向水浴中加入渗透剂JFC 2.5g/L,扩散剂DN 1.2g/L,硫酸钠8 g/L,活性染料活性艳蓝L-R 3% (owf),壳聚糖4% (owf),浴比50:1,并通过pH缓冲剂醋酸-醋酸钠将染液的PH值调节为5,循环加料化料20min,然后染色机升温,升温速度为1°C /min,温度升至65°C时,保温染色60min,然后染色机降温,降温速度为2°C/min,当温度降至30°C时,将染料水排出并重新注入清水,用清水冲洗15min ;
(5)皂洗:将染色后的真丝织物经过室温清水冲洗1min后,再用低温皂洗剂JY-1103D lg/L,浴比为20:1,在70°0下冲洗15 min,最后再用50°C的清水冲洗15min ;
(6)固色:将清洗后的真丝织物放入固色液中进行固色,所述固色液含有食盐5g/L,固色剂TCD-R 4g/L,50%的冰醋酸lg/L,浴比为20:1,固色温度70°C,固色时间为40min,然后温度降低,50°C用清水冲洗15min,然后通过烘干机在80°C预烘4 min,然后在110°C焙烘 3 min ;
(7)后整理:将真丝织物放入柔软处理液中进行柔软处理,分两步进行,具体为:
(a)用含有纤维素酶2% (owf ),通过pH缓冲剂醋酸-醋酸钠将pH值调节为5时,浴比为20:1的处理液中进行处理,温度为55°C,反应30min,然后水洗;
(b)经过步骤a后,再将真丝织物放入防紫外线处理液中进行处理,用防紫外整理剂UV-BS 4 g/L,在40°C的水浴中处理30 min,浴比为20:1;
(c)经过步骤b后,再将真丝织物放入混合处理液中进行处理,用柔软剂EQ200 2 g/L,抗菌整理剂GQ-100 2 g/L,防缩防皱整理剂GFR-8 1.2 g/L,在40°C的水浴中处理30 min,浴比为20:1 ;
(8)烘干:将柔软处理后的真丝织物放入烘干机中进行烘干处理,烘干温度110°C,机车速为70m/min ;
(9)定型:将烘干的真丝织物放入定型机中进行定型处理,定型温度165°C,机车速为30m/min,超喂 8% ;
(10)轧光:将定型后的真丝织物放入轧光机进行轧光处理,乳光温度125°C,机车速为25m/min ;
(11)收卷:将真丝织物进行收卷。
[0019] 本发明采用上述实施例的技术方案,在染色过程中,避免了大量的无机盐的使用,并且真丝织物织物其上染率在90%以上,大大超过了同类产品的上染率,其固色率可以在80%以上,固色效果好,同时染色后得到的纤维织物,还对其进行皂洗色牢度和耐摩擦色牢度的测试,测试结果显示,其干、湿摩擦牢度、皂洗牢度均较好,均达4级以上,同时其抗菌性、柔软性、抗紫外线性等性能都较好。
[0020] 由此可见,采用本发明的技术方案的染色方法得到的纤维织物,其更方各方面性能都较为优越。
[0021] 上述实施例只为说明本发明的技术构思及特点,其目的是让熟悉该技术领域的技术人员能够了解本发明的内容并据以实施,并不能以此来限制本发明的保护范围。凡根据本发明精神实质所作出的等同变换或修饰,都应涵盖在本发明的保护范围之内。

Claims (8)

1.一种真丝织物的无盐染色工艺,其特征在于:包括以下步骤: (1)前处理:对真丝织物进行前处理,具体为:用尿素1-1.5g/L,无磷除油剂4.5-5.5g/L,十二烷基苯磺酸钠1-1.5 g/L,60%双氧水2-3 g/L,氧化退浆剂OS 0.8-1.2 g/L,在30°C水浴中处理2-3 min,浴比为20: 1,水浴然后升温,升温速度为2.5°C /min,当温度升至90°C后,在此温度下保持30-40min,然后水浴温度以1.5°C /min的速度降温,当温度降至60°C时,将处理后的废水排出,然后重新注入清水在室温下冲洗至洗液为中性,最后晾干; (2)预定型:对真丝织物通过预定型机作预定型处理,预定型过程中定型温度为160-170°C,车速为 20-30m/min,超喂 