CN103966766A - Anti-static inflaming retarding non-woven fabric material for sound absorbing cotton - Google Patents
Anti-static inflaming retarding non-woven fabric material for sound absorbing cotton Download PDFInfo
- Publication number
- CN103966766A CN103966766A CN201410165054.3A CN201410165054A CN103966766A CN 103966766 A CN103966766 A CN 103966766A CN 201410165054 A CN201410165054 A CN 201410165054A CN 103966766 A CN103966766 A CN 103966766A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven fabric
- fabric material
- polypropylene
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a non-woven fabric material, in particular to an anti-static inflaming retarding non-woven fabric material for sound absorbing cotton. The non-woven fabric material is composed of, by weight, 100 parts of isotatic polypropylene, 12-15 parts of return polypropylene, 1-2 parts of cerium oxide, 2-3 parts of sodium silicate, 12-15 parts of chlorcosane, 2-3 parts of silicon dioxide, 10-12 parts of peach pits, 6-9 parts of activated carbon, 2-3 parts of scutellariabaicalensis, 1-2 parts of liquorice, 1-2 parts of orange peels, 2-3 parts of eclipta and 4-5 parts of additives. The non-woven fabric material comprises the chlorcosane, the silicon dioxide, the activated carbon, Chinese herbal medicine plant fibers and other raw materials, the non-woven fabric material has the good properties of sound absorption, noise reduction, static electricity resistance and inflaming retarding, in addition, the return polypropylene is reused, production cost is lowered, and resource waste is avoided. After a plurality of layers of non-woven fabric materials are stacked, the sound absorbing cotton can be made, the process is simple, and the application prospect is wide.
Description
Technical field
The present invention relates to a kind of acoustical cotton, be specifically related to a kind of acoustical cotton anti-static flame-retardant non-woven material.
Background technology
Nonwoven fabric is environment-friendly materials of new generation, have moistureproof ventilative, light weight is pliable and tough, not combustion-supporting, the characteristic such as nontoxic, and manufacturing technique is relatively simple, its range of application is more and more wider, has using value using nonwoven fabric as sound-absorbing material, it is poor that it can improve traditional sound-absorbing material feature of environmental protection, cause a disease carcinogenic, inflammable, water imbibition is poor, the problems such as service life is short, all start to greatly develop nonwoven fabric sound-absorbing material at home and abroad, but existing nonwoven fabric sound-absorbing material exists composition single, only use chemical fibre material or natural fiber material, its environment for use is restricted, therefore be necessary to improve original formula of non-woven cloth, pass through multiple fiber doping with it, prepare the sound-absorbing nonwoven fabric of high comprehensive performance, required fully to meet consumer's daily life.
Summary of the invention
The object of the invention is to, for the deficiency of current material, provide a kind of acoustical cotton anti-static flame-retardant non-woven material, to achieve these goals, the technical solution used in the present invention is as follows:
A kind of acoustical cotton anti-static flame-retardant non-woven material, it is characterized in that, this material is made up of the raw material of following weight portion: isotactic polypropylene 100, feed back polypropylene 12-15, cerium oxide 1-2, sodium metasilicate 2-3, chlorinated paraffin wax 12-15, silica 2-3, peach-pit shell 10-12, active carbon 6-9, root of large-flowered skullcap 2-3, Radix Glycyrrhizae 1-2, tangerine peel 1-2, eclipta 2-3, auxiliary agent 4-5;
Described auxiliary agent is made up of the raw material of following weight portion: nano-sized carbon 1-2, kaolin 8-10, nano diatomite 1-2, polytetrafluoroethylene powder 3-4, titanate coupling agent TMC-TTS 3-4, tetra isopropyl two (dioctyl phosphorous acid acyloxy) titanate esters 2-3, jade powder 1-2, Diethylene Glycol Dibenzoate 3-4, n-propyl gallate 1-2, coix seed oil 1-2, vanadium diboride 2-3; Its special Preparation Method is that kaolin is placed in calcining furnace and at 700-730 DEG C, is calcined after 3-4 hour, pulverizes, and mixes with other leftover materials, grinds 1-2 hour, to obtain final product.
Described a kind of acoustical cotton anti-static flame-retardant non-woven material, is characterized in that, nonwoven cloth material is made by following step:
(1) root of large-flowered skullcap, Radix Glycyrrhizae, tangerine peel, eclipta mixed and pulverize as 200-250 order powder, for subsequent use;
(2) walnut shell is sent in retort, at 530-620 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder;
(3) isotactic polypropylene, feed back polypropylene are heated to molten condition, add step (1), (2) material, stir;
(4) in step (3) material, add other residual components, fully stir, mix, spray silk by nozzle and make nonwoven fabric.
