CN104927585A - 喷绘广告用发光漆 - Google Patents

喷绘广告用发光漆 Download PDF

Info

Publication number
CN104927585A
CN104927585A CN201510408181.6A CN201510408181A CN104927585A CN 104927585 A CN104927585 A CN 104927585A CN 201510408181 A CN201510408181 A CN 201510408181A CN 104927585 A CN104927585 A CN 104927585A
Authority
CN
China
Prior art keywords
luminous paint
jet
parts
printed advertisements
advertisements
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510408181.6A
Other languages
English (en)
Other versions
CN104927585B (zh
Inventor
张曙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Jinfans Intelligent Marking Co., Ltd.
Original Assignee
Shanghai G-Face Signage Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai G-Face Signage Co Ltd filed Critical Shanghai G-Face Signage Co Ltd
Priority to CN201510408181.6A priority Critical patent/CN104927585B/zh
Publication of CN104927585A publication Critical patent/CN104927585A/zh
Application granted granted Critical
Publication of CN104927585B publication Critical patent/CN104927585B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种喷绘广告用发光漆。所述喷绘广告用发光漆，包括下述重量份的组分：环氧树脂10-30份，过氯乙烯树脂10-30份，甲苯二异氰酸酯5-8份，高岭土4-8份，发光粉2-10份，钛白粉1-3份，纳米二氧化硅0.4-1份，正硅酸丁酯4-8份，成膜助剂0.5-3份，抗污除菌剂0.2-2份，溶剂15-35份。本发明的喷绘广告用发光漆，具有良好的抗污防腐蚀效果，尤其具有抗菌效果，形成的漆膜有良好的耐冲击性。