5-10% ; (3)改性处理:将定型后的真丝织物浸入到含有阳离子活性改性剂的改性液中进行改性处理,具体为使用的改性液为:改性剂3-8% (owf),碳酸钠3-9 g/L,浴比50:1,在50-70°C的水浴中浸泡处理30-60 min,然后水洗,最后在100°C烘干即可; (4)染色:将改性处理后的真丝织物进行染色处理,具体为:室温下将纤维织物浸入染色机的清水中,然后向水浴中加入渗透剂1.5-2.5g/L,扩散剂DN 0.8-1.2g/L,硫酸钠6_8g/L,活性染料2-3% (owf),壳聚糖3-4% (owf ),浴比50:1,并通过pH缓冲剂醋酸-醋酸钠将染液的PH值调节为4-5,循环加料化料20min,然后染色机升温,升温速度为1°C /min,温度升至55-65°C时,保温染色40-60min,然后染色机降温,降温速度为2°C /min,当温度降至30°C时,将染料水排出并重新注入清水,用清水冲洗15min ; (5)皂洗:将染色后的真丝织物经过室温清水冲洗1min后,再用低温皂洗剂lg/L,浴比为20:1,在60-70 °C下冲洗15 min,最后再用40-50 °C的清水冲洗15min ; (6)固色:将清洗后的真丝织物放入固色液中进行固色,所述固色液含有食盐3-5g/L,固色剂2-4g/L,50%的冰醋酸lg/L,浴比为20:1,固色温度60-70 °C,固色时间为30-40min,然后温度降低,40-50°C用清水冲洗15min,然后通过烘干机在80°C预烘4 min,然后在110 °C焙烘3 min ; (7)后整理:将真丝织物放入柔软处理液中进行柔软处理,分两步进行,具体为: (a)用含有纤维素酶2% (owf),通过pH缓冲剂醋酸-醋酸钠将pH值调节为4.8-5时,浴比为20:1的处理液中进行处理,温度为45-55°C,反应20-30min,然后水洗; (b)经过步骤a后,再将真丝织物放入防紫外线处理液中进行处理,用防紫外整理剂UV-BS 3-4 g/L,在 30-40°C的水浴中处理 20-30 1^11,浴比为20:1; (c)经过步骤b后,再将真丝织物放入混合处理液中进行处理,用柔软剂1-2 g/L,抗菌整理剂1-2 g/L,防缩防皱整理剂GFR-8 0.8-1.2 g/L,在30-40°C的水浴中处理20-30min,浴比为20:1 ; (8)烘干:将柔软处理后的真丝织物放入烘干机中进行烘干处理,烘干温度100-110 °C,机车速为 65-70m/min ; (9)定型:将烘干的真丝织物放入定型机中进行定型处理,定型温度155-165Ό,机车速为 25-30m/min,超喂 5-8% ; (10)轧光:将定型后的真丝织物放入轧光机进行轧光处理,乳光温度115-125°C,机车速为 20-25m/min ; (11)收卷:将真丝织物进行收卷。
2.根据权利要求1所述的真丝织物的无盐染色工艺,其特征在于:所述步骤I中的无磷除油剂为无磷中性去油灵TF-104M。
3.根据权利要求1所述的真丝织物的无盐染色工艺,其特征在于:所述步骤3中的改性剂为阳离子改性剂CY-210。
4.根据权利要求1所述的真丝织物的无盐染色工艺,其特征在于:所述步骤4中的渗透剂为渗透剂JFC。
5.根据权利要求1所述的真丝织物的无盐染色工艺,其特征在于:所述步骤4中的活性染料为活性红L-S、活性黄L-3R、活性艳蓝L-R中的一种。
6.根据权利要求1所述的真丝织物的无盐染色工艺,其特征在于:所述步骤5中的低温皂洗剂为JY-1103D皂洗剂。
7.根据权利要求1所述的真丝织物的无盐染色工艺,其特征在于:所述步骤6中的固色剂为TCD-R。
8.根据权利要求1所述的真丝织物的无盐染色工艺,其特征在于:所述步骤7中的柔软剂为酯基季铵盐柔软剂,抗菌整理剂为抗菌整理剂GQ-1OO。
CN201510154318.XA 2015-04-02 2015-04-02 一种真丝织物的无盐染色工艺 Pending CN104746365A (zh)