CN106555273A - A kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material - Google Patents
A kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material Download PDFInfo
- Publication number
- CN106555273A CN106555273A CN201510623050.XA CN201510623050A CN106555273A CN 106555273 A CN106555273 A CN 106555273A CN 201510623050 A CN201510623050 A CN 201510623050A CN 106555273 A CN106555273 A CN 106555273A
- Authority
- CN
- China
- Prior art keywords
- nonwoven cloth
- acoustical cotton
- cloth material
- root
- heat insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material, the nonwoven cloth material is prepared by the raw materials in：Isotactic polypropylene 100, nano silicon 2-3, hollow glass micro-ball 1-2, rutile type titanium white 1-2, smoke sheet rubber 7-9, dimethyl fumarate 12-15, calcium stearate 2-3, zeolite 6-9, diatomite 3-4, activated carbon 8-10, wolf's milk 2-3, root of large-flowered skullcap 1-2, root of kudzu vine 1-2, auxiliary agent 4-5.A kind of acoustical cotton described in the invention with Wear-resistant heat insulation nonwoven cloth material containing the raw material such as nano silicon, hollow glass micro-ball, enhance the mechanical property of material, make its flexible wear-resisting, stretch-proof impact, thermal-isulation ventilation, the raw materials such as zeolite, diatomite, activated carbon and Chinese herbal medicine fiber, increased the absorbing sound and lowering noise effect of material, can be prepared by acoustical cotton after non-woven fabrics multiple-layer stacked of the present invention, process is simple, range of application are wide.
Description
Technical field
The invention belongs to nonwoven cloth material field, more particularly, to a kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material.
Background technology
Non-woven fabrics is the environment-friendly materials of a new generation, with moistureproof ventilative, light weight is flexible, it is not combustion-supporting, the characteristic such as nontoxic, and manufacturing process is relatively easy, its range of application is more and more wider, using non-woven fabrics as the great using value of sound-absorbing material, it is poor that it can improve traditional sound-absorbing material feature of environmental protection, cause a disease carcinogenic, it is inflammable, water imbibition is poor, the problems such as service life is short, at home and abroad all start to greatly develop non-woven fabrics sound-absorbing material, but existing non-woven fabrics sound-absorbing material to there is composition single, chemical fibre material or natural fiber material are used only, it is restricted its use environment, it is therefore desirable to improving original formula of non-woven cloth, adulterated by multiple fiber with which, prepare the sound-absorbing non-woven fabrics of high comprehensive performance, fully to meet needed for consumer's daily life.
The content of the invention
In view of this, it is contemplated that proposing a kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material, to improve the mechanical performance of non-woven fabrics.
To reach above-mentioned purpose, what the technical scheme of the invention was realized in：
A kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material, the material are prepared by the raw materials in：Isotactic polypropylene 100, nano silicon 2-3, hollow glass micro-ball 1-2, rutile type titanium white 1-2, smoke sheet rubber 7-9, dimethyl fumarate 12-15, calcium stearate 2-3, zeolite 6-9, diatomite 3-4, activated carbon 8-10, wolf's milk 2-3, root of large-flowered skullcap 1-2, root of kudzu vine 1-2, auxiliary agent 4-5；Described auxiliary agent is made up of the raw material of following weight portion：Nano-sized carbon 1-2, kaolin 8-10, nano diatomite 1-2, polytetrafluoroethylene powder 3-4, titanate coupling agent TMC-TTS 3-4, tetra isopropyl two (dioctyl phosphito acyloxy) titanate esters 2-3, jade powder 1-2, Diethylene Glycol Dibenzoate 3-4, propylgallate 1-2, coix seed oil 1-2, vanadium diboride 2-3；Its special Preparation Method is that kaolin is placed in calcining furnace to calcine at 700-730 DEG C after 3-4 hours, crushes, mixes with other leftover materials, grinds 1-2 hours, obtain final product.
Described a kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material, it is characterised in that nonwoven cloth material is obtained by below step：
(1) wolf's milk, the root of large-flowered skullcap, the root of kudzu vine are mixed and are crushed for 200-250 mesh powder, it is standby；
(2) zeolite, diatomite are put into in calcining furnace the calcining 3-4 hours at 710-740 DEG C, after taking out cooling, are ground into the powder of 300-400 mesh；
(3) isotactic polypropylene is heated to into molten condition, adds step (1), (2) material, stir；
(4) other residual components are added in step (3) material, is sufficiently stirred for, is well mixed, non-woven fabrics is made by nozzle spinneret.
