CN103692706A - Antistatic sound-absorbing cotton and preparation method thereof - Google Patents
Antistatic sound-absorbing cotton and preparation method thereof Download PDFInfo
- Publication number
- CN103692706A CN103692706A CN201310601447.XA CN201310601447A CN103692706A CN 103692706 A CN103692706 A CN 103692706A CN 201310601447 A CN201310601447 A CN 201310601447A CN 103692706 A CN103692706 A CN 103692706A
- Authority
- CN
- China
- Prior art keywords
- parts
- sound
- powder
- antistatic
- back layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antistatic sound-absorbing cotton. The antistatic sound-absorbing cotton comprises a top layer, a back layer and a cellucotton layer sandwiched between the top layer and the back layer, wherein the top layer and the back layer are made of a non-woven fabric material. The antistatic sound-absorbing cotton is characterized in that the non-woven fabric is prepared from the following raw materials by weight through melt-blowing: 100 parts of isotatic polypropylene, 7 to 9 parts of fatty alcohol-polyoxyethylene ether, 2 to 3 parts of alkyl ethyl ether polysiloxane polysilicone, 2 to 3 parts of aluminum phosphate, 1 to 2 parts of tin oxide, 13 to 16 parts of glycerol triacetate, 1 to 2 parts of magnesium silicate, 1 to 2 parts of nanometer silica, 2 to 3 parts of calcium alginate, 1 to 2 parts of sodium silicate, 20 to 24 parts of twigs, 1 to 2 parts of mint leaves, 2 to 3 parts of licorice, 3 to 4 parts of gynostemma pentaphylla and 4 to 5 parts of an auxiliary agent. According to the invention, a melt-blowing process is used for preparation of the non-woven fabric and has the advantages of easiness, good controllability and high production efficiency; and the prepared sound-absorbing cotton provided by the invention has the advantages of an antistatic property, soft hand feel, smoothness, good surface flatness, strong adsorptivity, a good sound-absorbing effect, etc.
Description
Technical field
The present invention relates to Nonwovens In Technology, be specifically related to a kind of antistatic sound-absorbing cotton and preparation method thereof.
Background technology
Noise directly affects the raising of people's physical and mental health and quality of life, for a long time in noise circumstance, can cause that hearing loss even may bring out some diseases.Will be away from noise, what we can do is exactly sound-absorbing and sound insulation.Acoustical cotton, the high-frequency noises vibrational energy that produces in life can be converted to acoustical cotton inside fine count fiber kinetic energy and lead into heat energy and disappear, reach the function of absorbing sound and lowering noise.
Acoustical cotton can be superimposed with multi-layer nonwoven fabrics, or other material of arranging in pairs or groups, and makes sound-absorbing, acoustic material.Nonwoven is that textile staple or long filament are carried out to orientation or random support row, forms fibre net structure, presents many tiny gaps, this gap can be regarded hole as, has adsorption function, therefore, acoustical cotton can be considered porous material, has good sound-absorbing, heat-insulation warm keeping performance.Acoustical cotton is widely used in the industries such as building, electrical equipment, automobile, machinery as a kind of gasket material, mainly play the effect of sound insulation.But all there is more deficiency in existing acoustical cotton product and manufacture method thereof, main manifestations is: not environmental protection of manufacture craft; Sound-absorbing effect is general; Chemical resistance is low, cannot meet Code in Hazardous Special Locations instructions for use; Temperature resistant grade is low; Do not carry out flame treatment; Product caking ability is inadequate, fugitive, tension intensity is poor; Outward appearance and flatness are inadequate, thickness relatively large deviation etc.
Summary of the invention
Object of the present invention is just to provide a kind of antistatic sound-absorbing cotton and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of antistatic sound-absorbing is cotton, by top coat, back layer, and the cellucotton layer being clipped between top coat and back layer forms, described top coat, back layer adopts nonwoven cloth material, nonwoven described in it is characterized in that is made by meltblown by the raw material of following weight portion: isotactic polypropylene 100, AEO 7-9, alkyl ethylether polysiloxanes silicone 2-3, aluminum phosphate 2-3, tin oxide 1-2, triacetin 13-16, magnesium silicate 1-2, nano silicon 1-2, calcium alginate 2-3, sodium metasilicate 1-2, branch 20-24, dried peppermint leaf 1-2, Radix Glycyrrhizae 2-3, gynostemma pentaphylla 3-4, auxiliary agent 4-5.
Described auxiliary agent is made by following raw materials in part by weight: clay 10-12, nano-sized carbon 1-2, polytetrafluoroethylene powder 3-4, antioxidant NBC 1-2, isopropyl distearyl acyl-oxygen base Aluminate 2-3, zinc dialkyl dithiophosphate 2-3, magnetite 2-3, epoxidized soybean oil 35-40, n-propyl gallate 3-4, coix seed oil 2-3, vanadium diboride 1-2, Tea Polyphenols 2-3; Preparation method sends into clay, magnetite in calcining furnace and calcine 2-3 hour at 720-740 ℃, then, takes out, and sends in the hydrochloric acid solution of 10-15% and soaks 2-3 hour, filters, and obtains filter residue, with clear water, cleans, and dries, grinds to form 400-600 order powder; Gained powder mixes with other residual components, is heated to 60-70 ℃, and stirring reaction 40-50 minute is cooling, grinds to form slurry, obtains.
