CN104928913B - A kind of textile fabric capable of releasing negative ion - Google Patents
A kind of textile fabric capable of releasing negative ion Download PDFInfo
- Publication number
- CN104928913B CN104928913B CN201410103380.1A CN201410103380A CN104928913B CN 104928913 B CN104928913 B CN 104928913B CN 201410103380 A CN201410103380 A CN 201410103380A CN 104928913 B CN104928913 B CN 104928913B
- Authority
- CN
- China
- Prior art keywords
- vermiculite
- textile fabric
- tourmaline
- releasing negative
- negative ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of textile fabric capable of releasing negative ion, coats one layer of vermiculite tourmaline clad by textile fabric outer surface and forms.Preparation process of the present invention is simple, and obtained textile fabric can persistently discharge anion, with its manufactured fabric wallpaper and automobile inside facing, purifies air excellent performance, fire-proof and thermal-insulation, noise reduction sound insulation.
Description
Technical field
It is releasable negative more particularly, to being prepared using vermiculite, tourmaline cladding the present invention relates to a kind of textile
The textile fabric of ion.
Background technology
Textile fabric used in existing fabric wallpaper and automobile inside facing, predominantly silk, hair, cotton, fiber crops etc. are natural
Fiber, they have, and well-pressed, elasticity is good, be not easily broken, be non-aging, is bright in luster, paste it is convenient, and with certain saturating
Gas and moisture resistance, it is wear-resisting, not fugitive color the advantages that.But its constituent is mainly organic matter, itself is simultaneously negative without release
Ion function, and inflammable characteristic greatly limit its use scope.Vermiculite is a kind of natural inorganic material, it has uniqueness
Electronic structure, being capable of lasting releasing negative oxygen ion.The characteristics of vermiculite has fusing point high, easily expansion of being heated, matter is crisp and soft, has
The performances such as well heat-insulated, sound insulation, fire prevention, drainage.Vermiculite is nonpoisonous and tasteless at the same time, and has good environmental protection characteristic.Using leech
Stone cladding prepares textile fabric, capable of purifying air both with negative ion-releasing function, and has flame-retarding characteristic, can improve product
Safety in utilization, has great Practical significance and promotional value.At present, it is domestic releasable negative there has been no being used to prepare on vermiculite
The report of ion textile fabric.
The content of the invention
It is an object of the present invention to overcome the above-mentioned drawbacks of the prior art and provide a kind of capable of releasing negative ion
Textile fabric.
The purpose of the present invention can be achieved through the following technical solutions：A kind of textile fabric capable of releasing negative ion, its
It is characterized in that, coating one layer of vermiculite tourmaline clad by textile fabric outer surface forms.The textile fabric can be made into fabric
Wallpaper or automobile inside.
The vermiculite tourmaline clad is according to volume ratio (55~56) by vermiculite, tourmaline, adhesive: (0.4~
0.5): (100~200) mixed preparing forms slurry layer.
The vermiculite is that vermiculite raw material is placed in puffing furnace in 600-900 DEG C, by the puffing expansion leech formed of 10s
Stone；The particle diameter of the expanded vermiculite is 0.5~4mm.
The particle diameter of the tourmaline is 200~6000 mesh.
The textile fabric include silk, hair, cotton or, fiber crops.
When crushing tourmaline, powder size will control the micro situation within 200-6000 mesh, and fineness exceedes this scope
When it is excessively careful be unfavorable for manufacturing process, and not up to the scope when powder cross conference and lead to not insert the vermiculite layers after expansion
Between influence anion burst size.Expanded vermiculite granularity will be controlled between 0.5-4MM, and particle is too small, influence plate bear from
Son release and the function of adjusting air humidity, particle is too big, can reduce the intensity of plate.
Therefore the key that granularity this details in particular range is technique is controlled in crushing process.