Relative to prior art, a kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material described in the invention has the advantage that：
A kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material of the present invention with the addition of the raw materials such as nano silicon, hollow glass micro-ball in isotactic polypropylene, enhance the mechanical property of material so as to flexible wear-resisting, stretch-proof impact, thermal-isulation ventilation；The raw materials such as zeolite, diatomite, activated carbon and Chinese herbal medicine fiber, increased the absorbing sound and lowering noise effect of material, and acoustical cotton prepared by non-woven fabrics of the present invention, safety and environmental protection, sound-absorbing soundproof effect are excellent, great using value.
Specific embodiment
It should be noted that in the case where not conflicting, the embodiment and the feature in embodiment in the present invention can be mutually combined.
A kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material, described non-woven fabrics are prepared by the raw materials in：Isotactic polypropylene 100, nano silicon 3, hollow glass micro-ball 2, rutile type titanium white 2, smoke sheet rubber 9, dimethyl fumarate 15, calcium stearate 3, zeolite 9, diatomite 4, activated carbon 10, wolf's milk 3, the root of large-flowered skullcap 2, the root of kudzu vine 2, auxiliary agent 5；Above-mentioned auxiliary agent is made up of the raw material of following weight portion：Nano-sized carbon 1, kaolin 8, nano diatomite 2, polytetrafluoroethylene powder 3, titanate coupling agent TMC-TTS 3, tetra isopropyl two (dioctyl phosphito acyloxy) titanate esters 3, jade powder 1, Diethylene Glycol Dibenzoate 4, propylgallate 2, coix seed oil 2, vanadium diboride 2；Its special Preparation Method is that kaolin is placed in calcining furnace to calcine at 700-730 DEG C after 3-4 hours, crushes, mixes with other leftover materials, grinds 1-2 hours, obtain final product.
A kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material, the material are obtained by following technique：
(1) wolf's milk, the root of large-flowered skullcap, the root of kudzu vine are mixed and are crushed for 250 mesh powder, it is standby；
(2) zeolite, diatomite are put in calcining furnace and are calcined 4 hours at 710-740 DEG C, after taking out cooling, be ground into the powder of 400 mesh；
(3) isotactic polypropylene is heated to into molten condition, adds step (1), (2) material, stir；
(4) other residual components are added in step (3) material, is sufficiently stirred for, is well mixed, non-woven fabrics is made by nozzle spinneret.
After nonwoven cloth material multiple-layer stacked of the present invention, you can acoustical cotton, the comprehensive Noise Reduction coefficient (NRC) of 5cm thickness non-woven fabrics acoustical cottons is obtained：0.87, oxygen index (OI)：25%, thermal conductivity factor (W/m.k)：0.036, hygroscopicity：≤ 5%.
Presently preferred embodiments of the present invention is the foregoing is only, not to limit the present invention, all any modification, equivalent substitution and improvements within the spirit and principles in the present invention, made etc., be should be included within the scope of the present invention.
Claims (2)
1. a kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material, it is characterised in that:The material is by following weight portion
Raw material make：Isotactic polypropylene 100, nano silicon 2-3, hollow glass micro-ball 1-2, golden red
Stone-type titanium dioxide 1-2, smoke sheet rubber 7-9, dimethyl fumarate 12-15, calcium stearate 2-3, zeolite 6-9,
Diatomite 3-4, activated carbon 8-10, wolf's milk 2-3, root of large-flowered skullcap 1-2, root of kudzu vine 1-2, auxiliary agent 4-5；It is described
Auxiliary agent be made up of the raw material of following weight portion：Nano-sized carbon 1-2, kaolin 8-10, nano diatomite 1-2,
Polytetrafluoroethylene powder 3-4, titanate coupling agent TMC-TTS 3-4, two (dioctyl phosphito of tetra isopropyl
Acyloxy) titanate esters 2-3, jade powder 1-2, Diethylene Glycol Dibenzoate 3-4, gallic acid
Propyl ester 1-2, coix seed oil 1-2, vanadium diboride 2-3；Its special Preparation Method is that kaolin is placed in calcining furnace
After 3-4 hours are calcined at 700-730 DEG C, crush, mix with other leftover materials, 1-2 is little for grinding
When, obtain final product.
2. a kind of acoustical cotton Wear-resistant heat insulation nonwoven cloth material according to claim 1, it is characterised in that：
Described nonwoven cloth material is obtained by following technique：
(1) wolf's milk, the root of large-flowered skullcap, the root of kudzu vine are mixed and are crushed for 200-250 mesh powder, it is standby；
(2) zeolite, diatomite are put into in calcining furnace the calcining 3-4 hours at 710-740 DEG C, take out cooling
Afterwards, it is ground into the powder of 300-400 mesh；
(3) isotactic polypropylene is heated to into molten condition, adds step (1), (2) material, fully stir
Mix uniform；
(4) other residual components are added in step (3) material, is sufficiently stirred for, is well mixed, by spray
Mouth spinneret makes non-woven fabrics.