The preparation method of described a kind of antistatic sound-absorbing cotton, is characterized in that comprising the following steps:
(1), dried peppermint leaf, Radix Glycyrrhizae, gynostemma pentaphylla are merged and pulverize 250-300 order powder, then, to the powder air blast of gained, it is seethed, to spray form triacetin in the powder seething, the two is fully mixed;
(2), branch is sent in retort, at 510-640 ℃, 3-4 hour is processed in charing, takes out, and is ground into powder;
(3), isotactic polypropylene is heated to molten condition, add step (1), (2) material, stir;
(4), in step (3) material, add other residual components, fully stir, mix, by nozzle, spray and thread make nonwoven.
The present invention has following beneficial effect: the present invention adopts meltblown to prepare nonwoven, have that technique is simple, raw material green cheap and easy to get, controllability good, production efficiency is high, and industrializing implementation is strong, can guarantee stable and reliable product quality, the acoustical cotton making has the advantages such as antistatic behaviour, soft, smooth, flat appearance degree is good, the strong sound-absorbing effect of adsorptivity is obvious.
The specific embodiment
Described a kind of antistatic sound-absorbing is cotton, by top coat, back layer, and the cellucotton layer being clipped between top coat and back layer forms, described top coat, back layer adopts nonwoven cloth material, nonwoven described in it is characterized in that is made by meltblown by the raw material of following weight portion: isotactic polypropylene 100, AEO 9, alkyl ethylether polysiloxanes silicone 2, aluminum phosphate 2, tin oxide 2, triacetin 15, magnesium silicate 1, nano silicon 2, calcium alginate 2, sodium metasilicate 1, branch 23, dried peppermint leaf 2, Radix Glycyrrhizae 2, gynostemma pentaphylla 4, auxiliary agent 4.
Described auxiliary agent by following weight portion (kilogram) raw material makes: clay 10, nano-sized carbon 1, polytetrafluoroethylene powder 3, antioxidant NBC 1, isopropyl distearyl acyl-oxygen base Aluminate 2, zinc dialkyl dithiophosphate 2, magnetite 3, epoxidized soybean oil 35, n-propyl gallate 3, coix seed oil 2, vanadium diboride 1, Tea Polyphenols 3; Preparation method sends into clay, magnetite in calcining furnace and calcine 2-3 hour at 720-740 ℃, then, takes out, and sends in the hydrochloric acid solution of 10-15% and soaks 2-3 hour, filters, and obtains filter residue, with clear water, cleans, and dries, grinds to form 400-600 order powder; Gained powder mixes with other residual components, is heated to 60-70 ℃, and stirring reaction 40-50 minute is cooling, grinds to form slurry, obtains.
Preparation method comprises the following steps:
(1), dried peppermint leaf, Radix Glycyrrhizae, gynostemma pentaphylla are merged and pulverize 250-300 order powder, then, to the powder air blast of gained, it is seethed, to spray form triacetin in the powder seething, the two is fully mixed;
(2), branch is sent in retort, at 510-640 ℃, 3-4 hour is processed in charing, takes out, and is ground into powder;
(3), isotactic polypropylene is heated to molten condition, add step (1), (2) material, stir;
(4), in step (3) material, add other residual components, fully stir, mix, by nozzle, spray and thread make nonwoven.
After tested, the distribution of fiber diameters of resulting materials is 1.62-1.79 μ m, and tearing strength is 548N/m, and oxygen index (OI) is 36.5%-51.2%, and noise reduction coefficient is 0.813-0.877.
Claims (2)
1. an antistatic sound-absorbing is cotton, by top coat, back layer, and the cellucotton layer being clipped between top coat and back layer forms, described top coat, back layer adopts nonwoven cloth material, nonwoven described in it is characterized in that is made by meltblown by the raw material of following weight portion: isotactic polypropylene 100, AEO 7-9, alkyl ethylether polysiloxanes silicone 2-3, aluminum phosphate 2-3, tin oxide 1-2, triacetin 13-16, magnesium silicate 1-2, nano silicon 1-2, calcium alginate 2-3, sodium metasilicate 1-2, branch 20-24, dried peppermint leaf 1-2, Radix Glycyrrhizae 2-3, gynostemma pentaphylla 3-4, auxiliary agent 4-5, described auxiliary agent is made by following raw materials in part by weight: clay 10-12, nano-sized carbon 1-2, polytetrafluoroethylene powder 3-4, antioxidant NBC 1-2, isopropyl distearyl acyl-oxygen base Aluminate 2-3, zinc dialkyl dithiophosphate 2-3, magnetite 2-3, epoxidized soybean oil 35-40, n-propyl gallate 3-4, coix seed oil 2-3, vanadium diboride 1-2, Tea Polyphenols 2-3, preparation method sends into clay, magnetite in calcining furnace and calcine 2-3 hour at 720-740 ℃, then, takes out, and sends in the hydrochloric acid solution of 10-15% and soaks 2-3 hour, filters, and obtains filter residue, with clear water, cleans, and dries, grinds to form 400-600 order powder, gained powder mixes with other residual components, is heated to 60-70 ℃, and stirring reaction 40-50 minute is cooling, grinds to form slurry, obtains.
2. the preparation method of a kind of antistatic sound-absorbing cotton according to claim 1, is characterized in that comprising the following steps:
(1), dried peppermint leaf, Radix Glycyrrhizae, gynostemma pentaphylla are merged and pulverize 250-300 order powder, then, to the powder air blast of gained, it is seethed, to spray form triacetin in the powder seething, the two is fully mixed;
(2), branch is sent in retort, at 510-640 ℃, 3-4 hour is processed in charing, takes out, and is ground into powder;
(3), isotactic polypropylene is heated to molten condition, add step (1), (2) material, stir;
(4), in step (3) material, add other residual components, fully stir, mix, by nozzle, spray and thread make nonwoven.