Beneficial effect of the present invention is, in isotactic polypropylene, add feed back polypropylene, avoid the wasting of resources, the raw material such as peach-pit shell, active carbon and Chinese herbal medicine after the charing adding, the sound-absorbing soundproof effect of having promoted nonwoven cloth material, the raw materials such as chlorinated paraffin wax, silica have given material good electrical insulating property, make its antistatic and safety fire-retardant, acoustical cotton prepared by this nonwoven cloth material group, has broad application prospects.
Detailed description of the invention
Embodiment
A kind of acoustical cotton anti-static flame-retardant non-woven material, described nonwoven fabric is made up of the raw material of following weight portion: isotactic polypropylene 100, feed back polypropylene 12-15, cerium oxide 1-2, sodium metasilicate 2-3, chlorinated paraffin wax 12-15, silica 2-3, peach-pit shell 10-12, active carbon 6-9, root of large-flowered skullcap 2-3, Radix Glycyrrhizae 1-2, tangerine peel 1-2, eclipta 2-3, auxiliary agent 4-5;
Above-mentioned auxiliary agent is made up of the raw material of following weight portion: nano-sized carbon 1, kaolin 8, nano diatomite 2, polytetrafluoroethylene powder 3, titanate coupling agent TMC-TTS 3, tetra isopropyl two (dioctyl phosphorous acid acyloxy) titanate esters 3, jade powder 1, Diethylene Glycol Dibenzoate 4, n-propyl gallate 2, coix seed oil 2, vanadium diboride 2; Its special Preparation Method is that kaolin is placed in calcining furnace and at 700-730 DEG C, is calcined after 3-4 hour, pulverizes, and mixes with other leftover materials, grinds 1-2 hour, to obtain final product.
A kind of acoustical cotton anti-static flame-retardant non-woven material, this material is made by following technique:
(1) root of large-flowered skullcap, Radix Glycyrrhizae, tangerine peel, eclipta mixed and pulverize and be 250 order powder, for subsequent use;
(2) walnut shell is sent in retort, at 530-620 DEG C, charing is processed 4 hours, takes out, and is ground into powder;
(3) isotactic polypropylene, feed back polypropylene are heated to molten condition, add step (1), (2) material, stir;
(4) in step (3) material, add other residual components, fully stir, mix, spray silk by nozzle and make nonwoven fabric.
After nonwoven cloth material multiple-layer stacked of the present invention, can make acoustical cotton, the comprehensive Noise Reduction coefficient (NRC) of the thick nonwoven fabric acoustical cotton of 5cm: 0.85, oxygen index (OI): 27%, hygroscopicity :≤5%, the resistivity of surface unit area is: 1.25 × 10
12.
Claims (2)
1. an acoustical cotton anti-static flame-retardant non-woven material, it is characterized in that, this material is made up of the raw material of following weight portion: isotactic polypropylene 100, feed back polypropylene 12-15, cerium oxide 1-2, sodium metasilicate 2-3, chlorinated paraffin wax 12-15, silica 2-3, peach-pit shell 10-12, active carbon 6-9, root of large-flowered skullcap 2-3, Radix Glycyrrhizae 1-2, tangerine peel 1-2, eclipta 2-3, auxiliary agent 4-5;
Described auxiliary agent is made up of the raw material of following weight portion: nano-sized carbon 1-2, kaolin 8-10, nano diatomite 1-2, polytetrafluoroethylene powder 3-4, titanate coupling agent TMC-TTS 3-4, tetra isopropyl two (dioctyl phosphorous acid acyloxy) titanate esters 2-3, jade powder 1-2, Diethylene Glycol Dibenzoate 3-4, n-propyl gallate 1-2, coix seed oil 1-2, vanadium diboride 2-3; Its special Preparation Method is that kaolin is placed in calcining furnace and at 700-730 DEG C, is calcined after 3-4 hour, pulverizes, and mixes with other leftover materials, grinds 1-2 hour, to obtain final product.
2. a kind of acoustical cotton anti-static flame-retardant non-woven material as claimed in claim 1, is characterized in that, described nonwoven cloth material is made by following technique:
(1) root of large-flowered skullcap, Radix Glycyrrhizae, tangerine peel, eclipta mixed and pulverize as 200-250 order powder, for subsequent use;
(2) walnut shell is sent in retort, at 530-620 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder;
(3) isotactic polypropylene, feed back polypropylene are heated to molten condition, add step (1), (2) material, stir;
(4) in step (3) material, add other residual components, fully stir, mix, spray silk by nozzle and make nonwoven fabric.