Description

喷绘广告用发光漆
技术领域
本发明涉及一种涂料，具体涉及一种喷绘广告用发光漆。
背景技术
发光漆是指能发出荧光、磷光或反光的漆。分为反光、磷光、荧光漆三种。反光漆由玻璃细珠配在清漆中，涂刷在铝粉底漆上而成；磷光漆由磷光颜料加漆料制成；荧光漆是由荧光颜料加漆料制成。常用于道路标志、安全信号、广告牌、路牌及夜光钟表等。
在《涂料工艺》一书是这样定义涂料的：“涂料是一种材料，这种材料可以用不同的施工工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。”属于有机化工高分子材料，所形成的涂膜属于高分子化合物类型。按照现代通行的化工产品的分类，涂料属于精细化工产品。现代的涂料正在逐步成为一类多功能性的工程材料，是化学工业中的一个重要行业。
喷绘广告，其富有创意的画面和文字给人以视觉上的享受，成为一道亮丽的风景线。但是，到了夜间，要使喷绘广告能被人们看清，就必须在其周围增设照明设备。因此，迫切需要能够提供一种喷绘广告用发光漆，能够克服上述弊病。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题是提供一种喷绘广告用发光漆。
本发明目的是通过如下技术方案实现的：
一种喷绘广告用发光漆，包括下述重量份的组分：
优选的，所述抗污除菌剂为吡啶硫酮锌、(反式)8-甲基-N-香草基-6-壬烯酰胺和甲基壬基甲酮中的一种或几种的混合物。
进一步优选的，所述抗抗污除菌剂由下述重量份的组分组成：
吡啶硫酮锌                      15-30份，
(反式)8-甲基-N-香草基-6-壬烯酰胺10-30份，
甲基壬基甲酮                    20-40份。
所述溶剂优选为丙酮、丙醇或乙酸乙酯。
所述成膜助剂优选为环己基-1,4-二甲醇单乙烯基醚、丙二醇苯醚或二者的混合物，进一步优选为环己基-1,4-二甲醇单乙烯基醚与丙二醇苯醚重量比1:2-2:1的混合物。
本发明中，
过氯乙烯树脂，是聚氯乙烯进一步氯化的产物。相对密度(20℃)为1.6g/cm3，含氯量为61％-65％，济南市嘉鸿化工有限公司、江苏苏州毅琳化工等公司均有生产。聚氯乙烯树脂在溶剂存在下经氯气氯化而制得，具有优良的溶介特性，良好的电绝缘性、热塑性和成膜性，化学性能极为稳定，耐腐蚀，耐水，不易燃烧，能溶于酮、氯代烃、芳烃、酯及部分醇类。是较好的成膜剂。
环氧树脂，优选为双酚A型环氧树脂，即二酚基丙烷环氧树脂，由双酚A和环氧氯丙烷制得。
环己基-1,4-二甲醇单乙烯基醚，CAS号：114651-37-5。
丙二醇苯醚，CAS号：41593-38-8。
吡啶硫酮锌，CAS号：13463-41-7。
(反式)8-甲基-N-香草基-6-壬烯酰胺，CAS号：219-484-1。
甲基壬基甲酮，CAS号：112-12-9。
正硅酸丁酯，CAS号：4766-57-8。
甲苯二异氰酸酯，CAS号：584-84-9。
高岭土，CAS号：52624-41-6。
钛白粉，优选为金红石型。
所述发光粉为市售产品，优选为YVO4：Eu发光粉，可以制备或购买得到，在王娟等的《稀土金属YVO4：Eu制备方法和性能研究》(《热加工工艺》2009年第38卷第14期)中1.1.1记载了多孔YVO4：Eu发光粉的制备，1.1.2记载了球状YVO4：Eu发光粉的制备。本发明优选为多孔YVO4：Eu发光粉。
本发明还提供了所述的喷绘广告用发光漆的制备方法，其包括以下步骤：
(1)按配比称取高岭土、钛白粉、发光粉和纳米二氧化硅，混合均匀后得到混合粉末；
(2)按配比称取环氧树脂和过氯乙烯树脂，加入溶剂后，搅拌均匀，再向其中加入步骤(1)得到的混合粉末；
(3)向步骤(2)得到的混合物中依次加入甲苯二异氰酸酯、正硅酸丁酯、抗污除菌剂、成膜助剂，搅拌均匀。
发明人通过大量实验发现，本发明的广告用发光漆具有良好的发光效果、抗污防腐蚀效果，尤其具有抗菌效果，形成的漆膜有良好的耐冲击性。
在研究中还发现，本发明中使用吡啶硫酮锌、(反式)8-甲基-N-香草基-6-壬烯酰胺和甲基壬基甲酮复配的抗污除菌剂，具有更好的抗污除菌效果，几种组分之间具有协同增效作用。另外，当同时使用环己基-1,4-二甲醇单乙烯基醚、丙二醇苯醚作为成膜助剂时，形成的漆膜的耐冲击性更理想，发光的余辉时间更长。
具体实施方式
下面结合实施例对本发明作进一步描述。
实施例中所述喷绘广告用发光漆的制备方法，均按照以下步骤进行：
(1)按配比称取高岭土、钛白粉、发光粉和纳米二氧化硅，混合均匀后得到混合粉末；
(2)按配比称取环氧树脂和过氯乙烯树脂，加入溶剂后，搅拌均匀，再向其中加入步骤(1)得到的混合粉末；
(3)向步骤(2)得到的混合物中依次加入甲苯二异氰酸酯、正硅酸丁酯、抗污除菌剂、成膜助剂，搅拌均匀。
实施例1
按照表1中对应的实施例1数据称取各组分，按照前述方法得到实施例1的喷绘广告用发光漆。
表1：实施例1-6的喷绘广告用发光漆配方表单位：公斤
实施例2
按照表1中对应的实施例2数据称取各组分，按照实施例1所述方法，获得实施例2的喷绘广告用发光漆。
实施例3
按照表1中对应的实施例3数据称取各组分，按照实施例1所述方法，获得实施例3的喷绘广告用发光漆。
实施例4
按照表1中对应的实施例4数据称取各组分，按照实施例1所述方法，获得实施例4的喷绘广告用发光漆。
实施例5
按照表1中对应的实施例5数据称取各组分，按照实施例1所述方法，获得实施例5的喷绘广告用发光漆。
实施例6
按照表1中对应的实施例6数据称取各组分，按照实施例1所述方法，获得实施例6的喷绘广告用发光漆。
测试例1
使用实施例1-6的喷绘广告用发光漆对合金板材进行喷绘制备广告牌，实施例1-6的喷绘方法、喷绘面积和厚度均相同，喷绘后的广告牌吸收12h日光后，置于黑暗无光处进行释放，发光波长大约在620nm波长处，测试10min内发光的亮度以及余辉时间，余辉时间是指亮度大于0.32mcd/m2(人眼最小分辨率)的时间，测试结果见表2。
表2：实施例1-6的发光测试结果
10min内亮度(mcd/m2) 余辉时间(min)
实施例1 820 547
实施例2 812 534
实施例3 809 519
实施例4 817 545
实施例5 896 606
实施例6 824 550
由表2数据可见，使用本发明的喷绘广告用发光漆，余辉时间长，10min内亮度高，尤其是实施例5与实施例1和6相比较，同时使用环己基-1,4-二甲醇单乙烯基醚、丙二醇苯醚作为成膜助剂时，形成的漆膜的发光效果更好。
分别对实施例1-6的喷绘广告用发光漆以及相应制得的广告牌的进行性能测试，喷绘后产生的漆膜厚度为1μm左右，测试标准及测试结果见表3。
表3：实施例1-6的性能测试表
注：
①耐酸性测定方法：5％NaCl溶液中，加入冰醋酸，调节pH至3.1-3.3，每天喷两次，每次10min，44天后测试；
②耐污染性测试方法：在试验片表面涂布マジツクインキ(注册商标)(红和黑)，放置24小时，用含浸了乙醇的布擦拭后，通过目测对外观进行评价：1级：完全没有油墨残留；2级：有少许油墨残留；3级：有较多油墨残留
③抗菌性测试方法：置于环境温度55℃、相对湿度85％环境下，持续观察。
表3结果显示，实施例1-6制得的喷绘广告用发光漆，具有良好的发光效果，抗污防腐蚀效果，尤其具有抗菌效果，形成的漆膜有良好的耐冲击性。
实施例1与实施例2-4相比较，使用了吡啶硫酮锌、(反式)8-甲基-N-香草基-6-壬烯酰胺和甲基壬基甲酮复配的抗污除菌剂，具有更好的抗污除菌效果，几种组分之间具有协同增效作用，在总量相同的情况下，比使用其中任意两组的组合效果更佳。
另外，实施例5与实施例1和6相比较，同时使用环己基-1,4-二甲醇单乙烯基醚、丙二醇苯醚作为成膜助剂时，表干时间最短，形成的漆膜的耐冲击性更理想，发光的余辉时间最长，抗腐蚀效果也更好。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。