Tourmaline has the function of releasing negative oxygen ion, but the amount of pure tourmaline releasing negative oxygen ion is few, speed is slow, presses
Tourmaline is mixed with expanded vermiculite according to ratio of the present invention, expanded vermiculite is a kind of insulator, and inside there are many micropores, can add up
Electric charge, forms the potential difference of various ranks, and " tourmaline " is a kind of special polarity crystalline solid of structure, has pyroelectricity and piezoelectricity
Property, be subject to vermiculite formed electric field excitation under and the change of ambient temperature under the action of, discharge substantial amounts of anion, bear from
Son forms negative oxygen ion by after the oxygen capture in air.Therefore, expanded vermiculite can improve tourmaline releasing negative oxygen ion
Ability, and because vermiculite has higher layer charge number, therefore there is higher cation exchange capacity and stronger cation
Exchange adsorption ability, can lasting releasing negative oxygen ion.
Compared with prior art, the textile fabric capable of releasing negative ion that the present invention is prepared has the characteristics that：
1. anion can persistently be discharged, improve the environment in indoor and automobile.
2. the pollutants such as purifying formaldehyde, toluene.
3. adjusting air humidity.
4. prevent fires, is heat-insulated.
5. can noise reduction, sound insulation.
Brief description of the drawings
Fig. 1 is textile fabric construction schematic diagram capable of releasing negative ion；
Description of symbols in figure：
1- vermiculite tourmaline clads, 2- textile fabrics.
Embodiment
The present invention is described in detail with specific embodiment below in conjunction with the accompanying drawings.
Embodiment 1
As shown in Figure 1, a kind of textile fabric capable of releasing negative ion, one layer of vermiculite electricity is coated by 2 outer surface of textile fabric
Gas stone clad 1 forms.The textile fabric can be made into fabric wallpaper or automobile inside.
The vermiculite tourmaline clad is to be mixed by vermiculite, tourmaline, adhesive according to volume ratio 55: 0.4: 100
It is formulated slurry layer.
The vermiculite is that vermiculite raw material is placed in puffing furnace in 600 DEG C, by the puffing expanded vermiculites formed of 10s；
The particle diameter of the expanded vermiculite is 0.5mm.The particle diameter of the tourmaline is 200 mesh.
The textile fabric is silk fiber.
Embodiment 2
A kind of textile fabric capable of releasing negative ion, one layer of vermiculite tourmaline clad group is coated by textile fabric outer surface
Into.The textile fabric can be made into fabric wallpaper or automobile inside.
The vermiculite tourmaline clad is to be mixed by vermiculite, tourmaline, adhesive according to volume ratio 56: 0.5: 200
It is formulated slurry layer.
The vermiculite is that vermiculite raw material is placed in puffing furnace in 900 DEG C, by the puffing expanded vermiculites formed of 10s；
The particle diameter of the expanded vermiculite is 4mm.
The particle diameter of the tourmaline is 6000 mesh.
The textile fabric is wool fibre.
Embodiment 3
A kind of textile fabric capable of releasing negative ion, one layer of vermiculite tourmaline clad group is coated by textile fabric outer surface
Into.The textile fabric can be made into fabric wallpaper or automobile inside.
The vermiculite tourmaline clad is according to volume ratio 56: 0.4 by vermiculite, tourmaline, adhesive: 150) is mixed
It is formulated slurry layer.
The vermiculite is that vermiculite raw material is placed in puffing furnace in 800 DEG C, by the puffing expanded vermiculites formed of 10s；
The particle diameter of the expanded vermiculite is 2mm.
The particle diameter of the tourmaline is 2000 mesh.
The textile fabric is flaxen fiber.
Claims (2)
1. a kind of textile fabric capable of releasing negative ion, it is characterised in that it is electric that one layer of vermiculite is coated by textile fabric outer surface
Stone clad forms；The vermiculite tourmaline clad is according to volume ratio by vermiculite, tourmaline, adhesive（55~56）：
（0.4~0.5）：（100~200）Mixed preparing forms slurry layer；The vermiculite be by vermiculite raw material be placed in puffing furnace in
600-900 DEG C, by the puffing expanded vermiculites formed of 10s；The particle diameter of the expanded vermiculite is 0.5 ~ 4mm；Described is electric
The particle diameter of stone is 200 ~ 6000 mesh.
A kind of 2. textile fabric capable of releasing negative ion according to claim 1, it is characterised in that the textile fabric
Including silk, hair, cotton or fiber crops.