Claims (7)

1.一种喷绘广告用发光漆，其特征在于，包括下述重量份的组分：
2.如权利要求1所述的喷绘广告用发光漆，其特征在于，所述成膜助剂为环己基-1,4-二甲醇单乙烯基醚、丙二醇苯醚或二者的混合物。
3.如权利要求2所述的喷绘广告用发光漆，其特征在于，所述成膜助剂为环己基-1,4-二甲醇单乙烯基醚与丙二醇苯醚重量比1:2-2:1的混合物。
4.如权利要求1所述的喷绘广告用发光漆，其特征在于，所述抗污除菌剂为吡啶硫酮锌、(反式)8-甲基-N-香草基-6-壬烯酰胺和甲基壬基甲酮中的一种或几种的混合物。
5.如权利要求4所述的喷绘广告用发光漆，其特征在于，所述抗污除菌剂由下述重量份的组分组成：
吡啶硫酮锌                        15-30份，
(反式)8-甲基-N-香草基-6-壬烯酰胺  10-30份，
甲基壬基甲酮                      20-40份。
6.如权利要求1-5中任一项所述的喷绘广告用发光漆，其特征在于，所述溶剂为丙酮、丙醇或乙酸乙酯。
7.权利要求1-6中任一项所述的喷绘广告用发光漆的制备方法，其特征在于，包括以下步骤：
(1)按配比称取高岭土、钛白粉、发光粉和纳米二氧化硅，混合均匀后得到混合粉末；
(2)按配比称取环氧树脂和过氯乙烯树脂，加入溶剂后，搅拌均匀，再向其中加入步骤(1)得到的混合粉末；
(3)向步骤(2)得到的混合物中依次加入甲苯二异氰酸酯、正硅酸丁酯、抗污除菌剂、成膜助剂，搅拌均匀。
CN201510408181.6A 2015-07-13 2015-07-13 喷绘广告用发光漆 Active CN104927585B (zh)